Co微合金化对M2高速钢组织和性能的影响

doi:10.13251/j.issn.0254-6051.2022.01.013

金属热处理 ›› 2022, Vol. 47 ›› Issue (1): 73-78.DOI: 10.13251/j.issn.0254-6051.2022.01.013

Co微合金化对M2高速钢组织和性能的影响

李亮军^1,2, 张家敏¹, 迟宏宵², 周健²

1.昆明理工大学材料科学与工程学院, 云南昆明 650093;
2.钢铁研究总院特殊钢研究院, 北京 100081

收稿日期:2021-07-22 修回日期:2021-09-08 出版日期:2022-01-25 发布日期:2022-02-18
通讯作者: 迟宏宵,高级工程师,博士,E-mail:chihongxiao@.163.com
作者简介:李亮军(1993—),男,硕士研究生,主要研究方向为高速钢方向,E-mail:1914935491@qq.com。

Effect of Co microalloying on microstructure and properties of M2 high speed steel

Li Liangjun^1,2, Zhang Jiamin¹, Chi Hongxiao², Zhou Jian²

1. Faculty of Materials Science and Engineering, Kunming University of Science and Technology, Kunming Yunnan 650093, China;
2. Research Institute of Special Steels, Central Iron and Steel Research Institute, Beijing 100081, China

Received:2021-07-22 Revised:2021-09-08 Online:2022-01-25 Published:2022-02-18

摘要/Abstract

摘要： 采用洛氏硬度计、扫描电镜和透射电镜等方法研究了在M2高速钢中添加微量Co对其回火组织和性能的影响。结果表明,两种试验钢回火之后的组织都为回火马氏体+少量残留奥氏体+碳化物。添加0.82%(质量分数,下同)Co使得M2高速钢的峰值硬度提高了约0.3 HRC,使600 ℃保温48 h之后的红硬性提高了约0.8 HRC,可以看出微量Co添加对M2高速钢的硬度和红硬性的提升效果不大,抗弯强度提高了约950 MPa,而使得M2高速钢的韧性略有降低,均为脆性断裂。通过对试验钢中的碳化物进行观察发现,两种试验钢析出的一次碳化物主要为大颗粒的MC型和M₆C型碳化物,通过TEM分析之后发现,添加0.82%的Co使得试验钢中马氏体板条上长条针状M₂C型的二次碳化物析出数量增多。

关键词: M2高速钢, 组织, 红硬性, 抗弯强度, 碳化物

Abstract: Effect of Co microalloying on its tempered microstructure and properties of the M2 high speed steel was studied by means of Rockwell hardness tester, scanning electron microscope and transmission electron microscope. The results show that the microstructure of the two tested steels after tempering is tempered martensite+a small amount of retained austenite+carbides. The addition of 0.82% (mass fraction, the same below) Co makes the peak hardness of M2 high-speed steel increasing by about 0.3 HRC and the hot hardness of M2 high-speed steel after holding at 600 ℃ for 48 h increasing by about 0.8 HRC. It can be seen that Co microalloying has little effect on the improvement of hardness and hot hardness of M2 high-speed steel, but makes the bonding strength increasing by about 950 MPa, while slightly decrease of the toughness of M2 high-speed steel, which is a brittle fracture mode. Through the observation of carbides in the tested steel, it is found that the primary carbides precipitated in the two tested steels are mainly large particle MC and M₆C carbides. After TEM analysis, it is found that the addition of 0.82%Co increases the number of long needle-like M₂C secondary carbides precipitated in martensitic lath of the tested steel.

Key words: M2 high speed steel, structure, hot hardness, bending strength, carbides

中图分类号:

TG142.1

李亮军, 张家敏, 迟宏宵, 周健. Co微合金化对M2高速钢组织和性能的影响[J]. 金属热处理, 2022, 47(1): 73-78.

Li Liangjun, Zhang Jiamin, Chi Hongxiao, Zhou Jian. Effect of Co microalloying on microstructure and properties of M2 high speed steel[J]. Heat Treatment of Metals, 2022, 47(1): 73-78.

