脱碳退火工艺对薄规格取向硅钢织构及磁性能的影响

doi:10.13251/j.issn.0254-6051.2024.06.003

金属热处理 ›› 2024, Vol. 49 ›› Issue (6): 17-22.DOI: 10.13251/j.issn.0254-6051.2024.06.003

脱碳退火工艺对薄规格取向硅钢织构及磁性能的影响

王艺橦, 刘旭明, 郭函, 耿志宇, 薛峰

鞍钢集团北京研究院有限公司, 北京 102211

收稿日期:2023-11-08 修回日期:2024-04-13 出版日期:2024-06-25 发布日期:2024-07-29
作者简介:王艺橦(1993—),女,研究员,博士,主要研究方向为取向硅钢的织构演变,E-mail: 929633853@qq.com
基金资助:
国家重点研发计划(2017YFB0304700)

Effect of decarburizing annealing process on texture and magnetic properties of thin-gauge oriented silicon steel

Wang Yitong, Liu Xuming, Guo Han, Geng Zhiyu, Xue Feng

Ansteel Beijing Research Institute Co., Ltd., Beijing 102211, China

Received:2023-11-08 Revised:2024-04-13 Online:2024-06-25 Published:2024-07-29

摘要/Abstract

摘要： 采用EBSD及XRD等对薄规格取向硅钢试样不同退火温度(820、840、860 ℃)及退火时间(120、150 s)处理后的组织、织构和磁性能进行对比。结果表明,升高脱碳退火温度及减小退火时间可降低取向硅钢的晶粒尺寸,提高有利织构的比例及再结晶比例,为二次再结晶过程中Goss晶粒的异常长大提供基础,从而提高取向硅钢的磁性能。当脱碳退火温度为860 ℃,退火时间为120 s时,取向硅钢试样的磁性能最优,磁感J₈₀₀为1.807 T,铁损P_1.7为1.07 W·kg^-1。

关键词: 取向硅钢, 脱碳退火, 织构, 磁性能

Abstract: Microstructure,texture and magnetic properties of thin-gauge oriented silicon steel after annealing at different temperatures (820, 840, 860 ℃) and time (120, 150 s) were compared by means of EBSD and XRD. The results show that increasing the decarburization annealing temperature and decreasing the decarburization annealing time can reduce the grain size, increase the proportion of favorable texture and recrystallization ratio of the oriented steel, which provide the basis for the abnormal growth of Goss grains in the process of secondary recrystallization, so as to improve the magnetic properties of the oriented silicon steel. When the decarburization annealing temperature is 860 ℃ and the annealing time is 120 s, the oriented silicon steel specimen obtains the best magnetic properties, with the magnetic induction intensity J₈₀₀ of 1.807 T and the core loss P_1.7 of 1.07 W·kg^-1.

Key words: oriented silicon steel, decarburizing annealing, texture, magnetic properties

中图分类号:

TM275

王艺橦, 刘旭明, 郭函, 耿志宇, 薛峰. 脱碳退火工艺对薄规格取向硅钢织构及磁性能的影响[J]. 金属热处理, 2024, 49(6): 17-22.

Wang Yitong, Liu Xuming, Guo Han, Geng Zhiyu, Xue Feng. Effect of decarburizing annealing process on texture and magnetic properties of thin-gauge oriented silicon steel[J]. Heat Treatment of Metals, 2024, 49(6): 17-22.

参考文献

[1]何忠治, 赵宇, 罗海文. 电工钢[M]. 北京:冶金工业出版社, 2012.
[2]毛卫民, 杨平. 电工钢的材料学基础[M]. 北京:高等教育出版社, 2013.
[3]王洋. 薄带连铸取向硅钢成分设计与组织织构调控机理的研究[D]. 沈阳:东北大学, 2017.
Wang Yang. Composition design of strip casting grain oriented silicon steels and microstructure texture regulation mechanism[D]. Shenyang: Northeastern University, 2017.
[4]宋红宇. 薄带连铸取向硅钢的组织、织构演化行为及控制机理[D]. 沈阳:东北大学, 2017.
Song Hongyu. Evolution behavior and control mechanism of microstructure and texture of strip casting grain-oriented silicon steel[D]. Shenyang: Northeastern University, 2017.
[5]张波. 超薄取向硅钢显微组织及织构演化行为与影响因素研究[D]. 北京:钢铁研究总院, 2021.
Zhang Bo. Study on microstructure and texture evolution and influencing factors during preparing ultra-thin grain-oriented silicon steel[D]. Beijing: Central Iron and Steel Research Institute, 2021.
[6]韩世绪. 退火参数对含铌取向硅钢组织、织构及磁性能的影响[D]. 唐山:华北理工大学, 2019.
Han Shixu. Effect of annealing parameters on microstructure texture and magnetic properties of niobium-containing orientated silicon steel[D]. Tangshan: North China University of Science and Technology, 2019.
[7]杨富尧, 何承绪, 孟利, 等. 薄规格冷轧取向硅钢脱碳板中析出相粒子及织构分布[J]. 材料热处理学报, 2015, 36(10):103-109.
Yang Fuyao, He Chengxu, Meng Li, et al. Precipitates distribution and textures in decarburized sheets of thin-gauge cold-rolled grain-oriented silicon steels[J]. Transactions of Materials and Heat Treatment, 2015, 36(10): 103-109.
[8]刘永珍, 董丽丽, 刘宝志, 等. 3.1%Si取向硅钢显微组织和宏观织构演变[J]. 金属热处理, 2023, 48(9): 238-241.
Liu Yongzhen, Dong Lili, Liu Baozhi, et al. Evolution of microstructure and macrotexture of 3.1%Si oriented silicon steel[J]. Heat Treatment of Metals, 2023, 48(9): 238-241.
[9]丁娇. 薄规格取向硅钢的塑性变形与再结晶[D]. 武汉:武汉科技大学, 2022.
[10]Dun Hao, Zhang Yuanxiang, Wang Nuojin, et al. Effect ofΣ3 grain boundaries on microstructure and properties of oriented Fe-6.5wt%Si in twin-roll strip casting[J]. Journal of Magnetism and Magnetic Materials, 2022, 559: 169522.
[11]董丽丽, 黄禄璐, 卢晓禹, 等. 高磁感取向硅钢的脱碳退火工艺[J]. 金属热处理, 2023, 48(3): 124-128.
Dong Lili, Huang Lulu, Lu Xiaoyu, et al. Decarburization annealing process of high magnetic induction oriented silicon steel[J]. Heat Treatment of Metals, 2023, 48(3): 124-128.
[12]喻春明, 张继明, 党波, 等. 高磁感取向硅钢轧制及热处理过程中的晶界和织构演化[J]. 金属热处理, 2021, 46(12): 204-208.
Yu Chunming, Zhang Jiming, Dang Bo, et al. Grain boundary and texture evolution of a high magnetic grain-oriented silicon steel during rolling and heat treatment[J]. Heat Treatment of Metals, 2021, 46(12): 204-208.

