渗碳淬火过程中C形试样组织与畸变演变行为的数值模拟

doi:10.13251/j.issn.0254-6051.2024.05.011

金属热处理 ›› 2024, Vol. 49 ›› Issue (5): 68-73.DOI: 10.13251/j.issn.0254-6051.2024.05.011

渗碳淬火过程中C形试样组织与畸变演变行为的数值模拟

许勇¹, 刘克², 邓瑶瑶³, 杨兵², 陆海龙¹, 罗艺²

1.宁夏机械研究院股份有限公司, 宁夏银川 750000;
2.江麓机电集团有限公司, 湖南湘潭 411100;
3.湖南湘投金天钛业科技股份有限公司, 湖南常德 415000

收稿日期:2023-11-10 修回日期:2024-03-27 出版日期:2024-05-25 发布日期:2024-06-28
作者简介:许勇(1983—),男,高级工程师,主要研究方向为压淬装备及零件的热处理工艺,E-mail:perfectlogic@yeah.net。

Numerical simulation of microstructure and distortion evolution behavior of C-type specimens during carburizing and quenching

Xu Yong¹, Liu Ke², Deng Yaoyao³, Yang Bing², Lu Hailong¹, Luo Yi²

1. Ningxia Machinery Research Institute Co., Ltd., Yinchuan Ningxia 750000, China;
2. Jianglu Machinery Electronics Group Co., Ltd., Xiangtan Hunan 411100, China;
3. Hunan Xiangtou Goldsky Titanium Industry Technology Co., Ltd., Changde Hunan 415000, China

Received:2023-11-10 Revised:2024-03-27 Online:2024-05-25 Published:2024-06-28

摘要/Abstract

摘要： 以18Cr2Ni2MoNbA钢C形试样为对象,采用有限元方法建立了温度场、组织场、应变场的多场耦合模型,研究了C形试样在悬挂方式下渗碳淬火过程中组织与畸变演变行为。结果表明:将计算的畸变结果与实测进行对比,结果吻合良好,C形试样缺口位置的畸变最大,冷却过程中宽度最大处的中心位置与缺口处表面位置之间的最大温差出现在淬火的2.78 s,达到383.437 ℃;马氏体转变最先是从缺口位置的心部开始,C形试样心部马氏体含量基本都能达到94%以上;淬火时表层马氏体转变滞后于心部,其马氏体转变量受残留奥氏体影响明显低于心部,最终转变量在83%左右。

关键词: 18Cr2Ni2MoNbA钢, C形试样, 渗碳, 淬火, 组织, 畸变

Abstract: Taking C-type specimen of 18Cr2Ni2MoNbA steel as the study object, the microstructure and distortion evolution behavior of the C-type specimens under suspension during carburizing and quenching were studied by using finite element method to establish a multi-field coupling model of temperature field, structure field and strain field. The results show that the calculated distortion results are in good agreement with the actual measurements. The maximum distortion is at the notch position of the C-type specimen. The maximum temperature difference between the center position of the maximum width and the surface position of the notch during cooling process appears at 2.78 s and reaches 383.437 ℃. The martensitic transformation first starts from the core of the notch position, and the content of martensite in the core of C-type specimen can generally reach over 94%. During quenching, the surface martensite transformation of the C-type specimen lags behind the core, the surface martensitic transformation content is significantly lower than that of the core under the influence of retained austenite, and the final transformation content is about 83%.

Key words: 18Cr2Ni2MoNbA steel, C-type specimen, carburizing, quenching, microstructure, distortion

中图分类号:

TG142.1

许勇, 刘克, 邓瑶瑶, 杨兵, 陆海龙, 罗艺. 渗碳淬火过程中C形试样组织与畸变演变行为的数值模拟[J]. 金属热处理, 2024, 49(5): 68-73.

Xu Yong, Liu Ke, Deng Yaoyao, Yang Bing, Lu Hailong, Luo Yi. Numerical simulation of microstructure and distortion evolution behavior of C-type specimens during carburizing and quenching[J]. Heat Treatment of Metals, 2024, 49(5): 68-73.

