中间退火对5182-O铝合金组织、性能及吕德斯带演变影响

doi:10.13251/j.issn.0254-6051.2024.12.035

金属热处理 ›› 2024, Vol. 49 ›› Issue (12): 213-220.DOI: 10.13251/j.issn.0254-6051.2024.12.035

中间退火对5182-O铝合金组织、性能及吕德斯带演变影响

吴万东¹, 孟双¹, 于俊芃¹, 徐志远¹, 王磊¹, 刘兵², 麻慧琳¹, 李延成¹

1.山东南山铝业股分有限公司国家铝合金压力加工工程技术研究中心, 山东烟台 265700;
2.上海汽车集团股份有限公司乘用车公司, 上海 201800

收稿日期:2024-06-13 修回日期:2024-10-21 出版日期:2024-12-25 发布日期:2025-02-05
作者简介:吴万东(1995—),男,工程师,硕士,主要研究方向为汽车车身用高性能铝合金研发,E-mail:wuwandong199509@163.com
基金资助:
山东省重点研发项目(2021SFGC1001)

Effect of intermediate annealing on microstructure, mechanical properties and Luders band evolution of 5182-O aluminum alloy

Wu Wandong¹, Meng Shuang¹, Yu Junpeng¹, Xu Zhiyuan¹, Wang Lei¹, Liu Bing², Ma Huilin¹, Li Yancheng¹

1. National Engineering Research Center for Plastic Working of Aluminum Alloys, Shandong Nanshan Aluminum Co., Ltd., Yantai Shandong 265700, China;
2. Passenger Car Company, Shanghai Automotive Group Co., Ltd., Shanghai 201800, China

Received:2024-06-13 Revised:2024-10-21 Online:2024-12-25 Published:2025-02-05

摘要/Abstract

摘要： 采用SEM、拓扑仪、万能拉伸试验机等设备,探究中间退火工艺对5182-O铝合金微观组织、成形性、力学性能及吕德斯带演变规律的影响。结果表明,经中间退火处理后,板材的第二相含量减少,晶粒尺寸从19 μm增长到34 μm,材料强度略微下降(R_m=273 MPa,R_p0.2=121 MPa)、伸长率小幅提升(A₅₀=27.8%),消除了屈服点延伸率(Yield point elongation,YPE),冲制零件表面吕德斯带显著改善。中间退火工艺能在保证汽车板内覆盖件用5182-O铝合金力学性能、成形性前提下,有效改善吕德斯带。吕德斯带明显改善主要归功于更匹配的晶粒尺寸和更少的大块Al₆(FeMn)第二相,减弱了塑性变形时的PLC效应。目前该工艺制备的板材已应用于国内一些主机厂汽车内覆盖件生产。

关键词: 5182-O铝合金, 吕德斯带, 力学性能, 微观组织, PLC效应

Abstract: Microstructure, forming property, mechanical properties and Luders band evolution of the 5182-O aluminum alloy materials were characterized by SEM, topometer and universal tensile testing machine. The results show that after intermediate annealing treatment, the content of the second phase in the sheet decreases, the grain size increases from 19 μm to 34 μm, the material strength slightly decreases (R_m=273 MPa, R_p0.2=121 MPa), the elongation slightly increases (A₅₀=27.8%), the yield point elongation (YPE) is eliminated, and the Luders band on the surface of the punched parts is significantly improved. The intermediate annealing process can effectively improve the Luders band while ensuring the mechanical properties and formability of the 5182-O aluminum alloy used for automotive panel coverings. The significant improvement in the Luders band is mainly attributed to a more matched grain size and less bulk Al₆(FeMn) second phases, which weakens the PLC effect during plastic deformation. At present, the board prepared by this process has been applied to the production of automotive interior panel in some domestic OEMs.

Key words: 5182-O aluminum alloy, Luders band, mechanical properties, microstructure, PLC effect

中图分类号:

TG146.2

吴万东, 孟双, 于俊芃, 徐志远, 王磊, 刘兵, 麻慧琳, 李延成. 中间退火对5182-O铝合金组织、性能及吕德斯带演变影响[J]. 金属热处理, 2024, 49(12): 213-220.

