稀土元素Er对Ti-6Al-4V-0.5Si合金组织与性能的影响

doi:10.13251/j.issn.0254-6051.2020.12.043

金属热处理 ›› 2020, Vol. 45 ›› Issue (12): 222-226.DOI: 10.13251/j.issn.0254-6051.2020.12.043

稀土元素Er对Ti-6Al-4V-0.5Si合金组织与性能的影响

刘超¹, 刘国威¹, 郭雷明^2,3, 杨继刚², 刘克敌², 王招招²

1.济南重工集团有限公司, 山东济南 250000;
2.河南科技大学材料科学与工程学院, 河南洛阳 471000;
3.广州纳联材料科技有限公司, 广东广州 510000

收稿日期:2020-07-25 出版日期:2020-12-25 发布日期:2021-01-14
作者简介:刘超(1992—),男,硕士,主要研究方向为金属材料的焊接及热处理,E-mail:645200978@qq.com
基金资助:
山东省重大科技创新工程项目(2019JZZY010428)

Effect of rare earth element Er on microstructure and properties of Ti-6Al-4V-0.5Si alloy

Liu Chao¹, Liu Guowei¹, Guo Leiming^2,3, Yang Jigang², Liu Kedi², Wang Zhaozhao²

1. Jinan Heavy Industry Group Co., Ltd., Jinan Shandong 250000, China;
2. School of Materials Science andEngineering, Henan University of Science and Technology, Luoyang Henan 471000, China;
3. Guangzhou Nalian Material Technology Co., Ltd., Guangzhou Guangdong 510000, China

Received:2020-07-25 Online:2020-12-25 Published:2021-01-14

摘要/Abstract

摘要： 利用粉末冶金工艺制备了Ti-6Al-4V-0.5Si-xEr(wt%)合金,随后采用OM、XRD、TEM和拉伸试验机等分析手段研究了Er元素含量对固溶时效态(950 ℃×30 min(WQ)+480 ℃×4 h(AQ))试验合金显微组织和性能的影响。结果表明:试验合金经固溶时效处理后均为等轴和片状的双态组织。烧结过程中产生的Er₂O₃氧化物颗粒可以作为形核中心促进α相和β相的析出,起到细化晶粒的作用。随着Er元素含量的增加,晶粒尺寸由10~20 μm细化至5~10 μm。当Er元素含量为1.2%时,试验合金的抗拉强度达到峰值,为930.5 MPa,此时伸长率为9.24%,比未添加Er元素时Ti-6Al-4V-0.5Si合金分别提高了22.3%和10.0%。试验合金的拉伸断口形貌显示有韧窝出现,仅有少量的解理台阶,韧窝的存在可以分散材料断裂时产生的应力,使材料断裂前承受更大的变形。

关键词: 钛合金, 错配度, 细化晶粒, 抗拉强度, 伸长率

Abstract: Ti-6Al-4V-0.5Si-xEr (wt%) alloy was prepared by powder metallurgy process, and the effect of Er content on the microstructure and properties of the alloys solution-treated+aged (950 ℃×30 min (WQ)+480 ℃×4 h (AQ)) was studied by means of OM, XRD, TEM and tensile testing machine. The results show that the tested alloys are all duplex microstructure with equiaxed and lamellar feature after solution and aging treatment. The Er₂O₃ particles produced in the sintering process can be used as nucleation core to promote the precipitation of α and β phases and play a role in grain refinement. With the increase of Er content, the grain size is refined from 10-20 μm to 5-10 μm. When the Er content is 1.2%, the tensile strength of the tested alloy reaches the peak of 930.5 MPa, and the corresponding elongation is 9.24%, which are 22.3% and 10.0% respectively higher than that of Ti-6Al-4V-0.5Si alloy with no Er addition. The tensile fracture morphologies of the tested alloy show dimples, with only a small amount of cleavage steps. The existence of dimples can disperse the stress generated during the fracture of the material and makes the material withstand greater deformation before fracture.

Key words: titanium alloy, misfit, grain refining, tensile strength, elongation

中图分类号:

TG156

刘超, 刘国威, 郭雷明, 杨继刚, 刘克敌, 王招招. 稀土元素Er对Ti-6Al-4V-0.5Si合金组织与性能的影响[J]. 金属热处理, 2020, 45(12): 222-226.

Liu Chao, Liu Guowei, Guo Leiming, Yang Jigang, Liu Kedi, Wang Zhaozhao. Effect of rare earth element Er on microstructure and properties of Ti-6Al-4V-0.5Si alloy[J]. Heat Treatment of Metals, 2020, 45(12): 222-226.

