激光熔覆Fe基非晶合金涂层裂纹分析

doi:10.13251/j.issn.0254-6051.2022.05.044

金属热处理 ›› 2022, Vol. 47 ›› Issue (5): 252-256.DOI: 10.13251/j.issn.0254-6051.2022.05.044

激光熔覆Fe基非晶合金涂层裂纹分析

欧阳昌耀¹, 白峭峰¹, 韩斌慧², 闫献国¹

1.太原科技大学机械工程学院, 山西太原 030024;
2.西安航空职业技术学院汽车工程学院, 陕西西安 710089

收稿日期:2021-12-24 修回日期:2022-03-14 出版日期:2022-05-25 发布日期:2022-06-16
通讯作者: 韩斌慧,教授,博士,E-mail: liuyang123vi@126.com
作者简介:欧阳昌耀(1997—),男,硕士研究生,主要研究方向为激光表面制造技术,E-mail: ouyangcy123@163.com。
基金资助:
陕西省自然科学基础研究计划(2020JM-713);山西省重点研发计划(201903D121051)

Analysis of cracks in laser clad Fe-based amorphous alloy coating

Ouyang Changyao¹, Bai Qiaofeng¹, Han Binhui², Yan Xianguo¹

1. School of Mechanical Engineering, Taiyuan University of Science and Technology, Taiyuan Shanxi 030024, China;
2. School of Automotive Engineering, Xi'an Aeronautical Polytechnic Institute, Xi'an Shaanxi 710089, China

Received:2021-12-24 Revised:2022-03-14 Online:2022-05-25 Published:2022-06-16

摘要/Abstract

摘要： 使用激光熔覆技术在304不锈钢基材表面熔覆铁基非晶合金涂层时产生了裂纹,通过对裂纹周围元素、硬度和裂纹易萌生处析出物的定性分析,研究了涂层裂纹成形机理。结果表明,涂层主要有α-Fe、α-Cr、碳化物(M₇C₃、M₅C₂)、硅化物(CrSi₂、FeSi)等物相。裂纹主要由热影响区较大的热应力以及C、Si元素偏析而成的高熔点及高硬度的碳硅化物造成,裂纹带附近组织较为疏松且存在较多的缝隙和孔隙,同时硬质相结合不牢固,使得裂纹带附近硬度相较于同一水平其他无缺陷处的要低。

关键词: 激光熔覆, Fe基非晶合金, 涂层物相, 裂纹

Abstract: Cracks occurred when Fe-based amorphous alloy coating was cladding on the surface of 304 stainless steel substrate by using laser cladding technology. The crack forming mechanism was studied by means of qualitative analysis of the elements, hardness and precipitates around the cracks. The results show that the coating mainly contains α-Fe, α-Cr, carbides (M₇C₃, M₅C₂), silicides (CrSi₂, FeSi) and other phases. The cracks are mainly caused by the large thermal stress in the heat-affected zone and the high melting point and high hardness carbon silicide formed by the segregation of C and Si elements. The structure near the crack zone is relatively loose and there are more gaps and pores. At the same time, the combination of the hard phase is not strong, so that the hardness near the crack zone is lower than that of other defect-free areas at the same level.

Key words: laser cladding, Fe-based amorphous alloy, coating phase, crack

中图分类号:

TG174.4

欧阳昌耀, 白峭峰, 韩斌慧, 闫献国. 激光熔覆Fe基非晶合金涂层裂纹分析[J]. 金属热处理, 2022, 47(5): 252-256.

Ouyang Changyao, Bai Qiaofeng, Han Binhui, Yan Xianguo. Analysis of cracks in laser clad Fe-based amorphous alloy coating[J]. Heat Treatment of Metals, 2022, 47(5): 252-256.

