正火轧制及后续正火工艺对S460NL高强度低温结构钢组织性能的影响

doi:10.13251/j.issn.0254-6051.2021.09.025

金属热处理 ›› 2021, Vol. 46 ›› Issue (9): 142-145.DOI: 10.13251/j.issn.0254-6051.2021.09.025

正火轧制及后续正火工艺对S460NL高强度低温结构钢组织性能的影响

潘中德¹, 张鹏程², 武会宾², 胡其龙¹

1.南京钢铁股份有限公司, 江苏南京 210035;
2.北京科技大学钢铁共性技术协同创新中心, 北京 100083

收稿日期:2021-05-27 出版日期:2021-09-25 发布日期:2021-12-09
通讯作者: 张鹏程,工程师,博士,E-mail:zhpch2008@163.com
作者简介:潘中德(1983—),男,高级工程师,主要研究方向为中厚板新产品研发、质量提升等,E-mail:panzhongde@njsteel.com.cn。
基金资助:
国家自然科学基金(51774033)

Effect of normalizing rolling and subsequent normalizing process on microstructure and properties of S460NL high-strength low-temperature structural steel

Pan Zhongde¹, Zhang Pengcheng², Wu Huibin², Hu Qilong¹

1. Nanjing Iron & Steel Co., Ltd., Nanjing Jiangsu 210035, China;
2. Collaborative Innovation Center of Steel Technology, University of Science and Technology Beijing, Beijing 100083, China

Received:2021-05-27 Online:2021-09-25 Published:2021-12-09

摘要/Abstract

摘要： 以EN10025-3标准为基本依据,采用中碳、低磷、低硫、低氮、低氢设计了正火高强度低温S460NL结构钢板的成分,通过高均质冶炼连铸工艺,生产了不同规格的正火轧制和正火轧制+正火钢板。结果表明,对于规格60 mm以下S460NL钢板,正火轧制工艺可以满足EN10025-3和EN10164 Z35标准性能要求,对于规格60 mm及以上S460NL钢板,需要增加正火工艺才能满足EN10025-3和EN10164 Z35标准的性能要求;正火轧制+正火态S460NL钢板经PWHT模拟焊热处理后的拉伸性能、－50 ℃冲击性能优异,符合标准要求。

关键词: S460NL钢, 正火工艺, 低温结构钢

Abstract: Based on EN10025-3 standard, the chemical composition of the normalized high-strength low-temperature structural steel S460NL was designed with medium carbon, low phosphorus, sulfur, nitrogen and hydrogen; then through high-homogeneous smelting and continuous casting process, the steel plates with different specifications were produced respectively by normalizing rolling and by normalizing rolling+normalizing. The results show that the steel plates by normalizing rolling process can meet the performance requirements of EN10025-3 standard and EN10164 Z35 standard for the S460NL steel plates with specifications below 60 mm, while for that 60 mm and above, additional normalizing process is required to meet such performance requirements. The normalizing-rolled+normalized S460NL steel plates have excellent tensile properties and excellent impact properties at －50 ℃ after PWHT simulated post welding heat treatment, which meets the standard requirements.

Key words: S460NL steel, normalizing process, low-temperature structural steel

中图分类号:

TG142

潘中德, 张鹏程, 武会宾, 胡其龙. 正火轧制及后续正火工艺对S460NL高强度低温结构钢组织性能的影响[J]. 金属热处理, 2021, 46(9): 142-145.

Pan Zhongde, Zhang Pengcheng, Wu Huibin, Hu Qilong. Effect of normalizing rolling and subsequent normalizing process on microstructure and properties of S460NL high-strength low-temperature structural steel[J]. Heat Treatment of Metals, 2021, 46(9): 142-145.

