自然时效对TiB2/7050铝基复合材料PLC效应的影响

doi:10.13251/j.issn.0254-6051.2024.05.013

金属热处理 ›› 2024, Vol. 49 ›› Issue (5): 81-87.DOI: 10.13251/j.issn.0254-6051.2024.05.013

自然时效对TiB₂/7050铝基复合材料PLC效应的影响

尚洪帅¹, 韩文峰², 揭招财², 袁斌先²

1.天津航天长征火箭制造有限公司, 天津 300462;
2.天津职业技术师范大学机械工程学院汽车模具智能制造技术国家地方联合工程实验室, 天津 300222

收稿日期:2023-11-04 修回日期:2024-03-21 出版日期:2024-05-25 发布日期:2024-06-28
通讯作者: 袁斌先,副教授,博士,E-mail:ybx2003@163.com
作者简介:尚洪帅(1986—),男,工程师,硕士,主要研究方向为航天先进成形工艺及热处理技术,E-mail:shs198607@126.com。
基金资助:
天津市教委科研计划(2020KJ106);天津市研究生科研创新项目(2022SKYZ159)

Effect of natural aging on Portevin-Le Chatelier effect of TiB₂/7050 aluminum matrix composites

Shang Hongshuai¹, Han Wenfeng², Jie Zhaocai², Yuan Binxian²

1. Tianjin Long March Lauch Vehicle Manufacturing Co., Ltd., Tianjin 300462, China;
2. National Local Joint Engineering Laboratory of Intelligent Manufacturing Oriented Automobile Die and Mould, School of Mechanical Engineering, Tianjin University of Technology and Education, Tianjin 300222, China

Received:2023-11-04 Revised:2024-03-21 Online:2024-05-25 Published:2024-06-28

摘要/Abstract

摘要： 研究了自然时效时间对TiB₂/7050铝基复合材料塑性失稳效应(PLC效应)的影响。首先,对固溶水冷后进行不同时间自然时效的TiB₂/7050铝基复合材料开展室温恒应变速率拉伸试验,然后分析平均应力跌幅、跌落时间、重加载时间以及临界应变,研究自然时效时间对PLC效应的影响,最后,利用扫描电镜观察拉伸断口微观形貌。结果表明,自然时效时间在1 h内,TiB₂/7050复合材料的强度变化不大,超过1 h后,屈服强度和抗拉强度均有明显增加。PLC带类型随自然时效时间的延长由具有跳变性质的B类(0~1 h)逐渐向连续传播的A类(1.5 h)演变,再向具有阶梯传播特性的D类(2~4 h)演变。当自然时效时间超过1 h后,TiB₂/7050铝基复合材料拉伸断口韧窝明显变浅,尺寸变小,这表明复合材料塑性随自然时效时间的延长而降低。因此,TiB₂/7050铝基复合材料的固溶处理与人工时效的间隔不应超过1 h。

关键词: TiB₂/7050铝基复合材料, 自然时效, PLC效应, 断口形貌

Abstract: Effect of natural aging time on Portevin-Le Chatelier effect (PLC effect) of TiB₂/7050 aluminum matrix composites was investigated. Firstly, room temperature constant strain rate tensile tests were carried out on the TiB₂/7050 aluminum matrix composites, which was solution treated and water cooled, and then naturally aged for different time. Then the average serration amplitude, fall time, recovery time and critical strain were analyzed to study the influence of natural aging time on PLC effect. Finally, the morphology of the tensile fracture was observed by means of scanning electron microscope. The results show that the natural aging time within 1 h has a little effect on strength of the TiB₂/7050 aluminum matrix composites, but the yield and tensile strengths increase significantly when the natural aging time is more than 1 h. The type of PLC bands evolves with the prolongation of natural aging time from the class B (0-1 h) with jumping nature to the class A (1.5 h) with continuous propagation, and then to the class D (2-4 h) with step propagation characteristics. When the natural aging time exceeds 1 h, the tensile fracture dimples of the TiB₂/7050 aluminum matrix composites become significantly shallower and the size becomes smaller, indicating that the plasticity of the composite decreases with the extension of natural aging time. Therefore, the interval between solution treatment and artificial aging of the TiB₂/7050 aluminum matrix composite should not beyond 1 h.

Key words: TiB₂/7050 aluminum matrix composites, natural aging, Portevin-Le Chatelier effect, fracture morphology

中图分类号:

TG156.1

尚洪帅, 韩文峰, 揭招财, 袁斌先. 自然时效对TiB₂/7050铝基复合材料PLC效应的影响[J]. 金属热处理, 2024, 49(5): 81-87.

Shang Hongshuai, Han Wenfeng, Jie Zhaocai, Yuan Binxian. Effect of natural aging on Portevin-Le Chatelier effect of TiB₂/7050 aluminum matrix composites[J]. Heat Treatment of Metals, 2024, 49(5): 81-87.

