退火处理对CP780钢组织和拉伸行为的影响

doi:10.13251/j.issn.0254-6051.2024.11.015

金属热处理 ›› 2024, Vol. 49 ›› Issue (11): 104-111.DOI: 10.13251/j.issn.0254-6051.2024.11.015

退火处理对CP780钢组织和拉伸行为的影响

曹洋洋^1,2, 李锋¹, 陈立佳¹, 谷雪忠², 王斌², 张鹏², 张哲峰²

1.沈阳工业大学材料科学与工程学院, 辽宁沈阳 110870;
2.中国科学院金属研究所, 辽宁沈阳 110016

收稿日期:2024-06-02 修回日期:2024-09-12 出版日期:2024-11-25 发布日期:2025-01-09
通讯作者: 王斌,副研究员,博士,E-mail:bwang12s@imr.ac.cn
作者简介:曹洋洋(1997—),女,硕士研究生,主要研究方向为高强钢的组织与性能,E-mail:448074857@qq.com。
基金资助:
吉林省与中国科学院科技合作高技术产业化专项(2021SYHZ0046)

Effect of annealing on microstructure and tensile behaviors of CP780 steel

Cao Yangyang^1,2, Li Feng¹, Chen Lijia¹, Gu Xuezhong², Wang Bin², Zhang Peng², Zhang Zhefeng²

1. School of Materials Science and Engineering, Shenyang University of Technology, Shenyang Liaoning 110870, China;
2. Institute of Metal Research, Chinese Academy of Sciences, Shenyang Liaoning 110016, China

Received:2024-06-02 Revised:2024-09-12 Online:2024-11-25 Published:2025-01-09

摘要/Abstract

摘要： 以CP780钢为研究对象,对其进行预拉伸变形及去应力退火处理,利用金相显微镜(OM)、扫描电镜(SEM)、维氏硬度计、拉伸试验机等手段对不同状态CP780钢的微观组织、硬度、拉伸性能及拉伸断裂形貌进行了系统研究。结果表明,不同状态CP780钢的显微组织主要为贝氏体与铁素体;在400~550 ℃去应力退火后,试样壁厚中心处出现的贝氏体带状组织是导致拉伸断口出现分层的主要原因;随去应力退火温度的升高,CP780钢因预拉伸变形导致的塑性降低现象得到改善,而强度则是先降低后增大再降低;在600 ℃去应力退火后,预拉伸变形CP780钢获得了最高的强塑性匹配,强塑积达到16.5 GPa·%。

关键词: CP780钢, 去应力退火, 微观组织, 拉伸性能, 断裂形貌

Abstract: Taking CP780 steel as the research object, the treatments of pre-stretch deformation and stress relief annealing was conducted on it. The microstructures, hardness, tensile properties and tensile fracture morphologies of the CP780 steel in different states were systematically studied by means of the optical microscopy (OM), scanning electron microscope (SEM), Vickers hardness tester and tensile testing machine. The results show that the microstructure of the CP780 steel in different states are mainly the bainite and ferrite. After stress relief annealing at 400-550 ℃, the bainite banded structure at the center of the specimen wall thickness is the main reason for the delamination of the tensile fracture surface. With the increase of annealing temperature, the plasticity reduction of the CP780 steel due to pre-stretch deformation is improved, and the strength firstly decreases, then increases and then reduces. The pre-stretch deformed CP780 steel stress relief annealed at 600 ℃ obtains the highest strength-plasticity combination, with product of strength and elongation reaching 16.5 GPa·%.

Key words: CP780 steel, stress relief annealing, microstructure, tensile properties, fracture morphologies

中图分类号:

TG156.23

曹洋洋, 李锋, 陈立佳, 谷雪忠, 王斌, 张鹏, 张哲峰. 退火处理对CP780钢组织和拉伸行为的影响[J]. 金属热处理, 2024, 49(11): 104-111.

Cao Yangyang, Li Feng, Chen Lijia, Gu Xuezhong, Wang Bin, Zhang Peng, Zhang Zhefeng. Effect of annealing on microstructure and tensile behaviors of CP780 steel[J]. Heat Treatment of Metals, 2024, 49(11): 104-111.