参考文献

[1] Guo W, Sun M, Qiu R, et al.Research progress on corrosion and aging of materials in deep-sea environment[J]. Corrosion Science and Protection Technology, 2017, 24(8): 125-135.
[2] 王科. 钛合金制备方法的研究进展[J]. 材料导报, 2014, 28(2): 143-146.
Wang Ke.Progress in manufacture of titanium alloy[J]. Materials Review, 2014, 28(2): 143-146.
[3] 韩鹏. 铒对高温钛合金组织和性能的影响[D]. 北京: 北京工业大学, 2012.
Han Peng.Influence of erbium on microstructure and properties of high temperature titanium alloy[D]. Beijing: Beijing University of Technology, 2012.
[4] Ertuan Z, Yuyong C, Fantao K, et al.Effect of yttrium on microstructure and mold filling capacity of a near-α high temperature titanium alloy[J]. China Foundry, 2012, 9(4): 344-348.
[5] 陈慧琴, 曹春晓. 等轴组织α-β钛合金热变形微观组织的表征[J]. 中国有色金属学报, 2012, 22(3): 22-30.
Chen Huiqin, Cao Chunxiao.Characterization of hot deformation microstructures of α-β titanium alloy with equiaxed structure[J]. Transactions of Nonferrous Metals Society of China, 2012, 22(3): 22-30.
[6] 张豪胤, 王文焱, 祝要民, 等. 固溶、时效对TC4钛合金组织和力学性能的影响[J]. 特种铸造及有色合金, 2014, 34(6): 659-661.
Zhang Haoyin, Wang Wenyan, Zhu Yaomin, et al.Effects of solution aging on microstructure and mechanical properties of TC4 alloy[J]. Special-cast and Non-ferrous Alloys, 2014, 34(6): 659-661.
[7] Huang C, Song B, Mao J, et al.The mathematical model of wetting angle of heterogeneous nucleation[J]. Science in China, 2004, 47(4): 391-397.
[8] 王斌. 稀土添加对粉末冶金钛合金组织与性能影响研究[D]. 长沙: 中南大学, 2011.
Wang Bin.Effect of rare earth elements on the microstructures and properties of powder metallurgical titanium alloys[D]. Changsha: Central South University, 2011.
[9] 刘延斌, 刘咏, 谌炎辉, 等. 稀土元素La对粉末冶金钛合金锻态组织与力学性能的影响[J]. 粉末冶金材料科学与工程, 2014(2): 223-229.
Liu Yanbin, Liu Yong, Chen Yanhui, et al.Effect of rare earth-La on microstructure and mechanical property of Powder forged Ti alloys[J]. Materials Science and Engineering of Powder Metallurgy, 2014(2): 223-229.
[10] Patil S, Kekade S, Phapale K, et al.Effect of α and β phase volume fraction on machining characteristics of titanium alloy Ti6Al4V[J]. Procedia Manufacturing, 2016, 6: 63-70.
[11] Nieh T G, Wadsworth J.Hall-Petch relation in nanocrystalline solids[J]. Scripta Metallurgica Et Materialia, 1991, 25(4): 955-958.

[1]	孙凯, 陈研, 杨绍斌. 时效温度对激光选区熔化TC21钛合金微观组织及硬度的影响[J]. 金属热处理, 2022, 47(4): 155-158.
[2]	王瑞琴, 葛鹏, 廖强, 侯鹏, 刘宇. 固溶冷却方式对短时用高温钛合金板材组织和性能的影响[J]. 金属热处理, 2022, 47(4): 196-198.
[3]	王绍灼, 孟晗, 王芬, 樊海卫, 李燕, 唐超. 改善低氧TC4-LC及重熔TC4钛合金性能的热处理工艺[J]. 金属热处理, 2022, 47(4): 204-207.
[4]	王敬元, 吴松全, 张博华, 辛社伟, 杨义, 王皞, 黄爱军. 固溶时效处理对BT25y钛合金显微组织及硬度的影响[J]. 金属热处理, 2022, 47(3): 14-19.
[5]	张颖, 王浩军, 陈素明, 胡广, 欧阳德来, 崔霞, 胡生双. 热处理对激光立体成形TB18钛合金组织和力学性能的影响[J]. 金属热处理, 2022, 47(3): 124-129.
[6]	张曼雪, 景然, 张雄, 张晴, 吴倩, 刘以柔. 铸态Ti-20Zr-10Nb-xMo合金的微观组织和耐腐蚀性能[J]. 金属热处理, 2022, 47(3): 147-150.
[7]	朱然, 谢地辉, 朱帅光, 张永康. 高频率Nd∶YLF平顶激光冲击对TC6钛合金表面应力及微变形的影响[J]. 金属热处理, 2022, 47(3): 204-209.
[8]	林基辉, 温亚辉, 范文博, 张腾, 刘晨雨, 薛元琳. 钛合金表面激光改性技术研究进展[J]. 金属热处理, 2022, 47(3): 215-221.
[9]	张世进, 李凯, 易丹青, 刘会群. 冷轧TA5钛合金退火过程的再结晶行为及织构演变[J]. 金属热处理, 2022, 47(2): 1-8.
[10]	向庆, 姜雪婷, 伍良银, 冉潇潇, 刘静, 杨峰. TA2钛合金真空感应碳氮共渗组织及耐磨损和耐腐蚀性能[J]. 金属热处理, 2022, 47(2): 99-104.
[11]	张颖, 王浩军, 陈素明, 胡广, 欧阳德来, 崔霞, 胡生双. 退火工艺对激光立体成形TC21钛合金组织和性能的影响[J]. 金属热处理, 2022, 47(2): 141-145.
[12]	刘昱君, 程晓农, 罗锐, 高佩. 热处理工艺对Inconel 617合金管组织性能的影响[J]. 金属热处理, 2022, 47(2): 173-177.
[13]	师佑杰, 李永刚, 李文辉, 王兴富. 深冷处理对TC4钛合金表面性能的影响[J]. 金属热处理, 2022, 47(2): 183-187.
[14]	李昂, 高坤元, 文胜平, 黄晖, 聂祚仁. 冷却条件对5E83铝合金搅拌摩擦焊接头组织与性能的影响[J]. 金属热处理, 2022, 47(1): 130-134.
[15]	谭皎, 张伯岩, 朱文光, 孙巧艳. 时效温度对Ti-5Al-4Zr-10Mo-3Cr钛合金微观组织及力学性能的影响[J]. 金属热处理, 2022, 47(1): 217-225.

稀土元素Er对Ti-6Al-4V-0.5Si合金组织与性能的影响

Effect of rare earth element Er on microstructure and properties of Ti-6Al-4V-0.5Si alloy

PDF

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

本文评价