Q345/40Cr钢双金属环件的热处理工艺及组织性能

doi:10.13251/j.issn.0254-6051.2023.03.032

摘要/Abstract

摘要： 对热辗扩Q345钢/40Cr钢双金属环件进行860~950 ℃淬火和520~610 ℃回火处理,并对热处理后的组织和性能进行了观察、分析和测试。双金属环件在890 ℃淬火后,进行不同温度回火,测试其力学性能。结果表明,淬火后晶粒细化,随着淬火温度的升高,晶粒变大。40Cr钢硬度先下降后升高,Q345钢硬度稍微下降,结合层靠近40Cr钢一侧硬度先下降后升高,靠近Q345钢一侧硬度下降。在860 ℃淬火时,40Cr钢一侧合金元素未完全溶解,在890 ℃淬火效果最佳。随着回火温度的升高,双金属环件的抗拉强度和硬度下降;40Cr钢的伸长率提高,Q345钢和结合层的伸长率先升高后降低;双金属环件的冲击性能提高。结合层断口在Q345钢一侧。双金属环件在890 ℃淬火、550 ℃回火后综合性能最好,可以满足实际使用要求。

关键词: 双金属环件, 淬火温度, 回火温度, 显微组织, 力学性能

Abstract: Rolled Q345/40Cr bimetal rings were quenched at 860-950 ℃ and tempered at 520-610 ℃, the microstructure and properties after heat treatment was observed, analyzed and tested. The results show that the grains are refined after quenching, and coarsened with the increase of quenching temperature. The hardness of the 40Cr steel and hardness of its adjacent bonding layer decreases first and then increases, while the hardness of the Q345 steel decreases slightly, and the hardness of its adjacent bonding layer decreases. The alloying elements in the 40Cr steel side dissolves incompletely when quenched at 860 ℃, and the optimal quenching temperature is 890 ℃. The results of mechanical properties tests show that after 890 ℃ quenching and with the increase of tempering temperature, the tensile strength and hardness of the bimetal ring decrease, the elongation of the Q345 steel and its adjacent bonding layer increases first and then decreases, and the impact property of the bimetal ring is improved. The fracture position of bonding layer is on the side of Q345 steel. The comprehensive performance of the bimetal ring is the best after quenching at 890 ℃ and tempering at 550 ℃, which meets the practical application requirements.

Key words: bimetal ring, quenching temperature, tempering temperature, microstructure, mechanical properties

中图分类号:

TG156

常耀东, 齐会萍, 贾燕龙, 李永堂, 武永红. Q345/40Cr钢双金属环件的热处理工艺及组织性能[J]. 金属热处理, 2023, 48(3): 195-202.

Chang Yaodong, Qi Huiping, Jia Yanlong, Li Yongtang, Wu Yonghong. Heat treatment process and microstructure and properties of Q345/40Cr bimetal ring[J]. Heat Treatment of Metals, 2023, 48(3): 195-202.

