固溶处理对7B04铝合金冷轧板组织性能的影响

doi:10.13251/j.issn.0254-6051.2020.09.019

金属热处理 ›› 2020, Vol. 45 ›› Issue (9): 105-110.DOI: 10.13251/j.issn.0254-6051.2020.09.019

固溶处理对7B04铝合金冷轧板组织性能的影响

李民¹, 李云², 徐玉国¹, 王佃刚³

1.烟台南山学院工学院,山东龙口 265713;
2.山东广播电视大学理工学院,山东济南 250010;
3.山东大学材料科学与工程学院,山东济南 250100

收稿日期:2020-03-30 出版日期:2020-09-25 发布日期:2020-12-29
通讯作者: 徐玉国,副教授,E-mail:371404645@qq.com
作者简介:李民(1978—),男,讲师,主要研究方向为铝合金材料成分设计、制备加工、热处理工艺等,E-mail:450339779@qq.com
基金资助:
山东省重点研发项目(2017GGX20130,2017CXGC0402);山东省高等学校科技计划项目(J18KB046);山东省自然科学基金(ZR2017MEM009)

Effect of solution treatment on microstructure and properties of cold rolling7B04 aluminum alloy sheet

Li Min¹, Li Yun², Xu Yuguo¹, Wang Diangang³

1. College of Engineering,Yantai Nanshan University,Longkou Shandong 265713,China;
2. Institute of Science and Technology,Shandong Radio and TV University,Jinan Shandong 250010,China;
3. School of Materials Science and Engineering,Shandong University,Jinan Shandong 250100,China

Received:2020-03-30 Online:2020-09-25 Published:2020-12-29

摘要/Abstract

摘要： 在实验室中制备了试验用7B04铝合金,经铸造-均质化退火-热轧-中间退火-冷轧后制得7B04铝合金板材,并对合金板材进行了后续固溶时效处理,研究了固溶处理对其组织和性能的影响。结果表明,470 ℃×1 h固溶+120 ℃×21 h时效处理铝合金冷轧板材再结晶明显,有少量晶粒处于伸长状态,除粗大第二相粒子外,未发现细小第二相粒子,综合力学性能较好,抗拉强度为596 MPa,屈服强度为537 MPa,伸长率为14.88%。固溶温度达到480 ℃时,合金再结晶明显,但保温时间不能超过0.5 h,否则合金强度和塑性下降。

关键词: 7B04铝合金, 冷轧板, 固溶处理, 时效处理, 微观组织, 性能

Abstract: 7B04 aluminum alloy were prepared in the laboratory,which was further prepared into 7B04 aluminum alloy sheets by casting+homogenization annealing+hot rolling+intermediate annealing+cold rolling process,then the effect of solid solution treatment on the microstructure and properties of the alloy sheet was studied.The results show that the recrystallization of cold rolling aluminum alloy sheet treated by solution treatment at 470 ℃ for 1 h and aged at 120 ℃ for 21 h is obvious,though a small amount of grains are in elongated state,and except for the coarse secondary phase particles,no small secondary phase particles are found.The comprehensive mechanical properties are good,the tensile strength is 596 MPa,the yield strength is 537 MPa,and the elongation is 14.88%.When the solution treatment temperature reaches 480 ℃,the alloy recrystallizes obviously,but the holding time should not exceed 0.5 h,otherwise the strength and plasticity of the cold rolling alloy sheet will be decreased.

Key words: 7B04 aluminum alloy, cold rolling sheet, solution treatment, aging treatment, microstructure, properties

中图分类号:

TG146.21

李民, 李云, 徐玉国, 王佃刚. 固溶处理对7B04铝合金冷轧板组织性能的影响[J]. 金属热处理, 2020, 45(9): 105-110.

Li Min, Li Yun, Xu Yuguo, Wang Diangang. Effect of solution treatment on microstructure and properties of cold rolling7B04 aluminum alloy sheet[J]. Heat Treatment of Metals, 2020, 45(9): 105-110.

