超高强度螺栓螺纹局部感应加热有限元分析与实践

doi:10.13251/j.issn.0254-6051.2023.12.046

金属热处理 ›› 2023, Vol. 48 ›› Issue (12): 281-284.DOI: 10.13251/j.issn.0254-6051.2023.12.046

超高强度螺栓螺纹局部感应加热有限元分析与实践

孙晓军¹, 杨晨辉¹, 贺连栋¹, 王鑫², 张一帆²

1.河南省紧固连接技术重点实验室, 河南信阳 464000;
2.河南工程学院机械工程学院, 河南郑州 451191

收稿日期:2023-08-01 修回日期:2023-11-04 出版日期:2023-12-25 发布日期:2024-01-29
作者简介:孙晓军(1983—),男,研究员,主要研究方向为紧固件热处理与表面处理工艺,E-mail:64903724@qq.com
基金资助:
河南省紧固连接技术重点实验室开放课题(JGLJ2207)

Finite element analysis and practice of local induction heating on threads of ultra-high strength bolts

Sun Xiaojun¹, Yang Chenhui¹, He Liandong¹, Wang Xin², Zhang Yifan²

1. Henan Provincial Key Laboratory of Fastening Technology, Xinyang Henan 464000, China;
2. Mechanical Engineering College, Henan University of Engineering, Zhengzhou Henan 451191, China

Received:2023-08-01 Revised:2023-11-04 Online:2023-12-25 Published:2024-01-29

摘要/Abstract

摘要： 超高强度螺栓局部感应回火加热速度快、效率高,绿色环保,逐步取代传统的铅浴回火。但其存在线圈设计单一,工艺调节费时费力的现状,故基于COMSOL软件建立了一种螺纹局部回火加热的有限元分析模型,并通过试验结果的对比,验证了分析模型的正确性。同时通过对线圈设计和工艺过程的调整优化,大大减少了螺纹感应加热时的轴向和径向温度的不均匀性,并最终使超高强度螺栓螺纹部分的回火硬度满足回火标准要求。

关键词: 超高强度, 局部回火, 有限元模型, 回火硬度

Abstract: Local induction tempering for ultra-high strength bolt with fast heating speed is high efficiency, green and environmental protection, and is gradually replacing the traditional lead bath tempering. However, the single coil design was time-consuming and labor-intensive in the process of adjusting, so a finite element model on local tempering heating of threads was built by COMSOL software. The correctness of the analysis model was verified by comparing with the experiment results. By adjusting and optimizing the coil design and process, the non-uniformity of axial and radial temperature during induction heating is greatly reduced, and ultimately the tempering hardness of the threaded part of the ultra-high strength bolt can meet the requirement of temper standard.

Key words: ultra-high strength, local tempering, finite element model, tempering hardness

中图分类号:

TG156.8

孙晓军, 杨晨辉, 贺连栋, 王鑫, 张一帆. 超高强度螺栓螺纹局部感应加热有限元分析与实践[J]. 金属热处理, 2023, 48(12): 281-284.

Sun Xiaojun, Yang Chenhui, He Liandong, Wang Xin, Zhang Yifan. Finite element analysis and practice of local induction heating on threads of ultra-high strength bolts[J]. Heat Treatment of Metals, 2023, 48(12): 281-284.

参考文献

[1]房玉佩, 谢振佳, 尚成嘉. 感应回火对1000 MPa级高强度低合金钢碳化物析出行为及韧性的影响[J]. 金属学报, 2014, 50(12): 1413-1420.
Fang Yupei, Xie Zhenjia, Shang Chengjia. Effect of induction tempering on carbide precipitation behavior and toughness of a 1000 MPa grade high strength low alloy steel[J]. Acta Metallurgica Sinica, 2014, 50(12): 1413-1420.
[2]王浩军, 杨平, 任树锋, 等. 30CrMnSiNi2A钢螺纹零件局部感应回火工艺[J]. 金属热处理, 2023, 48(10): 168-174.
Wang Haojun, Yang Ping, Ren Shufeng, et al. Local induction tempering process of 30CrMnSiNi2A steel threaded parts[J]. Heat Treatment of Metals, 2023, 48(10): 168-174.
[3]陆文杰. 30CrMnSiNi2A螺纹件局部感应回火工艺模拟研究[D]. 南昌: 南昌航空大学, 2017.
Lu Wenjie. Simulation analysis of local induction tempering process of 30CrMnSiNi2A thread parts[D]. Nanchang: Nanchang Hangkong University, 2017.
[4]孙枫, 佟小军, 李国庆, 等. 超高强度钢制螺栓的短时回火工艺[J]. 金属热处理, 2014, 39(7): 89-92.
Sun Feng, Tong Xiaojun, Li Guoqing, et al. Short-time tempering process for ultra-high strength steel bolts[J]. Heat Treatment of Metals, 2014, 39(7): 89-92.
[5]杨晨光. 42CrMo钢轴类件变功率感应加热数值模拟研究[D]. 秦皇岛: 燕山大学, 2010.
Yang Chenguang. The 42CrMo steel shaft piece variable power induction heating numerical simulation study[D]. Qinhuangdao: Yanshan University, 2010.
[6]张雪彪, 陈诚, 刘玉君, 等. 钢板移动式感应加热的多场耦合数值分析[J]. 哈尔滨工程大学学报, 2015, 36(4): 473-478.
Zhang Xuebiao, Chen Cheng, Liu Yujun, et al. Numerical analysis of multi-field coupled process of steel plate bending by moveable induction heating[J]. Journal of Harbin Engineering University, 2015, 36(4): 473-478.
[7]于新年, 李新平, 宋毅飞, 等. 30CrMnSiNi2A钢零件感应加热局部回火工艺[J]. 金属热处理, 2011, 36(9): 50-53.
Yu Xinnian, Li Xinping, Song Yifei, et al. Induction heating local tempering process for 30CrMnSiNi2A steel parts[J]. Heat Treatment of Metals, 2011, 36(9): 50-53.
[8]HB/Z 136—2000, 航空结构钢热处理工艺[S]. 北京: 中国航空工业总公司, 2000.