Wu Wandong, Meng Shuang, Yu Junpeng, Xu Zhiyuan, Wang Lei, Liu Bing, Ma Huilin, Li Yancheng. Effect of intermediate annealing on microstructure, mechanical properties and Luders band evolution of 5182-O aluminum alloy[J]. Heat Treatment of Metals, 2024, 49(12): 213-220.

参考文献

[1]张震, 王鸿斌, 王贺, 等. 汽车车身板用变形铝合金研究进展[J]. 精密成形工程, 2022, 14(1): 71-78.
Zhang Zhen, Wang Hongbin, Wang He, et al. Research progress of wrought aluminum alloy for automobile body sheet[J]. Journal of Netshape Forming Engineering, 2022, 14(1): 71-78.
[2]房洪杰, 刘慧, 孙杰, 等. 5×××系铝合金研究现状及发展趋势[J]. 材料导报, 2023(21): 1-15.
Fang Hongjie, Liu Hui, Sun Jie, et al. Research status and development trend of 5××× series aluminum alloys[J]. Material Reports, 2023(21): 1-15.
[3]郑雪芹. 汽车新材料的应用及发展趋势[J]. 汽车纵横, 2021(11): 73-76.
Zheng Xueqin. Application and development trend of new automotive materials[J]. Auto Review, 2021(11): 73-76.
[4]胡斌. 汽车行业发展对轻质结构部件的需求与展望[J]. 精密成形工程, 2020, 12(3): 120-124.
Hu Bin. Demand and prospect for lightweight structural components in automotive industry[J]. Journal of Netshape Forming Engineering, 2020, 12(3): 120-124.
[5]苑锡妮, 杨兵, 曾渝, 等. 5×××系铝合金汽车板研究进展[J]. 轻合金加工技术, 2018(6): 8-13.
Yuan Xini, Yang Bing, Zeng Yu, et al. Research development of 5××× series Al alloy sheet for automotive[J]. Light Alloy Fabrication Technology, 2018(6): 8-13.
[6]Ramer L, Phillippi M, Tack W T, et al. Locally reversing sensitization in 5××× aluminum plate[J]. Journal of Materials Engineering and Performance, 2012, 21(6): 1025-1029.
[7]麻慧琳, 吴万东, 徐志远, 等. 不同变形量 5182-O 铝合金汽车板 PLC 效应表现和吕德斯带演变[J]. 精密成形工程, 2023, 15(12): 50-57.
Ma Huilin, Wu Wandong, Xu Zhiyuan, et al. PLC effect and Luders band performance of 5182-O aluminum alloy automotive plate under different deformation[J]. Journal of Netshape Forming Engineering, 2023, 15(12): 50-57.
[8]Reyne B, Manach P Y, Mos N. Macroscopic consequences of Piobert-Lüders and Portevin-Le Chatelier bands during tensile deformation in Al-Mg alloys[J]. Materials Science and Engineering A, 2019, 746.
[9]Coër J, Manach P Y, Laurent H, et al. Piobert-Lüders plateau and Portevin-Le Chatelier effect in an Al-Mg Alloy in simple shear[J]. Mechanics Research Communications, 2013, 48: 1-7.
[10]Cottrell A H, Bilby B A. Dislocation theory of yielding and stain ageing of iron[J]. Proceedings of the Physical Society, 1949, 62(1): 49-62.
[11]Wu C H, Li H, Bian T J, et al. Natural aging behaviors of Al-Cu-Li alloy: PLC effect, properties and microstructure evolution[J]. Materials Characterization, 2022, 184.
[12]曹高辉, 苑锡妮, 曹零勇. 5754-O铝合金吕德斯带表面缺陷解决方案的应用[J]. 宝钢技术, 2022(3): 56-62.
Cao Gaohui, Yuan Xini, Cao Lingyong. Application of surface defect solution of 5754-O aluminum[J]. Baosteel Technology, 2022(3): 56-62.
