调质处理对34CrNiMo6钢连杆锻件组织与硬度的影响

doi:10.13251/j.issn.0254-6051.2024.05.029

金属热处理 ›› 2024, Vol. 49 ›› Issue (5): 173-178.DOI: 10.13251/j.issn.0254-6051.2024.05.029

调质处理对34CrNiMo6钢连杆锻件组织与硬度的影响

蒲博闻¹, 刘玉婷¹, 王延荣¹, 刁占英¹, 何敬卫²

1.中国北方发动机研究所天津, 天津 300400;
2.石家庄高能装备制造有限公司, 河北石家庄 050000

收稿日期:2023-11-12 修回日期:2024-04-06 出版日期:2024-05-25 发布日期:2024-06-28
作者简介:蒲博闻（1993—），男，助理研究员，博士，主要研究方向为工程材料及加工工艺，E-mail：pubowen1993@163.com。

Effect of quenching and tempering on microstructure and hardness of 34CrNiMo6 steel forged connecting rods

Pu Bowen¹, Liu Yuting¹, Wang Yanrong¹, Diao Zhanying¹, He Jingwei²

1. China North Engine Research Institute Tianjin, Tianjin 300400, China;
2. Shijiazhuang Gaoneng Equipment Manufacturing Co., Ltd., Shijiazhuang Hebei 050000, China

Received:2023-11-12 Revised:2024-04-06 Online:2024-05-25 Published:2024-06-28

摘要/Abstract

摘要： 通过微观组织表征、显微硬度测试及相图计算,研究了调质处理对34CrNiMo6钢连杆锻件微观组织与显微硬度的影响,同时基于微观组织演变规律,揭示了连杆锻件调质前后近表面和内部显微硬度变化的机制。结果表明,连杆锻件组织为珠光体和索氏体,表面有轻微脱碳。调质处理后,连杆锻件晶粒尺寸降低,局部应变均匀性变好,在近表面同时存在不显著脱碳层和弥散碳化物颗粒,硬度起伏变化明显;内部组织为均匀回火索氏体,显微硬度均值虽然较热处理前有所降低,但均匀组织降低了硬度的分散性。

关键词: 合金钢, 连杆锻件, 调质处理, 微观组织, 显微硬度

Abstract: Effect of quenching and tempering on microstructure and microhardness of 34CrNiMo6 steel forged connecting rods was studied by means of microstructure characterization, microhardness testing and phase diagram calculation. Based on the evolution of microstructure, the change regulation of surface and internal microhardness before and after quenching and tempering of the forged connecting rods was revealed. The results show that the forged connecting rod is composed of pearlite and sorbite, with slight decarburization on the surface. After quenching and tempering, the grain size of the forged connecting rod decreases and its local strain uniformity gets well. There is a non-significant decarburization layer and dispersed carbide particles on the near surface, thus the hardness variation of the near surface is obvious. Although the average micro-hardness after heat treatment is lower than that before heat treatment, the internal microstructure is uniform tempered sorbite, which reduces the dispersion of hardness.

Key words: alloy steel, forged connecting rod, quenching and tempering, microstructure, microhardness

中图分类号:

蒲博闻, 刘玉婷, 王延荣, 刁占英, 何敬卫. 调质处理对34CrNiMo6钢连杆锻件组织与硬度的影响[J]. 金属热处理, 2024, 49(5): 173-178.

Pu Bowen, Liu Yuting, Wang Yanrong, Diao Zhanying, He Jingwei. Effect of quenching and tempering on microstructure and hardness of 34CrNiMo6 steel forged connecting rods[J]. Heat Treatment of Metals, 2024, 49(5): 173-178.

