AZ80挤压镁合金微弧涂层的耐蚀性能

doi:10.13251/j.issn.0254-6051.2024.01.041

金属热处理 ›› 2024, Vol. 49 ›› Issue (1): 256-261.DOI: 10.13251/j.issn.0254-6051.2024.01.041

AZ80挤压镁合金微弧涂层的耐蚀性能

汤嘉琪¹, 薛玉娜¹, 王灿坤², 申毅¹, 刘晓龙³, 姬蕴卓¹, 方烨¹, 王博瑶¹

1. 西安石油大学材料科学与工程学院, 陕西西安 710065;
2. 新疆油田公司工程技术处, 新疆克拉玛依 834009;
3. 西安福莱特热处理有限公司, 陕西西安 710065

收稿日期:2023-08-02 修回日期:2023-11-09 发布日期:2024-02-29
通讯作者: 薛玉娜,讲师,博士,E-mail: ynxue@xsyu.edu.cn
作者简介:汤嘉琪(2001—),女,主要研究方向为材料的腐蚀与防护,E-mail: tjq18395400014@163.com。
基金资助:
西安市科技计划(22GXFW0106);西安石油大学2021年省级大学生创新创业训练计划(S202110705109);陕西省自然科学基础研究计划青年项目(2022JQ-339)

Corrosion properties of micro-arc oxidation coating on AZ80 extruded magnesium alloy

Tang Jiaqi¹, Xue Yuna¹, Wang Cankun², Shen Yi¹, Liu Xiaolong³, Ji Yunzhuo¹, Fang Ye¹, Wang Boyao¹

1. School of Materials Science and Engineering, Xi'an Shiyou University, Xi'an Shaanxi 710065, China;
2. Engineering Technology Department of Xinjiang Oilfield Company, Karamay Xinjiang 834009, China;
3. Xi'an Flit Heat Treatment Co., Ltd., Xi'an Shaanxi 710065, China

Received:2023-08-02 Revised:2023-11-09 Published:2024-02-29

摘要/Abstract

摘要： 针对镁合金裸露动件的服役环境及表面防护特点,采用微弧氧化(MAO)表面处理技术在AZ80挤压合金表面制备MAO涂层,通过连续盐雾加速腐蚀试验,研究了AZ80合金基体及MAO涂层的静态腐蚀性能,并对AZ80合金基体和MAO涂层试样进行预腐蚀,通过慢应变速率拉伸试验研究了MAO涂层及预腐蚀时间对AZ80镁合金腐蚀行为的影响。结果表明,MAO涂层具有较好的静态防护性能,盐雾腐蚀6天后出现点蚀现象,涂层破裂后的腐蚀行为取决于AZ80合金基体的耐蚀性。在慢应变速率拉伸状态下,随着预腐蚀时间的延长,AZ80基体和MAO涂层的应力腐蚀敏感性增加,MAO涂层的应力腐蚀敏感性指数明显小于AZ80合金基体。MAO涂层试样对AZ80基体有明显的防护作用,可有效提高镁合金的耐蚀性。

关键词: AZ80挤压镁合金, 微弧氧化, 盐雾腐蚀, 应力腐蚀

Abstract: Aiming at the service environment and surface protection characteristics of magnesium alloy exposed moving parts, micro-arc oxidation (MAO) coating was prepared on AZ80 extruded magnesium alloy. The static corrosion properties of the AZ80 alloy substrate and MAO coating were studied by continuous slat fog corrosion test. Moverover, pre-corrosion of the AZ80 alloy substrate and MAO coating was carried out, and the effect of MAO coating and pre-corrosion time on the corrosion behavior of the AZ80 alloy were analyzed through slow strain rate tensile test. The results show that the MAO coating has good static protection properties. While after salt fog corrosion for 6 days, the pitting corrosion occurs, and then after the coating is damaged the corrosion depends on the corrosion resistance of the AZ80 alloy substrate. Under the slow strain rate tensile condition, the stress corrosion sensitivity increases with the prolongation of the pre-corrosion time, while the stress corrosion sensitivity index of MAO coating is obviously smaller than that of the AZ80 substrate. The MAO coating has obvious protective effect for the AZ80 substrate, which can effectively improve the dynamic corrosion resistance of the magnesium alloy.

Key words: AZ80 extruded magnesium alloy, micro-arc oxidation, salt spray corrosion, stress corrosion

中图分类号:

TG142.2

汤嘉琪, 薛玉娜, 王灿坤, 申毅, 刘晓龙, 姬蕴卓, 方烨, 王博瑶. AZ80挤压镁合金微弧涂层的耐蚀性能[J]. 金属热处理, 2024, 49(1): 256-261.

