热轧+淬火配分处理对Q235钢组织及性能的影响

doi:10.13251/j.issn.0254-6051.2021.11.011

摘要/Abstract

摘要： 采用光学显微镜、扫描电镜、电子万能试验机、数显显微硬度计,研究了一步法淬火配分(Q&P)工艺和热轧一步法淬火配分(HR-Q&P)工艺在不同配分温度下处理后Q235钢的组织和力学性能。结果表明:HR-Q&P工艺使试验钢晶粒明显细化,显微组织由马氏体、铁素体和贝氏体组成,在350 ℃配分下,屈服强度和抗拉强度都达到最大值,分别为449 MPa和560 MPa,伸长率与原样相比下降了8%,但仍然超过30%;硬相的马氏体和贝氏体的同时出现,导致断口出现二次裂纹;一步法Q&P工艺下,与未处理试验钢相比,抗拉强度提高约32%,屈服强度提高近1倍,伸长率保持在26%以上。

关键词: Q&P工艺, 热轧, Q235钢, 马氏体, 断口形貌

Abstract: Effect of partitioning temperature during one-step quenching and partitioning (Q&P) process and one-step hot rolling + quenching and partitioning (HR-Q&P) process on microstructure and mechanical properties of the Q235 steel was studied by means of optical microscope (OM), scanning electron microscope (SEM), electronic universal testing machine and digital microhardness tester. The results show that the grains of the tested steel are obviously refined by HR-Q&P process, and the microstructure is composed of martensite, ferrite and bainite. When partitioned at 350 ℃ by HR-Q&P process, the yield strength and tensile strength of the steel reach the maximum, the values of which are 449 MPa and 560 MPa, respectively, while the elongation decreases by 8% compared with the as-received one, but still exceeds 30%. The hard phases of martensite and bainite appear at the same time during HR-Q&P process, resulting in secondary cracking. Under the one-step Q&P process, compared with the as-received tested steel, the tensile strength increases by about 32%, the yield strength increases by nearly one times, and the elongation remains above 26%.

Key words: Q&P process, hot rolling, Q235 steel, martensite, fracture morphology

中图分类号:

TG156.93

孟晓越, 林万明, 宁安刚, 马荣泽, 张志伟. 热轧+淬火配分处理对Q235钢组织及性能的影响[J]. 金属热处理, 2021, 46(11): 71-77.

Meng Xiaoyue, Lin Wanming, Ning Angang, Ma Rongze, Zhang Zhiwei. Effect of hot rolling + quenching and partitioning on microstructure and properties of Q235 steel[J]. Heat Treatment of Metals, 2021, 46(11): 71-77.