参考文献

[1]Ramasamy M, Daniel A A, Nithya M. A review on aluminium (Al7050) metal matrix composite characteristics reinforced with titanium[J]. Materials Today: Proceedings, 2021, 43: 1720-1723.
[2]Xiong Yifeng, Wang Wenhu, Shi Yaoyao, et al. Investigation on surface roughness, residual stress and fatigue property of milling in-situ TiB₂/7050Al metal matrix composites[J]. Chinese Journal of aeronautics, 2021, 34(4): 451-464.
[3]Ma Y, Addad A, Ji G, et al. Atomic-scale investigation of the interface precipitation in a TiB₂ nanoparticles reinforced Al-Zn-Mg-Cu matrix composite[J]. Acta Materialia, 2020, 185: 287-299.
[4]Duan M, Li Y, Yang X, et al. Mechanical responses of in-situ TiB₂/7050 composite subjected to monotonic and cyclic loadings: A comparative study with 7050-Al[J]. International Journal of Fatigue, 2022, 163: 107102.
[5]聂金凤, 范勇, 赵磊, 等. 颗粒增强铝基复合材料强韧化机制的研究新进展[J]. 材料导报, 2021, 35(9): 9009-9015.
Nie Jinfeng, Fan Yong, Zhao Lei, et al. Latest research progress on the strengthening and toughening mechanism of particle reinforced aluminum matrix composites[J]. Materials Reports, 2021, 35(9): 9009-9015.
[6]Chen Jie, Yu Weiwei, Zuo Zhenyu, et al. Effects of in-situ TiB₂ particles on machinability and surface integrity in milling of TiB₂/2024 and TiB₂/7075 Al composites[J]. Chinese Journal of Aeronautics, 2021, 34(6): 110-124.
[7]Yilmaz A. The Portevin-Le Chatelier effect: A review of experimental findings[J]. Science and Technology of Advanced Materials, 2011, 12(6): 063001.
[8]Choi Y, Ha J, Lee M G, et al. Observation of Portevin-Le Chatelier effect in aluminum alloy 7075-W under a heterogeneous stress field[J]. Scripta Materialia, 2021, 205: 114178.
[9]Mansouri L Z, Coër J, Thuillier S, et al. Investigation of Portevin-Le Châtelier effect during Erichsen test[J]. International Journal of Material Forming, 2020, 13: 687-697.
[10]Zhu H F, Liu J, Wu Y, et al. Hot deformation behavior and workability of in-situ TiB₂/7050Al composites fabricated by powder metallurgy[J]. Materials, 2020, 13: 5319.
[11]Zhou P, Song Y, Hua L, et al. Mechanical behavior and deformation mechanism of 7075 aluminum alloy under solution induced dynamic strain aging[J]. Materials Science and Engineering A, 2019, 759: 498-505.
[12]洪天然. 原位自生TiB₂/2009复合材料固溶时效行为研究[D]. 上海: 上海交通大学, 2016.
Hong Tianran. Study on solution and ageing behaviors of in-situ TiB₂/2009 composites[D]. Shanghai: Shanghai Jiao Tong University, 2016.
[13]Jung S H, Bae G, Kim M, et al. Effect of natural aging time on anisotropic plasticity and fracture limit of Al7075 alloy[J]. Materials Today Communications, 2022, 31: 103553.
[14]Matsumoto K, Aruga Y, Tsuneishi H, et al. Effects of precipitation state on serrated flow in Al-Mg (-Zn) alloys[J]. Materials Transactions, 2016, 57(7): 1101-1108.
[15]Chen B, Xi X, Gu T, et al. Influence of heat treatment on microstructure evolution and mechanical properties of TiB₂/Al 2024 composites fabricated by directed energy deposition[J]. Journal of Materials Research and Technology, 2020, 9(6): 14223-14236.
[16]郝世明, 毛建伟, 谢敬佩. 原位内生颗粒增强TiB₂/7055铝基复合材料的组织[J]. 材料热处理学报, 2015, 36(5): 29-34.
Hao Shiming, Mao Jianwei, Xie Jingpei. Microstructure of in-situ TiB₂ particle reinforced 7055 aluminum alloy matrix composites[J]. Transactions of Materials and Heat Treatment, 2015, 36(5): 29-34.
[17]Lebedkina T A, Lebyodkin M A. Effect of deformation geometry on the intermittent plastic flow associated with the Portevin-Le Chatelier effect[J]. Acta Materialia, 2008, 56(19): 5567-5574.
[18]Azarniya A, Taheri A K, Taheri K K. Recent advances in ageing of 7××× series aluminum alloys: A physical metallurgy perspective[J]. Journal of Alloys and Compounds, 2019, 781: 945-983.
[19]符师桦, 蔡玉龙, 张青川, 等. 自然时效对6061铝合金锯齿形屈服的影响[J]. 稀有金属材料与工程, 2017, 46(12): 3728-3732.
Fu Shihua, Cai Yulong, Zhang Qingchuan, et al. Influence of nature aging on serrated yielding of 6061 Al-based alloy[J]. Rare Metal Materials and Engineering, 2017, 46(12): 3728-3732.
[20]张建波, 张永安, 何振波, 等. 自然时效对7N01铝合金组织和性能的影响[J]. 稀有金属, 2012, 36(2): 191-195.
Zhang Jianbo, Zhang Yongan, He Zhenbo, et al. Effect of natural ageing on properties and microstructure of 7N01 aluminum alloys[J]. Chinese Journal of Rare Metals, 2012, 36(2): 191-195.
[21]Azarniya A, Taheri A K, Taheri K K. Recent advances in ageing of 7××× series aluminum alloys: A physical metallurgy perspective[J]. Journal of Alloys and Compounds, 2019, 781: 945-983.
[22]Wciślik W, Lipiec S. Void-induced ductile fracture of metals: Experimental observations[J]. Materials, 2022, 15: 6473.
[23]Cao J, Li F, Li P, et al. Analysis of ductile-brittle competitive fracture criteria for tension process of 7050 aluminum alloy based on elastic strain energy density[J]. Materials Science and Engineering A, 2015, 637: 201-214.
[24]Wang Y, Pan Q, Wei L, et al. Fracture toughness and fatigue crack growth analysis of 7050-T7451 alloy thick plate with different thicknesses[J]. Journal of Central South University, 2014, 21: 2977-2983.
[25]Han G, Zhang W, Zhang G, et al. High-temperature mechanical properties and fracture mechanisms of Al-Si piston alloy reinforced with in situ TiB₂ particles[J]. Materials Science and Engineering A, 2015, 633 161-168.

