N含量对13Cr超级马氏体不锈钢耐蚀性的影响

doi:10.13251/j.issn.0254-6051.2021.12.017

摘要/Abstract

摘要： 对13Cr超级马氏体不锈钢进行氮合金化,采用淬火-配分热处理工艺,研究了不同N含量对13Cr钢的微观组织及电化学腐蚀行为的影响。结果表明:随N含量增加,板条马氏体组织表现出明显的细化行为,奥氏体含量增加,且有VN生成,从而防止N与Cr结合生成Cr₂N,促使Cr在材料表面形成以Cr₂O₃为主的致密腐蚀产物膜,提高材料耐蚀性;试验钢表面以局部腐蚀为主,试样表面有点蚀发生。随着N含量的增加,形成腐蚀产物膜的孔隙度减小;表面钝化膜为双电层结构,增加了钝化膜的稳定性,点蚀坑数量明显减少且变小;提高N含量有利于试样耐点蚀性能的改善,0.35%N试验钢表面腐蚀产物附着牢固,平整且致密,晶粒大小均匀,可起到良好的保护作用。

关键词: 超级马氏体不锈钢, N元素, 耐蚀性能

Abstract: Nitrogen alloying of 13Cr super-martensitic stainless steel was carried out, quenching and partitioning process was adopted to study the influence of different N content on microstructure and electrochemical corrosion behavior, the results show that with the increase of N content, the lath martensite shows an obvious fining behavior. The austenite content is increased through the formation of VN, which prevents the combination of N and Cr to form Cr₂N, and the Cr forms a corrosion product film dominated by Cr₂O₃ on the surface of the steel, thus improving the corrosion resistance of the steel. The surface of the tested steel is dominated by local corrosion, and pitting corrosion occurs in the specimens. With the increase of N content, the porosity of the corrosion product film decreases, and the surface passivation film is of an electric double layer structure, which increases the stability of the passivation film, and the number of pitting pits is significantly reduced and the pits are smaller. The increase of N content results in the improvement of pitting resistance of the specimens, the corrosion products on surface of the tested steel containing 0.35%N are firmly attached, smooth and compact, and the grain size is uniform, playing a good protective role.

Key words: super-martensitic stainless steel, nitrogen element, corrosion resistance

中图分类号:

TG172.9

李苗苗, 邹德宁, 佟立波, 庞阳. N含量对13Cr超级马氏体不锈钢耐蚀性的影响[J]. 金属热处理, 2021, 46(12): 107-112.

Li Miaomiao, Zou Dening, Tong Libo, Pang Yang. Effect of N content on corrosion resistance of 13Cr super-martensitic stainless steel[J]. Heat Treatment of Metals, 2021, 46(12): 107-112.

