热处理对SLM成形15-5PH不锈钢组织和力学性能的影响

doi:10.13251/j.issn.0254-6051.2023.11.020

摘要/Abstract

摘要： 分别对激光选区熔化(SLM)成形的15-5PH不锈钢试样进行620 ℃×4 h时效处理和1030 ℃×1 h固溶+550 ℃×4 h时效处理,比较不同状态SLM成形15-5PH不锈钢试样的微观组织及力学性能。结果表明,相对于SLM成形态试样,当不同热处理试样抗拉强度相当时,时效态试样显微组织主要为细小的树枝状晶粒,为马氏体、片状珠光体和铁素体的混合组织;固溶+时效态试样的显微组织主要由回火马氏体+铁素体+部分逆转变奥氏体组成,晶粒内部的树枝状结构基本消失,晶粒长大。与时效态相比,固溶+时效态试样的屈服强度、屈强比分别提高了33%、32%;冲击吸收能量、断后伸长率及断面收缩率分别降低了72.0%、35.5%、18.7%。

关键词: 激光选区熔化, 热处理, 15-5PH不锈钢, 组织, 力学性能

Abstract: 15-5PH stainless steel specimens were prepared by selective laser melting (SLM) forming process and then were aged at 620 ℃ for 4 h, and solution treated at 1030 ℃ for 1 h plus aged at 550 ℃ for 4 h, respectively. The microstructure and mechanical properties of the 15-5PH stainless steel specimens formed by SLM under different states were compared. The results show that compared to SLMed specimen, when the tensile strength of the specimens obtained by different heat treatments is equivalent, the microstructure of the aged specimen is mainly composed of fine dendritic grains which is mix structure of martensite, lamellar pearlite and ferrite, while the microstructure of the solution treated+aged specimen is mainly composed of tempered martensite+acicular ferrite+partial reversed austenite. The dendritic structure inside the grains almost disappears and the grains grow. Compared with the aged specimen, the yield strength and yield ratio of the solution treated+aged specimens are increased by 33% and 32%, respectively, and the impact absorbed energy, elongation after fracture, and the percentage reduction of area are decreased by 72.0%, 35.5% and 18.7%, respectively.

Key words: selective laser melting, heat treatment, 15-5PH stainless steel, microstructure, mechanical properties

中图分类号:

王陆阳, 孙东辉, 黄瑞, 黄红武. 热处理对SLM成形15-5PH不锈钢组织和力学性能的影响[J]. 金属热处理, 2023, 48(11): 132-136.

Wang Luyang, Sun Donghui, Huang Rui, Huang Hongwu. Effect of heat treatment on microstructure and mechanical properties of 15-5PH stainless steel by selective laser melting[J]. Heat Treatment of Metals, 2023, 48(11): 132-136.

