GH2909合金锻件持久缺口敏感性组织分析

doi:10.13251/j.issn.0254-6051.2020.05.004

金属热处理 ›› 2020, Vol. 45 ›› Issue (5): 17-22.DOI: 10.13251/j.issn.0254-6051.2020.05.004

GH2909合金锻件持久缺口敏感性组织分析

李钊¹, 王涛¹, 徐雄^1,2, 罗俊鹏³, 盛俊英³

1. 中国航发北京航空材料研究院先进高温结构材料重点实验室, 北京 100095;
2. 北京科技大学冶金与生态工程学院, 北京 100083;
3. 中国航发南方工业有限公司, 湖南株洲 412002

收稿日期:2020-02-19 出版日期:2020-05-25 发布日期:2020-09-02
作者简介:李钊(1985—),男,工程师,硕士,主要研究方向为高温合金,E-mail: gh720li@sina.com
基金资助:
装备预研重点实验室基金(6142903190205)

Structure analysis on stress rupture notch sensitivity for GH2909 alloy forgings

Li Zhao¹, Wang Tao¹, Xu Xiong^1,2, Luo Junpeng³, Sheng Junying³

1. Science and Technology on Advanced High Temperature Structural Materials Laboratory, AECC Beijing Institute of Aeronautical Materials, Beijing 100095, China;
2. School of Metallurgical and Ecological Engineering, University of Science and Technology Beijing, Beijing 100083, China;
3. AECC South Industry Company Limited, Zhuzhou Hunan 412002, China

Received:2020-02-19 Online:2020-05-25 Published:2020-09-02

摘要/Abstract

摘要： 针对GH2909合金锻件呈现的不同程度缺口敏感性问题,采用金相分析、扫描电镜、断口分析等手段,开展持久试样组织分析。结果表明:在某种特定的析出相分布状态下,GH2909合金是否呈现持久缺口敏感性是一个概率性事件;当Laves相连接成薄膜包覆晶界时,合金呈现缺口敏感性的概率显著提升。

关键词: GH2909合金, 缺口敏感性, 持久, 晶界

Abstract: Structure analysis on stress rupture specimens were conducted by the means of metallographic and SEM methods, to define the problem of different level notch sensitivity for GH2909 alloy forgings. The results show that whether the alloy exhibits persistent notch sensitivity is a probabilistic event to the GH2909 alloy with a particular phase distribution. The occurrence probability of notch sensitivity increases apparently when the Laves phase precipitates in film-like shape on grain boundary.

Key words: GH2909 alloy, notch sensitivity, rupture, grain boundary

中图分类号:

TG113

李钊, 王涛, 徐雄, 罗俊鹏, 盛俊英. GH2909合金锻件持久缺口敏感性组织分析[J]. 金属热处理, 2020, 45(5): 17-22.

Li Zhao, Wang Tao, Xu Xiong, Luo Junpeng, Sheng Junying. Structure analysis on stress rupture notch sensitivity for GH2909 alloy forgings[J]. Heat Treatment of Metals, 2020, 45(5): 17-22.