参考文献

[1]赵继维, 李人宪. 高功率密度柴油机连杆强度分析[J]. 柴油机, 2010, 32(5): 23-26.
Zhao Jiwei, Li Renxian. Strength analysis on connecting rod of a high powder density diesel engine[J]. Diesel Engine, 2010, 32(5): 23-26.
[2]胡丰泽, 张波, 马茂, 等. 舰船柴油机用34CrNiMo6钢工艺性能的研究[J]. 机械管理开发, 2011(3): 12-13.
Hu Fengze, Zhang Bo, Ma Mao, et al. Research on 34CrNiMo6 processing property used for naval vessel engines[J]. Mechanical Management and Development, 2011(3): 12-13.
[3]王银燕, 张鹏奇, 王善. 柴油机连杆杆身疲劳强度可靠性分析[J]. 哈尔滨工程大学学报, 2001(1): 67-71.
Wang Yinyan, Zhang Pengqi, Wang Shan. Reliability analysis of diesel engine connecting rod fatigue strength[J]. Journal of Harbin Engineering University, 2001(1): 67-71.
[4]方琴, 陈庚, 吴永波, 等. 热处理对34CrNiMo6钢组织和力学性能的影响[J]. 铸造技术, 2017, 38(8): 1866-1867.
Fang Qin, Chen Geng, Wu Yongbo, et al. Influence of heat treatment on microstructure and mechanical properties of 34CrNiMo6 steel[J]. Foundry Technology, 2017, 38(8): 1866-1867.
[5]赵帆, 胡昊, 刘雅政, 等. 基于23MnNiMoCr54钢复杂显微组织和表面脱碳演变规律的退火条件控制[J]. 材料导报, 2022, 36(1): 130-135.
Zhao Fan, Hu Hao, Liu Yazheng, et al. Annealing condition control based on the evolution of complex microstructure and surface decarburization in 23MnNiMoCr54 steel[J]. Materials Reports, 2022, 36(1): 130-135.
[6]Gildersleeve M J. Relationship between decarburisation and fatigue strength of through hardened and carburising steels[J]. Materials Science and Technology, 1991, 7(4): 307-310.
[7]鲁修宇, 吴超, 罗德信, 等. 55SiCr弹簧钢脱碳与氧化行为研究[J]. 热处理技术与装备, 2016, 37(2): 63-66.
Lu Xiuyu, Wu Chao, Luo Dexin, et al. Behavioral research on decarburization and oxidation of the 55SiCr spring steel[J]. Heat Treatment Technology and Equipment, 2016, 37(2): 63-66.
[8]张凯, 陈银莉, 孙彦辉, 等. 加热过程中H₂O(g)对55SiCr弹簧钢脱碳的影响[J]. 金属学报, 2018, 54(10): 1350-1358.
Zhang Kai, Chen Yinli, Sun Yanhui, et al. Effect of H₂O(g) on decarburization of 55SiCr spring steel during the heating process[J]. Acta Metallurgica Sinica, 2018, 54(10): 1350-1358.
[9]王萍, 沈千成, 吴旭明, 等. 加热气氛对GCr15轴承钢氧化和脱碳特性的影响[J]. 热加工工艺, 2018, 47(22): 78-81.
Wang Ping, Shen Qiancheng, Wu Xuming, et al. Effect of heating atmosphere on oxidation and decarburization properties of GCr15 bearing steel[J]. Hot Working Technology, 2018, 47(22): 78-81.
[10]李京, 王剑, 高磊, 等. 34CrNiMo6钢连杆热处理工艺研究[J]. 热加工工艺, 2017, 46(6): 234-235, 240.
Li Jing, Wang Jian, Gao Lei, et al. Study on heat treatment technology of 34CrNiMo6 steel connecting rod[J]. Hot Working Technology, 2017, 46(6): 234-235, 240.
[11]Yang H, Gao T, Liu G, et al. Simultaneously improving strength and ductility for Al-Cu-Mg alloy via threadiness array of TiC nanoparticles[J]. Materialia, 2019, 6: 100333.
[12]Pu Bowen, Zhang Xiang, Chen Xiaofeng, et al. Exceptional mechanical properties of aluminum matrix composites with heterogeneous structure induced by in-situ graphene nanosheet-Cu hybrids[J]. Composites Part B: Engineering, 2022, 234: 109731.
[13]Zhang C L, Liu Y Z, Zhou L Y, et al. Forming condition and control strategy of ferrite decarburization in 60Si2MnA spring steel wires for automotive suspensions[J]. International Journal of Minerals, Metallurgy and Materials, 2012, 19(2): 116-121.
[14]何珺, 张辉, 刘哲, 等. 35CrMo钢过冷奥氏体转变曲线的测定[J]. 金属热处理, 2017, 42(12): 6-9.
He Jun, Zhang Hui, Liu Zhe, et al. Determination of CCT curves of 35CrMo steel[J]. Heat Treatment of Metals, 2017, 42(12): 6-9.
[15]杨顺贞, 唐建永, 吕均益, 等. 回火温度对1Cr13不锈钢组织与力学性能的影响[J]. 热加工工艺, 2012, 41(12): 181-183, 186.
Yang Shunzhen, Tang Jianyong, Lü Junyi, et al. Effect of tempering temperature on microstructure and mechanical properties of 1Cr13 stainless steel[J]. Hot Working Technology, 2012, 41(12): 181-183, 186.
[16]孙维连, 杨钰瑛. 35CrMo钢拉杆显微组织与性能[J]. 金属热处理, 2005, 30(11): 79-82.
Sun Weilian, Yang Yuying. Microstructure and properties of pulling pole of 35CrMo steel[J]. Heat Treatment of Metals, 2005, 30(11): 79-82.

