激光熔覆H13钢的裂纹敏感性及形成机理

doi:10.13251/j.issn.0254-6051.2020.06.043

摘要/Abstract

摘要： 采用同轴送粉激光熔覆方法在H13钢基体上多道搭接熔覆H13钢,用光学显微镜、SEM和XRD对熔覆层的组织特征进行分析,用着色渗透法检验熔覆层裂纹,通过图像处理定量表征裂纹密度,研究了工艺参数对裂纹敏感性的影响,并分析研究了裂纹形成机制。结果表明,H13钢激光熔覆层的组织主要由枝晶状奥氏体转变的马氏体和残留奥氏体组成;熔覆层裂纹敏感性较大,主要是热裂,裂纹在奥氏体柱状枝晶间萌生并扩展;激光功率对裂纹敏感性影响大,功率越大裂纹敏感性越低,优化工艺参数可以获得无裂纹缺陷熔覆层。

关键词: 激光熔覆, H13钢, 裂纹, 组织

Abstract: A multitrack overlapping clad layer was fabricated on H13 steel substrate by laser cladding with coaxial powder feeding, the microstructure characteristics were studied by means of optical microscope (OM), SEM and XRD. The clad layer cracks were detected by penetrant inspection method, and the crack density was quantitatively characterized by image processing. The effects of the laser cladding process parameters on crack sensitivity were studied, and the mechanism of crack formation was analyzed. The results show that the microstructure of H13 steel clad layer is mainly composed of martensite and residual austenite transformed from dendrite-like austenite. The crack sensitivity of the clad layer is high, most of them are thermal cracks, which initiates and propagates between austenite columnar dendrites. The laser power has a significant impact on the crack sensitivity of the clad layer, the higher the power, the lower the crack sensitivity, and the clad layer without cracks can be obtained by optimizing process parameters.

Key words: laser cladding, H13 steel, crack, microstructure

中图分类号:

TG174.44

杨伟, 曾大新, 刘建永, 李峰光. 激光熔覆H13钢的裂纹敏感性及形成机理[J]. 金属热处理, 2020, 45(6): 206-211.

Yang Wei, Zeng Daxin, Liu Jianyong, Li Fengguang. Crack sensitivity and formation mechanism of laser clad H13 steel[J]. Heat Treatment of Metals, 2020, 45(6): 206-211.