[13]Kang J R, Liu X, Wang T Z. The effects of ultrasonic vibration on Portevin-Le Chatelier (PLC) effect and stress-strain behavior in aluminum alloy 2024[J]. Scripta Materialia, 2023, 224: 115121 .
[14]曹鹏涛. 铝合金中Portevin-Le Chatelier效应的多尺度实验和机理研究[D]. 合肥: 中国科学技术大学, 2010: 72-73.
Cao Pengtao. Muliti-scale experimental and theoretical investigations on the Porevin-Le Chatelier effect in Al alloy[D]. Hefei: University of Science and Technology of China, 2010: 72-73.
[15]刘颢文, 张青川, 曹鹏涛, 等. Al-Mg合金中析出强化相对Portevin-Le Chatelier效应的影响[J]. 实验力学, 2007(Z1): 390-394.
Liu Haowen, Zhang Qingchuan, Cao Pengtao, et al. The influence of the precipitation on the Portevin-Le Chatelier effect in Al-Mg alloy[J]. Journal of Experimental Mechanics, 2007(Z1): 390-394.
[16]黎凤, 许泽兵, 任月路, 等. 预拉伸对5182-O和5754-O铝合金屈服平台的影响[J]. 轻合金加工技术, 2020, 48(11): 26-31, 45.
Li Feng, Xu Zebing, Ren Yuelu, et al. Influence of pre-stretching on yield platform of 5182-O and 5754-O aluminum alloys[J]. Light Alloy Fabrication Technology, 2020, 48(11): 26-31, 45.
[17]马青梅, 李菁菁, 张国文, 等. 退火及冷却方式对 5182 铝合金屈服平台的影响[J]. 材料热处理学报, 2019, 40(9): 21-25.
Ma Qingmei, Li Jingjing, Zhang Guowen, et al. Effect of annealing and cooling rate on yield plateau of 5182 alloy[J]. Transactions of Materials and Heat Treatment, 2019, 40(9): 21-25.
[18]孟凡林, 曹零勇, 王宇, 等. 冷轧变形量及完全退火对汽车用5182板材组织和性能的影响[J]. 有色金属加工, 2015, 44(5): 28-32.
Meng Fanlin, Cao Linyong, Wang Yu, et al. Effects of cold rolling reduction and full annealing on microstructures and properties of 5182 aluminum alloys for ABS[J]. Nonferrous Metals Processing, 2015, 44(5): 28-32.
[19]王宇, 曹零勇, 李俊鹏, 等. 中间退火对汽车用5182铝合金板组织和性能的影响[J]. 材料工程, 2016, 44(9): 76-81.
Wang Yu, Cao Lingyong, Li Junpeng, et al. Effect of intermediate annealing on microstructure and property of 5182 aluminum alloy sheet for automobile[J]. Journal of Materials Engineering, 2016, 44(9): 76-81.
[20]张希园. 中间退火对高镁铝合金组织和力学性能的影响[J]. 轻合金加工技术, 2023, 51(4): 11-14.
Zhang Xiyuan. Effect of intermediate annealing on the microstructure and mechanical properties of high magnesium aluminum alloy[J]. Light Alloy Fabrication Technology, 2023, 51(4): 11-14.
[21]章国华, 曹城. 中间退火对5182铝合金模组外箱体表面褶皱的改善[C]//中国有色金属加工工业协会, 2020, 8: 206-213.
Zhang Guohua, Cao Cheng. Improvement of surface folding of 5182 aluminum alloy module by intermediate annealing[C]//China Nonferrous Metal Processing Industry Association, 2020, 8: 206-213.
[22]王祝堂, 田荣璋. 铝合金及其加工手册[M]. 长沙: 中南大学出版社, 2005: 70-73.
Wang Zhutang, Tian Rongzhang. Aluminum Alloy and Its Processing Manual[M]. Changsha: Central South University Press, 2005: 70-73.
[23]Jobba M, Mishra R K, Niewczas M, et al. Flow stress and work-hardening behaviour of Al-Mg binary alloys[J]. International Journal of Plasticity, 2015, 65: 43-60.

