高压扭转变形Mg-Zn-Y合金的组织演化和时效行为

doi:10.13251/j.issn.0254-6051.2021.01.031

金属热处理 ›› 2021, Vol. 46 ›› Issue (1): 167-172.DOI: 10.13251/j.issn.0254-6051.2021.01.031

高压扭转变形Mg-Zn-Y合金的组织演化和时效行为

王金辉, 尹晓明, 李彦生, 渠成, 徐瑞

燕山大学材料科学与工程学院亚稳材料制备技术与科学国家重点实验室河北省金属产品工艺与性能综合优化实验室,河北秦皇岛 066004

收稿日期:2020-06-29 出版日期:2021-01-25 发布日期:2021-01-26
通讯作者: 徐瑞,教授,博士,E-mail:xurui@ysu.edu.cn
作者简介:王金辉(1995—),女,硕士研究生,主要研究方向为第一性原理和镁合金大塑性变形等,E-mail:1439217124@qq.com。

Microstructure evolution and aging behavior of Mg-Zn-Y alloy processed by high pressure torsion

Wang Jinhui, Yin Xiaoming, Li Yansheng, Qu Cheng, Xu Rui

State Key Laboratory of Metastable Materials Science & Technology,Hebei Key Lab of for Optimizing Metal Product Technology and Performance,College of Materials Science and Engineering,Yanshan University,Qinhuangdao Hebei 066004,China

Received:2020-06-29 Online:2021-01-25 Published:2021-01-26

摘要/Abstract

摘要： 采用透射电镜(TEM)、扫描电镜(SEM)、X射线衍射(XRD)仪和显微硬度计研究了高压扭转(HPT)变形Mg-Zn-Y合金的微观组织演变和时效行为。结果表明,在HPT变形前后,合金中的第二相颗粒是W相和Mg₂₄Y₅相,且在HPT处理后没有观察到任何新沉淀物的形成,说明HPT变形并未导致合金发生相变。同时,发现HPT变形过程是伴随着形变孪晶的产生和大量位错增殖而进行的,其中形变孪晶在HPT处理过程中被第二相颗粒所细分。与未变形合金相比,HPT变形可以加速时效进程,即在更短的时效时间达到相对高的峰值硬度。对HPT变形7圈的试样进行175 ℃×8 h时效处理后,峰值显微硬度达到约114 HV0.1。经过时效处理后,析出相优先在位错和孪晶界处形核,说明位错和孪晶界充当析出相优先形核位点。

关键词: 镁合金, 高压扭转(HPT), 微观组织, 析出相, 孪晶

Abstract: Microstructure evolution and aging behavior of high-pressure torsion (HPT) deformed Mg-Zn-Y alloy were studied by using transmission electron microscope (TEM),scanning electron microscope (SEM),X-ray diffraction (XRD) instrument and microhardness tester. The results show that before and after HPT deformation,the second phase particles in the alloy are W phase and Mg₂₄Y₅ phase,and the formation of any new precipitates is not observed after HPT processing,indicating that HPT deformation does not lead to phase transformation of the alloy.At the same time,it is found that the HPT deformation process is accompanied by the generation of deformation twins and the multiplication of a large number of dislocations.The deformation twins are subdivided by the second phase particles during the HPT process.Compared with undeformed alloys,HPT deformation can accelerate the aging process,that is,reach a relatively high peak hardness under a shorter aging time.The specimens after HPT deformed 7 turns of are aged at 175 ℃ for 8 h,the peak microhardness reaches about 114 HV0.1.After aging treatment,the precipitated phase preferentially nucleates at the dislocations and twin boundary,indicating that dislocations and twin boundary act as preferential nucleation sites for the precipitated phases.

Key words: magnesium alloy, high pressure torsion (HPT), microstructure, precipitated phases, twin

中图分类号:

TG146.2

王金辉, 尹晓明, 李彦生, 渠成, 徐瑞. 高压扭转变形Mg-Zn-Y合金的组织演化和时效行为[J]. 金属热处理, 2021, 46(1): 167-172.

Wang Jinhui, Yin Xiaoming, Li Yansheng, Qu Cheng, Xu Rui. Microstructure evolution and aging behavior of Mg-Zn-Y alloy processed by high pressure torsion[J]. Heat Treatment of Metals, 2021, 46(1): 167-172.