参考文献

[1]邓波, 韩光炜, 冯涤. 低膨胀高温合金的发展及在航空航天业的应用[J]. 航空材料学报, 2003, 23(S1): 244-249.
Deng Bo, Han Guangwei, Feng Di. Development of low thermal expansion superalloys and their application in aerospace[J]. Journal of Aeronautical Materials, 2003, 23(S1): 244-249.
[2]Heck K A, Smith J S, Smith R. Inconel alloy 783: An oxidation-resistant, low expansion superalloy for gas turbine applications[J]. Journal of Engineering for Gas Turbines and Power, 1998, 120: 363-369.
[3]赵宇新, 张绍维. GH909合金在700 ℃长期时效稳定性研究[J]. 航空材料学报, 2006, 26(3): 56-59.
Zhao Yuxin, Zhang Shaowei. Long time thermal stability of superallooy GH909 at 700 ℃[J]. Journal of Aeronautical Materials, 2006, 26(3): 56-59.
[4]赵宇新, 张绍维. GH909合金长期时效后组织和性能的研究[J]. 航空材料学报, 2000, 20(3): 6-10.
Zhao Yuxin, Zhang Shaowei. A study on microstructure and mechanical properties of GH909 after long time aging[J]. Journal of Aeronautical Materials, 2000, 20(3): 6-10.
[5]Balachander M A, Vishwakarma K, Richards N L. Overaged metallography of alloy 909, a low coefficient of expansion superalloy[J]. Material Science and Technology, 2012, 28(3): 380-384.
[6]Heck K A, Smith D F, Smith J S, et al. The physical metallurgy of silicon-containing low expansion superalloy[J]. Superalloys, 1988: 151-160.
[7]Balachander M A, Vishwakarma K, Tang B, et al. Microstructure characterization of solution treated(ST) and solution treated and aged (STA) Incoloy 909[J]. Material Science and Technology, 2011, 27(4): 805-810.
[8]Guo Xiping, Kusabiraki Kiyoshi, Saji Shigeoki, et al. Intragranular precipitates in incoloy alloy 909[J]. Scripta Material, 2001, 44(1): 55-60.
[9]任金桥. GH2909合金产品局部宏观成分偏析[J]. 特钢技术, 2011, 17(1): 16-23.
Ren Jinqiao. Discussion on reasons of local macro composition segregation forming in GH2909 alloy[J]. Special Steel Technology, 2011, 17(1): 16-23.
[10]Yao Z H, Wu S C, Dong J X, et al. Constitutive behavior and processing maps of low-expansion GH909 superallog[J]. International Journal of Minerals, Metallurgy and Materials, 2017, 24(4): 432-443.
[11]Covarrubias O, Elizarraras O, Colas R. Effect of heat treatment on mechanical properties of alloy 909[J]. Materials Science and Technology, 2011, 27(6): 1092-1097.
[12]王信才, 韩光炜, 杨玉军. 低膨胀GH2909合金锻造工艺研究[J]. 特钢技术, 2017, 23(3): 33-37.
Wang Xincai, Han Guangwei, Yang Yujun. Study on the forging process of low expansion alloy GH2909[J]. Special Steel Technology, 2017, 23(3): 33-37.
[13]高玉魁, 赵宇新, 殷源发. 低膨胀高温合金GH909再结晶研究[J]. 金属热处理, 2005, 30(1): 77-79.
Gao Yukui, Zhao Yuxin, Yin Yuanfa. Study of recrystallization of low expansion superalloy GH909[J]. Heat Treatment of Metals, 2005, 30(1): 77-79.
[14]樊照远, 李许明, 宋传荣, 等. Si含量对GH2909合金性能的影响[J]. 热加工工艺, 2017, 46(14): 107-109.
Fan Zhaoyuan, Li Xuming, Song Chuanrong, et al. Effect of Si content on properties of GH2909 alloy[J]. Hot Working Technology, 2017, 46(14): 107-109.
[15]邱伟, 魏志坚, 夏欲明, 等. 低膨胀GH907合金环轧件高温持久缺口敏感性的研究[C]//第十二届全国塑性工程学术年会暨第四届全球华人塑性加工技术研讨会论文集, 2011: 492-495.
[16]蔡大勇, 张伟红, 刘文昌, 等. Inconel 718合金中δ相溶解动力学及对缺口敏感性的影响[J]. 有色金属, 2003, 55(1): 4-7.
Cai Dayong, Zhang Weihong, Liu Wenchang, et al. Dissolution kinetics of δ phase and effect on notch sensitivity of Inconel 718[J]. Nonferrous Metals, 2003, 55(1): 4-7.
[17]蔡大勇, 姜涛, 张伟红, 等. 高温保持对Inconel 718合金缺口敏感性的影响[J]. 材料工程, 2003(S1): 213-215.
Cai Dayong, Jiang Tao, Zhang Weihong, et al. Influence of high temperature duration on the notch sensitivity of Inconel 718[J]. Journal of Materials Engineering, 2003(S1): 213-215.
[18]郑欣, 师玉英, 陈玉宝. 时效处理对GH4169合金组织和性能的影响[J]. 金属热处理, 2018, 43(6): 162-165.
Zheng Xin, Shi Yuying, Chen Yubao. Effect of aging treatment on microstructure and properties of GH4169 alloy[J]. Heat Treatment of Metals, 2018, 43(6): 162-165.

