感应淬火条件下Cu-Ni低碳低合金钢的强化机制

doi:10.13251/j.issn.0254-6051.2023.04.033

金属热处理 ›› 2023, Vol. 48 ›› Issue (4): 204-210.DOI: 10.13251/j.issn.0254-6051.2023.04.033

感应淬火条件下Cu-Ni低碳低合金钢的强化机制

孙铭璇¹, 孟利¹, 张宁¹, 张波¹, 梁丰瑞², 罗小兵²

1.钢铁研究总院有限公司冶金工艺研究所, 北京 100081;
2.钢铁研究总院有限公司工程用钢研究院, 北京 100081

收稿日期:2022-09-29 修回日期:2022-12-29 发布日期:2023-05-27
通讯作者: 孟利,高级工程师,研究生导师,博士,E-mail:li_meng@126.com
作者简介:孙铭璇(1998—),女,硕士研究生,主要研究方向为钢的组织性能及强韧化机制,E-mail:15652712727@163.com。
基金资助:
国家重点研发计划(2017YFB0903901)

Strengthening mechanism of Cu-Ni-bearing low-carbon low-alloyed steel under induction quenching treatment

Sun Mingxuan¹, Meng Li¹, Zhang Ning¹, Zhang Bo¹, Liang Fengrui², Luo Xiaobing²

1. Metallurgical Technology Institute, Central Iron and Steel Research Institute, Beijing 100081, China;
2. Research Institute of Engineering Steels, Central Iron and Steel Research Institute, Beijing 100081, China

Received:2022-09-29 Revised:2022-12-29 Published:2023-05-27

摘要/Abstract

摘要： 采用电子背散射衍射(EBSD)、扫描电镜(SEM)、X射线衍射仪(XRD)和TEM原位拉伸试验等分析了含Cu-Ni低碳低合金钢经感应加热淬火＋时效的显微组织及Cu粒子与强度的关系,并对强化机制进行了量化分析。结果表明,试验钢经980 ℃感应淬火+670 ℃时效的综合性能优于1030 ℃感应淬火+680 ℃时效;含Cu-Ni低碳低合金钢呈现多种强化机制,包括沉淀强化、晶界强化、位错强化、固溶强化和点阵阻力,其中沉淀强化与晶界强化为主要强化机制,二者占比超过70%;理论计算出Cu粒子在Orowan机制中最小临界尺寸为28.50 nm,在TEM原位拉伸中观测到位错在Cu粒子周围发生塞积,并按照绕过机制与尺寸为44.57 nm的Cu粒子发生交互作用。

关键词: 含Cu-Ni钢, 感应淬火, Cu粒子, 强化机制

Abstract: Microstructure and the relationship between Cu particles and strength of the Cu-Ni-bearing low-carbon low-alloyed steel under induction-heat quenching and aging was analyzed by means of electron back-scatter diffraction(EBSD), scanning electron microscope(SEM), X-ray diffractometer(XRD) and in-situ tension in transmission electron microscope(TEM), and the quantitative analysis of strengthening mechanism was discussed. The results show that the comprehensive properties of the tested steel after induction quenching at 980 ℃ and aging at 670 ℃ is better than that induction quenching at 1030 ℃ and aging at 680 ℃.There are many strengthening mechanisms for the Cu-Ni-bearing low-carbon low-alloyed steel, including precipitation strengthening, grain size strengthening, forest dislocations strengthening, solid solution strengthening and lattice friction stress, among which precipitation strengthening and grain size strengthening are the main strengthening method, accounting for more than 70%. In theoretical calculation, the minimum critical size of Cu particles is 28.50 nm in Orowan mechanism, and the dislocation pile-up around the Cu particles, and they interact with a Cu particle with size of 44.57 nm according to the bypass mechanism during in-situ tension in TEM.

Key words: Cu-Ni-bearing steel, induction quenching, Cu particle, strengthening mechanism

中图分类号:

TG142.33

孙铭璇, 孟利, 张宁, 张波, 梁丰瑞, 罗小兵. 感应淬火条件下Cu-Ni低碳低合金钢的强化机制[J]. 金属热处理, 2023, 48(4): 204-210.

Sun Mingxuan, Meng Li, Zhang Ning, Zhang Bo, Liang Fengrui, Luo Xiaobing. Strengthening mechanism of Cu-Ni-bearing low-carbon low-alloyed steel under induction quenching treatment[J]. Heat Treatment of Metals, 2023, 48(4): 204-210.

