OD1422 mm的X80级管线钢SH-CCT曲线测定与分析

doi:10.13251/j.issn.0254-6051.2020.06.021

金属热处理 ›› 2020, Vol. 45 ›› Issue (6): 93-97.DOI: 10.13251/j.issn.0254-6051.2020.06.021

OD1422 mm的X80级管线钢SH-CCT曲线测定与分析

于晨阳¹, 池强², 张伟卫², 胡美娟², 陈庆龙¹, 葛加林¹

1. 西安石油大学材料科学与工程学院, 陕西西安 710065;
2. 中国石油集团石油管工程技术研究院, 陕西西安 710065

收稿日期:2019-12-23 出版日期:2020-06-25 发布日期:2020-09-02
通讯作者: 张伟卫,高级工程师,硕士,E-mail:zhangweiwei008@cnpc.com.cn
作者简介:于晨阳(1994—),女,硕士研究生,主要研究方向为石油管的使役性能及安全性,E-mail:2517917293@qq.com。
基金资助:
国家重点研发计划(2017YFB0304900);西安石油大学研究生创新与实践能力培养计划(YCS18212046)

Determination and analysis of SH-CCT curve of X80 pipeline steel with OD1422 mm

Yu Chenyang¹, Chi Qiang², Zhang Weiwei², Hu Meijuan², Chen Qinglong¹, Ge Jialin¹

1. School of Material Science and Engineering, Xi'an Shiyou University, Xi'an Shaanxi 710065, China;
2. Tubular Goods Research Center of CNPC, Xi'an Shaanxi 710065, China

Received:2019-12-23 Online:2020-06-25 Published:2020-09-02

摘要/Abstract

摘要： 采用Gleeble3500热-力学模拟试验机,对外径为φ1422 mm的X80管线钢焊接热影响区(HAZ)在不同冷却速度下的热循环过程进行了模拟,利用热膨胀法绘制模拟焊接热影响区连续冷却组织转变曲线(SH-CCT);结合光学显微组织和硬度测试等分析手段,研究了φ1422 mm的X80管线钢在不同冷却速度条件下焊接热影响区的组织变化规律。结果表明,冷却速度对X80管线钢的相变行为和微观结构具有显著影响。当冷却速度为1 ℃/s时,组织转变为贝氏体;当冷却速度达到7 ℃/s时,开始产生马氏体组织;当冷却速度为20 ℃/s时,组织内较高位错密度的板条贝氏体较多,组织晶粒较小。当冷却速度在7~20 ℃/s之间时,X80管线钢热影响区的显微硬度和冲击性能都大于母材。

关键词: X80管线钢, SH-CCT曲线, 热影响区, 显微硬度, 冲击性能

Abstract: The Gleeble3500 thermo-mechanical simulation tester was used to simulate the thermal cycling process of the X80 pipeline steel with OD1422 mm at different cooling rates. The thermal expansion method was used to simulate the continuous cooling transformation curve of simulated heat affected zone (SH-CCT). Combined with microstructure analysis and hardness test, the microstructure change of welding heat affected zone (HAZ) of the X80 pipeline steel at different cooling rate conditions was studied. The test results show that the cooling rate has a significant effect on the phase transformation behavior of the steel. When the cooling rate is 1 ℃/s, the microstructure is transformed into bainite. When the cooling rate is 7 ℃/s, the martensitic transformation begins. When the cooling rate is 20 ℃/s, more lath bainite with higher dislocation density is obtained and the grain size is smaller. When the cooling rate is between 7 ℃/s and 20 ℃/s, the microhardness and impact property are greater than the base metal.

Key words: X80 pipeline steel, SH-CCT curve, heat affected zone(HAZ), microhardness, impact property

中图分类号:

TG115.2

于晨阳, 池强, 张伟卫, 胡美娟, 陈庆龙, 葛加林. OD1422 mm的X80级管线钢SH-CCT曲线测定与分析[J]. 金属热处理, 2020, 45(6): 93-97.