参考文献

[1]李宝奎, 顾敏, 朱全意, 等. 渗碳淬火工艺因素对20CrNi2Mo钢热处理畸变影响的研究[J]. 热处理, 2007, 22(2): 51-54.
Li Baokui, Gu Min, Zhu Quanyi, et al. Effectof carburizing and quenching process on heat treatment distortion of 20CrNi2Mo steel[J]. Heat Treatment, 2007, 22(2): 51-54.
[2]邓影洲. 薄壁齿轮渗碳淬火畸变的分析与改进[J]. 热处理技术与装备, 2013, 34(4): 19-21.
Deng Yingzhou. Analysis and improve on distortion for carburized and quenched thin gear[J]. Heat Treatment Technology and Equipment, 2013, 34(4): 19-21.
[3]陈国民. 对齿轮热处理畸变控制技术的评述[J]. 金属热处理, 2012, 37(2): 1-13.
Chen Guomin. Review on distortion control technology of gear heat treatment[J]. Heat Treatment of Metals, 2012, 37(2): 1-13.
[4]潘健生, 王婧, 顾剑锋. 热处理数值模拟进展之一——扩展求解域热处理数值模拟[J]. 金属热处理, 2012, 37(1): 7-13.
Pan Jiansheng, Wang Jing, Gu Jianfeng. One of progress in heat treatment numerical simulation——Numerical model of heat treatment with expanded solution domain[J]. Heat Treatment of Metals, 2012, 37(1): 7-13.
[5]金妙, 刘宁, 刘爱军, 等. 钢的热处理数值模拟技术的现状与发展[J]. 热处理, 2019, 34(1): 23-28.
Jin Miao, Liu Ning, Liu Aijun, et al. Recent situation and development of numerical simulation technology for heat treatment process of steel[J]. Heat Treatment, 2019, 34(1): 23-28.
[6]任鑫, 窦春岳, 高志玉, 等. 热处理数值模拟技术的研究进展[J]. 材料导报, 2021, 35(19): 19186-19194.
Ren Xin, Dou Chunyue, Gao Zhiyu, et al. Research progress of numerical simulation in heat treatment[J]. Materials Reports, 2021, 35(19): 19186-19194.
[7]王鑫. 高速机车齿轮渗碳淬火工艺及其畸变的数值模拟研究[D]. 北京: 机械科学研究总院, 2019.
Wang Xin. Numerical simulation research on carburizing-quenching process and distortion of high speed locomotive gears[D]. Beijing: China Academy of Machinery Science and Technology, 2019.
[8]牛山廷. 淬火冷却过程三维有限元模拟及工艺参数优化的研究[D]. 济南: 山东大学, 2007.
Niu Shanting. Research on 3D finite element simulation and parameter optimization for quenching processes[D]. Jinan: Shandong University, 2007.
[9]秦盛伟, 张棒, 赵辉辉, 等. 18CrNiMo7-6渗碳钢相变塑性系数对残余应力的影响[J]. 表面技术, 2020, 49(12): 138-143.
Qin Shengwei, Zhang Bang, Zhao Huihui, et al. Effect of transformation plasticity coefficient on residual stress of 18CrNiMo7-6 carburizing steel[J]. Surface Technology, 2020, 49(12): 138-143.
[10]但文蛟. 高强度汽车板相变诱发塑性本构模型及硬化特性研究[D]. 上海: 上海交通大学, 2008.
Dan Wenjiao. Study on constitutive model with trip behavior of high strength auto sheet and its hardening properties[D]. Shanghai: Shanghai Jiao Tong University, 2008.

[1]	鲍峥, 程翔, 王若民, 缪春辉, 陈国宏, 汤文明. 不同服役期TP347HFG钢管显微组织与力学性能的对比[J]. 金属热处理, 2024, 49(5): 10-16.
[2]	杨希锐, 江宝世, 胡锋涛, 李艳军, 盛超杰, 王晨. 高温长期服役S30432钢管的组织与性能[J]. 金属热处理, 2024, 49(5): 17-21.
[3]	郭炜, 管博, 陈威, 吴丹. 多次闭模压缩对不同Si含量AZ31合金显微组织和耐磨性能的影响[J]. 金属热处理, 2024, 49(5): 36-39.
[4]	张帅坤, 张超勇, 吴剑钊, 唐莉梅. 40Cr钢滚刀织构表面激光淬火的数值模拟[J]. 金属热处理, 2024, 49(5): 47-54.
[5]	梁祥, 高翔, 李云龙, 徐志锋, 张正, 闫利青, 余欢. 深冷处理对叠层穿刺C_f/Al基复合材料组织特征和拉伸性能的影响[J]. 金属热处理, 2024, 49(5): 74-80.
[6]	臧凯, 王守乾, 朱治愿. 固溶时效处理对21-4NWNb合金组织与性能的影响[J]. 金属热处理, 2024, 49(5): 88-93.
[7]	赵倩, 董福宇, 吴福川, 张悦, 徐欣. 固溶时效对Ti-5Al-3.5Fe-7Mo-4Cr合金组织与性能的影响[J]. 金属热处理, 2024, 49(5): 100-105.
[8]	李波, 向伟, 张枫, 秦锋英, 袁武华. 预时效处理对亚稳态β钛合金TB18组织性能的影响[J]. 金属热处理, 2024, 49(5): 106-111.
[9]	王泽龙, 冯兆龙, 李伟, 孙思博. 冷塑性变形及退火工艺对Ti45Nb合金组织和性能的影响[J]. 金属热处理, 2024, 49(5): 112-117.
[10]	邢振强, 庞景宇, 张宏伟, 纪宇, 朱正旺, 张龙, 王爱民, 张海峰. 冷轧、退火和时效对Fe₅₀Ni₂₅Cr₁₅Al₁₀高熵合金组织和性能的影响[J]. 金属热处理, 2024, 49(5): 118-123.
[11]	刘晨希, 胡昕明, 欧阳鑫, 邢梦楠, 王储. 淬火温度对690 MPa级低焊接裂纹敏感性容器钢组织性能的影响[J]. 金属热处理, 2024, 49(5): 124-129.
[12]	张增光, 史吉鹏, 王新宇, 刘艳梅, 杨立新, 康冲, 刘刚. 退火温度对Ti60钛合金激光焊接接头组织与力学性能的影响[J]. 金属热处理, 2024, 49(5): 130-134.
[13]	张正华, 李霄, 王艳松, 肖世俊. 中间回火对15Cr1Mo1V钢补焊热影响区组织和力学性能的影响[J]. 金属热处理, 2024, 49(5): 140-145.
[14]	张勇, 马青山, 李如杨, 胡效东. S11306铁素体不锈钢厚板焊后热处理特性[J]. 金属热处理, 2024, 49(5): 146-152.
[15]	乔鹏飞, 吴忠旺, 张慧敏, 金自力, 任慧平, 郭欢. 不同终轧温度下高强无取向电工钢的热轧和常化组织与织构[J]. 金属热处理, 2024, 49(5): 153-157.

渗碳淬火过程中C形试样组织与畸变演变行为的数值模拟

Numerical simulation of microstructure and distortion evolution behavior of C-type specimens during carburizing and quenching

PDF

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

本文评价