终轧温度对2205/Q345C复合板界面组织和力学性能的影响

doi:10.13251/j.issn.0254-6051.2021.07.021

摘要/Abstract

摘要： 采用真空对称组坯+热轧法制备2205/Q345C复合钢板,研究了终轧温度对复合板界面微观组织、元素扩散、硬度分布及剪切强度的影响。结果表明:终轧温度为950~1100 ℃时2205/Q345C复合板的界面结合良好,基层Q345C钢板为铁素体+珠光体组织,复层2205双相不锈钢为奥氏体+铁素体组织。在界面附近,Q345C钢中的C向2205钢中扩散形成了脱碳层,而2205钢形成了“渗碳层”,且二者的深度均随终轧温度的增加而增加。2205钢中的Cr、Ni元素向Q345C钢中连续扩散,Cr原子扩散的剧烈程度高于Ni原子,扩散距离大于Ni原子,且二者的扩散距离均随终轧温度的升高而增加。随着终轧温度的升高,复合板的硬度变化不大,在界面附近2205钢硬度最高而Q345C钢硬度值最低,而界面的剪切强度略有降低,但均大于420 MPa,符合GB/T 8165—2008《不锈钢复合板和钢带》中剪切强度≥210 MPa的要求,且剪切断口中裂纹源区面积减小。终轧温度为950~1100 ℃时2205/Q345C复合板均获得了良好的力学性能。

关键词: 不锈钢复合板, 终轧温度, 微观组织, 元素扩散, 力学性能

Abstract: Effect of final rolling temperature on the interface microstructure, element diffusion, hardness distribution and shear strength of 2205/Q345C clad steel plates prepared by vacuum hot rolling method were studied. The results show that the interface of the clad plates are all well bonded when the final rolling temperature is in the range of 950-1100 ℃, which is composed of ferrite + pearlite at the Q345C steel side and austenite + ferrite at the 2205 steel side. Near the interface of clad plate, the C atoms diffuses from Q345C steel into 2205 steel, causing a decarburized layer formed in Q345C steel, while a “carburized layer” formed in 2205 steel, and the thicknesses of both the decarburized layer and “carburized layer” increase with the increase of the final rolling temperature. Meanwhile, the Cr and Ni atoms diffuse continuously from Q345C steel into 2205 steel, and the diffusion distance of Cr atoms is greater than that of Ni atoms. With the increase of the final rolling temperature, the diffusion distances of Cr atoms and Ni atoms increase. Also with the increase of the final rolling temperature, the hardness of the clad plate changes little, and the hardness of 2205 steel near the interface is the highest while that of Q345C steel is the lowest. At the same time, the interfacial shear strength of the clad plates decreases, but all of them are greater than 420 MPa, which conforms to the requirement of shear strength ≥210 MPa in the standard of GB/T 8165—2008 Stainless Steel Clad Plates and Strips. In conclusion, when the final rolling temperature is in the range of 950-1100 ℃, the 2205/Q345C clad plates can obtain good mechanical properties.

Key words: stainless steel clad plate, final rolling temperature, microstructure, element diffusion, mechanical properties

中图分类号:

TB33

张永健, 陈俊宏, 陈祯, 王娇娇, 惠卫军, 王小勇, 杨建炜. 终轧温度对2205/Q345C复合板界面组织和力学性能的影响[J]. 金属热处理, 2021, 46(7): 108-113.

Zhang Yongjian, Chen Junhong, Chen Zhen, Wang Jiaojiao, Hui Weijun, Wang Xiaoyong, Yang Jianwei. Effect of final rolling temperature on interfacial microstructure and mechanical properties of 2205/Q345C steel clad plate[J]. Heat Treatment of Metals, 2021, 46(7): 108-113.