[1]	许忠智, 韩顺, 耿如明, 雷斯敏, 厉勇, 王春旭. 回火温度对A330M超高强度钢组织性能的影响[J]. 金属热处理, 2023, 48(6): 46-51.
[2]	马蓼奕, 慈言海, 李世键, 杨立新, 刘刚, 崔晶. 基于热处理模拟仿真的超高强度钢制复杂零件构型优化与验证[J]. 金属热处理, 2023, 48(4): 229-234.
[3]	许忠智, 黄顺喆, 戴建科, 韩顺, 厉勇, 王春旭, 张海鸥. 淬火温度对电弧微铸锻AerMet100钢组织与性能的影响[J]. 金属热处理, 2023, 48(2): 124-130.
[4]	肖凯, 韩顺, 许忠智, 耿如明, 夏慧敏, 徐正伟, 厉勇, 王春旭. Ni含量对A330M超高强度钢组织性能的影响[J]. 金属热处理, 2023, 48(11): 45-49.
[5]	唐远寿, 司宇, 徐正萌, 于硕硕, 曹鹏军, 栗克建, 冯毅, 高翔. 超高强度钢在汽车轻量化中的应用及研究进展[J]. 金属热处理, 2023, 48(10): 247-254.
[6]	高齐, 杨卓越, 丁雅莉. G50超高强度钢大规格锻件退火工艺优化[J]. 金属热处理, 2023, 48(1): 169-174.
[7]	索忠源, 杜阳, 付立铭, 单爱党. 配分工艺对5CrMnNiMo超高强度钢摩擦磨损性能的影响[J]. 金属热处理, 2022, 47(7): 134-137.
[8]	索忠源, 杜阳, 付立铭, 单爱党. Q&P工艺对5CrMnNiMo超高强度钢组织及性能的影响[J]. 金属热处理, 2022, 47(5): 217-220.
[9]	王玉岱, 刘洋, 朱言言, 田象军, 程序, 冉先喆, 钱婷婷. 热处理对复合制造AerMet100超高强度钢组织均匀性与拉伸性能的影响[J]. 金属热处理, 2022, 47(4): 1-9.
[10]	高齐, 杨卓越, 王敖. 淬火冷却规范对G50钢微观组织和力学性能的影响[J]. 金属热处理, 2022, 47(12): 95-98.
[11]	宁静, 杨鹏, 高齐, 苏杰. 回火温度对30Cr3Si2NiMoWNb钢组织性能的影响[J]. 金属热处理, 2022, 47(11): 95-99.
[12]	王海波, 徐震霖, 胡学文, 彭欢. 热轧超高强度复相钢的氢脆敏感性[J]. 金属热处理, 2021, 46(8): 51-55.
[13]	刘靖宝, 田秀刚, 张杰, 魏焕君, 杨丽娜, 王朝, 李孟星. 低成本800 MPa级镀锌超高强度双相钢的微观组织与性能[J]. 金属热处理, 2021, 46(8): 73-76.
[14]	熊金生, 宁静, 苏杰, 姜庆伟. 固溶温度对G33超高强度钢微观组织和力学性能的影响[J]. 金属热处理, 2021, 46(7): 160-164.
[15]	李战卫, 沈奎, 于学森, 张宇. 超高强度帘线钢LX92A连续和等温冷却下的相变行为[J]. 金属热处理, 2021, 46(5): 32-37.

超高强度螺栓螺纹局部感应加热有限元分析与实践

Finite element analysis and practice of local induction heating on threads of ultra-high strength bolts

PDF

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

本文评价