正火温度对USS122G超高强度不锈钢组织及性能的影响

doi:10.13251/j.issn.0254-6051.2020.11.014

金属热处理 ›› 2020, Vol. 45 ›› Issue (11): 73-77.DOI: 10.13251/j.issn.0254-6051.2020.11.014

正火温度对USS122G超高强度不锈钢组织及性能的影响

白若昕^1,2, 刘振宝², 曹建春¹, 杨哲^2,3

1.昆明理工大学材料科学与工程学院, 云南昆明 650093;
2.钢铁研究总院特殊钢研究所, 北京 100081;
3.重庆大学材料科学与工程学院, 重庆 400030

收稿日期:2020-04-24 出版日期:2020-11-25 发布日期:2020-12-29
通讯作者: 刘振宝,教授,博士,E-mail:liuzhenbao@nercast.com
作者简介:白若昕(1994—),男,硕士研究生,主要研究方向为超高强度不锈钢材料,E-mail:157807584@qq.com。
基金资助:
国家重点研发计划(2016YFB0300104)

Effect of normalizing temperature on microstructure and properties of USS122G ultra-high strength stainless steel

Bai Ruoxin^1,2, Liu Zhenbao², Cao Jianchun¹, Yang Zhe^2,3

1. Faculty of Materials Science and Engineering, Kunming University of Science and Technology, Kunming Yunnan 650093, China;
2. Institute for Special Steels, Central Iron and Steel Research Institute, Beijing 100081, China;
3. School of Materials Science and Engineering, Chongqing University, Chongqing 400030, China

Received:2020-04-24 Online:2020-11-25 Published:2020-12-29

摘要/Abstract

摘要： 通过光学显微镜、电子显微镜、物理化学相分析等表征方法研究了不同正火温度对USS122G超高强度不锈钢的微观组织和硬度的影响。结果表明:随着正火温度的升高,试验钢硬度降低,残留奥氏体含量增加,第二相含量减少,原奥氏体晶粒变大。综合分析不同正火温度对钢中第二相的种类、质量分数与硬度以及晶粒大小的影响,最终确定该试验钢的最佳正火温度为1020 ℃。

关键词: 正火温度, 硬度, 第二相, 显微组织, 超高强度不锈钢

Abstract: Effect of normalizing temperature on the microstructure and hardness of USS122G ultra-high strength stainless steel was studied by means of optical microscope, electron scanning microscope, physicochemical phase analysis, etc. The results indicate that with the increase of normalizing temperature, the hardness and the secondary phase content decrease, while the retained austenite content and the prior austenite grain size increase. By comprehensive analysis of the relationship between the normalizing temperature with the type, mass fraction, hardness and grain size of the secondary phase in the steel, it is concluded that the optimum normalizing temperature of the tested steel is 1020 ℃.

Key words: normalizing temperatures, hardness, secondary phase, microstructure, ultra-high strength stainless steel

中图分类号:

TG156

白若昕, 刘振宝, 曹建春, 杨哲. 正火温度对USS122G超高强度不锈钢组织及性能的影响[J]. 金属热处理, 2020, 45(11): 73-77.

Bai Ruoxin, Liu Zhenbao, Cao Jianchun, Yang Zhe. Effect of normalizing temperature on microstructure and properties of USS122G ultra-high strength stainless steel[J]. Heat Treatment of Metals, 2020, 45(11): 73-77.

