2507超级双相不锈钢中第二相的析出行为

doi:10.13251/j.issn.0254-6051.2022.05.015

金属热处理 ›› 2022, Vol. 47 ›› Issue (5): 92-97.DOI: 10.13251/j.issn.0254-6051.2022.05.015

2507超级双相不锈钢中第二相的析出行为

谷国超^1,2, 李瑞芬³, 辛振民^1,2, 袁召富^1,2, 崔树刚^1,2, 许文花^1,2, 吕宇鹏^1,2

1.山东大学材料液固结构演变与加工教育部重点实验室, 山东济南 250061;
2.山东大学材料科学与工程学院, 山东济南 250061;
3.山东省产品质量检验研究院, 山东济南 250102

收稿日期:2021-12-27 修回日期:2022-03-17 出版日期:2022-05-25 发布日期:2022-06-16
作者简介:谷国超(1982—),男,讲师,博士,主要研究方向为金属热处理,E-mail: guochaogu@sdu.edu.cn
基金资助:
山东省重点研发计划(重大科技创新工程)(2019JZZY010358,2020CXGC010305,2021ZLGX01);国家重点研发计划(2017YFB 0305101)

Precipitation behavior of second phase in super duplex stainless steel 2507

Gu Guochao^1,2, Li Ruifen³, Xin Zhenmin^1,2, Yuan Zhaofu^1,2, Cui Shugang^1,2, Xu Wenhua^1,2, Lü Yupeng^1,2

1. Key Laboratory for Liquid-Solid Structural Evolution and Processing of Materials, Ministry of Education, Shandong University, Ji'nan Shandong 250061, China;
2. School of Materials Science and Engineering, Shandong University, Ji'nan Shandong 250061, China;
3. Shandong Institute for Product Quality Inspection, Ji'nan Shandong 250102, China

Received:2021-12-27 Revised:2022-03-17 Online:2022-05-25 Published:2022-06-16

摘要/Abstract

摘要： 利用OM、SEM和EBSD等研究了经1100 ℃保温30 min固溶的热轧超级双相不锈钢(SDSS)2507在不同时效温度(750~1000 ℃)及时间(1~240 min)下的第二相析出行为。结果表明,固溶态SDSS 2507的微观组织主要是铁素体和奥氏体。在750～1000 ℃时效处理后有σ相和χ相析出。时效温度较低时,χ相从铁素体相析出且稳定存在。随着时效温度的升高,σ相主要通过α→σ+γ₂共析反应生成,随着时效时间的延长,组织中亚稳态χ相溶解并促进σ相析出。另外,时效温度也会影响第二相形貌:高温时效时(＞950 ℃),析出相形貌主要为片状σ相和γ₂相,低温时效时析出物主要呈颗粒状。由第二相析出行为及第二相的TTT曲线可知,热轧变形使SDSS 2507第二相形核的孕育期缩短,析出速度提高,析出敏感温度约为950 ℃。

关键词: 2507超级双相不锈钢, σ相, 时效处理, 析出行为

Abstract: Second phase precipitation behavior of solid solution treated (1100 ℃×30 min) super duplex stainless steel 2507 hot raled plate after aging at different temperatures (750-1000 ℃) and time (1-240 min) was investigated by using OM, SEM and EBSD. The results show that the microstructure of the tested steel is composed of austenite and ferrite after solution treatment, while after aging at 750-1000 ℃, σ phase and χ phase are detected and identified. When the aging temperature is lower, χ phase precipitates from ferrite phase and exists stably. With aging temperature increasing, the σ phase is formed mainly by the reaction α→σ+γ₂. In addition, with the longer holding time, the metastable χ phase dissolves and promotes σ phase precipitation. Additionally, the aging temperature influences the morphology of the precipitates. At higher aging temperatures (＞950 ℃), the morphology of precipitated phase is mainly sheet σ and γ₂, while at lower aging temperatures, the granular σ phase and χ phase are mainly observed. According to the precipitation behavior and the calculation of TTT diagram of the precipitates, it can be seen that hot rolling deformation shortens the nucleation incubation period of the second phases in the SDSS 2507, increases the precipitation rate, and the precipitation sensitive temperature is about 950 ℃.

Key words: super duplex stainless steel 2507, σ phase, aging treatment, precipitation behavior

中图分类号:

TG142.1

谷国超, 李瑞芬, 辛振民, 袁召富, 崔树刚, 许文花, 吕宇鹏. 2507超级双相不锈钢中第二相的析出行为[J]. 金属热处理, 2022, 47(5): 92-97.

Gu Guochao, Li Ruifen, Xin Zhenmin, Yuan Zhaofu, Cui Shugang, Xu Wenhua, Lü Yupeng. Precipitation behavior of second phase in super duplex stainless steel 2507[J]. Heat Treatment of Metals, 2022, 47(5): 92-97.