参考文献

[1]阮建平. 国际政治经济学视角下的“冰上丝绸之路”倡议[J]. 海洋开发与管理, 2017, 34(11): 3-9.
Ruan Jianping. From the perspective of IPE: The initiative of ice silk road[J]. Ocean Development and Management, 2017, 34(11): 3-9.
[2]刘振宇, 周砚磊, 狄国标, 等. 高强度厚规格海洋平台用钢研究进展及应用[J]. 中国工程科学, 2014, 16(2): 31-38.
Liu Zhenyu, Zhou Yanlei, Di Guobiao, et al. Research progress and application of high performance offshore platform steel[J]. Chinese Engineering Science, 2014, 16(2): 31-38.
[3]尚成嘉, 李秀程, 谢振家. 高性能海洋工程用钢的智慧研发之一[J]. 鞍钢技术, 2018(1): 1-6.
Shang Chengjia, Li Xiucheng, Xie Zhenjia. Development of high performance steel for marine engineering[J]. Angang Technology, 2018(1): 1-6.
[4]刘振宇, 唐帅, 陈俊, 等. 海洋平台用钢的研究生产现状与发展趋势[J]. 鞍钢技术, 2015(1): 1-7.
Liu Zhenyu, Tang Shuai, Chen Jun, et al. Latest progress on development and production of steels for offshore platform and their development tendency[J]. Angang Technology, 2015(1): 1-7.
[5]Nishida S, Matsuoka T, Wada T. Technology and products of JFE steel's three plate mills[J]. JFE Technical Report, 2005, 5(3): 1-9.
[6]Ryuji U, Masaaki F, Takehiro I. Steels for marine transportation and construction[J]. Nippon Steel Technical Report, 2012, 101: 37-47.
[7]王宏颖. Q460D高强钢的回火工艺[J]. 金属热处理, 2019, 44(11): 185-187.
Wang Hongying. Tempering process of Q460D high strength steel[J]. Heat Treatment of Metals, 2019, 44(11): 185-187.
[8]Hayashi K, Nagao A, Matsuda Y. 550 MPa and 610 MPa class high strength steel plates with excellent toughness for tanks and penstocks produced using carbide morphology controlling technology[J]. JFE Technical Report, 2008(11): 19-25.
[9]孙乐飞, 王福明, 闰博. 大厚度海洋平台高强钢焊接热影响区的组织和性能[J]. 金属热处理, 2013, 38(11): 14-17.
Sun Lefei, Wang Fuming, Yan Bo. Microstructure and mechanical properti es of HAZ in high strength and heavy steel plate for offshore platform[J]. Heat Treatment of Metals, 2013, 38(11): 14-17.
[10]Hideaki M, Norio K, Syuichi H. Corrosion and its properties of welded joint of seawater resistant low alloy steel[J]. Sumitomo Metal, 1996, 48(2): 68-75.
[11]侯志国, 刘希琴, 刘子利, 等. 正火处理对新型低温钢组织和力学性能的影响[J]. 钢管, 2015, 44(2): 11-17.
Hou Zhiguo, Liu Xiqin, Liu Zili, et al. Effects by normalization treatment on microstructure and mechanical properties of new-type steel for low temperature service[J]. Steel Pipe, 2015, 44(2): 11-17.
[12]魏同锋, 甘立建, 王启迪. Nb对低碳微合金钢组织与性能的影响[J]. 热加工工艺, 2015, 44(14): 126-128.
Wei Tongfeng, Gan Lijian, Wang Qidi. Effect of Nb on microstructure and properties of low-carbon microalloyed steel[J]. Hot Working Technology, 2015, 44(14): 126-128.
[13]冯春, 方鸿生, 白秉哲, 等. 0.02%Nb空冷仿晶界型铁素体/粒状贝氏体复相钢的相变及强韧性[J]. 金属学报, 2010, 46(4): 473-478.
Feng Chun, Fang Hongsheng, Bai Bingzhe, et al. Phase transformation and strength-toughness of a F_GBA/B_G diphase steel containing 0.02%Nb[J]. Acta Metallurgic Sinica, 2010, 46(4): 473-478.

[1]	王玉岱, 刘洋, 朱言言, 田象军, 程序, 冉先喆, 钱婷婷. 热处理对复合制造AerMet100超高强度钢组织均匀性与拉伸性能的影响[J]. 金属热处理, 2022, 47(4): 1-9.
[2]	梁恩溥, 徐乐, 杨勇, 王毛球. 添加Al、Cu对40CrNi3MoV钢组织和力学性能的影响[J]. 金属热处理, 2022, 47(4): 17-23.
[3]	祁晓亮, 李岩, 定巍, 赵增武. 含Al中锰TRIP钢原始组织对临界退火后组织与力学性能的影响[J]. 金属热处理, 2022, 47(4): 24-29.
[4]	王英虎, 郑淮北, 刘庭耀, 宋令玺, 白青青. 固溶处理对53Cr21Mn9Ni4N耐热钢组织及碳化物的影响[J]. 金属热处理, 2022, 47(4): 39-45.
[5]	杨静, 董楠, 姜周华, 韩培德. 合金元素在fcc-Fe/NbX(X=C,N)界面的偏析及影响[J]. 金属热处理, 2022, 47(4): 57-62.
[6]	陈连生, 张露友, 田亚强, 杨子旋, 李红斌, 潘红波, 魏英立. 低碳高强舰船用钢的CCT曲线及其组织性能[J]. 金属热处理, 2022, 47(4): 63-68.
[7]	王云龙, 余伟, 张昳, 史佳新, 李明辉. 奥氏体化温度对贝氏体钢等温转变及力学性能的影响[J]. 金属热处理, 2022, 47(4): 80-85.
[8]	白青青, 张志宏, 郑淮北, 王英虎. 2507超级双相不锈钢中σ相的析出行为[J]. 金属热处理, 2022, 47(4): 108-115.
[9]	付锡彬, 陈子豪, 张可, 赵时雨, 孙新军, 朱正海, 梁小凯, 雍岐龙. 淬火温度对高Ti低合金耐磨钢组织及力学性能的影响[J]. 金属热处理, 2022, 47(4): 122-127.
[10]	宿鹏吉, 麻永林, 董丽丽, 杨雪峰. 磁场预退火处理对CGO钢组织与织构的影响[J]. 金属热处理, 2022, 47(4): 128-132.
[11]	李立, 曾艳, 吴晓春. 4Cr5Mo2VCo钢的热处理工艺优化[J]. 金属热处理, 2022, 47(4): 133-140.
[12]	戴建科, 韩顺, 厉勇, 刘宪民, 王春旭, 庞学东, 李建新. 航空齿轮钢C69高温渗碳后的组织性能[J]. 金属热处理, 2022, 47(4): 219-225.
[13]	张宁, 高星, 王芝林, 蒋波, 刘雅政. 18CrNiMo7-6钢齿轮组织性能异常分析[J]. 金属热处理, 2022, 47(4): 268-273.
[14]	黄龙, 邓想涛, 王昭东. 回火温度对颗粒增强型低合金耐磨钢组织和性能的影响[J]. 金属热处理, 2022, 47(3): 1-6.
[15]	陈连生, 房宁, 曹仲乾, 杨子旋, 李红斌, 潘红波, 田亚强. 压下率对两相区温轧淬火配分中锰钢组织性能的影响[J]. 金属热处理, 2022, 47(3): 28-33.

正火轧制及后续正火工艺对S460NL高强度低温结构钢组织性能的影响

Effect of normalizing rolling and subsequent normalizing process on microstructure and properties of S460NL high-strength low-temperature structural steel

PDF

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

本文评价