GH2909合金锻件持久缺口敏感性组织分析

Structure analysis on stress rupture notch sensitivity for GH2909 alloy forgings

PDF

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

本文评价

[1]	朱婷, 鹿宪珂, 杨森. 退火处理对铜导线晶界特征分布及导电性能的影响[J]. 金属热处理, 2021, 46(9): 85-89.
[2]	刘翊安, 张晓宇, 孙欢迎, 庞国星, 吴伟. 冷拉伸预变形及热处理对Hastelloy C-276合金晶界特征的影响[J]. 金属热处理, 2021, 46(7): 13-17.
[3]	王小艳, 韩俊杰, 孙道锋, 任琪琪, 杨淏鑫, 张永建. 晶界特征分布对哈氏合金力学性能的影响[J]. 金属热处理, 2021, 46(6): 205-208.
[4]	杨晋萍, 宋国斌, 董勇军, 崔崇, 段文峰, 石全强, 单以银. 某燃气轮机涡轮叶片长期服役后的微观组织与性能[J]. 金属热处理, 2021, 46(6): 213-220.
[5]	顾洋, 宋帅, 武会宾, 张志慧, 张鹏程. 热处理工艺对7%Cr钢显微组织及耐蚀性能的影响[J]. 金属热处理, 2021, 46(4): 42-48.
[6]	石如星, 禹兴胜, 元亚莎, 何春静, 陈明, 代博杰. 加氢反应器用2.25Cr-1Mo-0.25V钢锻件的持久性能[J]. 金属热处理, 2021, 46(4): 182-186.
[7]	喻春明, 张继明, 党波, 张毅. 高磁感取向硅钢轧制及热处理过程中的晶界和织构演化[J]. 金属热处理, 2021, 46(12): 204-208.
[8]	邓辉. 低硬度P91钢管长时服役后的组织性能和安全性评价[J]. 金属热处理, 2021, 46(12): 209-213.
[9]	彭思远, 邓想涛, 梁亮, 付天亮, 刘宁, 王昭东. 淬火温度对新型NM450抗腐蚀磨损钢组织和性能的影响[J]. 金属热处理, 2021, 46(12): 223-228.
[10]	秦升学, 王艳, 张弘斌, 周海萍, 刘杰. 固溶处理对GH99合金组织的影响[J]. 金属热处理, 2020, 45(8): 173-178.
[11]	王芬玲, 刘禹炯, 王天剑, 裴玉冰, 巩秀芳. 热处理工艺对12Cr钢组织与性能的影响[J]. 金属热处理, 2020, 45(7): 42-44.
[12]	武志广, 龚雪婷, 李鑫, 赵吉庆, 韩少强, 龚志华. 正火冷速对2.25Cr-1Mo钢持久性能的影响[J]. 金属热处理, 2020, 45(6): 55-59.
[13]	范德良, 王志武, 句光宇. P91钢管道异常低硬度部位的组织和性能[J]. 金属热处理, 2020, 45(3): 1-6.
[14]	王方军, 刘璇, 刘应龙, 吴畏. 固溶温度对冷轧态690合金组织及晶界分布特征的影响[J]. 金属热处理, 2020, 45(3): 151-157.
[15]	王敏婷, 申利雄, 曹明飞, 赵磊, 李哲. 一种基于晶界硬化效应的微细切削本构模型[J]. 金属热处理, 2020, 45(11): 248-254.