参考文献

[1] 李波,刘大海,邓小范,等.预变形对7075-T6铝合金时效成形回弹及力学性能的影响[J].材料热处理学报,2017,38(8):62-68.
Li Bo,Liu Dahai,Deng Xiaofan,et al.Effect of pre-deformation on springback and mechanical properties of 7075-T6 aluminum alloy during creep aging forming[J].Transactions of Materials and Heat Treatment,2017,38(8):62-68.
[2] 黄超群,赵天生,高飞.热处理对7×××系铝合金组织及性能影响的研究进展[J].材料导报A,2019,29(12):98-103.
Huang Chaoqun,Zhao Tiansheng,Gao Fei.Research development of heat-treatment process influence on microstructure and properties for 7××× series aluminum alloys[J].Materials Reports A,2019,29(12):98-103
[3] 刘馨忆,王晨充,赵彦林.多级时效处理对Al-4.74Zn-2.13Mg-1.20Cu合金性能的影响[J].材料热处理学报,2019,40(5):58-64.
Liu Xinyi,Wang Chenchong,Zhao Yanlin.Effect of multi-stage aging treatment on properties of Al-4.74Zn-2.13Mg-1.20Cu alloy[J].Transactions of Materials and Heat Treatment,2019,40(5):58-64.
[4] Lin Huaqiang,Ye Lingying,Sun Lin,et al.Effect of three-step homogenization on microstructure and properties of 7N01 aluminum alloys[J].Transactions of Nonferrous Metals Society of China,2018,28(5):829-838.
[5] Wang Feifan,Meng Wen,Zhang Hongwei,et al.Effects of under-aging treatment on microstructure and mechanical properties of squeeze-cast Al-Zn-Mg-Cu alloy[J].Transactions of Nonferrous Metals Society of China,2018,28(10):1920-1927.
[6] Sun Siyu,Liu Peng,Hu Jiaying,et al.Effect of solid solution plus double aging on microstructural characterization of 7075 Al alloys fabricated by selective laser melting(SLM)[J].Optics and Laser Technology,2019,114:158-163.
[7] Wan Li,Deng Yunlai,Ye Lingying,et al.The natural ageing effect on pre-ageing kinetics of Al-Zn-Mg alloy[J].Journal of Alloys and Compounds,2018,776:469-474.
[8] Zhang Zhiqiang,Yu Jianhao,He Dongye.Influence of contact solid-solution treatment on microstructures and mechanical properties of 7075 aluminum alloy[J].Materials Science and Engineering A,2019,743:500-503.
[9] 王建,杨文静,李卓梁,等.7B04 铝合金的超塑变形行为及其机理[J].材料研究学报,2018,32(9):675-684.
Wang Jian,Yang Wenjing,Li Zhuoliang,et al.Superplastic behavior and deformation mechanism of 7B04 Al-alloy[J].Chinese Journal of Materials Research,2018,32(9):675-684.
[10] 陈雷,马月,杨晓禹,等.铸造方式对7B04 铝合金扁铸锭质量的影响[J].有色金属加工,2018,47(1):22-26.
Chen Lei,Ma Yue,Yang Xiaoyu,et al.Effect of casting method on quality of 7B04 aluminum alloy flat ingot[J].Nonferrous Metals Processing,2018,47(1):22-26.
[11] 王晨光,陈跃良,张勇,等.7B04 铝合金在模拟海洋大气环境下的腐蚀行为[J].航空材料学报,2017,37(1):59-64.
Wang Chenguang,Chen Yueliang,Zhang Yong,et al.Corrosion behavior of 7B04 Al-alloy in simulated marine atmospheric environment[J].Journal of Aeronautical Materials,2017,37(1):59-64.
[12] 刘慧,孙杰,房洪杰,等.微量Ce对7B04铝合金组织性能影响[J].金属热处理,2018,43(10):31-35.
Liu Hui,Sun Jie,Fang Hongjie,et al.Effect of trace cerium on microstructure and properties of 7B04 aluminum alloy[J].Heat Treatment of Metals,2018,43(10):31-35.
[13] 曲世永,李民,史春丽,等.Al-8.0Zn-2.3Cu-2.0Mg-0.2Zr铝合金的均匀化及固溶处理[J].金属热处理,2017,42(6):114-118.
Qu Shiyong,Li Min,Shi Chunli,et al.Homogenizing and solution of Al-8.0Zn-2.3Cu-2.0Mg-0.2Zr aluminum alloy[J].Heat Treatment of Metals,2017,42(6):114-118.
[14] 韩翠红,张海刚,李铸铁,等.Al-6.3Zn-2.4Mg-2.3Cu合金的均匀化处理工艺[J].金属热处理,2018,43(8):166-169.
Han Cuihong,Zhang Haigang,Li Zhutie,et al.Homogenization process of Al-6.3Zn-2.4Mg-2.3Cu alloy[J].Heat Treatment of Metals,2018,43(8):166-169.
[15] 房洪杰,孙杰,汪洪波,等.微量稀土元素Ce对7136铝合金微观组织和性能的影响[J].中国稀土学报,2016,34(3):313-319.
Fang Hongjie,Sun Jie,Wang Hongbo,et al.Effects of trace of Ce element on microstructure and properties of 7136 aluminum alloy[J].Journal of the Chinese Society of Rare Earths,2016,34(3):313-319.
[16] 房洪杰,孙杰,刘慧,等.复合添加Cr、Mn、Ti对7136铝合金组织及力学性能的影响[J].金属热处理,2017,42(4):53-57.
Fang Hongjie,Sun Jie,Liu Hui,et al.Effect of Cr,Mn,Ti content on microstructure and mechanical properties of 7136 aluminum alloy[J].Heat Treatment of Metals,2017,42(4):53-57.