参考文献

[1] 翁宇庆, 陈蕴博, 刘玠, 等. 特殊钢在先进装备制造业应用中的战略研究[M]. 北京: 冶金工业出版社, 2012.
[2] Wang S, Liu B X, Chen C X, et al. Microstructure, mechanical properties and interface bonding mechanism of hot-rolled stainless steel clad plates at different rolling reduction ratios[J]. Journal of Alloys and Compounds, 2018, 766: 517-526.
[3] Liu B X, Yin F X, Dai X L, et al. The tensile behaviors and fracture characteristics of stainless steel clad plates with different interfacial status[J]. Materials Science and Engineering A, 2017, 679: 172-182.
[4] 金贺荣, 韩民峰, 段昌新. 压下率对316L/EH40复合板界面微观形貌的影响[J]. 钢铁, 2019, 54(12): 62-69.
Jin Herong, Han Minfeng, Duan Changxin. Effect of reduction rates on interfacial microstructure morphologies of 316L/EH40 clad plate[J]. Iron and Steel, 2019, 54(12): 62-69.
[5] 刘利香, 张学岭. 不同制坯工艺对不锈钢复合板坯料轧制的影响研究[J]. 宽厚板, 2019, 25(6): 5-9.
Liu Lixiang, Zhang Xueling. Effects of different composite slab bonding processes on stainless steel clad plate rolling[J]. Wide and Heavy Plate, 2019, 25(6): 5-9.
[6] 王泽鹏, 张红梅, 付魁军, 等. 压下率对热轧不锈钢复合板组织与性能的影响[J]. 金属热处理, 2016, 41(9): 103-106.
Wang Zepeng, Zhang Hongmei, Fu Kuijun, et al. Effect of reduction ratio on microstructure and properties of hot-rolled stainless steel clad plate[J]. Heat Treatment of Metals, 2016, 41(9): 103-106.
[7] 黄庆学, 李海斌, 周存龙, 等. 复合板轧制压下率对碳钢组织及相变的影响[J]. 材料热处理学报, 2014, 35(3): 149-153.
Huang Qingxue, Li Haibin, Zhou Cunlong, et al. Effect of reduction rate on microstructure and transformation behavior of carbon steel by rolling clad plate[J]. Transactions of Materials and Heat Treatment, 2014, 35(3): 149-153.
[8] Liu B X, Wang S, Fang W, et al. Microstructure and mechanical properties of hot rolled stainless steel clad plate by heat treatment[J]. Materials Chemistry and Physics, 2018, 216: 460-467.
[9] 丁海民, 范孝良, 王进峰, 等. 热轧复合不锈钢-碳钢复合板界面特征[J]. 材料热处理学报, 2011, 32(11): 18-22.
Ding Haimin, Fan Xiaoliang, Wang Jinfeng, et al. Interface characterization of hot-rolled stainless steel/carbon steel clad[J]. Transactions of Materials and Heat Treatment, 2011, 32(11): 18-22.
[10] 胡晓英. 终轧温度对Q345B热轧钢板组织和性能的影响探究[J]. 宽厚板, 2020, 26(1): 29-33.
Hu Xiaoying. Investigating effects of finish rolling temperature on microstructure and mechanical properties of Q345B hot rolled steel plate[J]. Wide and Heavy Plate, 2020, 26(1): 29-33.
[11] 谯明亮, 史根豪, 洪君, 等. 终轧温度对Q420qENH钢板组织性能的影响[J]. 轧钢, 2019, 36(3): 18-21.
Qiao Mingliang, Shi Genhao, Hong Jun, et al. Effect of finishing rolling temperature on the microstructure and properties of Q420qENH plate[J]. Steel Rolling, 2019, 36(3): 18-21.
[12] 韩承良, 王彦锋, 杨永达, 等. 终轧温度对Q420qE钢板组织性能的影响[J]. 轧钢, 2018, 35(2): 26-28.
Han Chengliang, Wang Yanfeng, Yang Yongda, et al. Effect of finishing rolling temperature on microstructure and mechanical properties of Q420qE plate[J]. Steel Rolling, 2018, 35(2): 26-28.
[13] 张开华, 叶晓瑜, 刘勇, 等. 终轧温度对高强度工程机械用钢组织性能的影响[J]. 钢铁钒钛, 2010, 31(3): 63-67.
Zhang Kaihua, Ye Xiaoyu, Liu Yong, et al. Effect of finishing rolling temperature on microstructures and mechanical properties of steel strip for engineering mechanism[J]. Iron Steel Vanadium Titanium, 2010, 31(3): 63-67.
[14] 肖丰强, 王东坡, 胡文彬, 等. 终轧温度对2205/Q235B双相不锈钢复合板组织和性能的影响[J]. 材料导报, 2020, 34(16): 16119-16124.
Xiao Fengqiang, Wang Dongpo, Hu Wenbin, et al. Effect of final rolling temperature on microstructure and properties of 2205/Q235B duplex stainless steel clad plate[J]. Materials Reports, 2020, 34(16): 16119-16124.
[15] Chen J, Dong F T, Jiang H L, et al. Influence of final rolling temperature on microstructure and mechanical properties in a hot-rolled TWIP steel for cryogenic application[J]. Materials Science and Engineering A, 2018, 724: 330-334.
[16] 白允强, 黄文, 王章忠, 等. 2205双相不锈钢/Q345低合金钢爆炸复合板的组织与力学性能[J]. 机械工程材料, 2012, 36(12): 33-36.
Bai Yunqiang, Huang Wen, Wang Zhangzhong, et al. Microstructure and mechanical properties of explosive clad plates of 2205 duplex stainless steel and Q345 low alloy steel[J]. Materials for Mechanical Engineering, 2012, 36(12): 33-36.
[17] 任永峰, 查小琴, 张凌峰. 2205双相不锈钢热轧复合板复层组织及性能研究[J]. 塑性工程学报, 2020, 27(3): 122-129.
Ren Yongfeng, Zha Xiaoqin, Zhang Lingfeng. Study on multiple layer microstructure and properties of 2205 duplex stainless steel hot rolled clad plates[J]. Journal of Plasticity Engineering, 2020, 27(3): 122-129.