H13钢表面镀铬和气体渗氮复合处理的组织及性能

doi:10.13251/j.issn.0254-6051.2020.05.002

金属热处理 ›› 2020, Vol. 45 ›› Issue (5): 5-11.DOI: 10.13251/j.issn.0254-6051.2020.05.002

H13钢表面镀铬和气体渗氮复合处理的组织及性能

李春明, 朱伟恒, 焦东玲, 魏兴钊

华南理工大学材料科学与工程学院, 广东广州 510640

收稿日期:2020-02-05 出版日期:2020-05-25 发布日期:2020-09-02
通讯作者: 朱伟恒,硕士,E-mail: zhuwh@scut.edu.cn
作者简介:李春明(1977—),男,硕士,主要研究方向为材料检验分析,E-mail: lichm@scut.edu.cn。
基金资助:
广东省自然科学基金(2016A030313450)

Microstructure and properties of H13 steel treated by chromium plating and gas nitriding

Li Chunming, Zhu Weiheng, Jiao Dongling, Wei Xingzhao

School of Materials Science and Engineering, South China University of Technology, Guangzhou Guangdong 510640, China

Received:2020-02-05 Online:2020-05-25 Published:2020-09-02

摘要/Abstract

摘要： 对调质后的H13钢进行镀铬+540 ℃气体渗氮处理,获得氮化铬表层,然后将其进行耐磨试验,并与同温度经常规气体渗氮及离子渗氮后的H13钢试样进行组织及耐磨性对比。结果表明:3种工艺处理后试样的主要磨损机制为粘着磨损和磨粒磨损,镀铬/渗氮试样表面摩擦因数最低,为0.44,耐磨性最好,但镀铬+渗氮层与基体的结合力最差。

关键词: H13钢, 渗氮, 氮化铬, 耐磨性

Abstract: The chromium nitride was obtained on the quenched and tempered H13 steel substrate by using chromium plating and gas nitriding at 540 ℃. Then the abrasion resistance test was performed and the microstructure and wear resistance of H13 steel specimens after conventional gas nitriding and ion nitriding at the same temperature were compared. The results show that the main wear mechanisms of the specimens after three different heat treatment are adhesion wear and abrasive wear. The chromium plated and gas nitrided specimens show the lowest average friction coefficient, 0.44, and the wear resistance is the best, but the adhesion between the Cr-plated+gas nitriding layer and the substrate is the worst.

Key words: H13 steel, nitriding, chromium nitride, wear resistance

中图分类号:

TG174.444

李春明, 朱伟恒, 焦东玲, 魏兴钊. H13钢表面镀铬和气体渗氮复合处理的组织及性能[J]. 金属热处理, 2020, 45(5): 5-11.

Li Chunming, Zhu Weiheng, Jiao Dongling, Wei Xingzhao. Microstructure and properties of H13 steel treated by chromium plating and gas nitriding[J]. Heat Treatment of Metals, 2020, 45(5): 5-11.