参考文献

[1]谢贵山, 黄宗斌, 赵肖斌, 等. 汽车车身的轻量化设计探讨[J]. 汽车零部件, 2023(2): 80-84.
Xie Guishan, Huang Zongbin, Zhao Xiaobin, et al. Discussion on lightweight design of automobile body[J]. Automobile Parts, 2023(2): 80-84.
[2]王鹏博, 张永强, 蔡宁, 等. CP780复相高强钢工频与中频电阻点焊接头性能对比分析[J]. 电焊机, 2022, 52(12): 70-76.
Wang Bocheng, Zhang Yongqiang, Cai Ning, et al. Comparison and analysis of performance of power frequency and intermediate frequency resistance spot welding joints of CP780 steel[J]. Electric Welding Machine, 2022, 52(12): 70-76.
[3]邹英, 刘华赛, 韩赟, 等. 800 MPa级热基镀锌复相钢的开发[J]. 金属热处理, 2022, 47(2): 65-69.
Zou Ying, Liu Huasai, Han Yun, et al. Development of 800 MPa grade hot-rolled galvanized complex phase steel[J]. Heat Treatment of Metals, 2022, 47(2): 65-69.
[4]谢春乾, 杨瑞枫, 李振, 等. 退火工艺对780 MPa级复相钢组织与性能的影响[J]. 金属热处理, 2018, 43(7): 171-174.
Xie Chunqian, Yang Ruifeng, Li Zhen, et al. Effect of annealing process on microstructure and properties of 780 MPa complex phase steel[J]. Heat Treatment of Metals, 2018, 43(7): 171-174.
[5]张骁杰, 李卫华, 刘俊祥, 等. 轻量化管状扭力梁横梁研究[J]. 汽车零部件, 2015(12): 83-85.
Zhang Xiaojie, Li Weihua, Liu Junxiang, et al. Research on the lightweight tubular torsion beam[J]. Automobile Parts, 2015(12): 83-85.
[6]Zhang W W, Han C, Yuan S J. Optimization of pre-form shapes by response surface methodology for hydro-forming of 780 MPa torsion beam[J]. International Journal of Advanced Manufacturing Technology, 2016, 85: 1227-1237.
[7]袁鸿志, 冯晓宇. 去应力退火工艺参数的研究[J]. 热处理技术与装备, 2014, 35(2): 48-50.
Yuan Hongzhi, Feng Xiaoyu. Research on process parameters of stress relief annealing[J]. Heat Treatment Technology and Equipment, 2014, 35(2): 48-50.
[8]Shao C W, Zhang P, Zhu Y K, et al. Improvement of low-cycle fatigue resistance in TWIP steel by regulating the grain size and distribution[J]. Acta Materialia, 2017, 134: 128-142.
[9]Zhang Y, Li W K, Jiang H Y, et al. Anisotropic mechanical properties of dual phase high strength steel sheets accounting for bake hardening process[J]. Journal of Plasticity Engineering, 2022, 29(7): 129-139.
[10]徐沛瑶, 李素云. 退火工艺对扭力梁横梁材料和性能的影响[J]. 传动技术, 2020, 34(1): 44-48.
Xu Peiyao, Li Suyun. Effect of annealing process on materials and properties of torsion beams[J]. Drive System Technique, 2020, 34(1): 44-48.
[11]柳志鹏, 谢振家, 罗登, 等. 中心偏析对FH40低温钢焊接组织性能的影响[J]. 工程科学学报, 2023, 45(8): 1335-1341.
Liu Zhipeng, Xie Zhenjia, Luo Deng, et al. Influence of central segregation on the welding microstructure and properties of FH40 cryogenic steel[J]. Chinese Journal of Engineering, 2023, 45(8): 1335-1341.
[12]纪元, 闵云峰, 李鹏善, 等. 钢中带状组织及其研究现状[J]. 中国冶金, 2016, 26(4): 1-9.
Ji Yuan, Min Yunfeng, Li Pengshan, et al. Research status of banding phenomena in steels[J]. China Metallurgy, 2016, 26(4): 1-9.
[13]谯德高, 赵小龙, 狄彦军, 等. 退火工艺对平整轧制后50W800无取向硅钢磁性能的影响[J]. 金属热处理, 2022, 47(11): 117-121.
Qiao Degao, Zhao Xiaolong, Di Yanjun, et al. Effect of annealing process on magnetic properties of flattening rolled 50W800 non-oriented silicon steel[J]. Heat Treatment of Metals, 2022, 47(11): 117-121.
[14]Jiang Bin, Li Xiaocheng, Zuo Pengpeng, et al. Effect of stress-relief annealing on isothermal fatigue life of a new hot stamping die steel 4Cr2Mo2V[J]. Materials Research Express, 2022, 9(2): 026516.
[15]张清清, 章传国, 郑磊. 去应力退火对X100M管线管组织性能的影响[J]. 焊管, 2016, 39(11): 1-4.
Zhang Qingqing, Zhang Chuanguo, Zheng Lei. Effects ofstress relief annealing on the microstructures and properties of X100M line pipe[J]. Welded Pipe and Tube, 2016, 39(11): 1-4.
[16]鲍丹. 我国率先研制成功第三代汽车钢[N]. 人民日报, 2011-02-24(1).
[17]董欣欣, 杨丽, 唐勤, 等. 热轧含钛低合金高强钢板断口分层机理研究[J]. 有色金属科学与工程, 2024, 15(1): 51-57.
Dong Xinxin, Yang Li, Tang Qin, et al. Study on lamination cracks of hot-rolling Ti-bearing HSLA plate[J]. Nonferrous Metals Science and Engineering, 2024, 15(1): 51-57.
[18]李永亮, 邝霜, 贾丽慧, 等. 800 MPa级汽车扭力梁用钢围管和焊缝矫直开裂机理研究[J]. 钢铁钒钛, 2021, 42(1): 184-190.
Li Yongliang, Kuang Shuang, Jia Lihui, et al. Research on cracking mechanism of girth and weld straightening of grade 800 MPa automobile torsion beam steel[J]. Iron Steel Vanadium Titanium, 2021, 42(1): 184-190.
[19]Yu Y S, Hu B, Gao M L, et al. Determining role of heterogeneous microstructure in lowering yield ratio and enhancing impact toughness in high-strength low-alloy steel[J]. International Journal of Minerals, Metallurgy and Materials, 2021, 28(5): 816-825.

