贝氏体等温淬火对Dievar热作模具钢高温摩擦磨损性能的影响

doi:10.13251/j.issn.0254-6051.2023.02.014

摘要/Abstract

摘要： 利用贝氏体等温淬火工艺在Dievar钢中制备不同体积比例的贝/马复相微观组织,通过对显微组织、宏观/微观硬度、磨面形貌、磨屑和磨损率的分析进一步研究了贝/马复相Dievar热作模具钢的高温摩擦磨损性能并探讨其磨损机制。结果表明,Dievar钢中下贝氏体含量随等温淬火保温时间的延长而增加,其中保温3、5、10 min时下贝氏体体积占比分别为32%、45%、63%。贝/马复相试样相比于传统油淬试样具有更高的回火抗性,不同等温试样硬度值均高于传统油淬试样硬度值。同等磨损条件下,等温淬火Dievar钢相较于常规热处理Dievar钢耐磨性更加优异。在400~600 ℃高温摩擦磨损试验条件下,Dievar钢表面氧化物为Fe₂O₃和Fe₃O₄。Dievar钢400~500 ℃高温磨损机制为磨粒-轻微氧化磨损;随着温度升高,氧化物颗粒尺寸变大,磨粒磨损加剧。当温度升至600 ℃时,常规油淬试样磨损机制为磨粒-氧化磨损,以磨粒磨损为主;而等温淬火试样磨损机制则以氧化磨损为主。

关键词: Dievar热作模具钢, 等温淬火, 贝/马复相组织, 硬度, 高温磨损机制, 高温磨损性能

Abstract: Mixed microstructure with different volume fractions of lower bainite and martensite was produced in Dievar steel by austempering, and then the high temperature frictional wear performance and mechanism of the Dievar steel were investigated based on the microstructure identification, hardness evaluation, worn surface morphology and wear rate analysis. The results show that the volume fraction of lower bainite in the Dievar steel increases with the increase of austempering time, where the bainitic volume fractions are 32%, 45% and 63% with isothermal holding for 3, 5 and 10 min respectively. Compared to the conventional oil quenched specimens, the specimens with the mixed microstructure have higher tempering resistance. The hardness values for austempered specimens are higher than that of oil quenched ones. In addition, the austempered specimens exhibit better wear resistance compared to the conventional oil quenched ones under the same wear condition. Under the high temperature friction and wear test conditions of 400-600 ℃, the surface oxides of the Dievar steel are Fe₂O₃ and Fe₃O₄. The high temperature wear mechanism at 400-500 ℃ for the Dievar steel is abrasive-slight oxidation wear. As the temperature increases, the size of oxide particles becomes larger and the abrasive wear is strengthened. When the temperature approaches to 600 ℃, the high temperature wear mechanism for the conventional oil quenched specimens is still maintained as abrasive-oxidation wear, mainly abrasive wear, however, it alters to the oxidation wear for the austempered specimens.

Key words: Dievar hot working die steel, austempering, bainite/martensite mixed microstructure, hardness, high temperature wear mechanism, high temperature wear property

中图分类号:

TG142.2

杨柳, 谢奕心, 鞠玉琳, 魏琪, 曹甫洋, 罗锐, 袁志钟, 程晓农. 贝氏体等温淬火对Dievar热作模具钢高温摩擦磨损性能的影响[J]. 金属热处理, 2023, 48(2): 85-93.

Yang Liu, Xie Yixin, Ju Yulin, Wei Qi, Cao Fuyang, Luo Rui, Yuan Zhizhong, Cheng Xiaonong. Effect of austempering on high temperature frictional wear property of Dievar hot working die steel[J]. Heat Treatment of Metals, 2023, 48(2): 85-93.