Tang Jiaqi, Xue Yuna, Wang Cankun, Shen Yi, Liu Xiaolong, Ji Yunzhuo, Fang Ye, Wang Boyao. Corrosion properties of micro-arc oxidation coating on AZ80 extruded magnesium alloy[J]. Heat Treatment of Metals, 2024, 49(1): 256-261.

参考文献

[1]United States Environmental Protection Agency. Light-duty automotive technology, carbon dioxide emissions, and fuel economy trends: 1975 through 2016: EPA-420-S-16-001[R].
[2]Gryguc A, Behravesh S B, Shaha S K, et al. Low-cycle fatigue characterization and texture induced ratcheting behaviour of forged AZ80 Mg alloys[J]. International Journal of Fatigue, 2018, 116: 429-438.
[3]Toscano D, Shaha S K, Behravesh B, et al. Effect of forging on the low cycle fatigue behavior of cast AZ31B alloy[J]. Materials Science and Engineering A, 2017, 706: 342-356.
[4]Birbilis N, Williams G, Gusieva K, et al. Poisoning the corrosion of magnesium[J]. Electrochemistry Communication, 2013, 34: 295-298.
[5]宋光铃. 镁合金腐蚀与防护[M]. 北京: 化学工业出版社, 2006: 45-180.
[6]Wang J, Pang X, Jahed H. Surface protection of Mg alloys in automotive applications: A review[J]. AIMS Materials Science, 2019, 6(4): 567-600.
[7]Jiang B L, Ge Y F. Micro-arc Oxidation (MAO) to Improve the Corrosion Resistance of Magnesium (Mg) Alloys[M]. Woodhead Publishing Limited, 2013: 163-196.
[8]Guo H, An M, Xu S, et al. Microarc oxidation of corrosion resistant ceramic coating on a magneisum alloy[J]. Materials Letters, 2006, 60(12): 1538-1541.
[9]韩恩厚, 宋单. 一种实现镁合金表面微弧氧化膜原位封孔的溶液及制备微弧氧化膜的方法: CN104213175A[P]. 2014-12-17.
[10]Song Y, Dong K, Shan D, et al. Investigation of a novel self-sealing pore micro-arc oxidation film on AM60 magnesium alloy[J]. Journal of Magnesium and Alloys, 2013, 1(1): 82-87.
[11]Xue Y N, Pang X, Jiang B L, et al. Corrosion and corrosion fatigue performances of micro-arc oxidation coating on AZ31B cast magnesium alloy[J]. Materials and Corrosion, 2019, 70(2): 268-280.
[12]Ezhilselvi V, Nithin J, Balaraju J N, et al. The influence of current density on the morphology and corrosion properties of MAO coatings on AZ31B magnesium alloy[J]. Surface and Coatings Technology, 2016, 288: 221-229.
[13]Duan H, Yan C, Wang F. Effect of electrolyte additives on performance of plasma electrolytic oxidation films formed on magnesium alloy AZ91D[J]. Electrochimica Acta, 2007, 52: 3785-3793.
[14]Gnedenkov S V, Khrisanfova O A, Zavidnaya A G, et al. Composition and adhesion of protective coatings on aluminum[J]. Surface and Coatings Technology, 2001, 145: 146-151.
[15]Xue Y N, Pang X, Jiang B L, et al. Characterization of the corrosion performances of as-cast Mg-Al and Mg-Zn magnesium alloys with micrarc oxidation coatings[J]. Materials and Corrosion, 2020, 71(6): 992-1006.
[16]Song G L, Atrens A. Corrosion mechanisms of magnesium alloys[J]. Advanced Engineering Materials, 2000, 1: 11-31.
[17]Ben Haroush M, Ben Hamu G, Eliezer D, et al. The relation between microstructure and corrosion behavior of AZ80 Mg alloy following different extrusion temperatures[J]. Corrosion Science, 2008, 50: 1766-1778.
[18]Luo S, Fu A, Liu M, et al. Stress corrosion cracking behavior and mechanism of super 13Cr stainless steel in simulated O₂/CO₂ containing 3.5wt%NaCl solution[J]. Engineering Failure Analysis, 2021, 130: 105748.
[19]Luo S, Liu M, Shen Y, et al. Sulfide stress corrosion cracking behavior of G105 and S135 high-strength drill pipe steels in H₂S environment[J]. Journal of Materials Engineering and Performance, 2019, 28(3): 1707-1718.
[20]Liu Q, Zhou Q, Venezuela J, et al. Hydrogen influence on some advanced high-strength steels[J]. Corrosion Science, 2017, 125: 114-138.
[21]Merson E, Poluyanov V, Myagkikh P, et al. Effect of strain rate and corrosion products on pre-exposure stress corrosion cracking in the ZK60 magnesium alloy[J]. Materials Science & Engineering A, 2022, 830: 142304.
[22]Nachtsheim J, Ma S, Burja J, et al. In vitro evaluation of stress corrosion cracking susceptibility of PEO-coated rare-earth magnesium alloy WE4 [J]. Surface and Coatings Technology, 2024: 130391.
[23]Fujii T, Ito D, Shimamura Y, et al. Growth characteristics of stress corrosion cracking in high-strength 7075 aluminum alloy in sodium chloride solutions [J]. Engineering Fracture Mechanics, 2023, 292: 109657.