参考文献

[1]华林, 钱东升. 轴承环轧制成形理论和技术[J]. 机械工程学报, 2014, 50(16): 70-76.
Hua Lin, Qian Dongsheng. Ring rolling forming theory and technology for bearing[J]. Journal of Mechanical Engineering, 2014, 50(16): 70-76.
[2]Hua Lin, Pan Libo, Lan Jian. Researches on the ring stiffness condition in radial-axial ring rolling[J]. Journal of Materials Processing Technology, 2009(5): 2570-2575.
[3]Hua Lin, Deng Jiadong, Qian Dongsheng, et al. Using upper bound solution to analyze force parameters of three-roll cross rolling of rings with small hole and deep groove[J]. The International Journal of Advanced Manufacturing Technology, 2015, 76(1): 353-366.
[4]李永堂, 丁双凤, 付建华, 等. 基于铸坯的42CrMo环件辗扩成形工艺热力耦合分析[J]. 材料热处理学报, 2017, 38(1): 171-177.
Li Yongtang, Ding Shuangfeng, Fu Jianhua, et al. Thermo-mechanical coupling analysis of 42CrMo ring rolling based on cast blank[J]. Transactions of Materials and Heat Treatment, 2017, 38(1): 171-177.
[5]李永堂, 齐会萍, 付建华, 等. 42CrMo钢铸造环坯辗扩成形理论与工艺分析[J]. 机械工程学报, 2014, 50(2): 77-85.
Li Yongtang, Qi Huiping, Fu Jianhua, et al. Theoretical and process analyses on the cast-blank rolling forming of 42CrMo bearing rings[J]. Journal of Mechanical Engineering, 2014, 50(2): 77-85.
[6]Liang Lei, Guo Lianggang, Liu Zhaohui, et al. On a precision forming criterion for groove-section profiled ring rolling process[J]. Journal of Materials Processing Technology, 2021, 296: 117207.
[7]Li Yongtang, Ju Li, Qi Huiping, et al. Technology and experiments of 42CrMo bearing ring forming based on casting ring blank[J]. Chinese Journal of Mechanical Engineering, 2014, 27(2): 418-427.
[8]王明礼. 42CrMo轴承套圈毛坯的铸辗复合工艺[J]. 轴承, 2013(12): 19-20.
Wang Mingli. Casting-rolling compound process of 42CrMo bearing ring blank[J]. Bearing, 2013(12): 19-20.
[9]秦芳诚, 李永堂, 齐会萍, 等. 基于铸坯的25Mn钢环件热辗扩成形力学性能分析[J]. 锻压装备与制造技术, 2015, 50(4): 78-81.
Qin Fangcheng, Li Yongtang, Qi Huiping, et al. Analysis of mechanical properties of hot rolling process for as-cast 25Mn steel ring[J]. China Metalforming Equipment and Manufacturing Technology, 2015, 50(4): 78-81.
[10]尉潇健, 齐会萍, 李永堂, 等. 离心铸造辗扩成形42CrMo钢环件热处理后的组织与性能[J]. 金属热处理, 2016, 41(12): 25-28.
Wei Xiaojian, Qi Huiping, Li Yongtang, et al. Microstructure and properties of 42CrMo steel ring formed by centrifugal casting and ring rolling after heat treatment[J]. Heat Treatment of Metals, 2016, 41(12): 25-28.
[11]秦芳诚. 环件铸辗复合成形中Q235B钢热变形及组织演变研究[D]. 太原: 太原科技大学, 2014.
Qin Fangcheng. Study on hot deformation and microstructure evolution of Q235B steel in ring casting and rolling composite forming[D]. Taiyuan: Taiyuan University of Science and Technology, 2014.
[12]齐会萍, 李永堂, 华林, 等. 环形零件辗扩成形工艺研究现状与发展趋势[J]. 机械工程学报, 2014, 50(14): 75-80.
Qi Huiping, Li Yongtang, Hua Lin, et al. Research status and developing trends on the rolling forming process of ring parts[J]. Journal of Mechanical Engineering, 2014, 50(14): 75-80.
[13]秦芳诚, 齐会萍, 李永堂, 等. 环形零件短流程铸辗复合成形技术研究进展[J]. 材料导报, 2020, 34(19): 19152-19165.
Qin Fangcheng, Qi Huiping, Li Yongtang, et al. Advances in compact cast-rolling forming of ring-shape parts[J]. Materials Reports, 2020, 34(19): 19152-19165.
[14]陈聪, 汪选国. 热处理对离心铸造高铬铸铁-不锈钢双金属管界面组织及性能的影响[J]. 热加工工艺, 2019, 48(4): 222-224, 229.
Chen Cong, Wang Xuanguo. Influence of heat treatment on microstructure and properties of composite interface of bimetal pipe made of high chromium cast iron and stainless steel by centrifugally casting[J]. Hot Working Technology, 2019, 48(4): 222-224, 229.
[15]陈林恒, 汤启波, 武会宾, 等. 淬火工艺对含Ni中锰钢组织和性能的影响[J]. 金属热处理, 2022, 47(2): 159-163.
Chen Linheng, Tang Qibo, Wu Huibin, et al. Effect of quenching process on microstructure and mechanical properties of medium manganese steel bearing Ni[J]. Heat Treatment of Metals, 2022, 47(2): 159-163
[16]韩星, 杨英春, 迟洋波, 等. 双金属层状复合铸锭热处理研究[J]. 铝加工, 2019(3): 19-22, 33.
Han Xing, Yang Yingchun, Chi Yangbo, et al. Study on heat treatment of bimetallic layered composite ingots[J]. Aluminum Fabrication, 2019(3): 19-22, 33.