自然时效对TiB₂/7050铝基复合材料PLC效应的影响

Effect of natural aging on Portevin-Le Chatelier effect of TiB₂/7050 aluminum matrix composites

PDF

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

本文评价

[1]	周泽宇, 韩明明, 肖翔, 付金来. 退火工艺对7X50铝合金丝材组织与自然时效性能的影响[J]. 金属热处理, 2023, 48(8): 161-165.
[2]	黄伟丽, 李红斌, 王杏娟, 陈连生, 田亚强, 牛跃威, 陈四平. MnS夹杂形态对冷轧退火Ti微合金钢延伸率的影响[J]. 金属热处理, 2023, 48(7): 73-78.
[3]	岳旭, 张明玉, 杨嘉珞, 同晓乐, 赵子博, 乔恩利, 张起, 叶红川. 热处理工艺对亚稳定β型钛合金组织与拉伸性能的影响[J]. 金属热处理, 2023, 48(7): 187-192.
[4]	李海涛, 于娟, 刘洪涛, 谢睿勋, 冯朝辉, 赵唯一. 新型高强韧铝锂合金的显微组织和性能[J]. 金属热处理, 2023, 48(4): 173-177.
[5]	闫洪涛, 王永金, 齐海龙, 黄岩, 张科明, 张澣斗, 母镕. 淬火温度对空冷贝氏体-马氏体复相耐磨钢组织性能的影响[J]. 金属热处理, 2023, 48(3): 129-134.
[6]	岳旭, 张明玉, 同晓乐, 乔恩利, 张起, 杨嘉珞, 叶红川. Ti-6.5Al-3.5Mo-1.5Zr-0.3Si合金中α′相和α″相的组织演变与力学性能[J]. 金属热处理, 2023, 48(3): 215-220.
[7]	马英建, 彭其春, 袁清, 梁亮, 齐江华, 肖爱达, 薛正良. 热轧低密度钢Fe-1.80Mn-1.05Al-0.09C的高温热塑性[J]. 金属热处理, 2023, 48(2): 43-49.
[8]	同晓乐, 张明玉, 岳旭, 杨斌, 王玉佳, 阿热达克·阿力玛斯. 固溶处理对TC11钛合金组织与性能的影响[J]. 金属热处理, 2023, 48(2): 195-199.
[9]	贾延祯, 易幼平, 黄始全, 董非, 黄珂. 时效工艺对超低温成形2060铝锂合金组织及性能的影响[J]. 金属热处理, 2023, 48(10): 66-71.
[10]	徐向美, 王琪晨. 预时效处理对AlZnMgCu铝合金自然时效和烘烤硬化行为的影响[J]. 金属热处理, 2023, 48(10): 188-191.
[11]	元亚莎, 汪雨昌, 王文焱, 石如星, 元莎, 张玉栋. 回火温度对55NiCrMoV7热作模具钢组织和性能的影响[J]. 金属热处理, 2023, 48(1): 133-138.
[12]	赵竞, 王丽萍, 冯义成, 姜文勇, 王雷, 郭二军. 硅含量对耐热球墨铸铁显微组织和力学性能的影响[J]. 金属热处理, 2022, 47(9): 227-233.
[13]	赵天生, 方羽, 孙誉宾. 成形速度对7050铝合金锻件力学性能和断口形貌的影响[J]. 金属热处理, 2022, 47(6): 103-106.
[14]	莫金强, 冯光宏, 徐梅, 张威, 李阳. 化学成分对316L奥氏体不锈钢组织及变形行为的影响[J]. 金属热处理, 2022, 47(5): 81-86.
[15]	陈东俊, 李广阳, 刘刚. 时效处理对AlSi9Cu3压铸铝合金组织和力学性能的影响[J]. 金属热处理, 2022, 47(4): 53-56.