3.1%Si取向硅钢显微组织和宏观织构演变

doi:10.13251/j.issn.0254-6051.2023.09.040

金属热处理 ›› 2023, Vol. 48 ›› Issue (9): 238-241.DOI: 10.13251/j.issn.0254-6051.2023.09.040

3.1%Si取向硅钢显微组织和宏观织构演变

刘永珍¹, 董丽丽^1,2, 刘宝志³, 张浩³, 麻永林¹

1.内蒙古科技大学材料与冶金学院, 内蒙古包头 014010;
2.内蒙古包钢钢联股份有限公司技术中心, 内蒙古包头 014010;
3.包头市威丰稀土电磁材料股份有限公司, 内蒙古包头 014010

收稿日期:2023-04-08 修回日期:2023-07-27 出版日期:2023-09-25 发布日期:2023-10-25
作者简介:刘永珍(1982—),女,讲师,博士研究生,主要研究方向为电磁冶金与材料新技术,E-mail:liuyz0424@163.com
基金资助:
内蒙古自治区自然科学基金(2020MS05046);内蒙古自治区科技计划(2021GG0047)

Evolution of microstructure and macrotexture of 3.1%Si oriented silicon steel

Liu Yongzhen¹, Dong Lili^1,2, Liu Baozhi³, Zhang Hao³, Ma Yonglin¹

1. School of Material and Metallurgy, Inner Mongolia University of Science and Technology, Baotou Inner Mongolia 014010, China;
2. Technology Center, Inner Mongolia Baogang Steel Union Co., Ltd., Baotou Inner Mongolia 014010, China;
3. Baotou Weifeng Rare Earth Electromagnetic Materials Co., Ltd., Baotou Inner Mongolia 014010, China

Received:2023-04-08 Revised:2023-07-27 Online:2023-09-25 Published:2023-10-25

摘要/Abstract

摘要： 采用蔡司显微镜、X射线衍射仪等检测手段分析Si含量为3.1%的取向硅钢在生产各个阶段(一次冷轧、脱碳退火、二次冷轧、高温退火、拉伸平整退火)的组织形貌和宏观织构。结果表明,Si含量为3.1%的普通级取向硅钢显微组织类型为铁素体,经脱碳退火初次再结晶后平均晶粒尺寸为10.23 μm,经高温退火二次再结晶后晶粒尺寸达到2.0 cm,经拉伸平整退火后取向硅钢的平均晶粒尺寸为2.3 cm,且均匀性提高。在脱碳退火阶段完成初次再结晶后的织构类型以γ织构为主,有一部分高斯织构{110}<001>,经高温退火二次再结晶后织构类型以高斯织构{110}<001>为主,经拉伸平整退火后,高斯织构达到最强最锋锐的程度。

关键词: 取向硅钢, 显微组织, 织构, 脱碳退火, 高温退火

Abstract: Microstructure and macroscopic textures of 3.1%Si oriented silicon steel during first cold rolling, decarburizing annealing, second cold rolling, high temperature annealing and tensile leveling annealing were analyzed by means of Zeiss microscope, X-ray diffractometer and other testing instruments. The results show that microstructure of the oriented silicon steel is ferrite. The average grain size is 10.23 μm after first recrystallization during decarburizing annealing, and reaches 2.0 cm after second recrystallization during high temperature annealing, and grows to 2.3 cm with increasing of uniformity after tensile leveling annealing. The main texture type of the oriented silicon steel after decarburization annealing is γ fiber texture, with a small amount of Goss texture {110}<001>. After high temperature annealing, the texture type is mainly Goss texture {110}<001>. After tensile leveling annealing, the Goss texture reaches the strongest and sharpest degree.

Key words: oriented silicon steel, microstructure, texture, decarburizing annealing, high temperature annealing

中图分类号:

TG142

刘永珍, 董丽丽, 刘宝志, 张浩, 麻永林. 3.1%Si取向硅钢显微组织和宏观织构演变[J]. 金属热处理, 2023, 48(9): 238-241.

Liu Yongzhen, Dong Lili, Liu Baozhi, Zhang Hao, Ma Yonglin. Evolution of microstructure and macrotexture of 3.1%Si oriented silicon steel[J]. Heat Treatment of Metals, 2023, 48(9): 238-241.

