300M钢等温淬火相变特性及力学性能

doi:10.13251/j.issn.0254-6051.2025.01.027

金属热处理 ›› 2025, Vol. 50 ›› Issue (1): 173-179.DOI: 10.13251/j.issn.0254-6051.2025.01.027

300M钢等温淬火相变特性及力学性能

赵晓宇¹, 张铮^1,2, 杨慧君¹, 石晓辉¹, 张敏^1,2, 乔珺威¹

1.太原理工大学材料科学与工程学院, 山西太原 030024;
2.太原理工大学山西航天装备热处理与表面处理技术创新中心, 山西太原 030024

收稿日期:2024-08-05 修回日期:2024-11-22 出版日期:2025-01-25 发布日期:2025-03-12
通讯作者: 张铮,讲师,E-mail:zhangzheng1980@126.com
作者简介:赵晓宇(1996—),男,硕士研究生,主要研究方向为300M钢的热处理工艺及力学性能,E-mail:18235117908@163.com。

Isothermal quenching phase transformation characteristics and mechanical properties of 300M steel

Zhao Xiaoyu¹, Zhang Zheng^1,2, Yang Huijun¹, Shi Xiaohui¹, Zhang Min^1,2, Qiao Junwei¹

1. College of Materials Science and Engineering, Taiyuan University of Technology, Taiyuan Shanxi 030024, China;
2. Shanxi Aerospace Equipment Heat Treatment and Surface Treatment Technology Innovation Centre, Taiyuan University of Technology, Taiyuan Shanxi 030024, China

Received:2024-08-05 Revised:2024-11-22 Online:2025-01-25 Published:2025-03-12

摘要/Abstract

摘要： 利用热膨胀仪、彩色金相、扫描电镜和透射电镜等研究了300M钢在Ms附近240~320 ℃范围内的等温淬火工艺对相变特性和力学性能的影响。结果表明,在Ms以下等温淬火时300M钢先产生无热马氏体,缩短贝氏体相变孕育期。与Ms以上的320 ℃等温淬火工艺相比,在Ms以下的260 ℃等温淬火时残留奥氏体由块状M/A岛的形态转变为存在于贝氏体板条之间的薄膜形态,且贝氏体板条平均宽度下降,抗拉强度由1550 MPa提高至1930 MPa,断裂总延伸率由7.7%提高至9.2%,强度和塑性同步提高。

关键词: 300M钢, 等温淬火, 彩色金相, 力学性能

Abstract: Effect of isothermal quenching process at 240-320 ℃ near Ms on the phase transformation characteristics and mechanical properties of 300M steel was studied by means of thermal dilatometer, color metallography, scanning electron microscopy and transmission electron microscopy. The results show that the isothermal quenching below Ms result in athermal martensite produces first and the incubation period of bainite transformation shortened of the 300M steel. Compared with the isothermal quenching process at 320 ℃ above Ms, the isothermal quenching process at 260 ℃ below Ms makes the retained austenite transform from blocky M/A islands to film between bainite laths, the average width of bainite lath decreases, the tensile strength increases from 1550 MPa to 1930 MPa and the total elongation increases from 7.7% to 9.2%, showing that the strength and plasticity increase simultaneously.

Key words: 300M steel, isothermal quenching, color metallography, mechanical properties

中图分类号:

TG161

赵晓宇, 张铮, 杨慧君, 石晓辉, 张敏, 乔珺威. 300M钢等温淬火相变特性及力学性能[J]. 金属热处理, 2025, 50(1): 173-179.

Zhao Xiaoyu, Zhang Zheng, Yang Huijun, Shi Xiaohui, Zhang Min, Qiao Junwei. Isothermal quenching phase transformation characteristics and mechanical properties of 300M steel[J]. Heat Treatment of Metals, 2025, 50(1): 173-179.