参考文献

[1] Mordike B L,Ebert T.Magnesium:Properties-applications-potential[J].Materials Science and Engineering A,2001,302(1):37-45.
[2] Sauvage X,Murashkin M Y,Straumal B B,et al.Ultrafine grained structures resulting from SPD-induced phase transformation in Al-Zn alloys[J].Advanced Engineering Materials,2016,17(12):1821-1827.
[3] Edalati K,Akama D,Nishio A,et al.Influence of dislocation-solute atom interactions and stacking fault energy on grain size of single-phase alloys after severe plastic deformation using high-pressure torsion[J].Acta Materialia,2014,69(5):68-77.
[4] Loucif A,Figueiredo R B,Baudin T,et al.Ultrafine grains and the Hall-Petch relationship in an Al-Mg-Si alloy processed by high-pressure torsion[J].Materials Science and Engineering A,2012,532:139-145.
[5] Mohebbi M S,Akbarzadeh A,Kim B H,et al.Analysis of strain rate sensitivity of ultrafine-grained AA1050 by stress relaxation test[J].Metallurgical and Materials Transactions A,2014,45(12):5442-5450.
[6] Sun W T,Qiao X G,Zheng M Y,et al.Altered ageing behaviour of a nanostructured Mg-8.2Gd-3.8Y-1.0Zn-0.4Zr alloy processed by high pressure torsion[J].Acta Materialia,2018,151:260-270.
[7] Robson J D,Paa-Rai C.The interaction of grain refinement and ageing in magnesium-zinc-zirconium (ZK) alloys[J].Acta Materialia,2015,95:10-19.
[8] 尹晓明,冯凯旋,刘瑞,等.高压扭转对 Mg-Zn-Y 合金第二相溶解的影响[J].金属热处理,2018,43(7):99-103.
Yin Xiaoming,Feng Kaixuan,Liu Rui,et al.Effect of high pressure torsion on dissolution of precipitates in Mg-Zn-Y alloy[J].Heat Treatment of Metals,2018,43(7):99-103.
[9] 杨丽娜,冯运莉,王明明.45 钢高压扭转过程中的组织与性能[J].金属热处理,2019,44(4):151-155.
Yang Lina,Feng Yunli,Wang Mingming.Microstructure and properties of 45 steel during high pressure torsion[J].Heat Treatment of Metals,2019,44(4):151-155.
[10] Li Y S,Qu C,Wang J H,et al.Exceptional aging hardening behaviour of nanocrystalline Mg-Y-Nd-Gd-Zr alloy prepared by high pressure torsion[J].Journal of Alloys and Compounds,2020,813:152123.
[11] Yuan Y C,Ma A B,Jiang J H,et al.Mechanical properties and precipitate behavior of Mg-9Al-1Zn alloy processed by equal-channel angular pressing and aging[J].Journal of Alloys and Compounds,2014,594:182-188.
[12] Ye J,Lin X P,Zhao T B,et al.Influence of pre-strain on the aging hardening effect of the Mg-9.02Zn-1.68Y alloy[J].Materials Science and Engineering A,2016,663:49-55.
[13] Starink M J,Cheng X,Yang S.Hardening of pure metals by high-pressure torsion:A physically based model employing volume-averaged defect evolutions[J].Acta Materialia,2013,61(1):183-192.
[14] Sun W T,Xu C,Qiao X G,et al.Evolution of microstructure and mechanical properties of an as-cast Mg-8.2Gd-3.8Y-1.0Zn-0.4Zr alloy processed by high pressure torsion[J].Materials Science and Engineering A,2017,700:312-320.
[15] Toth L S,Gu C.Ultrafine-grain metals by severe plastic deformation[J].Materials Characterization,2014,92(6):1-14.
[16] Qiao X G,Zhao Y W,Gan W M,et al.Hardening mechanism of commercially pure Mg processed by high pressure torsion at room temperature[J].Materials Science and Engineering A,2014,619:95-106.
[17] Zhang J,Gao N,Starink M J.Microstructure development and hardening during high pressure torsion of commercially pure aluminium:Strain reversal experiments and a dislocation based model[J].Materials Science and Engineering A,2011,528 (6):2581-2591.
[18] Kim W J,Chung C S,Ma D S,et al.Optimization of strength and ductility of 2024 Al by equal channel angular pressing (ECAP) and post-ECAP aging[J].Scripta Materialia,2003,49(4):333-338.
[19] Mohamed I F,Yonenaga Y,Lee S,et al.Age hardening and thermal stability of Al-Cu alloy processed by high-pressure torsion[J].Materials Science and Engineering A,2015,627:111-118.
[20] Dogan E,Wang S,Vaughan M W,et al.Dynamic precipitation in Mg-3Al-1Zn alloy during different plastic deformation modes[J].Acta Materialia,2016,116:1-13.
[21] Sun W T,Qiao X G,Zheng M Y,et al.Exceptional grain refinement in a Mg alloy during high pressure torsion due to rare earth containing nanosized precipitates[J].Materials Science and Engineering A,2018,728:115-123.
[22] Xin Y,Wang M,Zhen Z,et al.Strengthening and toughening of magnesium alloy by {1012} extension twins[J].Scripta Materialia,2012,66(1):25-28.
[23] Zhang H,Huang G S,Wang L F,et al.Improved formability of Mg-3Al-1Zn alloy by pre-stretching and annealing[J].Scripta Materialia,2012,67(5):495-498.
[24] Gharghouri M A,Weatherly G C,Embury J D.The interaction of twins and precipitates in a Mg-7.7at.%Al alloy[J].Philosophical Magazine A,1998,78(5):1137-1149.
[25] Tang L L,Zhao Y H,Islamgaliev R K,et al.Microstructure and thermal stability of nanocrystalline Mg-Gd-Y-Zr alloy processed by high pressure torsion[J].Journal of Alloys and Compounds,2017,721:577-585.
[26] Nie J F,Zhu Y M,Liu J Z,et al.Periodic segregation of solute atoms in fully coherent twin boundaries[J].Science,2013,340:957-960.

