极限模焊工况下大厚度SA387Gr11CL2钢板的力学性能

李样兵¹, 柳付芳², 赵国昌³, 龙杰¹, 袁锦程¹, 吴艳阳¹

1.舞阳钢铁有限责任公司科技部, 河南舞钢 462500;
2.舞阳钢铁有限责任公司第一轧钢厂, 河南舞钢 462500;
3.舞阳钢铁有限责任公司, 河南舞钢 462500

收稿日期:2020-06-28 出版日期:2020-12-25 发布日期:2021-01-14
作者简介:李样兵(1985—),男,工程师,硕士,主要研究方向为铬钼钢,E-mail: wgkjblyb@163.com
基金资助:
国家重点研发计划(2017YFB0305300)

Mechanical properties of large thickness SA387Gr11CL2 steel plate under the condition of limit PWHT

Li Yangbing¹, Liu Fufang², Zhao Guochang³, Long Jie¹, Yuan Jincheng¹, Wu Yanyang¹

1. Ministry of Science and Technology, Wuyang Iron and Steel Co., Ltd., Wugang Henan 462500, China;
2. Wuyang Iron and Steel Co., Ltd. No. 1 Rolling Mill, Wugang Henan 462500, China;
3. Wuyang Iron and Steel Co., Ltd., Wugang Henan 462500, China

Received:2020-06-28 Online:2020-12-25 Published:2021-01-14

摘要/Abstract

摘要： 针对设计院和制造厂提出的越来越严格的模焊工艺要求,结合136 mm厚钢板研究了极限模焊工况对大厚度SA387Gr11CL2钢力学性能的影响。结果表明,在保温温度690 ℃、保温时间24 h、装出炉温度200 ℃、升降温速率30 ℃/h的极严格模焊工艺制度下,钢的全厚度(表面下1.6 mm、板厚1/4处及板厚1/2处)室温拉伸性能尚可,但0 ℃及以下随着冲击温度的降低,相应冲击吸收能量逐渐下降,板厚1/2处-20 ℃冲击吸收能量已经接近标准要求的下限,富余量很小,结合金相和扫描电镜进行组织分析,表明过分加严模焊工艺会引起显微组织中碳化物沿晶界偏聚并长大,使钢板韧性明显变差。

关键词: SA387Gr11CL2钢板, 焊后热处理, 模拟, 力学性能

Abstract: According to the more strict requirements of PWHT put forward by the design institute and the manufacturer, the influence of the limit PWHT condition on the mechanical properties was studied with 136 mm thickness SA387Gr11CL2 steel plate. The results show that the tensile properties of the steel with full thickness (1.6 mm under the surface, 1/4 of plate thickness and 1/2 of plate thickness) at room temperature are still acceptable. However, at 0 ℃ and below, the corresponding impact absorbed energy decreases gradually with the decrease of impact temperature. The -20 ℃ impact absorbed energy at 1/2 of the plate thickness has reached the lower limit of the standard requirements, and the surplus is not enough. The microstructure analysis combined with metallography and SEM shows that the carbide in the microstructure will segregate and grow along the grain boundary due to excessive rigor PWHT, resulting in obviously worse toughness of the steel plate.

Key words: SA387Gr11CL2 steel plate, post-welding heat treatment (PWHT), simulation, mechanical properties

中图分类号:

TG142.1⁺2

李样兵, 柳付芳, 赵国昌, 龙杰, 袁锦程, 吴艳阳. 极限模焊工况下大厚度SA387Gr11CL2钢板的力学性能[J]. 金属热处理, 2020, 45(12): 193-196.

Li Yangbing, Liu Fufang, Zhao Guochang, Long Jie, Yuan Jincheng, Wu Yanyang. Mechanical properties of large thickness SA387Gr11CL2 steel plate under the condition of limit PWHT[J]. Heat Treatment of Metals, 2020, 45(12): 193-196.

