固溶处理对高速轧制N06625镍基合金线材组织与性能的影响

doi:10.13251/j.issn.0254-6051.2024.04.029

金属热处理 ›› 2024, Vol. 49 ›› Issue (4): 182-185.DOI: 10.13251/j.issn.0254-6051.2024.04.029

固溶处理对高速轧制N06625镍基合金线材组织与性能的影响

谷宇, 王岩, 李吉东, 曾莉, 韩东

太原钢铁(集团)有限公司先进不锈钢材料国家重点实验室, 山西太原 030003

收稿日期:2023-10-24 修回日期:2024-03-14 出版日期:2024-04-25 发布日期:2024-05-27
作者简介:谷宇(1979—),男,高级工程师,博士,主要研究方向为镍基合金产品与技术开发,E-mail:guyu01@tsico.com.cn
基金资助:
山西省关键核心技术和共性技术研发攻关专项(20201102017)

Effect of solution treatment on microstructure and properties of high speed rolled N06625 nickel based alloy wire rod

Gu Yu, Wang Yan, Li Jidong, Zeng Li, Han Dong

State Key Laboratory of Advanced Stainless Steel, Taiyuan iron and Steel Group Co., Ltd., Taiyuan Shanxi 030003, China

Received:2023-10-24 Revised:2024-03-14 Online:2024-04-25 Published:2024-05-27

摘要/Abstract

摘要： 采用高速线材轧制机组实现了大卷重N06625合金线材的生产,并对其不同温度(1000~1200 ℃)固溶后的组织与性能开展了研究。结果表明,N06625合金高速轧制线材的轧态晶粒尺寸极其细小,其合理的固溶处理制度为1180~1200 ℃×40 min;经1200 ℃固溶后,线材的强度和硬度较低,伸长率及断面收缩率优异,完全满足后续拔丝生产,且此时合金的组织调整完全,即发生完全静态再结晶,基体中只有少量小尺寸的Nb析出物,不会对后续冷拔变形产生不利影响。

关键词: N06625合金, 高速线材, 显微组织, 性能

Abstract: Production of N06625 alloy wire rod with large coil weight was realized by using the high-speed wire rolling mill, and the microstructure and properties after solution treatment at different temperatures(1000-1200 ℃) were studied. The results show that the grain size of the high speed rolled N06625 alloy wire rod is extremely small, and the reasonable solution treatment is at 1180-1200 ℃ for 40 min. After solution treatment at 1200 ℃, the strength and hardness of the wire rod are low, and the elongation and reduction of area are excellent, which fully meet the subsequent drawing process. Besides, the microstructure of the wire rod is completely regulated, that is, static recrystallization is completed, where there are only a few small-sized Nb precipitates in the matrix, which will not affect the subsequent cold drawing deformation.

Key words: N06625 alloy, high speed wire rod, microstructure, properties

中图分类号:

TG335.3

谷宇, 王岩, 李吉东, 曾莉, 韩东. 固溶处理对高速轧制N06625镍基合金线材组织与性能的影响[J]. 金属热处理, 2024, 49(4): 182-185.

Gu Yu, Wang Yan, Li Jidong, Zeng Li, Han Dong. Effect of solution treatment on microstructure and properties of high speed rolled N06625 nickel based alloy wire rod[J]. Heat Treatment of Metals, 2024, 49(4): 182-185.

参考文献

[1]高钰璧, 丁雨田, 孟斌, 等. Inconel 625合金中析出相演变研究进展[J]. 材料工程, 2020, 48(5): 13-22.
Gao Yubi, Ding Yutian, Meng Bin, et al. Research progress in evolution of precipitated phases in Inconel 625 superalloy[J]. Journal of Materials Engineering, 2020, 48(5): 13-22.
[2]Chen X, Lin Y C, Chen M, et al. Microstructural evolution of a nickel-based superalloy during hot deformation[J]. Materialsand Design, 2015, 77: 41-49.
[3]王方军, 刘应龙, 时瑶, 等. 等温退火处理对Inconel 625合金箔材组织和性能的影响[J]. 金属热处理, 2022, 47(3): 77-81.
Wang Fangjun, Liu Yinglong, Shi Yao, et al. Effect of isothermal annealing treatment on microstructure and properties of Inconel 625 alloy foil[J]. Heat Treatment of Metals, 2022, 47(3): 77-81.
[4]蔡远飞, 隋毅, 朱治愿, 等. 超低铁Inconel 625合金的热处理[J]. 金属热处理, 2018, 43(9): 175-181.
Cai Yuanfei, Sui Yi, Zhu Zhiyuan, et al. Heat treatment of ultra-low iron Inconel 625 alloy[J]. Heat Treatment of Metals, 2018, 43(9): 175-181.
[5]王岩, 徐芳泓, 李阳, 等. 应变速率对617B镍基高温合金组织演变的影响[J]. 稀有金属材料与工程, 2014, 43(12): 3027-3030.
Wang Yan, Xu Fanghong, Li Yang, et al. Effect of strain rate on the microstructural evolution of 617B Ni-base superalloy[J]. Rare Metal Materials and Engineering, 2014, 43(12): 3027-3030.
[6]Wang J, Dong J X, Zhang M C, et al. Hot working characteristics of nickel-base superalloy 740H during compression[J]. Materials Science and Engineering A, 2013, 566: 61-70.
[7]Zhang P, Hu C, Zhu Q, et al. Hot compression deformation and constitutive modeling of GH4698 alloy[J]. Materials and Design, 2015, 65: 1153-1160.
[8]王岩. 镍基合金N06625变形-热处理组织演变特性研究[C]//2019年(首届)中国金属学会不锈钢科技发展论坛. 2019: 98-102.
[9]丁雨田, 马元俊, 豆正义, 等. 固溶处理温度对GH3625合金热挤压管材微观组织和力学性能的影响[J]. 材料导报, 2018, 32(8): 1311-1317.
Ding Yutian, Ma Yuanjun, Dou Zhengyi, et al. Effect of solution treatment temperature on microstructure and mechanical properties of GH3625 alloy hot extruded tube[J]. Materials Reports, 2018, 32(8): 1311-1317.
[10]蔡梅, 刘建平, 吴香菊, 等. GH625合金锻造工艺研究[J]. 沈阳航空航天大学学报, 2011, 28(4): 52-59.
Cai Mei, Liu Jianping, Wu Xiangju, et al. Technical study on GH625 alloy forging[J]. Journal of Shenyang Aerospace University, 2011, 28(4): 52-59.
[11]Jiang H, Dong J X, Zhang M C, et al. The recrystallization model and microstructure prediction of alloy 690 during hot deformation[J]. Materials and Design, 2016, 104: 162-173.