调质处理对34CrNiMo6钢连杆锻件组织与硬度的影响

Effect of quenching and tempering on microstructure and hardness of 34CrNiMo6 steel forged connecting rods

PDF

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

本文评价

[1]	郭炜, 管博, 陈威, 吴丹. 多次闭模压缩对不同Si含量AZ31合金显微组织和耐磨性能的影响[J]. 金属热处理, 2024, 49(5): 36-39.
[2]	王泽龙, 冯兆龙, 李伟, 孙思博. 冷塑性变形及退火工艺对Ti45Nb合金组织和性能的影响[J]. 金属热处理, 2024, 49(5): 112-117.
[3]	张增光, 史吉鹏, 王新宇, 刘艳梅, 杨立新, 康冲, 刘刚. 退火温度对Ti60钛合金激光焊接接头组织与力学性能的影响[J]. 金属热处理, 2024, 49(5): 130-134.
[4]	张勇, 马青山, 李如杨, 胡效东. S11306铁素体不锈钢厚板焊后热处理特性[J]. 金属热处理, 2024, 49(5): 146-152.
[5]	刘干, 孔祥磊, 黄明浩, 王杨, 张英慧. 冷却速率对超高强度X90M管线钢相变行为的影响[J]. 金属热处理, 2024, 49(5): 162-167.
[6]	赵忠超, 汲庆涛, 曹善鹏, 唐和壮, 李宾良, 牛博雅, 孙有政. 固溶处理对7175铝合金组织和力学性能的影响[J]. 金属热处理, 2024, 49(5): 186-192.
[7]	刘子知, 孙福臻, 李晓旭, 李蕙宇, 张泉达, 穆雪松, 赵岩. 固溶时效处理对稀土铝合金力学性能及组织的影响[J]. 金属热处理, 2024, 49(5): 193-198.
[8]	王利鹏, 葛君超, 代昆宏. 热处理工艺对低碳高铜HSLA钢组织与力学性能的影响[J]. 金属热处理, 2024, 49(5): 199-203.
[9]	邓德伟, 万泓明, 汪红所, 陈文博, 连世伟. 激光熔覆Stellite6+WC复合涂层对不锈钢叶片耐水蚀性能的影响[J]. 金属热处理, 2024, 49(5): 243-251.
[10]	吕犇, 万训智, 刘澄. 一种低碳合金渗碳钢轧辊的失效行为[J]. 金属热处理, 2024, 49(5): 272-277.
[11]	李为先, 彭伟, 胡杰, 刘腾轼, 周路海, 董瀚. Cu对390 MPa级CrNiMo系低合金船用钢板力学性能的影响[J]. 金属热处理, 2024, 49(4): 1-7.
[12]	张亮, 黄学启, 刘李斌, 李振, 谢春乾, 史昌, 刘兴全. 合金化镀锌双相钢DP980的研制开发[J]. 金属热处理, 2024, 49(4): 34-37.
[13]	徐国进, 韩思聪, 朱孜毅, 罗俊锋, 何金江, 陈畅, 陈桂. 热处理制度对高纯钴微观组织及磁性能的影响[J]. 金属热处理, 2024, 49(4): 61-65.
[14]	郑磊, 徐达, 鲁宇杰, 廖文超, 殷安民, 陈候. 激光增材制造316L不锈钢退火过程中微观组织演变和力学性能[J]. 金属热处理, 2024, 49(4): 66-77.
[15]	翟鹏飞, 潘浩, 邢淑清, 宫美娜, 刘永珍, 麻永林. 脉冲磁场时效处理对A356铝合金组织和性能的影响[J]. 金属热处理, 2024, 49(4): 138-145.