参考文献

[1]Guan H, Luo A H. Development and application of a new hot-work die steel for hot stamping[J]. Baosteel Technology Research, 2017, 11(2): 11-17.
[2]Chen S H, Li S, Wu X C. High temperature friction and wear property of hot stamping tool steel SDCM[J]. Tribology, 2016, 36(5): 538-545.
[3]Zhou Q C, Wu X C, Shi N N, et al. Microstructure evolution and kinetic analysis of DM hot-working die steels during tempering[J]. Materials Science and Engineering A, 2011, 528(18): 5696-5700.
[4]Mao W W, Ning A G, Guo H J. Nanoscale precipitates and comprehensive strengthening mechanism in AISI H13 steel[J]. International Journal of Minerals Metallurgy & Materials, 2016, 23(9): 1056-1064.
[5]Mao Mingtao, Guo Hanjie, Wang Fei, et al. Chemical composition and structural identification of primary carbides in as-cast H13 steel[J]. International Journal of Minerals Metallurgy and Materials, 2019, 26 (7): 839-848.
[6]Erry Yulian T Adesta, Muhammad Riza, Avicena. Comparative investigation on tool wear during end milling of AISI H13 steel with different tool path strategies[J]. IOP Conference Series: Materials Science and Engineering, 2018, 343: 012020.
[7]Li Hongbo, Li Ban, Deng Chengxu, et al. Morphology and wear resistance of HVOF sprayed H13-WC/Ni gradient coating on H13 steel surface[J]. Journal of Physics: Conference Series, 2019, 1213(5): 052020.
[8]Liu Yu, Qin Shengwei, Zuo Xunwei. Investigation of quenching stress of 42CrMo treated by alternately timed quenching process[J]. Heat Treatment and Surface Engineering, 2015, 1(1-2): 23-31.
[9]杨福宝, 白秉哲, 刘东雨, 等. 无碳化物贝氏体-马氏体复相高强度钢的组织与性能[J]. 金属学报, 2004, 40(3): 296-300.
Yang Fubao, Bai Bingzhe, Liu Dongyu, et al. Microstructure and properties of a carbide-free bainite/martensite ultra-high strength steel[J]. Acta Metallurgica Sinica, 2004, 40(3): 296-300.
[10]Matsumura O, Sakuma Y, Takechi H. Trip and its kinetic aspects in austempered 0.4C-1.5Si-0.8Mn steel[J]. Scripta Metallurgica, 1987, 21(10): 1301-1306.
[11]田保红, 郑世安. 马氏体-下贝氏体复相组织强韧化机理研究及实际应用[J]. 河南科技大学学报: 自然科学版, 1993(4): 29-34.
Tian Baohong, Zheng Shian. Strengthening and toughening mechanism of martensite-lower bainite duplex structure and its application[J]. Journal of Henan University of Science and Technology (Natural Science), 1993(4): 29-34.
[12]崔君军, 陈礼清, 李海智, 等. 等温淬火低合金贝氏体球墨铸铁的回火组织与力学性能[J]. 金属学报, 2016, 52(7): 778-786.
Cui Junjun, Chen Liqing, Li Haizhi, et al. Tempering structure and mechanical properties of isothermally quenched low alloy bainite ductile iron[J]. Acta Metallurgica Sinica, 2016, 52(7): 778-786.
[13]何文超, 李志敏, 张旭, 等. 贝氏体等温淬火对H13热作模具钢组织及热疲劳性能的影响[J]. 材料热处理学报, 2021, 42(5): 81-87.
He Wenchao, Li Zhimin, Zhang Xu, et al. Effect of bainite isothermal quenching on microstructure and thermal fatigue performance of H13 hot working die steel[J]. Transactions of Materials and Heat Treatment, 2021, 42(5): 81-87.
[14]张朋, 张福成, 王天生, 等. 低碳合金钢表面硬贝氏体的制备及其组织特征[J]. 材料热处理学报, 2009, 30(4): 44-47.
Zhang Peng, Zhang Fucheng, Wang Tiansheng, et al. Preparation and microstructural characterization of hard bainite in surface layer of low-carbon alloy steel[J]. Transactions of Materials and Heat Treatment, 2009, 30(4): 44-47.
[15]张朋, 张福成, 王天生. 渗碳 20CrMnMoAl 钢表面硬贝氏体的制备及其组织特征[J]. 金属学报, 2011, 47(8): 1038-1045.
Zhang Peng, Zhang Fucheng, Wang Tiansheng, et al. Preparation and microstructure of hardbainite in surface layer of carburized 20CrMnMoAl steel[J]. Acta Metallurgica Sinica, 2011, 47(8): 1038-1045.
[16]刘健波, 张学宾, 杨留栓, 等. 等温淬火时间对 D2 钢组织与力学性能的影响[J]. 材料热处理学报, 2019, 40(8): 110-115.
Liu Jianbo, Zhang Xuebin, Yang Liushuan, et al. Effect of austempering time on microstructure and mechanical properties of D2 steel[J]. Transactions of Materials and Heat Treatment, 2019, 40(8): 110-115.