[1]	李为先, 彭伟, 胡杰, 刘腾轼, 周路海, 董瀚. Cu对390 MPa级CrNiMo系低合金船用钢板力学性能的影响[J]. 金属热处理, 2024, 49(4): 1-7.
[2]	黄东, 蒋义然. S355低合金结构钢的动态连续冷却转变曲线及力学性能[J]. 金属热处理, 2024, 49(4): 38-41.
[3]	唐恩, 彭侠超, 刘红亮, 张瑞, 王坤. 合金元素对高碳珠光体盘条钢组织和性能的影响[J]. 金属热处理, 2024, 49(4): 42-47.
[4]	郑磊, 徐达, 鲁宇杰, 廖文超, 殷安民, 陈候. 激光增材制造316L不锈钢退火过程中微观组织演变和力学性能[J]. 金属热处理, 2024, 49(4): 66-77.
[5]	陶天成, 臧凯, 朱治愿. 长期时效对GH4169合金组织与性能的影响[J]. 金属热处理, 2024, 49(4): 83-88.
[6]	渠静雯, 李博帅, 张海芹, 石明华, 陈秋羽, 李洁, 王曦. 成品退火工艺对Zr-4合金管材显微组织和力学性能的影响[J]. 金属热处理, 2024, 49(4): 95-103.
[7]	董泰励, 李昉, 陈庚, 张晨, 郭子龙, 陈康华, 陈送义. 自然时效耦合预拉伸提升Al-Zn-Mg-Cu合金力学性能和腐蚀抗力[J]. 金属热处理, 2024, 49(4): 104-110.
[8]	李菁菁, 王存宇, 杜敏, 徐海峰, 俞峰, 曹文全. 退火工艺对30Cr15Mo1N钢组织和力学性能的影响[J]. 金属热处理, 2024, 49(4): 110-115.
[9]	谭科杰, 谢锦丽, 秦海龙, 徐斌, 董行, 毕中南, 张继. 热处理对增材制造TS5镍基高温合金组织与性能的影响[J]. 金属热处理, 2024, 49(4): 116-122.
[10]	谢红申, 李明, 冷婉晴, 刁晓刚, 李洲, 徐流杰. 等温淬火对高钒耐磨合金组织与力学性能的影响[J]. 金属热处理, 2024, 49(4): 123-131.
[11]	王艺橦, 侯华兴, 张弛, 潘栋. 高能电脉冲处理对海洋结构用钢焊接接头组织及性能的影响[J]. 金属热处理, 2024, 49(4): 131-137.
[12]	翟鹏飞, 潘浩, 邢淑清, 宫美娜, 刘永珍, 麻永林. 脉冲磁场时效处理对A356铝合金组织和性能的影响[J]. 金属热处理, 2024, 49(4): 138-145.
[13]	韦辽, 杨屹. 磁场处理对YG8硬质合金性能及耐磨性的影响[J]. 金属热处理, 2024, 49(4): 161-167.
[14]	孙进宝, 王少华, 刘惠, 李国爱, 王海龙, 张景亮, 周志宇. 稳定化退火对新型5×××铝合金组织与性能的影响[J]. 金属热处理, 2024, 49(4): 175-182.
[15]	王树梁, 王春光, 李爱菊, 王雪兆. 固溶工艺对Mg-7.5Gd-3Y-0.5Zr合金微观组织及动态冲击行为的影响[J]. 金属热处理, 2024, 49(4): 186-194.

固溶处理对高速轧制N06625镍基合金线材组织与性能的影响

Effect of solution treatment on microstructure and properties of high speed rolled N06625 nickel based alloy wire rod

PDF

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

本文评价