参考文献

[1]夏伟军, 赵青卿, 袁武华, 等. 300M钢的高温氧化行为[J]. 金属热处理, 2020, 45(11): 49-55.
Xia Weijun, Zhao Qingqing, Yuan Wuhua, et al. High temperature oxidation behavior of 300M steel[J]. Heat Treatment of Metals, 2020, 45(11): 49-55.
[2]牛艳娥, 赵芃沛, 李宁, 等. 国内外超高强度钢的研究现状及应用[J]. 兵器装备工程学报, 2021, 42(7): 274-279.
Niu Yan'e, Zhao Pengpei, Li Ning, et al. Research status and application of ultra-high strength steel at home and abroad[J]. Journal of Ordnance Equipment Engineering, 2021, 42(7): 274-279.
[3]刘笑笑, 张铮, 张杰, 等. 回火温度对柔性齿轮钢40CrNiMo组织及力学性能的影响[J]. 金属热处理, 2021, 46(8): 99-104.
Liu Xiaoxiao, Zhang Zheng, Zhang Jie, et al. Effect of tempering temperature on microstructure and mechanical properties of 40CrNiMo steel for flexible gear[J]. Heat Treatment of Metals, 2021, 46(8): 99-104.
[4]袁培柏. 300M钢制飞机起落架零件的真空淬火[J]. 金属热处理, 1991, 16(10): 29-33.
[5]田俊羽, 徐光, 黄浩, 等. Ms以下温度等温淬火对中碳贝氏体钢相变和性能影响[J]. 钢铁研究学报, 2019, 31(5): 468-474.
Tian Junyu, Xu Guang, Huang Hao, et al. Effects of below-Ms austempering temperature on baintie transformation and properties of a medium-carbon bainitic steel[J]. Journal of lron and Steel Research, 2019, 31(5): 468-474.
[6]Zhao J, Guo K, He Y M, et al. Extremely high strength achievement in medium-C nanobainite steel[J]. Scripta Materialia, 2018, 152: 20-23.
[7]吴忠潮, 周拥军, 段宝玉, 等. 20Si2Mn2CrNi钢Ms点下的等温转变组织及其强韧性[J]. 金属热处理, 2023, 48(7): 15-21.
Wu Zhongchao, Zhou Yongjun, Duan Baoyu, et al. Isothermal microstructure and strength and toughness of 20Si2Mn2CrNi steel below Ms[J]. Heat Treatment of Metals, 2023, 48(7): 15-21.
[8]Zhao Leijie, Qian Lihe, Meng Jiangying, et al. Below-Ms austempering to obtain refined bainitic structure and enhanced mechanical properties in low-C high-Si/Al steels[J]. Scripta Materialia, 2016, 112: 96-100.
[9]Zhu Kangying, Bouaziz Olivier, Oberbillig Carla, et al. An approach to define the effective lath size controlling yield strength of bainite[J]. Materials Science and Engineering A, 2010, 527(24): 6614-6619.
[10]Navarro-López A, Sietsma J, Santofimia M J. Effect of prior athermal martensite on the isothermal transformation kinetics below Ms in a low-C high-Si steel[J]. Metallurgical and Materials Transactions A, 2016, 47(3): 1028-1039.
[11]Tomita Yoshiyuki, Okawa Takeyoshi. Effect of microstructure on mechanical properties of isothermally bainite-transformed 300M steel[J]. Materials Science and Engineering A, 1993, 172(1): 145-151.
[12]Zhou Mingxing, Xu Guang, Wang Li, et al. Effects of austenitization temperature and compressive stress during bainitic transformation on the stability of retained austenite[J]. Transactions of the Indian Institute of Metals, 2017, 70(6): 1447-1453.
[13]Garcia-Mateo C, Caballero F G, Bhadeshia H K D H. Acceleration of low-temperature bainite[J]. ISIJ International, 2003, 43(11): 1821-1825.
[14]Qian Lihe, Li Zhi, Wang Tongliang, et al. Roles of pre-formed martensite in below-Ms bainite formation, microstructure, strain partitioning and impact absorption energies of low-carbon bainitic steel[J]. Journal of Materials Science and Technology, 2022, 96: 69-84.
[15]Matsuda Hiroshi, Bhadeshia Harshad K D H. Kinetics of the bainite transformation[J]. Proceedings of the Royal Society A, 2004, 460: 1707-1722.
[16]Mondal Jayanta, Das Karabi, Das Siddhartha. Isothermal transformation kinetics, microstructure and mechanical properties of a carbide free bainitic steel[J]. Materials Characterization, 2021, 177: 111166.
[17]Kawata Hiroyuki, Hayashi Kunio, Sugiura Natsuko, et al. Effect of martensite in initial structure on bainite transformation[J]. Materials Science Forum, 2010, 638-642: 3307-3312.
[18]Shibata A, Morito S, Furuhara T, et al. Local orientation change inside lenticular martensite plate in Fe-33Ni alloy[J]. Scripta Materialia, 2005, 53(5): 597-602.
[19]Gong W, Tomota Y, Harjo S, et al. Effect of prior martensite on bainite transformation in nanobainite steel[J]. Acta Materialia, 2015, 85: 243-249.
[20]Gao Guhui, Zhang Han, Gui Xiaolu, et al. Enhanced ductility and toughness in an ultrahigh-strength Mn-Si-Cr-C steel: The great potential of ultrafine filmy retained austenite[J]. Acta Materialia, 2014, 76: 425-433.