参考文献

[1]袁傲明, 李晶琨, 高晓丹, 等. 冷轧与时效工艺对2205双相不锈钢σ相析出的影响[J]. 金属热处理, 2021, 46(10): 26-30.
Yuan Aoming, Li Jingkun, Gao Xiaodan, et al. Effect of cold rolling and aging process on σ phase precipitation of 2205 duplex stainless steel[J]. Heat Treatment of Metals, 2021, 46(10): 26-30.
[2]向红亮, 刘东, 阮方如, 等. 时效析出相对铸造2507 超级双相不锈钢力学及耐蚀性能的影响[J]. 金属学报, 2010, 46(8): 941-945.
Xiang Hongliang, Liu Dong, Ruan Fangru, et al. Effects of precipitation for aging on mechanical and corrosion resistance properties of cast 2507 super duplex stainless steel[J]. Acta Metallurgica Sinica, 2010, 46(8): 941-945.
[3]钱张信, 石旭麟, 纪显彬, 等. 时效工艺对2507不锈钢σ相析出及力学性能的影响[J]. 金属热处理, 2018, 43(7): 124-127.
Qian Zhangxin, Shi Xulin, Ji Xianbin, et al. Effect of aging process on σ-phase precipitation and mechanical properties of 2507 stainless steel[J]. Heat Treatment of Metals, 2018, 43(7): 124-127.
[4]高晓丹, 任学平, 李晶琨, 等. 时效工艺对2205双相不锈钢σ相析出行为的影响[J]. 金属热处理, 2020, 45(10): 1-5.
Gao Xiaodan, Ren Xueping, Li Jingkun, et al. Effect of aging process on σ phase precipitation of 2205 duplex stainless steel[J]. Heat Treatment of Metals, 2020, 45(10): 1-5.
[5]Calliari I, Zanesco M, Ramous E. Influence of isothermal aging on secondary phases precipitation and toughness of a duplex stainless steel SAF 2205[J]. Journal of Materials Science, 2006, 41(22): 7643-7649.
[6]Sousa R O, Lacerda P, Ferreira P J. On the precipitation of sigma and Chi phases in a cast super duplex stainless steel[J]. Metallurgical and Materials Transactions A, 2019, 50(10): 4758-4778.
[7]向红亮, 何福善, 刘东. 时效温度对铸造超级双相不锈钢析出相的影响[J]. 金属学报, 2009, 45(12): 1456-1460.
Xiang Hongliang, He Fushan, Liu Dong. Effects of aging temperature on precipitation phase of a cast super duplex stainless steel[J]. Acta Metallurgica Sinica, 2009, 45(12): 1456-1460.
[8]马明, 丁桦, 唐正友, 等. 2205双相不锈钢中σ相的析出行为[J]. 东北大学学报, 2014, 35(4): 504-507.
Ma Ming, Ding Hua, Tang Zhengyou, et al. Precipitation behavior of σ phase in duplex stainless steel 2205[J]. Journal of Northeastern University (Nature Science), 2014, 35(4): 504-507.
[9]孙祺, 王剑, 何燕, 等. 时效时间对2205双相不锈钢中第二相析出行为的影响[J]. 金属热处理, 2016, 41(2): 63-67.
Sun Qi, Wang Jian, He Yan, et al. Influence of aging time on precipitation behavior of 2205 duplex stainless steel[J]. Heat Treatment of Metals, 2016, 41(2): 63-67.
[10]Zhang Binbin, Jiang Zhouhua, Li Huabing et al. Precipitation behavior and phase transformation of hyper duplex stainless steel UNS S32707 at nose temperature[J]. Materials Characterization, 2017, 129: 31-39.
[11]Jeon Soon-Hyeok, Kim Hye-Jin, Park Yong-Soo. Effects of inclusions on the precipitation of chi phases and intergranular corrosion resistance of hyper duplex stainless steel[J]. Corrosion Science, 2014, 87: 1-5.
[12]Escriba D M, Materna-Morris E, Plaut R L, et al. Chi-phase precipitation in a duplex stainless steel[J]. Materials Characterization, 2009, 60(11): 1214-1219.
[13]Jang Younghwan, Kim Sangshilc, Lee Jehyun. Effect of different Mo contents on tensile and corrosion behaviors of CD4MCU cast duplex stainless steels[J]. Metallurgical and Materials Transactions A, 2005, 36(5): 1229-1236.
[14]梁田. 核电用双相不锈钢中σ相析出机制研究[D]. 北京: 中国科学院大学, 2013.
Liang Tian. The precipitation mechanism of σ phase in duplex stainless steel for nuclear power station[D]. Beijing: University of Chinese Academy of Sciences, 2013.
[15]Ni Y, Jin Y M, Khachaturyan A G. The transformation sequences in the cubic→tetragonal decomposition[J]. Acta Materialia, 2007, 55(14): 4903-4914.
[16]Yang S M, Chen Y C, Chen C H, et al. Microstructural characterization of δ/γ/σ/γ₂/χ phases in silver-doped 2205 duplex stainless steel under 800 ℃ aging[J]. Journal of Alloys and Compounds, 2015, 633: 48-53.
[17]马明. 双相不锈钢热变形行为及组织演变[D]. 沈阳: 东北大学, 2016.
Ma Ming. Hot deformation behavior and microstructural evolution of duplex stainless steels[D]. Shenyang: Northeastern University, 2016.
[18]Biezma M V, Martin U, Linhardt P. Non-destructive techniques for the detection of sigma phase in duplex stainless steel: A comprehensive review[J]. Engineering Failure Analysis, 2021, 122: 105227.
[19]Llorca-Isern N, Lopez-Luque H, Lopez-Jimenez I, et al. Identification of sigma and Chi phases in duplex stainless steels[J]. Materials Characterization, 2016, 112: 20-29.