[1]	张帅坤, 张超勇, 吴剑钊, 唐莉梅. 40Cr钢滚刀织构表面激光淬火的数值模拟[J]. 金属热处理, 2024, 49(5): 47-54.
[2]	乔鹏飞, 吴忠旺, 张慧敏, 金自力, 任慧平, 郭欢. 不同终轧温度下高强无取向电工钢的热轧和常化组织与织构[J]. 金属热处理, 2024, 49(5): 153-157.
[3]	李为先, 彭伟, 胡杰, 刘腾轼, 周路海, 董瀚. Cu对390 MPa级CrNiMo系低合金船用钢板力学性能的影响[J]. 金属热处理, 2024, 49(4): 1-7.
[4]	薛润东, 方锡祯. 热处理工艺和铜含量对高硅无取向硅钢织构的影响[J]. 金属热处理, 2024, 49(4): 78-82.
[5]	魏辉, 林媛, 王红霞, 王士嘉, 李旭, 张文康, 王一德. 二次冷轧中间退火温度对3.5%Si无取向硅钢组织织构的影响机理[J]. 金属热处理, 2024, 49(3): 37-43.
[6]	尤文豪, 陈霞, 陈彬. 常化工艺对取向硅钢组织织构和磁性能的影响[J]. 金属热处理, 2024, 49(3): 50-55.
[7]	刘再旺, 郭敏, 滕华湘, 杨利斌, 梁轩, 刘广会, 刘顺明. 退火温度对超深冲搪瓷钢成型性能及再结晶织构的影响[J]. 金属热处理, 2024, 49(3): 91-97.
[8]	张瑞, 唐恩, 袁清, 任杰, 莫家璇. 快速退火对冷轧超低碳钢组织和性能的影响[J]. 金属热处理, 2024, 49(3): 116-121.
[9]	孙文科, 吴忠旺, 任慧平, 张慧敏, 郭欢, 赵小龙, 罗晓阳, 狄彦军. 低温高磁感取向硅钢板坯后续工艺流程中的织构演变[J]. 金属热处理, 2024, 49(2): 40-44.
[10]	何承渝, 蔡晨, 谷宇, 李静媛. 不同冷轧压下率对因瓦合金组织与性能的影响[J]. 金属热处理, 2024, 49(2): 120-127.
[11]	朱嘉武, 欧阳晟. 退火对FeCoNi_2-xMnGa_x高熵合金微观组织、力学性能和磁性能的影响[J]. 金属热处理, 2024, 49(1): 22-31.
[12]	张巧霞, 张博厚, 徐国进, 郝海英, 罗俊锋, 何金江. 热处理及轧制过程中NiPt5合金微观组织及磁性能演变[J]. 金属热处理, 2024, 49(1): 206-210.
[13]	杨源远, 王栋, 黄利, 刘宝志. HiB与CGO取向硅钢的对比及其常化退火工艺[J]. 金属热处理, 2024, 49(1): 228-234.
[14]	陈燕蕊, 吕科, 李岩, 任少卿, 赵明静, 董瑞, 定巍. 烧结温度对2∶17H型高性能SmCo合金微观结构和磁性能的影响[J]. 金属热处理, 2023, 48(9): 35-41.
[15]	谢尚恒, 孙有平, 朱嘉欣, 方德俊. 微量Zr对深冷轧制Al-Cu-Mg合金微观组织及性能的影响[J]. 金属热处理, 2023, 48(9): 174-179.

脱碳退火工艺对薄规格取向硅钢织构及磁性能的影响

Effect of decarburizing annealing process on texture and magnetic properties of thin-gauge oriented silicon steel

PDF

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

本文评价