参考文献

[1]王园园. 微合金化超低碳马氏体不锈钢13Cr5Ni2Mo的组织和性能研究[D]. 沈阳: 东北大学, 2010.
Wang Yuanyuan. Study on microstructure and properties of Nb-V-N micro-alloying 13Cr5Ni2Mo super low carbon matensitic stainless steel[D]. Shenyang: Northeastern University, 2010.
[2]Rodrigues C, Lorenzo P, Sokolowski A, et al. Titanium and molybdenum content in supermartensitic stainless steel[J]. Materials Science and Engineering A, 2007, 460-461: 149-152.
[3]秦紫瑞, 姚曼. 超低碳Cr26-Ni28-Mo5-Cu3-Nb0. 35铸造不锈钢的组织和耐蚀性能[J]. 特殊钢, 1995, 16(4): 11-16.
Qin Zirui, Yao Man. Structure and anti-corrosion behavior of extra-low carbon 26Cr-28Ni-5Mo-3Cu-0.35Nb cast stainless steel[J]. Special Steel, 1995, 16(4): 11-16.
[4]Liu Y J, Lu X H, Zhao G X, et al. Corrosion behaviors of super 13Cr martensitic stainless steel under drilling and completion fluids environment[J]. Journal of Materials Engineering, 2012, 2(10): 17-21.
[5]Yue J, Qiang J, Shi Q L. Structure and properties of ultra-low carbon maraging steel 00Cr13Ni7Co5Mo4W[J]. Special Steel, 2014, 35(5): 64-67.
[6]Ahmad R R, Hamed Z A. Mechanical properties and corrosion resistance of normal strength and high strength steels in chloride solution[J]. Journal of Naval Architecture and Marine Engineering, 2011, 7(2): 93-100.
[7]Song Y Y, Ping D H, Yin F X, et al. Microstructural evolution and low temperature impact toughness of a Fe-13%Cr-4%Ni-Mo martensitic stainless steel[J]. Materials Science & Engineering A, 2010, 527(3): 614-618.
[8]Ma X P, Wang L J, Liu C M, et al. Microstructure and properties of 13Cr5Ni1Mo0.025Nb0.09V0.06N super martensitic stainless steel[J]. Materials Scienceand Engineering A, 2012, 539(30): 271-279.
[9]Hsieh C C, Lin D Y, Chang T C. Microstructural evolution during the δ/σ/γ phase transformation of the SUS 309LSi stainless steel after aging under various nitrogen atmospheric ratios[J]. Materials Science and Engineering A, 2008, 475(1/2): 128-135.
[10]Fomina O V, Vikhareva T V. Structure formation of the nitrogen-containing austenitic 04Kh20N6G11M2AFB steel at hot deformation: Part II. Influence of the phase composition and conditions of hot deformation on the process of dynamic recrystallization[J]. Inorganic Materials: Applied Research, 2018, 9(6): 1070-1075.
[11]Kostin M V. Phase transformations in a corrosion-resistant high-chromium nitrogen-bearing steel[J]. Russian Metallurgy, 2011(9): 813-825.
[12]Lee J B, Yoon S I. Effect of nitrogen alloying on the semiconducting properties of passive films and metastable pitting susceptibility of 316L and 316LN stainless steels[J]. Materials Chemistry and Physics, 2010, 122(1): 194-199.
[13]Leim K, Zhu X M. Role of nitrogen in pitting corrosion resistance of a high-nitrogen face-centered-cubic phase formed on austenitic stainless steel[J]. Journal of the Electrochemical Society, 2005, 152(8): 291-295.
[14]Ningshen S, Mudali U K, Mittal V K, et al. Semiconducting and passive film properties of nitrogen-containing type 316LN stainless steels[J]. Corrosion Science, 2007, 49(2): 481-496.
[15]Ha H Y, Lee T H, Kim S J. Role of nitrogen in the active-passive transition behavior of binary Fe-Cr alloy system[J]. Electrochimica Acta, 2012, 80: 432-439.
[16]Ha H Y, Jang H J, Kwon H S, et al. Effects of nitrogen on the passivity of Fe-20Cr alloy[J]. Corrosion Science, 2009, 51(1): 48-53.
[17]Lothongkum G, Wongpanya P, Morito S, et al. Effect of nitrogen on corrosion behavior of 28Cr-7Ni duplex and microduplex stainless steels in air-saturated 3.5wt% NaCl solution[J]. Corrosion Science, 2006, 48(1): 137-153.
[18]翟瑞银, 吴狄峰, 常锷. 氮对低碳马氏体不锈钢组织和性能的影响[J]. 宝钢技术, 2013(5): 32-36.
Zhai Ruiyin, Wu Difeng, Chang E. Effect of nitrogen on microstructure and properties of low carbon martensitic stainless steel[J]. Baosteel Technology, 2013(5): 32-36.
[19]Moyer K. A modified vacuum gas carburizing process to improve corrosion and wear resistance of nitrogen martensitic stainless steels in salt water environments[J]. Ginekologia Polska, 2008, 79(8): 544-549.
[20]李堃, 杨吉春, 何耀宇, 等. 氮对2Cr13马氏体不锈钢耐腐蚀性能的影响[J]. 内蒙古科技大学学报, 2017, 46(1): 13-16.
Li Kui, Yang Jichun, He Yaoyu, et al. Effect of nitrogen on corrosion resistance of 2Cr13 martensitic stainless steel[J]. Journal of Inner Mongolia University of Science and Technology, 2017, 46(1): 13-16.
[21]张威, 王铎. 超级马氏体不锈钢SuperCr13在模拟地层水环境中的腐蚀行为[J]. 腐蚀与防护, 2013, 34(8): 702-705.
Zhang Wei, Wang Duo. Corrosion behaviour of super martensitic stainless steel SuperCr13 in simulated formation water environment[J]. Corrosion and Protection, 2013, 34(8): 702-705.
[22]曾潮流, 王文, 吴维. 熔融盐热腐蚀的电化学阻抗模型[J]. 金属学报, 1999, 35(7): 751-754.
Zeng Chaoliu, Wang Wen, Wu Wei. Electrochemical impedance models for molten salts induced corrosion[J]. Acta Metallurgica Sinica, 1999, 35(7): 751-754.
[23]曹楚南, 张鉴清. 电化学阻抗谱导论[M]. 北京: 科学出版社, 2002: 166-190.