2507超级双相不锈钢中第二相的析出行为

Precipitation behavior of second phase in super duplex stainless steel 2507

PDF

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

本文评价

[1]	牛红康, 王迪玮, 田青超. Ni、Fe合金化及时效时间对锰铜基阻尼合金相变行为的影响[J]. 金属热处理, 2022, 47(5): 1-6.
[2]	陈东俊, 李广阳, 刘刚. 时效处理对AlSi9Cu3压铸铝合金组织和力学性能的影响[J]. 金属热处理, 2022, 47(4): 53-56.
[3]	白青青, 张志宏, 郑淮北, 王英虎. 2507超级双相不锈钢中σ相的析出行为[J]. 金属热处理, 2022, 47(4): 108-115.
[4]	胡静, 陶科, 杨庆松, 李刚, 张德汉. 机械抛光后的时效工艺对0Cr25Al5电热合金拉拔性能的影响[J]. 金属热处理, 2022, 47(4): 171-177.
[5]	杨春苗, 王珊, 王淑慧, 李延珍, 刘文文. RRA过程中预时效时间对7A85铝合金组织性能的影响[J]. 金属热处理, 2022, 47(3): 44-47.
[6]	王英虎, 郑淮北, 白青青, 宋令玺, 姚斌, 王利伟. 无磁钻铤用Cr-Mn-Ni-N系高氮钢平衡凝固相变与析出行为[J]. 金属热处理, 2022, 47(3): 173-180.
[7]	何婵, 邹德宁, 赵洁, 陈兴润, 钱张信. 2507超级双相不锈钢的流变应力本构关系及热加工图[J]. 金属热处理, 2022, 47(1): 94-99.
[8]	谭皎, 张伯岩, 朱文光, 孙巧艳. 时效温度对Ti-5Al-4Zr-10Mo-3Cr钛合金微观组织及力学性能的影响[J]. 金属热处理, 2022, 47(1): 217-225.
[9]	丁轩, 甘玉荣, 蒋爱娟, 李辉, 杨明球. 时效处理对7A55铝合金微观组织和性能的影响[J]. 金属热处理, 2021, 46(9): 120-123.
[10]	王晓东, 陈蕴博, 左玲立, 游龙, 陈冲, 毛丰, 张峻嘉. V-N微合金化CrSiMn系低合金铸钢中的析出行为[J]. 金属热处理, 2021, 46(8): 15-19.
[11]	高志喆, 程福超, 冯一帆, 孙健, 王永金. 时效时间对低密度超高锰铸钢组织性能的影响[J]. 金属热处理, 2021, 46(8): 115-120.
[12]	韩茜, 李茂扬, 秦国飞, 李旭东, 董超, 张美丽, 代卫丽. 固溶时效处理对8030铝合金导线组织性能的影响[J]. 金属热处理, 2021, 46(8): 125-132.
[13]	杨晓伟, 陈焕德, 周云, 张宇. 轧制工艺对V-Nb微合金化HRB600E钢筋组织及性能的影响[J]. 金属热处理, 2021, 46(8): 150-155.
[14]	张可人, 许晓静, 张洁. 多级固溶时效对7×××系超高强冷挤压铝合金组织性能的影响[J]. 金属热处理, 2021, 46(7): 165-167.
[15]	王玲奇, 何燕霖, 潘乐. 回火温度对高氮不锈轴承钢显微组织与力学性能的影响[J]. 金属热处理, 2021, 46(6): 8-13.