[17]张君, 董笑鹏. 钢的(M+B)复相热处理技术研究[J]. 机电产品开发与创新, 2007, 20(5): 3-4.
Zhang Jun, Dong Xiaopeng. Development of steel in (M+B) duplex heat treatment[J]. Development and Innovation of Machinery and Electrical Products, 2007, 20(5): 3-4.
[18]刘波, 黄晓艳. 国家标准《金属材料硬度值的换算》解读[J]. 铸造技术, 2018, 39(3): 736-738.
Liu Bo, Huang Xiaoyan. Interpretation of national standard “conversion of hardness values of metallic materials”[J]. Foundry Technology, 2018, 39(3): 736-738.
[19]Wilson J E, Stott F H, Wood G C. The development of wear-protective oxides and their influence on sliding friction[J]. Proceedings of the Royal Society A: Mathematical, Physical and Engineering Science, 1980, 369(1739): 557-574.
[20]吴帅, 付航涛, 连勇, 等. 一种新型热作模具钢的高温磨损性能研究[J]. 摩擦学学报, 2016, 36(1): 104-109.
Wu Shuai, Fu Hangtao, Lian Yong, et al. Investigation on high temperature wear behavior of a newly developed hot-work tool steel[J]. Tribology, 2016, 36(1): 104-109.
[21]Ma Ye, Yue Caichao, Liu Ming, et al. Effects of heat treatment on microstructure and mechanical properties of new hot work die steel[J]. Die and Mould Manufacture, 2018, 18(2): 82-85.
[22]Archard J F, Hirst W. The wear of metals under unlubricated conditions[J]. Proceedings of the Royal Society of London Series A Mathematical and Physical Sciences, 1956, 236 (1206): 397-410.
[23]Wei Minxian, Wang Shuqi, Cui Xianghong. Comparative research on wear characteristics of spheroidal graphite cast iron and carbon steel[J]. Wear, 2012, 274: 84-93.
[24]Wang Shuqi, Wang Feng, Cui Xianghong, et al. Effect of secondary carbides on oxidation wear of the Cr-Mo-V cast steels[J]. Materials Letters, 2008, 62: 279-281.
[25]张秋阳, 丁红燕, 周广宏, 等. 含Fe₂O₃摩擦层的促进形成对H13和45钢磨损性能的影响[J]. 摩擦学学报, 2017, 37(6): 823-830.
Zhang Qiuyang, Ding Hongyan, Zhou Guanghong, et al. Formation of tribo-layer in the presence of Fe₂O₃ particles and its influence on wear performance of H13 and 45 steel[J]. Tribology, 2017, 37(6): 823-830.
[26]Wang Shuqi, Wei Minxian, Zhao Yutao. Effects of the tribo-oxide and matrix on dry sliding wear characteristics and mechanisms of a cast steel[J]. Wear, 2010, 269(5/6): 424-434.
[27]王树奇, 崔向红, 陈康敏, 等. 精铸热锻模具钢的合金成分设计及其高温磨损性能研究[J]. 摩擦学学报, 2006, 26(4): 382-386.
Wang Shuqi, Cui Xianghong, Chen Kangmin, et al. Alloying design and high-temperature wear property of cast hot-forging die steel[J]. Tribology, 2006, 26(4): 382-386.
[28]陈磊, 姜伟, 崔向红, 等. 不同滑动条件下H13钢的高温磨损行为[J]. 润滑与密封, 2021, 46(4): 122-129.
Chen Lei, Jiang Wei, Cui Xianghong, et al. High temperature wear behaviors of H13 steel under different sliding conditions[J]. Lubrication Engineering, 2021, 46(4): 122-129.
[29]段明伟, 王志航, 黄英豪, 等. H13钢激光涂覆层的高温磨损性能[J]. 钢铁钒钛, 2019, 40(3): 136-141.
Duan Mingwei, Wang Zhihang, Huang Yinghao, et al. High temperature wear behavior of laser coating on H13 steel[J]. Iron Steel Vanadium Titanium, 2019, 40(3): 136-141.
[30]Wei M X, Wang F, Wang S Q, et al. Comparative research on the elevated-temperature wear resistance of a cast hot-working die steel[J]. Materials and Design, 2009, 30(9): 3608-3614.
[31]隋鹤龙. 新型高Cr热作模具钢的组织与性能[D]. 长春: 吉林大学, 2006.
[32]谢冬柏, 高飞, 王福会, 等. H13 钢的马氏体/贝氏体组织与性能[J]. 金属热处理, 2002, 27(5): 11-14.
Xie Dongbai, Gao Fei, Wang Fuhui, et al. M/B microstructure and mechanical properties of H13 steel[J]. Heat Treatment of Metals, 2002, 27(5): 11-14.
[33]桂晓露, 张宝祥, 高古辉, 等. Q-P-T处理贝氏体/马氏体复相高强钢疲劳断裂特性研究[J]. 金属学报, 2016, 52(9): 1036-1044.
Gui Xiaolu, Zhang Baoxiang, Gao Guhui, et al. Fatigue behavior of bainite/martensite multiphase high strength steel treated by quenching-partitioning-tempering process[J]. Acta Metallurgica Sinica, 2016, 52(9): 1036-1044.