300M钢等温淬火相变特性及力学性能

Isothermal quenching phase transformation characteristics and mechanical properties of 300M steel

PDF

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

本文评价

[1]	李建国, 贾冬生, 赵银虎, 刘玉宝, 王旭, 赵磊城, 兰岳光. 稀土Ce对32MnMoNiCu铸钢微观组织与力学性能的影响[J]. 金属热处理, 2025, 50(1): 47-52.
[2]	黄威明, 周海安, 赵秋红, 许文兵, 于鑫泓, 冯以盛, 张云山, 赵而团. 热处理对51CrMnV弹簧钢力学性能和疲劳性能的影响[J]. 金属热处理, 2025, 50(1): 75-80.
[3]	高鑫, 李明东, 苏杰, 姜庆伟, 夏世洪, 张永强, 宁静. 两相区淬火温度对Cr-Mn-Si低合金钢组织及性能的影响[J]. 金属热处理, 2025, 50(1): 119-125.
[4]	郝莹, 王明伟. 时效处理对石墨烯/Al-Zn-Mg-Cu合金复合材料性能的影响[J]. 金属热处理, 2025, 50(1): 133-139.
[5]	滕宏胤, 王银军, 吴索团. 不同材料夹送辊堆焊层退火处理后的组织及性能对比[J]. 金属热处理, 2025, 50(1): 155-161.
[6]	朱晓龙, 王争辉, 王文焱, 谢敬佩, 刁晓刚, 张飞扬. TiC纳米颗粒强化9Cr耐热钢的微观组织及力学性能[J]. 金属热处理, 2025, 50(1): 187-194.
[7]	刘锦润, 郎宇平, 陈海涛, 冯翰秋, 高智君, 张正富. 氮对冷轧022Cr18Ni8N亚稳奥氏体不锈钢组织及力学性能的影响[J]. 金属热处理, 2025, 50(1): 195-200.
[8]	王成, 刘亚军, 陈志辉, 童善康, 甘晓龙. 冷却温度对热轧双相钢组织和力学性能的影响[J]. 金属热处理, 2025, 50(1): 213-218.
[9]	王欢欢, 卢苏君, 李渊, 徐宁, 朱廷贤, 王旭, 魏宁, 吴大莉, 彭威中. 机器学习预测退火温度和时间对SUS321不锈钢力学性能的影响[J]. 金属热处理, 2025, 50(1): 266-271.
[10]	周浩, 王帅, 曾燕屏, 马志宝, 周德, 郭德瑞, 董树青. 长时在役Inconel 783高温合金螺栓的显微组织和力学性能[J]. 金属热处理, 2024, 49(9): 36-42.
[11]	陈子健, 林业佳, 李传强, 邓仁昡, 董勇, 章争荣. 微合金化调控7075铝合金的微观组织与力学性能[J]. 金属热处理, 2024, 49(9): 58-63.
[12]	任广笑, 王超, 曹喜娟, 王凯, 王红霞, 程伟丽, 牛晓峰. 时效处理对Mg-Y-Gd-Zn-Zr合金中LPSO相演变及性能的影响[J]. 金属热处理, 2024, 49(9): 96-102.
[13]	任鹏帅, 秦凤, 周骞, 赵雷杰, 崔护, 彭子奥, 武常生. 等温淬火对含铝无碳化物贝氏体钢组织和性能的影响[J]. 金属热处理, 2024, 49(9): 103-109.
[14]	张宇, 李圣阳, 魏晓蓼, 柴志松, 李泳. 铬合金化Q&P钢的热处理工艺优化与碳配分行为[J]. 金属热处理, 2024, 49(9): 110-116.
[15]	张青科, 诸汇涛, 陈根保, 陈立田, 夏亚金, 胡方勤, 宋振纶. 形变热处理对新型无Ti马氏体时效钢焊缝组织与力学性能的影响[J]. 金属热处理, 2024, 49(9): 117-124.