固溶处理对7B04铝合金冷轧板组织性能的影响

Effect of solution treatment on microstructure and properties of cold rolling7B04 aluminum alloy sheet

PDF

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

本文评价

[1]	王玉岱, 刘洋, 朱言言, 田象军, 程序, 冉先喆, 钱婷婷. 热处理对复合制造AerMet100超高强度钢组织均匀性与拉伸性能的影响[J]. 金属热处理, 2022, 47(4): 1-9.
[2]	张子延, 陈君, 陈晓亚, 李全安, 刘建鑫. 固溶时效处理对Mg-4Sm-3Gd-0.5Zr合金显微组织和耐蚀性能的影响[J]. 金属热处理, 2022, 47(4): 10-16.
[3]	梁恩溥, 徐乐, 杨勇, 王毛球. 添加Al、Cu对40CrNi3MoV钢组织和力学性能的影响[J]. 金属热处理, 2022, 47(4): 17-23.
[4]	祁晓亮, 李岩, 定巍, 赵增武. 含Al中锰TRIP钢原始组织对临界退火后组织与力学性能的影响[J]. 金属热处理, 2022, 47(4): 24-29.
[5]	陈保安, 张静媛, 祝志祥, 韩钰, 潘学东, 张磊, 陈素红. 化学成分对高强Al-Mg-Si合金组织和性能的影响[J]. 金属热处理, 2022, 47(4): 30-38.
[6]	王英虎, 郑淮北, 刘庭耀, 宋令玺, 白青青. 固溶处理对53Cr21Mn9Ni4N耐热钢组织及碳化物的影响[J]. 金属热处理, 2022, 47(4): 39-45.
[7]	陈东俊, 李广阳, 刘刚. 时效处理对AlSi9Cu3压铸铝合金组织和力学性能的影响[J]. 金属热处理, 2022, 47(4): 53-56.
[8]	陈连生, 张露友, 田亚强, 杨子旋, 李红斌, 潘红波, 魏英立. 低碳高强舰船用钢的CCT曲线及其组织性能[J]. 金属热处理, 2022, 47(4): 63-68.
[9]	王云龙, 余伟, 张昳, 史佳新, 李明辉. 奥氏体化温度对贝氏体钢等温转变及力学性能的影响[J]. 金属热处理, 2022, 47(4): 80-85.
[10]	陈思君, 陈送义, 陈庚, 袁丁玲, 陈康华. Mg含量对2A14铝合金组织和力学性能的影响[J]. 金属热处理, 2022, 47(4): 86-92.
[11]	骆再斌, 范子泽, 彭振. 轻质高熵合金的研究进展[J]. 金属热处理, 2022, 47(4): 100-107.
[12]	白青青, 张志宏, 郑淮北, 王英虎. 2507超级双相不锈钢中σ相的析出行为[J]. 金属热处理, 2022, 47(4): 108-115.
[13]	陈刚, 罗小兵, 柴锋, 杨才福, 张正延, 杨丽. 轧制加热温度对高强度低合金钢组织及冲击性能的影响[J]. 金属热处理, 2022, 47(4): 116-121.
[14]	李立, 曾艳, 吴晓春. 4Cr5Mo2VCo钢的热处理工艺优化[J]. 金属热处理, 2022, 47(4): 133-140.
[15]	吕杰晟, 宋志刚, 何建国, 丰涵, 郑文杰, 朱玉亮. S32205双相不锈钢冷轧退火组织转变及强塑化机理分析[J]. 金属热处理, 2022, 47(4): 141-145.