退火处理对CP780钢组织和拉伸行为的影响

Effect of annealing on microstructure and tensile behaviors of CP780 steel

PDF

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

本文评价

[1]	陈子健, 林业佳, 李传强, 邓仁昡, 董勇, 章争荣. 微合金化调控7075铝合金的微观组织与力学性能[J]. 金属热处理, 2024, 49(9): 58-63.
[2]	任鹏帅, 秦凤, 周骞, 赵雷杰, 崔护, 彭子奥, 武常生. 等温淬火对含铝无碳化物贝氏体钢组织和性能的影响[J]. 金属热处理, 2024, 49(9): 103-109.
[3]	汲庆涛, 孙有政, 杨慧, 赵忠超, 史晓明. 时效时间对7175铝合金组织和力学性能的影响[J]. 金属热处理, 2024, 49(9): 242-246.
[4]	曹中玉, 贾华坡, 赵保伟. 两相区退火温度对汽车用0.2C-8Mn-2Al钢组织与力学性能的影响[J]. 金属热处理, 2024, 49(9): 247-250.
[5]	张宏亮, 王明欣, 张京兵, 李玉涛, 金头男. TiC含量对AlCoCrFeNi高熵合金熔覆层组织与耐磨性的影响[J]. 金属热处理, 2024, 49(9): 275-279.
[6]	刘运娜, 孙笠灿, 戴观文, 刘献达, 宋仁伯, 张朝磊. 冷却速率和Nb微合金化对25MnV非调质钢组织和硬度的影响[J]. 金属热处理, 2024, 49(8): 31-35.
[7]	华文娟, 张建勋. 时效处理对电弧熔丝增材制造2319铝合金性能及断裂行为的影响[J]. 金属热处理, 2024, 49(8): 60-66.
[8]	刘静, 赵科, 王丽阁. 退火对Co_xFe₃₅Mn₂₅Cr₁₅Ni₁₀Ti₅高熵合金微观组织及硬度的影响[J]. 金属热处理, 2024, 49(8): 94-101.
[9]	周瑞虎, 樊启刚, 曾志鹏. 轴承套圈碳氮共渗工艺的改进[J]. 金属热处理, 2024, 49(8): 152-155.
[10]	刘梓峰, 赵旭亮, 罗皓. 淬火温度对4Cr4Mo3W2V1模具钢组织与硬度的影响[J]. 金属热处理, 2024, 49(8): 170-173.
[11]	梁科, 武猛, 张习烨, 行志刚. 退火温度对汽车后背门板用Fe-0.12C-4.85Mn-0.24Si钢组织与力学性能的影响[J]. 金属热处理, 2024, 49(8): 174-177.
[12]	李正龙, 庞景宇, 汤广全, 程陆凡, 张财伟, 侯星宇, 李文, 张海峰. 变形热处理对Ti₄₅Zr₂₀Nb₁₅V_(10-x)Al₁₀Mo_x难熔高熵合金组织与性能的影响[J]. 金属热处理, 2024, 49(7): 47-53.
[13]	陈保安, 李梦琳, 陈瑞, 多俊龙, 韩钰, 祝志祥, 杨长龙, 缪姚军. 添加稀土对Al-Mg-Si合金微观组织和性能的影响[J]. 金属热处理, 2024, 49(7): 100-105.
[14]	周蕾, 王莹, 张永健, 赵晓丽, 惠卫军. V+Ti微合金化Mn-Cr系贝氏体型非调质钢的氢脆敏感性[J]. 金属热处理, 2024, 49(7): 106-112.
[15]	蒋军杰, 王永彪, 肖志玲, 樊江磊, 张正文. 退火温度对激光选区熔化成形TA15钛合金微观组织与力学性能的影响[J]. 金属热处理, 2024, 49(7): 241-248.