参考文献

[1]Speich G R, Dabkowski D S, Porter L F. Strength and toughness of Fe-10Ni alloys containing C, Cr, Mo, and Co[J]. Metallurgical Transactions, 1973, 4(1): 303-315.
[2]Wang R, Andrén H O, Wisell H, et al. The role of alloy composition in the precipitation behavior of high speed steels[J]. Acta Metallurgica et Materialia, 1992, 40(7): 1727-1738.
[3]刘贵立, 张国英, 曾梅光, 等. Co、Al对二次硬化钢微结构影响的穆谱研究[J]. 机械工程学报, 2002, 38(12): 149-152.
Liu Guili, Zhang Guoying, Zeng Meiguang, et al. Investigation on influence of Co, Al on microstructures of secondary-hardening steel by Mosbauer spectroscopy[J]. Journal of Mechanical Engineering, 2002, 38(12): 149-152.
[4]Dobrzański L A, Kasprzak W. The influence of 5% cobalt addition on structure and working properties of the 9-2-2-5, 11-2-2-5 and 11-0-2-5 high-speed steels[J]. Journal of Materials Processing Technology, 2001, 109(1): 52-64.
[5]Kashchuk V A. Cast high-speed steels alloyed with cobalt[J]. Metal Science and Heat Treatment, 1961, 3(1/2): 72-74.
[6]刘宇, 李丽声, 高德生, 等. 钴对M42型超硬高速钢组织和性能的影响[J]. 钢铁, 1989(1): 36-40, 35.
Liu Yu, Li Lisheng, Gao Desheng, et al. Influence of cobalt on structure and property of M42 type superhard high speed steel[J]. Iron and Steel, 1989(1): 36-40, 35.
[7]王金双. M35高速钢热处理工艺研究[J]. 金华职业技术学院学报, 2004, 4(1): 17-19.
Wang Jinshuang. Study on the heat treatment process of M35 high speed steel[J]. Journal of Jinhua College of Profession and Technology, 2004, 4(1): 17-19.
[8]Luo Y W, Guo H J, Sun X L, et al. Influence oftempering time on the microstructure and mechanical properties of AISI M42 high-speed steel[J]. Metallurgical and Materials Transactions A, 2018, 49(12): 5976-5986.
[9]刘宇, 陈景榕. 钴在钼系高速钢中的机制[J]. 钢铁, 1991, 26(5): 41-45.
Liu Yu, Chen Jingrong. Mechanism of cobalt in molybdenum high speed steels[J]. Iron and Steel, 1991, 26(5): 41-45.
[10]戚正风, 冯屈原, 吴立志, 等. 高速钢的红硬性[J]. 金属热处理, 2001, 26(12): 8-10.
Qi Zhengfeng, Feng Quyuan, Wu Lizhi, et al. Red hardness of high speed steel[J]. Heat Treatment of Metals, 2001, 26(12): 8-10.
[11]张永, 马党参, 刘建华, 等. 淬火和回火温度对W4Mo2Cr4VNb高速钢组织和力学性能的影响[J]. 金属热处理, 2007, 32(5): 63-65.
Zhang Yong, Ma Dangshen, Liu Jianhua, et al. Influence of quenching and tempering temperature on microstructures and mechanical properties of W4Mo2Cr4VNb high speed steel[J]. Heat Treatment of Metals, 2007, 32(5): 63-65.
[12]余洪波, 吴立志, 张占普. M2高速钢的强韧化处理[J]. 物理测试, 2004(3): 16-18.
Yu Hongbo, Wu Lizhi, Zhang Zhanpu. Strengthening and toughing of HSS M2[J]. Physics Examination and Testing, 2004(3): 16-18.

[1]	王玉岱, 刘洋, 朱言言, 田象军, 程序, 冉先喆, 钱婷婷. 热处理对复合制造AerMet100超高强度钢组织均匀性与拉伸性能的影响[J]. 金属热处理, 2022, 47(4): 1-9.
[2]	张子延, 陈君, 陈晓亚, 李全安, 刘建鑫. 固溶时效处理对Mg-4Sm-3Gd-0.5Zr合金显微组织和耐蚀性能的影响[J]. 金属热处理, 2022, 47(4): 10-16.
[3]	梁恩溥, 徐乐, 杨勇, 王毛球. 添加Al、Cu对40CrNi3MoV钢组织和力学性能的影响[J]. 金属热处理, 2022, 47(4): 17-23.
[4]	祁晓亮, 李岩, 定巍, 赵增武. 含Al中锰TRIP钢原始组织对临界退火后组织与力学性能的影响[J]. 金属热处理, 2022, 47(4): 24-29.
[5]	陈保安, 张静媛, 祝志祥, 韩钰, 潘学东, 张磊, 陈素红. 化学成分对高强Al-Mg-Si合金组织和性能的影响[J]. 金属热处理, 2022, 47(4): 30-38.
[6]	王英虎, 郑淮北, 刘庭耀, 宋令玺, 白青青. 固溶处理对53Cr21Mn9Ni4N耐热钢组织及碳化物的影响[J]. 金属热处理, 2022, 47(4): 39-45.
[7]	陈东俊, 李广阳, 刘刚. 时效处理对AlSi9Cu3压铸铝合金组织和力学性能的影响[J]. 金属热处理, 2022, 47(4): 53-56.
[8]	陈连生, 张露友, 田亚强, 杨子旋, 李红斌, 潘红波, 魏英立. 低碳高强舰船用钢的CCT曲线及其组织性能[J]. 金属热处理, 2022, 47(4): 63-68.
[9]	贾昌远, 霍元明, 何涛, 霍存龙, 刘克然. 40CrNiMo钢高温拉伸变形行为和组织演变规律[J]. 金属热处理, 2022, 47(4): 69-74.
[10]	王云龙, 余伟, 张昳, 史佳新, 李明辉. 奥氏体化温度对贝氏体钢等温转变及力学性能的影响[J]. 金属热处理, 2022, 47(4): 80-85.
[11]	刘丽艳, 毕文珍, 韦习成. Mn元素对热冲压钢镀锌层组织演变的影响[J]. 金属热处理, 2022, 47(4): 93-99.
[12]	付锡彬, 陈子豪, 张可, 赵时雨, 孙新军, 朱正海, 梁小凯, 雍岐龙. 淬火温度对高Ti低合金耐磨钢组织及力学性能的影响[J]. 金属热处理, 2022, 47(4): 122-127.
[13]	宿鹏吉, 麻永林, 董丽丽, 杨雪峰. 磁场预退火处理对CGO钢组织与织构的影响[J]. 金属热处理, 2022, 47(4): 128-132.
[14]	李立, 曾艳, 吴晓春. 4Cr5Mo2VCo钢的热处理工艺优化[J]. 金属热处理, 2022, 47(4): 133-140.
[15]	吕杰晟, 宋志刚, 何建国, 丰涵, 郑文杰, 朱玉亮. S32205双相不锈钢冷轧退火组织转变及强塑化机理分析[J]. 金属热处理, 2022, 47(4): 141-145.

Co微合金化对M2高速钢组织和性能的影响

Effect of Co microalloying on microstructure and properties of M2 high speed steel

PDF

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

本文评价