高压扭转变形Mg-Zn-Y合金的组织演化和时效行为

Microstructure evolution and aging behavior of Mg-Zn-Y alloy processed by high pressure torsion

PDF

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

本文评价

[1]	陈保安, 张静媛, 祝志祥, 韩钰, 潘学东, 张磊, 陈素红. 化学成分对高强Al-Mg-Si合金组织和性能的影响[J]. 金属热处理, 2022, 47(4): 30-38.
[2]	连轶博, 杨春雷, 王国栋, 宋威. 固溶处理对GH4080A高温合金微观组织的影响[J]. 金属热处理, 2022, 47(4): 46-52.
[3]	陈东俊, 李广阳, 刘刚. 时效处理对AlSi9Cu3压铸铝合金组织和力学性能的影响[J]. 金属热处理, 2022, 47(4): 53-56.
[4]	陈思君, 陈送义, 陈庚, 袁丁玲, 陈康华. Mg含量对2A14铝合金组织和力学性能的影响[J]. 金属热处理, 2022, 47(4): 86-92.
[5]	李立, 曾艳, 吴晓春. 4Cr5Mo2VCo钢的热处理工艺优化[J]. 金属热处理, 2022, 47(4): 133-140.
[6]	张骥俊, 邢彦锋, 曹菊勇. 超声振动对CMT电弧增材制造铝合金组织与性能的影响[J]. 金属热处理, 2022, 47(4): 159-164.
[7]	胡静, 陶科, 杨庆松, 李刚, 张德汉. 机械抛光后的时效工艺对0Cr25Al5电热合金拉拔性能的影响[J]. 金属热处理, 2022, 47(4): 171-177.
[8]	杨春苗, 王珊, 王淑慧, 李延珍, 刘文文. RRA过程中预时效时间对7A85铝合金组织性能的影响[J]. 金属热处理, 2022, 47(3): 44-47.
[9]	陈善勇, 王快社, 乔柯, 王文. 碱热处理对搅拌摩擦加工AZ31镁合金耐腐蚀性能的影响[J]. 金属热处理, 2022, 47(3): 61-66.
[10]	梅金娜, 姜凤阳, 卫娜, 刘浪浪, 思芳, 刘松涛, 王俊勃, 刘江南. 轧制变形对高熵合金微观组织和力学性能的影响[J]. 金属热处理, 2022, 47(3): 67-71.
[11]	熊金生, 宁静, 苏杰, 姜庆伟. 淬火温度对低钴二次硬化钢组织和性能的影响[J]. 金属热处理, 2022, 47(3): 92-96.
[12]	叶拓, 唐明, 刘吉兆, 刘伟, 吴远志, 刘巍, 徐文. 固溶温度对7075铝合金板材组织与力学性能的影响[J]. 金属热处理, 2022, 47(3): 119-123.
[13]	叶拓, 何玉兵, 何文鹏, 刘巍, 袁浩登, 吴远志, 刘伟, 刘吉兆. 轧制态6082-T6铝合金的热压缩力学行为及微观组织分析[J]. 金属热处理, 2022, 47(2): 26-30.
[14]	郝天赐, 吴雍壕, 阴树标, 曹建春, 罗瀚宇. Zr对Ti-Mo复合微合金化钢形变奥氏体静态再结晶动力学和析出相的影响[J]. 金属热处理, 2022, 47(2): 41-47.
[15]	闵旭东, 黄元春, 肖政兵, 刘宇, 任贤魏, 邹倜. 预处理对汽车用Al-Mg-Si合金组织和晶间腐蚀行为的影响[J]. 金属热处理, 2022, 47(2): 78-85.