参考文献

[1]李新创. 新时代钢铁工业高质量发展之路[J]. 钢铁, 2019, 54(1): 1-7.
Li Xinchuang. Road map to high-quality development of iron and steel industry in new age[J]. Iron and Steel, 2019, 54(1): 1-7.
[2]朱滔, 尹洪顶. 新冠肺炎疫情影响下我国钢铁工业发展思路[J]. 重型机械, 2020(4): 1-5.
Zhu Tao, Yin Hongding. Development thinking of China's iron and steel industry under the influence of novel coronavirus pneumonia epidemic[J]. Heavy Machinery, 2020(4): 1-5.
[3]Ritchie R O. The conflicts between strength and toughness[J]. Natural Materials, 2011(10): 817-822.
[4]Lee C G, Kim S, Lee T, et al. Effects of volume fraction and stability of retained austenite on formability in a 0.1C-1.5Si-1.5Mn-0.5Cu TRIP-aided cold-rolled steel sheet[J]. Materials Science and Engineering A, 2004, 371(1/2): 16-23.
[5]Pierman A P, Bouaziz O, Pardoen T, et al. The influence of microstructure and composition on the plastic behaviour of dual-phase steels[J]. Acta Materialia, 2014, 73: 298-311.
[6]Speer J, Matlock D K, Cooman B C D, et al. Carbon partitioning into austenite after martensite transformation[J]. Acta Materialia, 2003, 51(9): 2611-2622.
[7]钟宁. 高强度Q&P钢和Q-P-T钢的研究[D]. 上海: 上海交通大学, 2009.
Zhong Ning. Research on high strength Q&P and Q-P-T steels[D]. Shanghai: Shanghai Jiao Tong University, 2009.
[8]徐祖耀. 钢热处理的新工艺[J]. 热处理, 2007(1): 1-11.
Xu Zuyao. New processes for steel heat treatment[J]. Heat Treatment, 2007(1): 1-11.
[9]John G Speer, David K Matlock. Q&P钢热处理工艺的开发进展(英文)[J]. 世界钢铁, 2009, 9(1): 31-35.
John G Speer, David K Matlock. Developments in the quenching and partitioning process[J]. World Steel, 2009, 9(1): 31-35.
[10]张玉杰, 王存宇, 刘文忠, 等. 变形温度对淬火配分钢微观组织和硬度的影响[J]. 材料热处理学报, 2013, 34(5): 97-102.
Zhang Yujie, Wang Cunyu, Liu Wenzhong, et al. Effect of deformation temperature on microstructure and hardness of a low carbon alloyed steel treated by quenching and partitioning process[J]. Transactions of Materials and Heat Treatment, 2013, 34(5): 97-102.
[11]王存宇, 常颖, 杨洁, 等. 热变形和淬火配分处理的复合作用对低碳合金钢马氏体相变机制的影响[J]. 金属学报, 2015, 51(8): 913-919.
Wang Cunyu, Chang Ying, Yang Jie, et al. The combined effect of hot deformation plus quenching and partitioning treatment on martensite transformation of low carbon alloyed steel[J]. Acta Metallurgica Sinica, 2015, 51(8): 913-919.
[12]李智超. Ms点的碳当量计算法[J]. 辽宁工程技术大学学报(自然科学版), 1998, 17(3): 293-295.
Li Zhichao. Carbon equivalent meter algorithm for Ms point[J]. Journal of Liaoning Technical University(Nature Science), 1998, 17(3): 293-295.
[13]丁树彭, 吴国梁, 宋哲, 等. 45钢在箱式炉中淬火加热时间的研究[J]. 金属热处理, 1980(8): 23-32.
Ding Shupeng, Wu Guoliang, Song Zhe, et al. Research on quenching heating time of 45 steel in box furnace[J]. Heat Treatment of Metals, 1980(8): 23-32.
[14]崔忠圻, 覃耀春. 金属学与热处理[M]. 北京: 机械工业出版社, 2007.
[15]Clarke A J, Speer J G, Miller M K, et al. Carbon partitioning to austenite from martensite or bainite during the quench and partition (Q&P) process: A critical assessment[J]. Acta Materialia, 2008, 56(1): 16-22.
[16]Toji Y, Matsuda H, Herbig M, et al. Atomic-scale analysis of carbon partitioning between martensite and austenite by atom probe tomography and correlative transmission electron microscopy[J]. Acta Materialia, 2014, 65: 215-228.
[17]谭小东, 许云波, 杨小龙, 等. 一步淬火分配钢的工艺设计与微观组织演变[J]. 东北大学学报(自然科学版), 2014, 35(5): 681-685.
Tan Xiaodong, Xu Yunbo, Yang Xiaolong, et al. Process design and microstructure evolution of one-step quenched and partitioned steel[J]. Journal of Northeastern University (Natural Science), 2014, 35(5): 681-685.
[18]李金鑫, 黄兴民, 张雷, 等. 淬火配分处理对锻态Fe-0.2C-9Mn-3.5Al钢显微组织及力学行为的影响[J]. 金属热处理, 2020, 45(2): 87-93.
Li Jinxin, Huang Xingmin, Zhang Lei, et al. Influence of quenching and partitioning treatment on microstructure and mechanical behaviors of forged Fe-0.2C-9Mn-3.5Al steel[J]. Heat Treatment of Metals, 2020, 45(2): 87-93.
[19]薛瑞锋, 冯运莉, 刘天宇. 温轧温度对中碳马氏体钢组织演变和力学性能的影响[J]. 热加工工艺, 2018, 47(9): 1-5.
Xue Ruifeng, Feng Yunli, Liu Tianyu. Effects of warm rolling temperature on microstructure evolution and mechanical properties of medium carbon martensite steel[J]. Hot Working Technology, 2018, 47(9): 1-5.
[20]Kumar A, Singh S B, Ray K K. Influence of bainite/martensite-content on the tensile properties of low carbon dual-phase steels[J]. Materials Science and Engineering A, 2008, 474(1/2): 270-282.
[21]Li Z C, Misra R D K, Cai Z H, et al. Mechanical properties and deformation behavior in hot-rolled 0.2C-1.5/3A1-8.5Mn-Fe TRIP steel: The discontinuous TRIP effect[J]. Materials Science and Engineering A, 2016, 673: 63-72.
[22]Cai Z H, Ding H, Misra R D K, et al. Unique serrated flow dependence of critical stress in a hot-rolled Fe-Mn-Al-C steel[J]. Scripta Materialia, 2014, 71: 5-8.
[23]王卫永, 刘天姿. 高强Q460钢高温冷却后力学性能研究[J]. 建筑材料学报, 2016, 19(1): 171-176.
Wang Weiyong, Liu Tianzi. Study on mechanical properties of high strength Q460 steel after cooling from high temperature[J]. Journal of Building Materials, 2016, 19(1): 171-176.
[24]钟群鹏, 赵子华, 张峥. 断口学的发展及微观断裂机理研究[J]. 机械强度, 2005(3): 358-370.
Zhong Qunpeng, Zhao Zihua, Zhang Zheng. Development of "fractography" and research of fracture micromechanism[J]. Journal of Mechanical Strength, 2005(3): 358-370.
[25]李秀程, 谢振家, 王学林, 等. 高强度低碳贝氏体钢拉伸断口分离现象及机理研究[J]. 金属学报, 2013, 49(2): 167-174.
Li Xiucheng, Xie Zhenjia, Wang Xuelin, et al. Split fracture phenomenon and mechanism in tensile tests of high strength low carbon bainitic steel[J]. Acta Metallurgica Sinica, 2013, 49(2): 167-174.