参考文献

[1] Gonzaga A C, Barbosa C, Tavares S S M, et al. Influence of post welding heat treatments on sensitization of AISI 347 stainless steel welded joints[J]. Journal of Materials Research and Technology, 2019, 9(1): 908-921.
[2] Gonçalves R B, Araújo P H D, Braga F J V, et al. Efeito do Tratamento Térmico De Solubilização e Estabilização Convencional e alternativo na microestrutura de uma junta soldada com aço inox 347[J]. Soldagem Inspeção, 2015, 20: 105-116.
[3] 房务农, 王笑梅, 戈兆文. 我国承压设备焊后热处理现状及对策[J]. 金属加工(热加工), 2019(3): 48-51.
Fang Wunong, Wang Xiaomei, Ge Zhaowen.Present situation and countermeasures of post weld heat treatment of pressure equipment in China[J]. Metal Processing (Thermal Processing), 2019(3): 48-51.
[4] 董家利, 房务农. 承压设备焊后热处理工艺[J]. 焊接, 2018(12): 37-41.
Dong Jiali, Fang Wunong.Post weld heat treatment process of pressure equipment[J]. Welding, 2018(12): 37-41.
[5] 王百森. Cr-Mo钢承压设备焊后热处理工艺的探讨[J]. 石油化工设备技术, 2009, 30(4): 48-51.
Wang Baisen.Discussion on post weld heat treatment process of Cr-Mo steel pressure equipment[J]. Petrochemical Equipment Technology, 2009, 30(4): 48-51.
[6] 王晓刚, 李海滨. 大厚度临氢SA387Gr11CL2钢板冲击性能不合的组织分析[J]. 宽厚板, 2015, 21(2): 34-37.
Wang Xiaogang, Li Haibin.Microstructure analysis of large thickness hydrogen exposed SA387Gr11CL2 steel plate with unqualified impact properties[J]. Wide and Heavy Plate, 2015, 21(2): 34-37.
[7] 刘宗昌. 材料组织结构转变原理[M]. 北京: 冶金工业出版社, 2006.
[8] 隋鹤龙, 赵楠, 邹扬, 等. 热处理工艺对临氢A387Gr11CL2抗回火脆化性能影响[C]//第九届中国钢铁年会论文集. 中国金属学会, 2013: 1599-1603.
Sui Helong, Zhao Nan, Zou Yang, et al.Effect of heat treatment on temper embrittlement resistance of hydrogen exposed A387Gr11CL2[C]// Proceedings of the 9th China Iron and Steel Annual Meeting. China Society of Metals, 2013: 1599-1603.
[9] 史伟, 李金梅, 王顺花, 等. 压力容器用铬钼钢冲击吸收能量偏低的原因综述[J]. 压力容器, 2015, 32(11): 1-5.
Shi Wei, Li Jinmei, Wang Shunhua, et al.The reason of low impact absorption energy of chromium Molybdenum steel for pressure vessel[J]. Pressure Vessel, 2015, 32(11): 1-5.
[10] 史伟, 张乃孔, 赵江涛, 等. 12Cr2Mo1锻件法兰低温冲击韧性不合格的原因分析[J]. 压力容器, 2011, 28(3): 61-63.
Shi Wei, Zhang Naikong, Zhao Jiangtao, et al.Analysis of unqualified low temperature impact toughness of 12Cr2Mo1 forging flange[J]. Pressure Vessel, 2011, 28(3): 61-63.

[1]	梁恩溥, 徐乐, 杨勇, 王毛球. 添加Al、Cu对40CrNi3MoV钢组织和力学性能的影响[J]. 金属热处理, 2022, 47(4): 17-23.
[2]	祁晓亮, 李岩, 定巍, 赵增武. 含Al中锰TRIP钢原始组织对临界退火后组织与力学性能的影响[J]. 金属热处理, 2022, 47(4): 24-29.
[3]	陈保安, 张静媛, 祝志祥, 韩钰, 潘学东, 张磊, 陈素红. 化学成分对高强Al-Mg-Si合金组织和性能的影响[J]. 金属热处理, 2022, 47(4): 30-38.
[4]	陈连生, 张露友, 田亚强, 杨子旋, 李红斌, 潘红波, 魏英立. 低碳高强舰船用钢的CCT曲线及其组织性能[J]. 金属热处理, 2022, 47(4): 63-68.
[5]	王云龙, 余伟, 张昳, 史佳新, 李明辉. 奥氏体化温度对贝氏体钢等温转变及力学性能的影响[J]. 金属热处理, 2022, 47(4): 80-85.
[6]	骆再斌, 范子泽, 彭振. 轻质高熵合金的研究进展[J]. 金属热处理, 2022, 47(4): 100-107.
[7]	吕杰晟, 宋志刚, 何建国, 丰涵, 郑文杰, 朱玉亮. S32205双相不锈钢冷轧退火组织转变及强塑化机理分析[J]. 金属热处理, 2022, 47(4): 141-145.
[8]	王琪, 吴光亮. 回火温度对1100 MPa级高强钢组织与性能的影响[J]. 金属热处理, 2022, 47(4): 146-150.
[9]	张骥俊, 邢彦锋, 曹菊勇. 超声振动对CMT电弧增材制造铝合金组织与性能的影响[J]. 金属热处理, 2022, 47(4): 159-164.
[10]	刘文彬, 乔龙阳, 潘新宇, 程格, 李爱娜, 裴新军. 淬火温度对刀剪用M390粉末冶金不锈钢组织和性能的影响[J]. 金属热处理, 2022, 47(4): 189-195.
[11]	王瑞琴, 葛鹏, 廖强, 侯鹏, 刘宇. 固溶冷却方式对短时用高温钛合金板材组织和性能的影响[J]. 金属热处理, 2022, 47(4): 196-198.
[12]	王绍灼, 孟晗, 王芬, 樊海卫, 李燕, 唐超. 改善低氧TC4-LC及重熔TC4钛合金性能的热处理工艺[J]. 金属热处理, 2022, 47(4): 204-207.
[13]	陈强, 陈林芳, 杨明华. 18CrNiMo7-6钢的可控气氛高温渗碳工艺[J]. 金属热处理, 2022, 47(4): 231-239.
[14]	刘乃瑜, 曹磊, 郑少梅. 不同沉积温度下CrCN涂层的力学性能[J]. 金属热处理, 2022, 47(4): 240-244.
[15]	杨杰, 汪西, 周杰, 武建祥, 屈志远, 代合平, 彭海军. 转向节锻件枝丫结构淬火裂纹形成机理[J]. 金属热处理, 2022, 47(4): 263-267.

极限模焊工况下大厚度SA387Gr11CL2钢板的力学性能

Mechanical properties of large thickness SA387Gr11CL2 steel plate under the condition of limit PWHT

PDF

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

本文评价