中间退火对5182-O铝合金组织、性能及吕德斯带演变影响

Effect of intermediate annealing on microstructure, mechanical properties and Luders band evolution of 5182-O aluminum alloy

PDF

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

本文评价

[1]	周浩, 王帅, 曾燕屏, 马志宝, 周德, 郭德瑞, 董树青. 长时在役Inconel 783高温合金螺栓的显微组织和力学性能[J]. 金属热处理, 2024, 49(9): 36-42.
[2]	陈子健, 林业佳, 李传强, 邓仁昡, 董勇, 章争荣. 微合金化调控7075铝合金的微观组织与力学性能[J]. 金属热处理, 2024, 49(9): 58-63.
[3]	任广笑, 王超, 曹喜娟, 王凯, 王红霞, 程伟丽, 牛晓峰. 时效处理对Mg-Y-Gd-Zn-Zr合金中LPSO相演变及性能的影响[J]. 金属热处理, 2024, 49(9): 96-102.
[4]	任鹏帅, 秦凤, 周骞, 赵雷杰, 崔护, 彭子奥, 武常生. 等温淬火对含铝无碳化物贝氏体钢组织和性能的影响[J]. 金属热处理, 2024, 49(9): 103-109.
[5]	张宇, 李圣阳, 魏晓蓼, 柴志松, 李泳. 铬合金化Q&P钢的热处理工艺优化与碳配分行为[J]. 金属热处理, 2024, 49(9): 110-116.
[6]	张青科, 诸汇涛, 陈根保, 陈立田, 夏亚金, 胡方勤, 宋振纶. 形变热处理对新型无Ti马氏体时效钢焊缝组织与力学性能的影响[J]. 金属热处理, 2024, 49(9): 117-124.
[7]	夏琳燕, 史湘琴, 刘逸卿, 周模豪, 邓蔚. 时效对铸造Al-Si-Cu-Mg合金力学性能和耐蚀性能的影响[J]. 金属热处理, 2024, 49(9): 152-157.
[8]	万志健, 安涛, 于文坛, 刘学华, 童乐, 赵海. 热处理工艺对42CrMo-R钢轮箍组织及力学性能的影响[J]. 金属热处理, 2024, 49(9): 158-164.
[9]	涂正平, 吴逸飞, 于安华, 陈晓伟, 王维俊. 超导磁体热处理对N50H不锈钢铠甲力学性能的影响[J]. 金属热处理, 2024, 49(9): 165-168.
[10]	赖春明, 李琴, 周家林, 吴兴欢, 黄艳. 焊后热处理对热丝TIG焊接10Cr9Mo1VNb锅炉用钢组织性能的影响[J]. 金属热处理, 2024, 49(9): 169-175.
[11]	刘强, 盛智勇, 张超, 李杰, 陈泽, 陈送义, 陈康华. 预变形对7085超强铝合金环件组织与性能的影响[J]. 金属热处理, 2024, 49(9): 176-184.
[12]	徐锋, 孙强, 贾云浩. 时效处理对15-5PH不锈钢室温和低温力学性能的影响[J]. 金属热处理, 2024, 49(9): 191-197.
[13]	马蓼奕, 董志, 杨立新, 李世键, 崔晶, 康冲. 淬火转移时间对16CrSiNi钢回火组织和性能的影响[J]. 金属热处理, 2024, 49(9): 198-203.
[14]	杨哲, 陈水胜. 时效工艺对ADC12铝合金析出相与力学性能的影响[J]. 金属热处理, 2024, 49(9): 216-220.
[15]	李喆, 李睿, 蔡磊, 靳军军. 固溶处理对机车车辆抱轴箱内壁堆焊层组织和力学性能的影响[J]. 金属热处理, 2024, 49(9): 226-231.