参考文献

[1]Robert R Aharonov, Bernard F Coll, Raymond P Fontana. Properties of chromium nitride coatings deposited by cathodic arc evaporation[J]. Surface and Coatings Technology, 1993, 61(1-3): 223-226.
[2]Kenji Sugiyama, Kazunori Hayashi, Jun Sasaki, et al. Microstructure and wear behaviour of chromium nitride films formed by ion-beam-enhanced deposition[J]. Surface and Coatings Technology, 1994, 66(1-3): 505-508.
[3]Wang Yongguang, Chen Yao, Zhao Dong, et al. Deformation mechanism of CrN/nitriding coated steel in wear and nano-scratch experiments under heavy loading conditions[J]. Applied Surface Science, 2018, 447(7): 100-106.
[4]Kabir M S, Munroe P, Zhou Z, et al. Scratch adhesion and tribological behavior of graded Cr/CrN/CrTiN coatings synthesized by closed-field unbalanced magnetron sputtering[J]. Wear, 2017, 380-381(6): 163-175.
[5]Fernandes F A P, Heck S C, Picone C A, et al. On the wear and corrosion of plasma nitride AISI H13[J]. Surface and Coatings Technology, 2020, 381(1): 1-12.
[6]Teng Yue, Guo Yuanyuan, Zhang Min, et al. Effect of Cr/CrN_x transition layer on mechanical properties of CrN coatings deposited on plasma nitrided austenitic stainless steel[J]. Surface and Coatings Technology, 2019, 367(3): 100-107.
[7]Zhang Jingwen, Li Zechao, Wang Yongxin, et al. A new method to improve the tribological performance of metal nitride coating: A case study for CrN coating[J]. Vacuum, 2020, 173(3): 1-9.
[8]Ovcharenko V D, Kuprin A S, Tolmachova G N, et al. Deposition of chromium nitride coatings using vacuum arc plasma in increased negative substrate bias voltage[J]. Vacuum, 2015, 117(7): 27-34.
[9]Mayr W, Lengauer W, Ettmayer P, et al. Phase equilibria and multiphase reaction diffusion in the Cr-C and the Cr-N systems[J]. Journal of Phase Equilibria, 1999, 20(1): 35-44.
[10]Russell S W, Li Jian, Alford T L, et al. Rapid thermal nitridation of thin chromium films[J]. Applied Surface Science, 1995, 90(4): 455-463.
[11]Buijnsters J G, Shankar P, Sietsma J, et al. Gas nitriding of chromium in NH₃-H₂ atmosphere[J]. Materials Science and Engineering: A, 2003, 341(1): 289-295.
[12]焦东玲, 黄海滨, 丁红珍, 等. 纯铁表面三价镀铬/渗氮复合处理制备CrN/Cr₂N涂层[J]. 材料热处理学报, 2017, 38(5): 129-133.
Jiao Dongling, Huang Haibin, Ding Hongzhen, et al. CrN/Cr₂N coating prepared by trivalent chromium electroplating and nitriding on pure iron[J]. Transaction of Materials and Heat Treatment, 2017, 38(5): 129-133.
[13]黄儒明, 代明江, 林松盛, 等. 电弧离子镀CrN薄膜的制备及性能研究[J]. 金属热处理, 2017, 42(10): 164-169.
Huang Ruming, Dai Mingjiang, Lin Songsheng, et al. Preparation and properties of CrN film by arc ion plating[J]. Heat Treatment of Metals, 2017, 42(10): 164-169.
[14]冯军, 金凡亚, 童洪辉, 等. 离子渗氮对TiN薄膜组织与性能的影响[J]. 金属热处理, 2015, 40(2): 140-143.
Feng Jun, Jin Fanya, Tong Honghui, et al. Effect of plasma nitriding on microstructure and properties of TiN thin film[J]. Heat Treatment of Metals, 2015, 40(2): 140-143.
[15]归静芝, 闵永安, 杨浩鹏, 等. H13钢低温等离子渗氮层的热疲劳性能[J]. 金属热处理, 2012, 37(4): 43-47.
Gui Jingzhi, Min Yong'an, Yang Haopeng, et al. Thermal fatigue property of H13 steel after plasma nitriding at low temperature[J]. Heat Treatment of Metals, 2012, 37(4): 43-47.
[16]罗顺, 林义民, 唐维学, 等. 离子渗氮压力对H13钢摩擦磨损性能的影响[J]. 金属热处理, 2011, 36(1): 97-99.
Luo Shun, Lin Yimin, Tang Weixue, et al. Effect of ion nitriding pressure on wear resistance of H13 steel[J]. Heat Treatment of Metals, 2011, 36(1): 97-99.
[17]潘应君, 吴新杰, 张细菊, 等. H13模具钢离子渗氮层的组织与性能[J]. 金属热处理, 2003, 28(5): 39-42.
Pan Yingjun, Wu Xinjie, Zhang Xiju, et al. Microstructure and properties of plasma nitride layer of H13 mould steel[J]. Heat Treatment of Metals, 2003, 28(5): 39-42.
[18]VDI 3198—1992, Beschichten von Werkzeugen der Kaltmassivum formung CVD- und PVD-Verfahren[S].