Yu Chenyang, Chi Qiang, Zhang Weiwei, Hu Meijuan, Chen Qinglong, Ge Jialin. Determination and analysis of SH-CCT curve of X80 pipeline steel with OD1422 mm[J]. Heat Treatment of Metals, 2020, 45(6): 93-97.

参考文献

[1]冯耀荣, 霍春勇, 吉玲康, 等. 我国高钢级管线钢和钢管应用基础研究进展及展望[J]. 石油科学通报, 2016, 1(1): 143-153.
[2]张圣柱, 程玉峰, 冯晓东, 等. X80管线钢性能特征及技术挑战[J]. 油气储运, 2019, 38(5): 481-495.
Zhang Shengzhu, Cheng Yufeng, Feng Xiaodong, et al. Performance characteristics and technical challenges of X80 pipeline steel[J]. Oil and Gas Storage and Transportation, 2019, 38(5): 481-495.
[3]高慧临. 管线钢与管线钢管[M]. 北京: 中国石化出版社, 2012.
[4]李红斌, 林哲, 方芳, 等. 应力作用下X100管线钢SH-CCT曲线[J]. 金属热处理, 2016, 41(11): 171-174.
Li Hongbin, Lin Zhe, Fang Fang, et al. SH-CCT curve of X100 pipeline steel under the action of stress[J]. Heat Treatment of Metals, 2016, 41(11): 171-174.
[5]张清清, 章传国, 郑磊. 热处理工艺对 X65MS 管线钢抗 HIC 性能的影响[J]. 金属热处理, 2016, 41(11): 116-121.
Zhang Qingqing, Zhang Chuanguo, Zheng Lei. Effects of heat treatments on the hydrogen-induced cracking resistance of X65 pipeline steels[J]. Heat Treatment of Metals, 2016, 41(11): 116-121.
[6]谭会杰, 王海燕, 李德超, 等. X80管线钢连续冷却相变及组织研究[J]. 金属热处理, 2015, 40(7): 91-94.
Tan Huijie, Wai Haiyan, Li Dechao, et al. Continuous cooling transformation and microstructure of X80 pipeline steel[J]. Heat Treatment of Metals, 2015, 40(7): 91-94.
[7]Mayur Pratap Singh, Kanwer Singh Arora, Nikhil Shajan. Comparative analysis of continuous cooling transformation behavior in CGHAZ of API X-80 and X-65 line pipe steels[J]. Journal of Thermal Analysis and Calorimetry, 2019, 137: 1155-1167.
[8]陈连生, 胡宝佳, 董福涛. 含 Cu 低碳钢 CCT 曲线及马氏体相变原位观察[J]. 金属热处理, 2017, 42(6): 13-17.
Chen Liansheng, Hu Baojia, Dong Futao. Continuous cooling transformation curve of Cu bearing low carbon steel and in-situ observation of its martensitic transformation[J]. Heat Treatment of Metals, 2017, 42(6): 13-17.
[9]乔桂英, 韩杨, 韩秀林, 等. 高铌高强管线钢焊接热影响区的组织与性能[J]. 钢铁研究学报, 2014, 26(10): 40-45.
Qiao Guiying, Han Yang, Han Xiulin, et al. Microstructure and mechanical properties of welding heat affected zone of a high-Nb high strength pipeline steel[J]. Journal of Iron and Steel Research, 2014, 26(10): 40-45.
[10]Chen X W, Qiao G Y, Wang X, et al. Study on microstructure and mechanical properties of welding coarse grain heat-affected zone of high-Nb X80 steels[J]. Advanced Science Letters, 2012, 13(1): 780-783.
[11]麻相湑, 麻永林, 邢淑清, 等. SS400钢SH-CCT曲线测定及组织性能分析[J]. 金属热处理, 2015, 40(9): 59-63.
Ma Xiangxu, Ma Yonglin, Xing Shuqing, et al. SH-CCT curves determination, microstructure and properties analysis of SS400 steel[J]. Heat Treatment of Metals, 2015, 40(9): 59-63.
[12]Gianetto J A, Fazeli F, Chen Y, et al. Microstructure and toughness of simulated grain coarsened heat affected zones in X80 pipe steels[C]//International Pipeline Conference. American Society of Mechanical Engineers. 2014: DOI: 10. 1115/IPC2014-33254.