参考文献

[1]Si J J, Mei J N, Wang R S, et al. Fe-B-Si-Zr bulk metallic glasses with ultrahigh compressive strength and excellent soft magnetic properties[J]. Materials Letters, 2016, 181: 282-284.
[2]Huang B, Yang Y, Wang A D, et al. Saturated magnetization and glass forming ability of soft magnetic Fe-based metallic glasses[J]. Intermetallics, 2017, 84: 74-81.
[3]Williams E, Lavery N. Laser processing of bulk metallic glass: A review[J]. Journal of Materials Processing Technology, 2017, 247: 73-91.
[4]Xiang X, Mi G, Xiong L, et al. Morphologies, microstructures and properties of TiC particle reinforced Inconel 625 coatings obtained by laser cladding with wire[J]. Journal of Alloys and Compounds, 2017, 740: 16-27.
[5]鲁耀钟, 雷卫宁, 任维彬, 等. 激光熔覆Inconel718合金裂纹分析及裂纹控制研究[J]. 表面技术, 2020, 49(9): 233-243.
Lu Yaozhong, Lei Weining, Ren Weibin, et al. Crack analysis and control of laser cladding Inconel718 alloy[J]. Surface Technology, 2020, 49(9): 233-243.
[6]梁鹏, 游娜, 郭计山. 球墨铸铁的激光熔覆研究[J]. 内燃机与配件, 2020(16): 103-105.
Liang Peng, You Na, Guo Jishan. The researching of laser cladding on ductile cast iron[J]. Internal Combustion Engines and Parts, 2020(16): 103-105.
[7]汪明文. Fe基非晶合金及复合粉末激光熔覆和性能研究[D]. 福州: 福建农林大学, 2016.
Wang Mingwen. Laser cladding and properties of Fe-based amorphous alloys and composite powders[D]. Fuzhou: Fujian Agriculture and Forestry University, 2016.
[8]Chen Z, Li R, Gu J, et al. Laser cladding of Ni60+17-4PH composite for a cracking-free and corrosion resistive coating[J]. International Journal of Modern Physics B, 2020, 34(1-3): 2040042.
[9]Shi B, Li T, Wang D, et al. Investigation on crack behavior of Ni60A alloy coating produced by coaxial laser cladding[J]. Journal of Materials Science, 2021, 56: 13323-13336.
[10]Martinez H A, Francis J A, Stevens N P C. An assessment of residual stress mitigation strategies for laser clad deposits[J]. Materials Science and Technology, 2016, 32(14): 1484-1494.
[11]王伟, 孙文磊, 于江通, 等. 激光熔覆工艺涂层裂纹控制的研究现状[J]. 热加工工艺, 2020, 49(20): 1-5.
Wang Wei, Sun Wenlei, Yu Jiangtong, et al. Research status of crack control of laser cladding process coatings[J]. Hot Working Technology, 2020, 49(20): 1-5.
[12]吴祖鹏. Ni60A合金激光熔覆裂纹气孔控制方法研究[D]. 大连: 大连理工大学, 2020.
Wu Zupeng. Study on crack and porosity control methods of laser cladding Ni60A alloy coating[D]. Dalian: Dalian University of Technology, 2020.
[13]刘鹏良. 激光熔覆裂纹产生影响因素与控制方法应用研究[D]. 乌鲁木齐: 新疆大学, 2019.
Liu Pengliang. Research on the influencing factors and control methods of laser cladding cracks[D]. Urumqi: Xinjiang University, 2019.
[14]胡立威. 激光熔覆制备Zr-Cu-Ni-Al非晶/晶态复合涂层及其耐蚀性研究[D]. 秦皇岛: 燕山大学, 2019.
Hu Liwei. The preparation and the anticorrosion properties of the Zr-Cu-Ni-Al metallic glasses/crystalline composite coatings by laser cladding[D]. Qinhuangdao: Yanshan University, 2019.

[1]	石淑婷, 舒林森, 何雅娟, 王家胜. 激光功率对27SiMn钢熔覆层组织与性能的影响[J]. 金属热处理, 2022, 47(5): 194-198.
[2]	董月, 舒林森. 离焦量对MoS₂改性Fe-Cr-Mo-Si合金涂层组织与性能的影响[J]. 金属热处理, 2022, 47(5): 246-251.
[3]	石如星, 林乙丑, 张沛, 齐国赛, 于文平, 苏文博. 旋回破碎机4Cr13钢主轴套激光淬火后的磨削裂纹分析[J]. 金属热处理, 2022, 47(5): 257-261.
[4]	赵子硕, 武美萍, 缪小进, 崔宸, 龚玉玲. 激光功率对FeCoNiCrMo高熵合金/氧化石墨烯复合涂层组织及耐腐蚀性能的影响[J]. 金属热处理, 2022, 47(4): 251-257.
[5]	杨杰, 汪西, 周杰, 武建祥, 屈志远, 代合平, 彭海军. 转向节锻件枝丫结构淬火裂纹形成机理[J]. 金属热处理, 2022, 47(4): 263-267.
[6]	林基辉, 温亚辉, 范文博, 张腾, 刘晨雨, 薛元琳. 钛合金表面激光改性技术研究进展[J]. 金属热处理, 2022, 47(3): 215-221.
[7]	董瑞, 陈林, 岑耀东, 包喜荣. 不同热处理条件下贝氏体钢的微观组织和疲劳裂纹扩展[J]. 金属热处理, 2022, 47(2): 153-158.
[8]	丁涛, 张云华, 李俊杰, 刘进, 刘艳. 不锈钢表面激光熔覆技术研究现状与展望[J]. 金属热处理, 2022, 47(2): 205-212.
[9]	卢庆亮, 王静, 戚小霞, 李燕乐, 李方义. 面向盾构机密封跑道修复的激光熔覆Fe基涂层制备工艺[J]. 金属热处理, 2022, 47(1): 202-211.
[10]	王春华, 王峰, 王凤良, 房洪杰, 杨丽娟. 多级固溶对7136-0.35La铝合金组织与性能的影响[J]. 金属热处理, 2021, 46(9): 124-128.
[11]	李礼, 叶宏, 刘越, 佘红艳, 屈威, 沈大臣, 陈梨. Cr12MoV钢表面激光熔覆Ni/Ni-WC梯度涂层的组织与耐磨性能[J]. 金属热处理, 2021, 46(9): 223-228.
[12]	龚玉玲, 武美萍, 崔宸, 缪小进. 搭接率对TC4表面Ni60A熔覆层组织性能的影响[J]. 金属热处理, 2021, 46(9): 229-233.
[13]	缪小进, 夏思海, 武美萍, 俞经虎, 赵子硕, 崔宸, 张春雷. 添加CeO₂对铝合金表面激光熔覆铝钛熔覆层性能的影响[J]. 金属热处理, 2021, 46(9): 234-240.
[14]	周建波, 张晶, 张蕾涛, 李海涛, 樊帅奇, 徐金富. 激光工艺参数对Ni60/WC涂层裂纹率及组织的影响[J]. 金属热处理, 2021, 46(9): 252-257.
[15]	马植甄, 朱佳浩, 张晖. Si对高熵合金涂层组织和高温抗氧化性能的影响[J]. 金属热处理, 2021, 46(8): 46-50.

激光熔覆Fe基非晶合金涂层裂纹分析

Analysis of cracks in laser clad Fe-based amorphous alloy coating

PDF

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

本文评价