热处理对铜锌合金微观组织和阻垢性能的影响

doi:10.13251/j.issn.0254-6051.2024.01.025

摘要/Abstract

摘要： 为了解决水垢对锅炉、管道等工业设备的损害问题,设计熔炼出一种新型的阻垢合金。通过扫描电镜、EDS能谱仪、X射线衍射仪、电化学工作站和接触角测量仪等设备对铜锌合金热处理前后的微观结构和表面性能进行表征。通过自主搭建的水循环平台进行试验,测定了水循环试验后溶液中剩余Ca²⁺浓度和铜锌合金阻垢率变化。收集循环水中的水垢,分析其微观形貌和晶体结构变化。结果表明,600 ℃热处理后铜锌合金的耐蚀性最好,自腐蚀电流密度为4.27 μA·cm^-2,并且具有最好的阻垢性能,试验溶液被600 ℃热处理的合金处理后静置0.5 h时,阻垢率可以达到90.27%,相较于铸态合金阻垢率(79.21%)提高了11.06%。该铜锌阻垢合金处理液具有一定时效性,在2 h内阻垢效果最佳。600 ℃热处理的铜锌合金使块状方解石转变为针状文石的能力更强,用其处理溶液后生成的水垢中方解石与文石比例为1.38∶1。

关键词: 热处理, 阻垢合金, 表面自由能, 极化曲线, 水垢形貌

Abstract: In order to solve the problem of incrustation damage to boilers, pipelines and other industrial equipment, a new type of incrustation inhibition alloy was designed and melted. The microstructure and surface properties of the copper-zinc alloy before and after heat treatment were characterized by means of scanning electron microscope, EDS energy spectrometer, X-ray diffractometer, electrochemical workstation and contact angle measuring instrument. The test was conducted on the independently built water circulation platform, and the residual Ca²⁺ concentration in the solution and the change of incrustation inhibition rate of the Cu-Zn alloy were determined after the water circulation experiment. The incrustation in the circulating water was collected and analyzed for micro-morphology and crystal structure changes. The results show that the copper-zinc alloy has the best corrosion resistance after heat treatment at 600 ℃, with a self-corrosion current density of 4.27 μA·cm^-2, and has the best incrustation inhibition properties, and the incrustation inhibition rate of the test solution can reach 90.27% when it is left to stand for 0.5 h after being treated with the alloy heat-treated at 600 ℃, which is an improvement of 11.06% in comparison with that of the as-cast alloy, the as-cast alloy has a incrustation inhibition rate of 79.21%.The copper-zinc incrustation inhibition alloy treatment solution has a certain timeliness, incrustation inhibition effect in 2 h is the best. The copper-zinc alloy after heat-treatment at 600 ℃ has a stronger ability to transform the block calcite into needle aragonite, the ratio of calcite to aragonite after the generation of incrustation by treating the solution with which is 1.38∶1.

Key words: heat treatment, incrustation inhibition alloy, surface free energy, polarization curve, incrustation morphology

中图分类号:

TG146.1

侯艳阳, 邬宇轩, 曹铸, 李静媛. 热处理对铜锌合金微观组织和阻垢性能的影响[J]. 金属热处理, 2024, 49(1): 160-165.

Hou Yanyang, Wu Yuxuan, Cao Zhu, Li Jingyuan. Effect of heat treatment on microstructure and incrustation inhibition properties of copper-zinc alloys[J]. Heat Treatment of Metals, 2024, 49(1): 160-165.