[1]	陈思君, 陈送义, 陈庚, 袁丁玲, 陈康华. Mg含量对2A14铝合金组织和力学性能的影响[J]. 金属热处理, 2022, 47(4): 86-92.
[2]	白青青, 张志宏, 郑淮北, 王英虎. 2507超级双相不锈钢中σ相的析出行为[J]. 金属热处理, 2022, 47(4): 108-115.
[3]	陈刚, 罗小兵, 柴锋, 杨才福, 张正延, 杨丽. 轧制加热温度对高强度低合金钢组织及冲击性能的影响[J]. 金属热处理, 2022, 47(4): 116-121.
[4]	李立, 曾艳, 吴晓春. 4Cr5Mo2VCo钢的热处理工艺优化[J]. 金属热处理, 2022, 47(4): 133-140.
[5]	王敬元, 吴松全, 张博华, 辛社伟, 杨义, 王皞, 黄爱军. 固溶时效处理对BT25y钛合金显微组织及硬度的影响[J]. 金属热处理, 2022, 47(3): 14-19.
[6]	罗迪强, 余音宏, 张真铭, 冯小明, 刘敏, 赖朝彬. 钇基稀土对高强船板钢夹杂物及低温冲击性能的影响[J]. 金属热处理, 2022, 47(3): 142-146.
[7]	李阔, 孙明月, 徐斌, 李殿中. 稀土H13模具钢横向冲击性能影响因素分析[J]. 金属热处理, 2022, 47(3): 181-185.
[8]	周钟平, 张小娟, 白鹭, 余方印, 闵永安. T250钢离子渗氮后的组织和性能[J]. 金属热处理, 2022, 47(3): 210-214.
[9]	吴迎飞, 孙中华, 王育飞, 王程明, 张雲飞, 彭会芬. 均匀化退火处理对因瓦合金铸锭组织及性能的影响[J]. 金属热处理, 2022, 47(2): 130-136.
[10]	师佑杰, 李永刚, 李文辉, 王兴富. 深冷处理对TC4钛合金表面性能的影响[J]. 金属热处理, 2022, 47(2): 183-187.
[11]	张孟良, 汤文博, 李百奇, 王笑生, 黎文强, 王腾飞. 等离子熔覆添加和内生联合WC颗粒增强铁基涂层的组织和性能[J]. 金属热处理, 2022, 47(2): 200-204.
[12]	朱林, 程向龙, 邹喜洋. 26CrMo4钢的热处理工艺[J]. 金属热处理, 2022, 47(1): 271-275.
[13]	丁轩, 甘玉荣, 蒋爱娟, 李辉, 杨明球. 时效处理对7A55铝合金微观组织和性能的影响[J]. 金属热处理, 2021, 46(9): 120-123.
[14]	缪小进, 夏思海, 武美萍, 俞经虎, 赵子硕, 崔宸, 张春雷. 添加CeO₂对铝合金表面激光熔覆铝钛熔覆层性能的影响[J]. 金属热处理, 2021, 46(9): 234-240.
[15]	于洪军, 宋传颂馨, 程福超, 高志喆, 陈小艳, 王永金, 张应超. 不同热处理条件下亚共晶高铬铸铁的组织和性能[J]. 金属热处理, 2021, 46(8): 56-60.

OD1422 mm的X80级管线钢SH-CCT曲线测定与分析

Determination and analysis of SH-CCT curve of X80 pipeline steel with OD1422 mm