AZ80挤压镁合金微弧涂层的耐蚀性能

Corrosion properties of micro-arc oxidation coating on AZ80 extruded magnesium alloy

PDF

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

本文评价

[1]	刘文明, 张新明, 程新路, 欧阳凯. 焊后热处理对S30408/Q345R不锈钢复合板耐蚀性能的影响[J]. 金属热处理, 2024, 49(1): 172-178.
[2]	张明鲲, 杨敏, 王宇, 赵祥, 井德强. 热处理对高速列车用7005铝合金焊接接头应力腐蚀敏感性的影响[J]. 金属热处理, 2023, 48(8): 166-171.
[3]	陈宇科, 原梅妮, 周鹏飞, 杭瑞月, 李茂华. 脉冲频率及占空比对Ti6Al4V合金微弧氧化膜层微观结构及性能的影响[J]. 金属热处理, 2023, 48(6): 9-15.
[4]	周永东, 龚兰芳, 刘梓屹. 焊后时效处理对7020铝合金应力腐蚀倾向影响[J]. 金属热处理, 2023, 48(6): 80-84.
[5]	林丹, 谷高扬, 商剑. 激光重熔处理对铝合金微弧氧化层组织及性能的影响[J]. 金属热处理, 2023, 48(4): 264-272.
[6]	马静, 罗鸿, 王申豪, 童安琪, 李建辉, 王建刚, 冯志浩, 陈义庆. 外加电位下X80双相管线钢在模拟沿海土壤环境中的应力腐蚀行为[J]. 金属热处理, 2023, 48(2): 30-35.
[7]	池海涛, 刘馥兵, 胡晓光. 7A41铝合金的力学性能和耐蚀性能[J]. 金属热处理, 2022, 47(8): 88-94.
[8]	王进, 余国庆, 王国迪, 张曼雪, 冯甜, 解念锁, 景然. 退火温度对MAO-TC4钛合金表面组织及腐蚀性能的影响[J]. 金属热处理, 2021, 46(6): 65-68.
[9]	赵新娥. 8418钢熔铝料桶开裂分析[J]. 金属热处理, 2021, 46(6): 236-239.
[10]	李军, 姜波, 王超, 宋仁国. 7075铝合金微弧氧化膜硅溶胶封孔工艺及其性能[J]. 金属热处理, 2021, 46(5): 224-228.
[11]	何巧成, 姜文勇, 陈鹿, 王长亮, 武鹏海. 硅酸盐体系电解液中添加Na₂WO₄对LY12铝合金陶瓷膜性能的影响[J]. 金属热处理, 2021, 46(4): 152-156.
[12]	岳佳宏, 孟璇, 姚小卫, 孔令飞, 杨阳, 秦国方. 渗氮后氧化处理40Cr钢的耐蚀性能[J]. 金属热处理, 2021, 46(4): 217-219.
[13]	伍宇昊, 魏晓伟, 谢晓伟. 瓷质氧化预处理对6061铝合金弱酸性介质中微弧氧化膜的影响[J]. 金属热处理, 2021, 46(3): 28-32.
[14]	余国庆, 景然, 王国迪, 张曼雪, 冯甜, 解念锁. MAO电压对TC4合金氧化膜层摩擦磨损性能的影响[J]. 金属热处理, 2021, 46(11): 126-130.
[15]	刘敬福, 周祥春, 曲迎东. Al-Zn-Mg合金应力腐蚀断裂的研究进展[J]. 金属热处理, 2020, 45(9): 21-28.