参考文献

[1]姜峰, 李修伦, 齐国鹏, 等. 三相流蒸发防垢节能技术[J]. 中国井矿盐, 2012, 43(1): 3-6.
Jiang Feng, Li Xiulun, Qi Guopeng, et al. Technology for scale prevention and energy saving by three-phase flow evaporation[J]. China Well and Rock Salt, 2012, 43(1): 3-6.
[2]赵萍. 斜翅管表面碳酸钙析晶垢结垢特性研究[D]. 上海: 上海理工大学, 2014.
[3]薛金权. 浅析工业锅炉水垢的成因、危害及防垢措施[J]. 科技资讯, 2015, 13(9): 71.
[4]冯尧奇, 宋学斌, 颜海龙. 工业循环水系统中结垢和腐蚀现象分析及控制方案[J]. 山东化工, 2021, 50(6): 166-167.
[5]陆柱. 一种新型净水材料——KDF[J]. 上海环境科学, 1994, 13(9): 38-39.
[6]Heskett D E. Method of treating fluids, EP0238639A1[P]. 1987-09-30.
[7]Wada Yoneji. Fluid filtering method, JPS6161848B2[P]. 1986-12-27.
[8]熊仁军, 刘卫平, 习兴梅, 等. 铜锌合金滤料在水处理中的应用及改进展望[J]. 工业安全与环保, 2004(10): 5-8.
Xiong Renjun, Liu Weiping, Xi Xingmei, et al. Application and amelioration prospect of copper-zinc alloy in water treatment[J]. Industrial Safety and Environmental Protection, 2004(10): 5-8.
[9]Freij S J, Godelitsas A, Putnis A. Crystal growth and dissolution processes at the calcite-water interface in the presence of zinc ions[J]. Journal of Crystal Growth, 2005, 273(3/4): 535-545.
[10]Shi Q, Zhang G, Feng Q, et al. Effect of the lattice ions on the calcite flotation in presence of Zn(II)[J]. Minerals Engineering, 2013, 40, 24-29.
[11]杨兰, 周勇. 水处理用铜锌合金的研究现状及进展[J]. 热处理技术与装备, 2014, 35(1): 30-33.
Yang Lan, Zhou Yong. Research status and developments on copper-zinc alloy in water treatment[J]. Heat Treatment Technology and Equipment, 2014, 35(1): 30-33.
[12]Chibowski E, Holysz L. Use of the Washburn equation for surface free energy determination[J]. Langmuir, 1992, 8(2): 1216-1217.
[13]Liang J S, Meng J P, Zhu D B, et al. Effect of heat treatment on the surface free energy of mineral tourmaline powders[J]. Journal of the Chinese Ceramic Society, 2008, 36(2): 257-260.
[14]和彦光, 王武义, 王仲楠, 等. 合金材料的阻垢机理及实验研究[J]. 材料科学与工艺, 2009, 17(6): 810-814.
He Yanguang, Wang Wuyi, Wang Zhongnan, et al. Mechanism and experimental study of scale inhibition by alloys[J]. Materials Science and Technology, 2009, 17(6): 810-814.
[15]Cheng L, Sturchio N C, Woicik J C, et al. High-resolution structural study of zinc ion incorporation at the calcite cleavage surface[J]. Surface Science, 1998, 415(1/2): 976-982.
[16]丁燕, 高明霞, 汤庆国, 等. 铜锌合金对碳酸钙水垢晶体结构的影响[J]. 河北工业大学学报, 2009, 38(4): 1-4.
Ding Yan, Gao Mingxia, Tang Qingguo, et al. Effect of copper-zinc alloy on the crystal structure of calcium carbonate scale[J]. Journal of Hebei University of Technology, 2009, 38(4): 1-4.
[17]Wang Man, Liang Jinsheng, Tang Qingguo. Surface free energy of copper-zinc alloy for energy-saving of boiler[J]. Rare Metals, 2006(S1): 324-327.
[18]汤庆国, 梁金生, 孟军平, 等. 热处理对铜锌阻垢合金性能的影响[J]. 材料科学与工艺, 2010, 18(3): 382-386.
Tang Qingguo, Liang Jinsheng, Meng Junping, et al. Effect of heat treatment on properties of scale inhibiting copper-zinc alloy[J]. Materials Science and Technology, 2010, 18(3): 382-386.