H13钢表面镀铬和气体渗氮复合处理的组织及性能

Microstructure and properties of H13 steel treated by chromium plating and gas nitriding

PDF

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

本文评价

[1]	罗建东, 胡雁鸿, 林育周. 双电源低温渗氮工艺在316不锈钢上的应用[J]. 金属热处理, 2022, 47(3): 7-13.
[2]	卢金生, 张衡, 许鸿翔, 郭诗蕊. 6.5 MW核电水泵内齿圈的离子渗氮工艺[J]. 金属热处理, 2022, 47(3): 97-101.
[3]	时海芳, 李强. 碳含量对Al_0.5Co_0.5NiCrFe高熵合金涂层组织与性能的影响[J]. 金属热处理, 2022, 47(3): 136-141.
[4]	吴方俊, 邓小云, 揭晓华, 郑开宏, 骆智超. 热作模具用H13和Dievar钢的热疲劳性能[J]. 金属热处理, 2022, 47(3): 165-172.
[5]	王荣, 龚玉辉, 殷学俊, 魏德强. 多道电子束扫描搭接率对40Cr钢组织与性能的影响[J]. 金属热处理, 2022, 47(3): 191-197.
[6]	周钟平, 张小娟, 白鹭, 余方印, 闵永安. T250钢离子渗氮后的组织和性能[J]. 金属热处理, 2022, 47(3): 210-214.
[7]	林基辉, 温亚辉, 范文博, 张腾, 刘晨雨, 薛元琳. 钛合金表面激光改性技术研究进展[J]. 金属热处理, 2022, 47(3): 215-221.
[8]	张孟良, 汤文博, 李百奇, 王笑生, 黎文强, 王腾飞. 等离子熔覆添加和内生联合WC颗粒增强铁基涂层的组织和性能[J]. 金属热处理, 2022, 47(2): 200-204.
[9]	王铎, 赵国华, 杨文灏, 王钰鹏, 王帅康, 鲍明东. 不同表面处理的H13钢耐铝液腐蚀的对比分析[J]. 金属热处理, 2022, 47(2): 219-223.
[10]	韩晓虎, 田林海, 王振霞, 黄天阳, 郑家圣, 王居庄, 唐宾, 吴玉程. 钨表面WTaTiVCr高熵合金层的组织与性能[J]. 金属热处理, 2022, 47(1): 185-191.
[11]	姜雪婷, 刘港, 周县, 肖飞燕, 刘静, 杨峰. Ti-6Al-4V合金渗氮层的生物腐蚀行为[J]. 金属热处理, 2022, 47(1): 197-201.
[12]	卢庆亮, 王静, 戚小霞, 李燕乐, 李方义. 面向盾构机密封跑道修复的激光熔覆Fe基涂层制备工艺[J]. 金属热处理, 2022, 47(1): 202-211.
[13]	张鹏奇, 尚洪宝, 李黎, 周志强. 离子硬化工艺在316L不锈钢阀内件中的应用[J]. 金属热处理, 2022, 47(1): 212-216.
[14]	武斌, 伍金荣, 柴慧, 李永坤. 亚温淬火对NiCrMo-3堆焊层耐磨性能的影响[J]. 金属热处理, 2022, 47(1): 276-280.
[15]	王会斌, 邱荣春, 陈葵, 刘香凝, 胡林森, 胡云波, 黄俊琼. 32Cr3MoVE钢的气体渗氮工艺[J]. 金属热处理, 2021, 46(9): 153-158.