参考文献

[1]张中武, 魏兴豪, 赵刚. 低合金高强钢的强韧化机理与焊接性能[J]. 鞍钢技术, 2018(4): 1-8.
Zhang Zhongwu, Wei Xinghao, Zhao Gang. Strengthening and toughening mechanism for high strength low alloy steel and its weldability[J]. Angang Technology, 2018(4): 1-8.
[2]陈连生, 徐静辉, 田亚强, 等. 含Cu低碳钢I&Q&P工艺处理后的组织与性能 [J]. 金属热处理, 2016, 41(8): 76-80.
Chen Liansheng, Xu Jinghui, Tian Yaqiang, et al. Effect of Cu partitioning on microstructure and mechanical properties of low-carbon steel by I&Q&P process[J]. Heat treatment of Metals, 2016, 41(8): 76-80.
[3]VanBohemen S M C, Sietsma J. Martensite formation in partially and fully austenitic plain carbon steels[J]. Metallurgical and Materials Transactions A, 2009, 40(5): 1059-1068.
[4]杜瑜宾, 胡小锋, 张守清, 等. 含1.4%Cu的HSLA钢的组织和力学性能[J]. 金属学报, 2020, 56(10): 1343-1354.
Du Yubin, Hu Xiaofeng, Zhang Shouqing, et al. Microstructure and mechanical properties of HSLA steel containing 1.4%Cu[J]. Acta Metallurgica Sinica, 2020, 56(10): 1343-1354.
[5]Fu W, Li C, Di X, et al. Improvement of Cu-rich precipitation strengthening for high-strength low carbon steel strengthened via Ti-microalloying[J]. Materials Letters, 2022, 316: 132031.
[6]Li C, Duan R, Fu W, et al. Improvement of mechanical properties for low carbon ultra-high strength steel strengthened by Cu-rich multistructured precipitation via modification to bainite[J]. Materials Science and Engineering A, 2021, 817: 141337.
[7]陈晨, 罗小兵, 梁丰瑞, 等. 淬火加热方法对含铜高强度球扁钢组织和性能的影响[J]. 热处理, 2021, 36(3): 31-36, 54.
Chen Chen, Luo Xiaobing, Liang Fengrui, et al. Effect of methods of heating for hardening on microstructure and properties of cooper-bearing high-strength flat bulb steel[J]. Heat Treatment, 2021, 36(3): 31-36, 54.
[8]朱志明, 柴锋, 梁丰瑞, 等. 低合金钢感应淬火温度场模拟与优化[J]. 钢铁研究学报, 2017, 29(1): 75-80.
Zhu Zhiming, Chai Feng, Liang Fengrui, et al. Temperature field simulation and optimization of low alloy-steel involved induction hardening[J]. Journal of Iron and Steel Research, 2017, 29(1): 75-80.
[9]柴希阳, 柴锋, 苏航, 等. 回火对感应淬火10CrNi3MoV球扁钢组织和性能的影响[J]. 金属热处理, 2015, 40(3): 77-81.
Chai Xiyang, Chai Feng, Su Hang, et al. Effects of tempering on microstructure and mechanical properties of induction hardened 10CrNi3MoV bulb flat steel[J]. Heat Treatment of Metals, 2015, 40(3): 77-81.
[10]李振团, 柴锋, 罗小兵, 等. 时效温度对Cu沉淀强化超高强海工钢力学性能的影响[J]. 材料导报, 2020, 34(6): 6132-6137.
Li Zhentuan, Chai Feng, Luo Xiaobing, et al. Effect of aging temperature on mechanical properties of ultra high strength marine engineering steel strengthened by Cu precipitation[J]. Materials Reports, 2020, 34(6): 6132-6137.
[11]刘庆冬. HSLA铁素体钢中Cu析出强化和奥氏体韧化的原子探针层析技术研究[D]. 上海: 上海大学, 2012.
Liu Qingdong. Atom probe tomography study on copper precipitation strengthening and reverse austenite toughening in HSLA ferritic steel[D]. Shanghai: Shanghai University, 2012.
[12]张正延, 柴锋, 罗小兵, 等. 调质态含Cu高强钢的强化机理及钢中Cu的析出行为[J]. 金属学报, 2019, 55(6): 783-791.
Zhang Zhengyan, Chai Feng, Luo Xiaobing, et al. The strengthening mechanism of Cu bearing high strength steel as-quenched and tempered and Cu precipitation behavior in steel[J]. Acta Metallurgica Sinica, 2019, 55(6): 783-791.
[13]Xiong Z, Timokhina I, Pereloma E. Clustering, nano-scale precipitation and strengthening of steels[J]. Progress in Materials Science, 2021, 118: 100764.
[14]Zhou R, Zhu L. Growth behavior and strengthening mechanism of Cu-rich particles in sanicro 25 austenitic heat-resistant steel after aging at 973 K[J]. Materials Science and Engineering A, 2020, 796: 139973.
[15]孙铭璇, 孟利, 张宁, 等. 低碳含Cu中厚钢板富Cu相的时效析出行为[J]. 金属热处理, 2023, 48(2): 94-102.
Sun Mingxuan, Meng Li, Zhang Ning, et al. Aging precipitation behavior of Cu-rich particles of low-carbon Cu-bearing medium and heavy steel plate[J]. Heat Treatment of Metals, 2023, 48(2): 94-102.
[16]Luo H, Wang X, Liu Z, et al. Influence of refined hierarchical martensitic microstructures on yield strength and impact toughness of ultra-high strength stainless steel[J]. Journal of Materials Science and Technology, 2020, 51: 130-136.
[17]沈俊昶, 罗志俊, 杨才福, 等. 低合金钢板条组织中影响低温韧性的“有效晶粒尺寸”[J]. 钢铁研究学报, 2014, 26(7): 70-76.
Shen Junchang, Luo Zhijun, Yang Caifu, et al. “Effective grain size” affecting low temperature toughness in lath structure of HSLA steel[J]. Journal of Iron and Steel Research, 2014, 26(7): 70-76.
[18]余永宁. 金属学原理[M]. 3版. 北京: 冶金工业出版社, 2020.
[19]张正延, 柴锋, 罗小兵, 等. 一种利用EBSD测量钢中位错密度的方法: CN108535295A[P]. 2018-09-14.
Zhang Zhengyan, Chai Feng, Luo Xiaobing, et al. Method for measuring dislocation density of steel through electron back-scattered diffraction (EBSD): CN108535295A[P]. 2018-09-14.
[20]雍岐龙. 钢铁材料中的第二相 [M]. 北京: 冶金工业出版社, 2006.
[21]Gutiérrez I, Altuna M A. Work-hardening of ferrite and microstructure-based modelling of its mechanical behaviour under tension [J]. Acta Materialia, 2008, 56(17): 4682-4690.