参考文献

[1]赵先存, 宋顺为, 杨志勇, 等. 高强度超高强度不锈钢[M]. 北京: 高等教育出版社, 2008.
[2]王晓辉, 罗海文. 飞机起落架用超高强度不锈钢的研究及应用进展[J]. 材料工程, 2019, 47(9): 1-12.
Wang Xiaohui, Luo Haiwen. Research and application progress in ultra-high strength stainless steel for aircraft landing gear[J]. Journal of Materials Engineering, 2019, 47(9): 1-12.
[3]刘振宝, 杨志勇, 雍歧龙, 等. 1900 MPa级超高强度不锈钢的研制[J]. 机械工程材料, 2008, 32(3): 48-51.
Liu Zhenbao, Yang Zhiyong, Yong Qilong, et al. A 1900 MPa grade ultra-high strength stainless steel[J]. Materials for Mechanical Engineering, 2008, 32(3): 48-51.
[4]王晓辉. USS122超高强度不锈钢热变形行为与强韧化机理的研究[D]. 昆明: 昆明理工大学, 2015.
Wang Xiaohui. Hot deformation behavior and strengthening and toughening mechanism of USS122G ultra-high strength stainless steel[D]. Kunming: Kunming University of Science and Technology, 2015.
[5]马森林, 吕景林. 齿轮锻坯等温正火预处理工艺方法探讨[J]. 热处理, 2003, 18(4): 46-49.
Ma Senlin, Lü Jinglin. Exploring on pretreatment process of isothermal normalizing for forged gear stock[J]. Heat Treatment, 2003, 18(4): 46-49.
[6]李荫现, 左彪, 李卫民, 等. 22CrMoH钢齿轮锻件等温正火工艺改进[J]. 热加工工艺, 2019, 48(6): 242-244.
Li Yinxian, Zuo Biao, Li Weimin, et al. Improvement of isothermal normalizing process for 22CrMoH steel gear forgings[J]. Hot Working Technology, 2019, 48(6): 242-244.
[7]Li Z X, Li C S, Zhang J, et al. Microstructure of hot rolled 1.0C-1.5Cr bearing steel and subsequent spheroidization annealing[J]. Metallurgical and Materials Transactions A, 2016, 47(7): 3607-3621.
[8]周金华, 陈迦杉, 申勇峰. 正火温度对GCr15轴承钢碳化物溶解扩散和冲击性能的影响[J]. 金属热处理, 2019, 44(3): 100-103.
Zhou Jinhua, Chen Jiashan, Shen Yongfeng. Effect of normalizing temperature on carbide solution-diffusion and impact properties of GCr15 bearing steel[J]. Heat Treatment of Metals, 2019, 44(3): 100-103.
[9]刘宗昌, 李文学, 高占勇, 等. 钢的退火软化机理[J]. 包头钢铁学院学报, 1998(3): 14-17.
Liu Zongchang, Li Wenxue, Gao Zhanyong, et al. Mechanism of annealing softening of the steels[J]. Journal of Baotou University of Iron and Steel Technolog, 1998(3): 14-17.
[10]Prawoto Y, Jasmawati N, Sumeru K. Effect of prior austenite grain size on the morphology and mechanical properties of martensite in medium carbon steel[J]. Journal of Materials Science and Technology, 2012, 28(5): 461-466.
[11]Sellars C M, Whiteman J A. Recrystallization and grain growth in hot rolling[J]. Metal Science, 1979, 13(3-4): 187-194.
[12]潘晓刚, 唐荻, 宋勇, 等. DP590级双相钢奥氏体晶粒长大模型[J]. 北京科技大学学报, 2013, 35(2): 189-194.
Pan Xiaogang, Tang Di, Song Yong, et al. Austenite grain growth model of DP590 dual-phase steel[J]. Journal of University of Science and Technology Beijing, 2013, 35(2): 189-194.
[13]余永宁. 金属学原理[M]. 北京: 冶金工业出版社, 2013.
[14]雍岐龙. 钢铁材料中的第二相[M]. 北京: 冶金工业出版社, 2006.
[15]张可, 赵时雨, 隋凤利, 等. 终轧温度对Ti-V-Mo复合微合金钢组织演变和硬度的影响[J]. 材料研究学报, 2019, 33(3): 191-198.
Zhang Ke, Zhao Shiyu, Sui Fengli, et al. Effect of finish rolling temperature on microstructure evolution and hardness of Ti-V-Mo complex microalloyed steel[J]. Chinese Journal of Materials Research, 2019, 33(3): 191-198.
[16]朱来斌. 固溶温度对一种超高强度不锈钢显微组织和力学性能的影响[J]. 金属功能材料, 2016, 23(3): 54-58.
Zhu Laibin. Effect of solution treating temperature on the microstructure and mechanical properties of a ultra-high strength stainless steel[J]. Metallic Functional Materials, 2016, 23(3): 54-58.
[17]Pan Tao, Chai Xiyang, Wang Jinguang, et al. Precipitation behavior of V-N microalloyed steels during normalizing[J]. Journal of Iron and Steel Research International, 2015, 22(11): 1037-1042.
[18]徐祖耀. 条状马氏体形态对钢力学性质的影响[J]. 热处理, 2009, 24(3): 1-6.
Xu Zuyao. Effect of lath martensite morphology on the mechanical properties of steel[J]. Heat Treatment, 2009, 24(3): 1-6.
[19]Morito S, Saito H, Ogawa T, et al. Effect of austenite grain size on the morphology and crystallography of lath martensite in low carbon steels[J]. ISIJ International, 2005, 45(1): 91-94.