参考文献

[1]吴伟辉, 杨永强, 毛星, 等. 激光选区熔化增材制造金属零件精度优化工艺分析[J]. 铸造技术, 2016, 37(12): 2636-2640.
Wu Weihui, Yang Yongqiang, Mao Xing, et al. Precision optimization process for metal part manufactured by selective laser melting[J]. Foundry Technology, 2016, 37(12): 2636-2640.
[2]程灵钰, 朱小刚, 刘正武, 等. 热处理对激光选区熔化成形316L不锈钢组织和力学性能的影响[J]. 材料热处理学报, 2020, 41(7): 80-86.
Cheng Lingyu, Zhu Xiaogang, Liu Zhengwu, et al. Effect of heat treatment on microstructure and mechanical properties of 316L stainless steel prepared by selective laser melting[J]. Transactions of Materials and Heat Treatment, 2020, 41(7): 80-86.
[3]郝志博, 葛昌纯, 黎兴刚, 等. 热处理对选区激光熔化镍基粉末高温合金组织与力学性能的影响[J]. 金属学报, 2020, 56(8): 1133-1143.
Hao Zhibo, Ge Changchun, Li Xinggang, et al. Effect of heat treatment on microstructure and mechanical properties of nickel-based powder metallurgy superalloy processed by selective laser melting[J]. Acta Metallurgica Sinica, 2020, 56(8): 1133-1143.
[4]Hu Z H, Zhu H H, Zhang H, et al. Experimental investigation on selective laser melting of 17-4PH stainless steel[J]. Optics and Laser Technology, 2017, 87: 17-25.
[5]丁利, 李怀学, 王玉岱, 等. 热处理对激光选区熔化成形316不锈钢组织与拉伸性能的影响[J]. 中国激光, 2015(4): 179-185.
Ding Li, Li Huaixue, Wang Yudai, et al. Heat treatment on microstructure and tensile strength of 316 stainless steel by selective laser melting[J]. Chinese Journal of Lasers, 2015(4): 179-185.
[6]Dilip J J S, Ram G D J, Starr T L, et al. Selective laser melting of HY100 steel: Process parameters, microstructure and mechanical properties[J]. Additive Manufacturing, 2017, 13: 49-60.
[7]胡志明, 姚文进, 于良. 激光选区熔化成型15-5PH不锈钢动态力学性能研究[J]. 弹道学报, 2021, 33(4): 77-82.
Hu Zhiming, Yao Wenjin, Yu Liang. Study on dynamic mechanical properties of 15-5PH stainless steel formed by selective laser melting[J]. Journal of Ballistics, 2021, 33(4): 77-82.
[8]Nong X D, Zhou X L. Effect of scanning strategy on the microstructure, texture, and mechanical properties of 15-5PH stainless steel processed by selective laser melting[J]. Materials Characterization, 2021, 174: 111012.
[9]Spierings A B, Start T L, Wegener K. Fatigue performance of additive manufactured metallic parts[J]. Rapid Prototyping Journal, 2013, 19(2): 88-94.
[10]Raft H K, Start T L, Stucker B E. A comparison of the tensile, fatigue, and fracture behavior of Ti-6Al-4V and 15-5PH stainless steel parts made by selective laser melting[J]. International Journal of Advanced Manufacturing Technology, 2013, 69(5): 1299-1309.
[11]仇振安, 王海涛, 李继良, 等. 热处理工艺对15-5PH不锈钢组织和力学性能的影响[J]. 金属热处理, 2014, 39(5): 77-81.
Qiu Zhen'an, Wang Haitao, Li Jiliang, et al. Effects of heat treatment on microstructure and mechanical properties of 15-5PH stainless steel[J]. Heat Treatment of Metals, 2014, 39(5): 77-81.
[12]边培莹. 热处理工艺对316L不锈钢粉末激光选区熔化成形的残余应力及组织的影响[J]. 材料热处理学报, 2019, 40(4): 90-97.
Bian Peiying. Effect of heat treatment on residual stress and microstructure of 316L stainless steel powder formed by selective laser melting[J]. Transactions of Materials and Heat Treatment, 2019, 40(4): 90-97.
[13]Jägle E A, Choi P P, Van Humbeeck J, et al. Precipitation and austenite reversion behavior of a maraging steel produced by selective laser melting[J]. Journal of Materials Research, 2014, 29: 2072-2079.
[14]Xu Z J, Zhang Y X. Quench rates in air, water, and liquid nitrogen, and inference of temperature in volcanic eruption columns[J]. Earth and Planetary Science Letters, 2002, 200(3/4): 315-330.
[15]赵喜伟, 安俊涛. 淬火温度对超高强海工钢屈强比的影响[J]. 宽厚板, 2021, 27(3): 41-43.
Zhao Xiwei, An Juntao. Effects of quenching temperature on yield to tensile strength ratio of ultra high strength offshore engineering steel[J]. Wide and Heavy Plate, 2021, 27(3): 41-43.
[16]罗小兵, 杨才福, 苏航, 等. 时效温度对HSLA高强船体钢组织性能的影响[J]. 材料热处理学报, 2021, 32(6): 73-77.
Luo Xiaobing, Yang Caifu, Su Hang, et al. Effect of aging temperature on microstructure and properties of HSLA ship-hull steel[J]. Transactions of Materials and Heat Treatment, 2021, 32(6): 73-77.