[17]陈刚, 姚远超, 贾寓真, 等. 热处理工艺对双金属带锯条背材30Cr4MoNiV钢组织和性能的影响[J]. 金属热处理, 2022, 47(1): 266-271.
Chen Gang, Yao Yuanchao, Jia Yuzhen, et al. Effect of heat treatment process on microstructure and properties of base steel 30Cr4MoNiV for bi-metal band saw blade[J]. Heat Treatment of Metals, 2022, 47(1): 266-271.
[18]战中学, 刘泽林, 刘国忠, 等. 40Cr热处理工艺剖析[J]. 中国高新技术企业, 2014(6): 42-44.
[19]郝震宇, 孙维, 汪开忠, 等. 热处理对Q345E钢风电锻件组织和力学性能的影响[J]. 热加工工艺, 2017, 46(10): 192-195, 199.
Hao Zhenyu, Sun Wei, Wang Kaizhong, et al. Influence of heat treatment on microstructure and mechanical properties of Q345E steel forgings for wind power[J]. Hot Working Technology, 2017, 46(10): 192-195, 199.
[20]梁慧慧, 李光. Q345钢热处理组织与性能研究[J]. 铸造技术, 2018, 39(9): 2087-2090.
Liang Huihui, Li Guang. Study on microstructure and properties of heat treatment Q345 steel[J]. Foundry Technology, 2018, 39(9): 2087-2090.
[21]赵勇桃, 姜亚君, 鲁海涛, 等. 热处理对国外P92钢显微组织及晶粒度的影响[J]. 金属热处理, 2020, 45(9): 57-62.
Zhao Yongtao, Jiang Yajun, Lu Haitao, et al. Effect of heat treatment on microstructure and grain size of imported P92 steel[J]. Heat Treatment of Metals, 2020, 45(9): 57-62.
[22]殷军伟, 周健, 蒋业华, 等. 热处理工艺对5Cr5Mo2V钢组织与性能的影响[J]. 金属热处理, 2021, 46(2): 55-60.
Yin Junwei, Zhou Jian, Jiang Yehua, et al. Effect of heat treatment process on microstructure and properties of 5Cr5Mo2V steel[J]. Heat Treatment of Metals, 2021, 46(2): 55-60.
[23]王世凯, 王睿, 康燕, 等. 淬火温度对Cr5MoVNi钢组织和性能的影响[J]. 金属热处理, 2022, 47(9): 125-130.
Wang Shikai, Wang Rui, Kang Yan, et al. Effect of quenching temperature on microstructure and properties of Cr5MoVNi steel[J]. Heat Treatment of Metals, 2022, 47(9): 125-130.
[24]Morito S, Saito H, Ogawa T, et al. Effect of austenite grain size on the morphology and crystallography of lath martensite in low carbon steels[J]. ISIJ International, 2005, 45(1): 91-94.
[25]Dhua S K, Ray A, Sarma D S. Effect of tempering temperatures on the mechanical properties and microstructures of HSLA-100 type copper-bearing steels[J]. Materials Science and Engineering A, 2001, 318(1-2): 197-210.
[26]宋歌, 吕婉姝, 刘玉荣, 等. 铬钼钢调质C90钢级小炉热处理制度研究[J]. 包钢科技, 2021, 47(3): 45-48, 57.
Song Ge, Lü Wanzhu, Liu Yurong, et al. Research on heat treatment schedule of hardening and tempering C90 steel grade chrome-molybdenum steel with rangette[J]. Science and Technology of Baotou Steel, 2021, 47(3): 45-48, 57.
[27]李灿明. 回火温度对1100 MPa钢组织和性能的影响[J]. 金属热处理, 2021, 46(4): 143-147.
Li Canming. Effect of tempering temperature on microstructure and properties of 1100 MPa steel[J]. Heat Treatment of Metals, 2021, 46(4): 143-147.
[28]王丙旭, 崔威威, 张宇, 等. 回火温度对300M钢组织和性能的影响[J]. 铸造技术, 2021, 42(8): 719-721.
Wang Bingxu, Cui Weiwei, Zhang Yu, et al. Effect of tempering temperatures on microstructure and mechanical properties of 300M steel[J]. Foundry Technology, 2021, 42(8): 719-721.
[29]秦芳诚, 齐会萍, 李永堂, 等. 42CrMo钢轴承环件铸辗成形及淬回火组织性能研究[J]. 机械工程学报, 2017, 53(2): 26-33.
Qin Fangcheng, Qi Huiping, Li Yongtang, et al. Study on microstructure and properties of 42CrMo bearing ring in cast-rolling forming and subsequent quenching and tempering[J]. Journal of Mechanical Engineering, 2017, 53(2): 26-33.
[30]武中豪. 热处理对7Cr14马氏体不锈钢组织与性能的影响[D]. 太原: 中北大学, 2021.
[31]李晴. 回火工艺参数对无碳化物贝氏体钢组织和性能的影响[D]. 西安: 西安工业大学, 2021.
[32]张凤明, 梁正伟, 何建中, 等. 贝氏体钢轨高温回火试验研究[J]. 包钢科技, 2021, 47(5): 68-71, 95.
Zhang Fengming, Liang Zhengwei, He Jianzhong, et al. Experimental research on high temperature tempering of bainite rail[J]. Science and Technology of Baotou Steel, 2021, 47(5): 68-71, 95.
[33]Zhang Han, Cheng Xiaole, Bai Bingzhe, et al. The tempering behavior of granular structure in a Mn-series low carbon steel[J]. Materials Science and Engineering A, 2011, 528(3): 920-924.
[34]黄少文, 周平, 张学民, 等. 回火热处理对低碳贝氏体钢显微组织和冲击断裂过程的影响[C]//第十二届中国钢铁年会论文集. 北京, 2019: 326-332.
[35]熊运霞. 工程机械用ZGMn13Cr2高锰钢热处理工艺研究[J]. 热加工工艺, 2020, 49(14): 128-130.
Xiong Yunxia. Study on heat treatment technology of ZGMn132Cr2 high manganese steel for construction machinery[J]. Hot Working Technology, 2020, 49(14): 128-130.