正火温度对USS122G超高强度不锈钢组织及性能的影响

Effect of normalizing temperature on microstructure and properties of USS122G ultra-high strength stainless steel

PDF

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

本文评价

[1]	张子延, 陈君, 陈晓亚, 李全安, 刘建鑫. 固溶时效处理对Mg-4Sm-3Gd-0.5Zr合金显微组织和耐蚀性能的影响[J]. 金属热处理, 2022, 47(4): 10-16.
[2]	梁恩溥, 徐乐, 杨勇, 王毛球. 添加Al、Cu对40CrNi3MoV钢组织和力学性能的影响[J]. 金属热处理, 2022, 47(4): 17-23.
[3]	陈连生, 张露友, 田亚强, 杨子旋, 李红斌, 潘红波, 魏英立. 低碳高强舰船用钢的CCT曲线及其组织性能[J]. 金属热处理, 2022, 47(4): 63-68.
[4]	付锡彬, 陈子豪, 张可, 赵时雨, 孙新军, 朱正海, 梁小凯, 雍岐龙. 淬火温度对高Ti低合金耐磨钢组织及力学性能的影响[J]. 金属热处理, 2022, 47(4): 122-127.
[5]	李立, 曾艳, 吴晓春. 4Cr5Mo2VCo钢的热处理工艺优化[J]. 金属热处理, 2022, 47(4): 133-140.
[6]	王琪, 吴光亮. 回火温度对1100 MPa级高强钢组织与性能的影响[J]. 金属热处理, 2022, 47(4): 146-150.
[7]	孙凯, 陈研, 杨绍斌. 时效温度对激光选区熔化TC21钛合金微观组织及硬度的影响[J]. 金属热处理, 2022, 47(4): 155-158.
[8]	章军, 赵四新. 冷锻齿轮用16MnCrS5钢的球化退火工艺[J]. 金属热处理, 2022, 47(4): 185-188.
[9]	刘文彬, 乔龙阳, 潘新宇, 程格, 李爱娜, 裴新军. 淬火温度对刀剪用M390粉末冶金不锈钢组织和性能的影响[J]. 金属热处理, 2022, 47(4): 189-195.
[10]	王瑞琴, 葛鹏, 廖强, 侯鹏, 刘宇. 固溶冷却方式对短时用高温钛合金板材组织和性能的影响[J]. 金属热处理, 2022, 47(4): 196-198.
[11]	王绍灼, 孟晗, 王芬, 樊海卫, 李燕, 唐超. 改善低氧TC4-LC及重熔TC4钛合金性能的热处理工艺[J]. 金属热处理, 2022, 47(4): 204-207.
[12]	戴建科, 韩顺, 厉勇, 刘宪民, 王春旭, 庞学东, 李建新. 航空齿轮钢C69高温渗碳后的组织性能[J]. 金属热处理, 2022, 47(4): 219-225.
[13]	苏勇, 王帅, 王吉星, 于兴福, 刘洪秀, 刘金玲. 复合化学热处理对G13Cr4Mo4Ni4V钢组织和硬度的影响[J]. 金属热处理, 2022, 47(4): 226-230.
[14]	张宁, 高星, 王芝林, 蒋波, 刘雅政. 18CrNiMo7-6钢齿轮组织性能异常分析[J]. 金属热处理, 2022, 47(4): 268-273.
[15]	王敬元, 吴松全, 张博华, 辛社伟, 杨义, 王皞, 黄爱军. 固溶时效处理对BT25y钛合金显微组织及硬度的影响[J]. 金属热处理, 2022, 47(3): 14-19.