感应淬火条件下Cu-Ni低碳低合金钢的强化机制

Strengthening mechanism of Cu-Ni-bearing low-carbon low-alloyed steel under induction quenching treatment

PDF

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

本文评价

[1]	毛晓峰, 李亚军, 邓诗贵, 李新凯, 赵欢, 王荣. 微合金中碳钢48MnV曲轴连杆轴颈感应淬火工艺的优化[J]. 金属热处理, 2023, 48(2): 212-218.
[2]	张金城, 孙胜辉, 蔡明晖, 赵文柱, 丁桦. 控轧控冷对Ti-Mo-Nb复合微合金化低碳钢组织和力学性能的影响[J]. 金属热处理, 2023, 48(1): 155-162.
[3]	王明明, 马飞, 裴未迟, 李冬冬, 龙海洋, 纪宏超, 刘帅. 汽车用高强塑积中锰钢的研究进展[J]. 金属热处理, 2022, 47(9): 272-280.
[4]	彭龙生, 林英华, 黄伟, 陈皓. 感应淬火对Cr12MoV钢轧辊硬度和硬化层深度的影响[J]. 金属热处理, 2022, 47(8): 118-122.
[5]	吴辉, 林升垚, 李新凯, 龚玉辉, 魏德强. 感应淬火对42CrMo钢曲轴连杆轴颈组织性能的影响[J]. 金属热处理, 2022, 47(2): 119-124.
[6]	代永娟, 武祥祥, 李佳坤, 国栋, 王波. 退火温度对Fe-24.38Mn-0.44C TWIP钢组织性能的影响[J]. 金属热处理, 2022, 47(2): 146-152.
[7]	何利军, 周龙, 汤淳坡, 郭小钢, 金晓, 赵彦芬, 薛飞, 张国栋. 长时服役后T92钢管的微观组织及力学性能变化[J]. 金属热处理, 2021, 46(7): 31-36.
[8]	权晨, 刘新宝, 朱麟, 李博, 王妮. 高铬耐热钢蠕变过程中的组织演化行为[J]. 金属热处理, 2021, 46(6): 135-145.
[9]	王磊, 马录, 杨波, 张凯, 宋阳, 王晔. 球墨铸铁零件高频感应淬火后显微组织异常原因分析[J]. 金属热处理, 2021, 46(6): 231-235.
[10]	米佩, 孙永鹏, 张勇. 矿用齿轨感应淬火裂纹产生原因及改进方法[J]. 金属热处理, 2021, 46(6): 250-252.
[11]	朱飞, 罗小兵, 杨才福, 柴锋, 张正延. 时效温度对直接淬火Ni-Cr-Mo-V-Cu钢组织及性能的影响[J]. 金属热处理, 2021, 46(11): 54-63.
[12]	史文杰, 王春华. Al-6.8Zn-2.3Mg-2.0Cu-0.15Sc合金的高温回归再时效工艺[J]. 金属热处理, 2020, 45(7): 63-67.
[13]	程毅, 徐金辉, 冯青松, 张斌, 邹小魁, 刘昌雨. 50AT尖轨感应淬火的数值模拟[J]. 金属热处理, 2020, 45(5): 199-205.
[14]	高宇, 高兴旺, 张根元. 台阶轴连续感应淬火组织硬度分布预测及其工艺优化[J]. 金属热处理, 2020, 45(5): 215-220.
[15]	付海峰, 李俏, 徐跃明. 重载齿轮热处理及应用[J]. 金属热处理, 2020, 45(3): 178-185.