参考文献

[1]员霄, 王井, 朱青海, 等. H13钢的铁基和钴基熔覆层组织与耐磨性[J]. 焊接学报, 2018, 39(12): 105-109.
Yuan Xiao, Wang Jing, Zhu Qinghai, et al. Microstructure and abrasion resistance of Fe-based and Co-based coatings of AISI H13[J]. Transactions of the China Welding Institution, 2018, 39(12): 105-109.
[2]杨晓红, 杭文先, 秦绍刚, 等. H13钢激光熔覆钴基复合涂层的组织及耐磨性[J]. 吉林大学学报(工学版), 2017, 47(3): 891-899.
Yang Xiaohong, Hang Wenxian, Qin Shaogang, et al. Microstructure and wear properties of Co-based composite coatings on H13 steel surface by laser cladding[J]. Journal of Jilin University(Engineering and Technology Edition), 2017, 47(3): 891-899.
[3]叶宏, 喻文新, 雷临萍, 等. H13钢激光熔覆Co基涂层工艺优化及组织性能[J]. 金属热处理, 2016, 41(12): 117-121.
Ye Hong, Yu Wenxin, Lei Linping, et al. Process optimization of Co-based coating on H13 steel by laser cladding and its microstructure and properties[J]. Heat Treatment of Metals, 2016, 41(12): 117-121.
[4]Gururaj Telasang, Jyotsna Dutta Majumdar, Nitin Wasekar, et al. Microstructure and mechanical properties of laser clad and post-cladding tempered AISI H13 tool steel[J]. Metallurgical and Materials Transactions A , 2015, 46(5): 2309-2321.
[5]陈菊芳, 李小平, 薛亚平. 45钢表面激光熔覆Fe901合金的摩擦磨损性能[J]. 中国激光, 2019, 46(5): 326-334.
Chen Jufang, Li Xiaoping, Xue Yaping. Friction and wear properties of laser cladding Fe901 alloy coating on 45 steel surface[J]. Chinese Journal of Lasers, 2019, 46(5): 326-334.
[6]刘海青, 葛超, 王志文, 等. 激光熔覆复合涂层裂纹控制研究进展[J]. 金属热处理, 2018, 43(8): 228-232.
Liu Haiqing, Ge Chao , Wang Zhiwen, et al. Research progress on crack control of laser clad composite coating[J]. Heat Treatment of Metals, 2018, 43(8): 228-232.
[7]于希辰, 王志文, 刘海青, 等. 后热处理对激光熔覆涂层应用的研究进展[J]. 金属热处理, 2019, 44(3): 114-119.
Yu Xichen, Wang Zhiwen, Liu Haiqing, et al. Research progress of application of post heat-treatment on laser cladded coatings[J]. Heat Treatment of Metals, 2019, 44(3): 114-119.
[8]Zhou S, Zeng X, Hu Q, et al. Analysis of crack behavior for Ni-based WC composite coatings by laser cladding and crack-free realization[J]. Applied Surface Science, 2008, 255(5): 1646-1653.
[9]Parisa Farahmand, Radovan Kovacevic. Laser cladding assisted with an induction heater (LCAIH) of Ni-60%WC coating[J]. Journal of Materials Processing Technology, 2015, 222: 244-258.
[10]Song W, Zhu P, Cui K. Effect of Ni content on cracking susceptibility and microstructure of laser-clad FeCrNiBSi alloy[J]. Surface and Coatings Technology, 1996, 80(3): 279.
[11]Song W, Echigoya J, Zhu B, et al. Effects of Co on the cracking susceptibility and the microstructure of Fe-Cr-Ni laser-clad layer[J]. Surface and Coatings Technology, 2001, 138(2): 291-295.
[12]王玉玲, 张翔宇, 孙树峰, 等. 稀土对激光熔覆3540Fe基合金涂层组织与性能的影响[J]. 金属热处理, 2018, 43(3): 100-103.
Wang Yuling, Zhang Xiangyu, Sun Shufeng, et al. Effect of rare earth on microstructure and properties of laser cladding 3540Fe-based alloy layer[J]. Heat Treatment of Metals, 2018, 43(3): 100-103.
[13]蔡川雄, 刘洪喜, 蒋业华, 等. 交变磁场对激光熔覆Fe基复合涂层组织结构及其耐磨性的影响[J]. 摩擦学学报, 2013, 33(3): 229-235.
Cai Chuanxiong, Liu Hongxi, Jiang Yehua, et al. Influence of AC magnetic field on microstructure and wear behaviors of laser cladding Fe-based composite coating[J]. Tribology, 2013, 33(3): 229-235.
[14]曹亚男, 张艳梅, 揭晓华, 等. 钢表面激光熔覆镍基合金涂层裂纹控制的研究[J]. 热加工工艺, 2012, 41(18): 133-136.
Cao Yanan, Zhang Yanmei, Jie Xiaohua, et al. Study on control of crack in laser cladding Ni-based coating on steel[J]. Hot Working Technology, 2012, 41(18): 133-136.
[15]Dubourg L, St-Georges L. Optimization of laser cladding process using taguchi and EM methods for MMC coating production[J]. Journal of Thermal Spray Technology, 2006, 15(4): 790-795.
[16]吴祖鹏. Ni60A合金激光熔覆裂纹气孔控制方法研究[D]. 大连: 大连理工大学, 2019.
Wu Zupeng. Study on crack and porosity control methods of laser cladding Ni60A alloy coating[D]. Dalian : Dalian University of Technology, 2019.
[17]Fu F, Zhang Y, Chang G, et al. Analysis on the physical mechanism of laser cladding crack and its influence factors[J]. Optik - International Journal for Light and Electron Optics, 2016, 127(1): 200-202.
[18]Kou S. Welding Metallurgy[M]. Canada: John Wiley and Sons Inc, 2003: 163-166.
[19]李林起, 姚成武, 黄坚, 等. 激光熔覆高硬度铁基涂层枝晶间残余奥氏体相特征[J]. 中国激光, 2017, 44(3): 136-142.
Li Linqi, Yao Chengwu, Huang Jian, et al. Characteristics of interdendritic residual austenite in laser cladding of high hardness iron-based coating[J]. Chinese Journal of Lasers, 2017, 44(3): 136-142.
[20]严凯, 陈长军, 张敏, 等. 激光增材制造H13钢及回火处理的组织和性能[J]. 中国表面工程, 2017, 30(2): 134-142.
Yan Kai, Chen Changjun, Zhang Min, et al. Microstructure and properties of laser additive manufacturing and tempered H13 steel[J]. China Surface Engineering, 2017, 30(2): 134-142.
[21]陈静, 杨海欧, 李延民, 等. 激光快速成形过程中熔覆层的两种开裂行为及其机理研究[J]. 应用激光, 2002, 22(3): 300-304.
Chen Jing, Yang Haiou, Li Yanmin, et al. The research on two kinds of cracking behavior and mechanism of cladding in rapid laser forming process[J]. Applied Laser, 2002, 22(3): 300-304.
[22]陈静, 林鑫, 王涛, 等. 316L不锈钢激光快速成形过程中熔覆层的热裂机理[J]. 稀有金属材料与工程, 2003, 32(3): 183-186.
Chen Jing, Lin Xin, Wang Tao, et al. The hot cracking mechanism of 316L stainless steel cladding in rapid laser forming process[J]. Rare Metal Materials and Engineering, 2003, 32(3): 183-186.
[23]张磊, 陈小明, 刘伟, 等. 激光熔覆Ni基合金裂纹的形成机理及敏感性[J]. 激光与光电子学进展, 2019, 56(11): 176-183.
Zhang Lei, Chen Xiaoming, Liu Wei, et al. Formation mechanism and sensitivity of cracks in laser-cladded Ni-based-alloy coatings[J]. Laser and Optoelectronics Progress, 2019, 56(11): 176-183.