参考文献

[1]罗勃. 无取向硅钢有机-无机复合极厚绝缘涂层的研究[D]. 上海: 上海交通大学, 2011.
[2]肖丽俊, 王海军, 项利, 等. 薄板坯连铸连轧工艺下Hi-B钢的组织及织构[J]. 工程科学学报, 2016, 38(2): 241-247.
Xiao Lijun, Wang Haijun, Xiang Li, et al. Microstructure and texture of Hi-B steel produced by TSCR process[J]. Chinese Journal of Engineering, 2016, 38(2): 241-247.
[3]李霞, 杨平, 贾志伟, 等. 低温取向硅钢常化工艺和渗氮工艺对组织、织构和磁性能的影响[J]. 工程科学学报, 2019, 41(5): 610-617.
Li Xia, Yang Ping, Jia Zhiwei, et al. Effects of normalizing process and nitriding process on the microstructure, texture, and magnetic properties in low-temperature grain-oriented silicon steel[J]. Chinese Journal of Engineering, 2019, 41(5): 610-617.
[4]刘恭涛, 李海蛟, 杨平, 等. 中温含铜取向硅钢的形变和再结晶织构特征[J]. 工程科学学报, 2016, 38(6): 812-819.
Liu Gongtao, Li Haijiao, Yang Ping, et al. Deformation and recrystallization texture features of medium temperature reheated grain oriented silicon steel containing copper[J]. Chinese Journal of Engineering, 2016, 38(6): 812-819.
[5]樊立峰, 项利, 唐广波, 等. 低温高磁感取向硅钢高温退火过程高斯晶粒的转变[J]. 北京科技大学学报, 2014, 36(3): 328-332.
Fan Lifeng, Xiang Li, Tang Guangbo, et al. Evolution of Goss grains during high-temperature annealing in high permeability grain-oriented silicon steel with slab reheating at low temperature[J]. Journal of University of Science and Technology Beijing, 2014, 36(3): 328-332.
[6]于雷, 罗海文. 部分再结晶退火对无取向硅钢的磁性能与力学性能的影响[J]. 金属学报, 2020, 56(3): 291-300.
Yu Lei, Luo Haiwen. Effect of partial recrystallization annealing on magnetic properties and mechanical properties of non-oriented silicon steel[J]. Acta Metallurgica Sinica, 2020, 56(3): 291-300.
[7]许占一, 沙玉辉, 张芳. 取向硅钢二次再结晶过程中的取向选择行为[J]. 金属学报, 2020, 56(8): 1067-1074.
Xu Zhanyi, Sha Yuhui, Zhang Fang. Orientation selection behavior during secondary recrystallization in grain-oriented silicon steel[J]. Acta Metallurgica Sinica, 2020, 56(8): 1067-1074.
[8]麻永林, 赵娜娜, 刘宝志, 等. 普通取向硅钢在冷轧及退火过程中的组织及织构演变[J]. 机械工程材料, 2017, 41(6): 25-29.
Ma Yonglin, Zhao Nana, Liu Baozhi, et al. Evolution of structure and texture of common grain oriented silicon steel during cold rolling and annealing[J]. Materials for Mechanical Engineering, 2017, 41(6): 25-29.

[1]	崔毅, 崔继红, 王艳, 张雲飞, 俞峰, 赵英利, 曹文全. 淬火工艺对GCr4Mo4V钢组织及耐磨性的影响[J]. 金属热处理, 2023, 48(9): 23-29.
[2]	李文刚, 炊鹏飞, 程尊鹏, 李春梅, 景然, 李江华, 廖仲尼. 硼含量对Ti-Zr-Nb-B合金显微组织及性能的影响[J]. 金属热处理, 2023, 48(9): 157-164.
[3]	戴钊, 郭智, 龙晓燕, 冯晓勇, 刘伟, 张福成, 李艳国. Si含量对高碳贝氏体钢微观组织与性能的影响[J]. 金属热处理, 2023, 48(9): 165-173.
[4]	谢尚恒, 孙有平, 朱嘉欣, 方德俊. 微量Zr对深冷轧制Al-Cu-Mg合金微观组织及性能的影响[J]. 金属热处理, 2023, 48(9): 174-179.
[5]	李鑫, 武志广, 赵吉庆, 杨钢. 20Cr1Mo1VTiB螺栓钢高温长期时效后的组织演变及力学性能[J]. 金属热处理, 2023, 48(9): 197-202.
[6]	申文竹, 王朋飞, 胡相平, 包菲菲, 侯鑫鑫, 曹立胜. IF钢冷轧和退火过程的织构演变规律[J]. 金属热处理, 2023, 48(9): 242-246.
[7]	李子岩, 许鸿翔, 陈业生, 刘志强, 郭敬强, 陈岩, 赵少甫. 42CrMo钢低速轴止推环调质开裂失效分析[J]. 金属热处理, 2023, 48(9): 283-287.
[8]	吴洋, 钱亚锋, 赵言辉. Al含量及时效时间对Mg-Al系镁合金力学性能和阻尼能力的影响[J]. 金属热处理, 2023, 48(8): 30-34.
[9]	刘绪玮, 汪志刚, 林杰, 尹铁淇, 叶洁云, 张迎晖. 临界区淬火工艺对Cr-Ti-B系微碳钢组织及织构的影响[J]. 金属热处理, 2023, 48(8): 72-79.
[10]	康聪, 焦振, 穆博涛, 任驰强, 高文超, 李维, 贠鹏飞, 欧阳文博. 退火处理对Ti6321合金显微组织与力学性能的影响[J]. 金属热处理, 2023, 48(8): 149-153.
[11]	李玲, 刘旭科, 孟庆宇, 刘少军, 李陶陶, 高阳. 30CrMnSi钢离子渗氮-激光淬火复合处理改性层的性能[J]. 金属热处理, 2023, 48(8): 185-189.
[12]	赵吉庆, 杨钢, 殷会芳. 淬火保温时间对FB2耐热钢组织与性能的影响[J]. 金属热处理, 2023, 48(8): 199-204.
[13]	何炜, 王燕燕, 舒林森. 扫描速度对高速激光熔覆316L不锈钢涂层组织与性能的影响[J]. 金属热处理, 2023, 48(8): 248-253.
[14]	刘民, 鲁美朋, 刘嘉晨, 顾宝兰, 郭静, 孙跃军, 宋明. 酸气后冷器封头开裂原因分析[J]. 金属热处理, 2023, 48(8): 265-271.
[15]	刘磊, 郭飞虎, 时朋召, 乔家龙, 仇圣桃. 初次再结晶退火温度对低温Hi-B钢组织和织构的影响[J]. 金属热处理, 2023, 48(7): 8-14.

3.1%Si取向硅钢显微组织和宏观织构演变

Evolution of microstructure and macrotexture of 3.1%Si oriented silicon steel

PDF

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

本文评价