固溶后冷却方式对Inconel X-750合金组织和性能的影响

doi:10.13251/j.issn.0254-6051.2020.01.021

摘要/Abstract

摘要： 采用SEM、TEM、EDAX和相分析等分析手段,研究Inconel X-750合金固溶后不同冷却方式下组织和性能的变化。结果显示:水冷和油冷抑制合金中γ′相的析出,时效后均析出球形的γ′相。炉冷后合金中析出一次立方体形γ′相和二次球形γ′相,时效后再次析出球形γ′相;水冷和油冷后晶界上无碳化物析出,时效后晶界上均析出细小针状M₂₃C₆。炉冷后合金晶界上析出块状M₂₃C₆,时效后碳化物尺寸略微长大,形状基本不变;炉冷+时效后合金的强度最高,水冷+时效后合金的冲击性能最好。

关键词: 镍基高温合金, 固溶冷却方式, γ′相, 碳化物, 性能

Abstract: SEM, TEM, EDAX and phase analysis were used to study the changes of microstructure and properties of Inconel X-750 alloy after solid solution with different cooling mode. The results show that the water cooling and oil cooling inhibit γ′ precipitation, however spherical γ′ is precipitated after aging. After the furnace cooling, a cubic γ′ and a secondary spherical γ′ are precipitated in the alloy, and the spherical γ′ is precipitated again after aging. There is no carbide precipitation on the grain boundary after water cooling and oil cooling, fine needle-like M ₂₃ C ₆ precipitates on the grain boundary after aging. The block M ₂₃ C ₆ precipitates on the grain boundary of the alloy after furnace cooling. The carbide size grows slightly and the shape is basically unchanged after aging; the strength of the alloy is the highest after furnace cooling+aging, and the impact property of the alloy is the best after water cooling+aging.

Key words: Ni-based superalloy, solution cooling mode, γ′ phase, carbide, properties

中图分类号:

TG156

张亚辉, 王立民, 胡日. 固溶后冷却方式对Inconel X-750合金组织和性能的影响[J]. 金属热处理, 2020, 45(1): 105-111.

Zhang Yahui, Wang Limin, Hu Ri. Effect of cooling mode on microstructure and properties of solution treated Inconel X-750 alloy[J]. HTM, 2020, 45(1): 105-111.

参考文献

[1]Ha J W, Seong B S, Jeong H W, et al. Effects of the aging temperature and stress relaxation conditions on γ′ precipitation in Inconel X-750[J]. Journal of Nuclear Materials, 2015, 457: 362-368.
[2]Marsh C, Depinoy S, Kaoumi D. Effect of heat treatment on the temperature dependence of the fracture behavior of X-750 alloy[J]. Materials Science and Engineering A, 2016, 677: 474-484.
[3]Hwang J Y, Banerjee R, Tiley J, et al. Nanoscale characterization of elemental partitioning between gamma and gamma prime phases in René 88 DT nickel-base superalloy[J]. Metallurgical and Materials Transactions A, 2009, 40(1): 24-35.
[4]Babu S S, Miller M K, Vitek J M, et al. Characterization of the microstructure evolution in a nickel base superalloy during continuous cooling conditions[J]. Acta Materialia, 2001, 49(20): 4149-4160.
[5]Sarosi P M, Wang B, Simmons J P, et al. Formation of multimodal size distributions of γ′ in a nickel-base superalloy during interrupted continuous cooling[J]. Scripta Materialia, 2007, 57(8): 767-770.
[6]Wen Y H, Simmons J P, Shen C, et al. Phase-field modeling of bimodal particle size distributions during continuous cooling[J]. Acta Materialia, 2003, 51(4): 1123-1132.
[7]Wen Y H, Wang B, Simmons J P, et al. A phase-field model for heat treatment applications in Ni-based alloys[J]. Acta Materialia, 2006, 54(8): 2087-2099.
[8]Singh A R P, Nag S, Chattopadhyay S, et al. Mechanisms related to different generations of γ′ precipitation during continuous cooling of a nickel base superalloy[J]. Acta Materialia, 2013, 61(1): 280-293.
[9]Singh A R P, Nag S, Hwang J Y, et al. Influence of cooling rate on the development of multiple generations of γ′ precipitates in a commercial nickel base superalloy[J]. Materials Characterization, 2011, 62(9): 878-886.
[10]Radis R, Schaffer M, Albu M, et al. Multimodal size distributions of γ′ precipitates during continuous cooling of UDIMET 720 Li[J]. Acta Materialia, 2009, 57(19): 5739-5747.
[11]Sarosi P M, Wang B, Simmons J P, et al. Formation of multimodal size distributions of γ′ in a nickel-base superalloy during interrupted continuous cooling[J]. Scripta Materialia, 2007, 57(8): 767-770.
[12]Mitchell R J, Preuss M, Hardy M C, et al. Influence of composition and cooling rate on constrained and unconstrained lattice parameters in advanced polycrystalline nickel—base superalloys[J]. Materials Science and Engineering A, 2006, 423(1/2): 282-291.
[13]Zhao S, Xie X, Smith G D, et al. Microstructural stability and mechanical properties of a new nickel-based superalloy[J]. Materials Science and Engineering A, 2003, 355(1/2): 96-105.
[14]Zhao S, Xie X, Smith G D, et al. Research and improvement on structure stability and corrosion resistance of nickel-base superalloy INCONEL alloy 740[J]. Materials and Design, 2006, 27(10): 1120-1127.
[15]李振江, 肖纳敏, 李殿中, 等. G18CrMo2-6钢回火组织及冲击韧性研究[J]. 金属学报, 2014, 50(7): 777-786.
Li Zhenjiang, Xiao Namin, Li Dianzhong, et al. Influence of microstructure on impact toughness of G18CrMo2-6 steel during tempering[J]. Acta Metallurgical Sinica, 2014, 50(7): 777-786.
[16]Ricker R E, Hall D E, Fink J L. The effect of aqueous environments on the fracture behavior of ductile nickel aluminide[J]. Scripta Metallurgica et Materialia, 1990, 24(2): 291-296.
[17]Grove C A, Petzold L D. Mechanisms of stress-corrosion cracking of alloy X-750 in high-purity water[J]. Journal of Materials for Energy Systems, 1985, 7(2): 147-162.
[18]Valle J A D, Picasso A C, Alvarez I, et al. Age-hardening behavior of Inconel X-750 superalloy[J]. Scripta Materialia, 1999, 41(3): 237-243.
[19]Valle J A D, Romero R, Picasso A C. Bauschinger effect in age-hardened Inconel X-750 alloy[J]. Materials Science and Engineering A, 2001, 311(1/2): 100-107.
[20]赵双群, 董建新, 谢锡善. Ni-Cr-Co基高温合金704 ℃和760 ℃时效组织稳定性[J]. 中国有色金属学报, 2003(3): 565-569.
Zhao Shuangqun, Dong Jianxin, Xie Xishan. Structure stability of Ni-Cr-Co base superalloy aged at 704 ℃ and 760 ℃[J]. The Chinese Journal of Nonferrous Metals, 2003(3): 565-569.
[21]侯介山, 郭建亭, 周兰章, 等. K44镍基高温合金长期时效过程中γ′相粗化对拉伸性能的影响[J]. 金属学报, 2006(5): 481-486.
Hou Jieshan, Guo Jianting, Zhou Lanzhang, et al. Effects of γ＇-precipitate coarsening on tensile properties of Ni base superalloy K44 during long-term aging[J]. Acta Metallurgica Sinica, 2006(5): 481-486.