热处理工艺对W3Mo4Cr5V6钢耐冲击磨粒磨损性能的影响

doi:10.13251/j.issn.0254-6051.2024.12.005

金属热处理 ›› 2024, Vol. 49 ›› Issue (12): 33-39.DOI: 10.13251/j.issn.0254-6051.2024.12.005

热处理工艺对W3Mo4Cr5V6钢耐冲击磨粒磨损性能的影响

赵峥嵘¹, 曹玉龙², 樊明强¹, 张雲飞¹, 赵英利¹

1.河钢材料技术研究院, 河北石家庄 052165;
2.武汉科技大学省部共建耐火材料与冶金国家重点实验室, 湖北武汉 430081

收稿日期:2024-05-02 修回日期:2024-09-07 出版日期:2024-12-25 发布日期:2025-02-05
作者简介:赵峥嵘(1994—),男,工程师,硕士,主要研究方向为工模具钢的研发与应用,E-mail:zhaozhengrong@hbisco.com
基金资助:
国家自然科学基金(52004188)

Effect of heat treatment on impact abrasive wear resistance of W3Mo4Cr5V6 steel

Zhao Zhengrong¹, Cao Yulong², Fan Mingqiang¹, Zhang Yunfei¹, Zhao Yingli¹

1. Material Technology Research Institute of HBIS Group, Shijiazhuang Hebei 052165, China;
2. The State Key Laboratory of Refractories and Metallurgy, Wuhan University of Science and Technology, Wuhan Hubei 430081, China

Received:2024-05-02 Revised:2024-09-07 Online:2024-12-25 Published:2025-02-05

摘要/Abstract

摘要： 采用MLD10磨粒磨损试验机和VL2000DX-SVF17SP型激光共聚焦显微镜研究了热处理工艺对W3Mo4Cr5V6钢经磨粒磨损后性能及粗糙度的影响。对比分析了不同热处理工艺条件下W3Mo4Cr5V6钢的磨损质量损失率、表面磨损形貌及粗糙度变化情况。结果表明,经不同热处理后W3Mo4Cr5V6钢的耐磨性较铸态有明显提高,相同试验条件下磨损质量损失量较铸态减少17~24.9 mg,1100 ℃×1 h淬火+550 ℃×2 h回火试样的磨损质量损失较少且硬度均匀性较好,耐磨性优异。随着磨损时间的增加,不同试样表面粗糙度均逐渐减小,其中1100 ℃×1 h淬火+550 ℃×2 h回火试样从Ra=9.30 μm减小到Ra=7.60 μm,且不同视场间粗糙度数值较稳定。试样在磨损过程中的质量损失主要是由磨料犁削、脆性断裂、疲劳脱落所引起。

关键词: 高速钢, 热处理, 磨粒磨损, 粗糙度

Abstract: Effect of heat treatment process on the properties and roughness of the W3Mo4Cr5V6 steel after abrasive wear was studied by means of MLD10 abrasive wear tester and VL2000DX-SVF17SP laser confocal microscope. The wear mass loss rate, surface wear morphology and roughness changes under different heat treatment conditions were compared and analyzed. The results show that the wear resistance of the W3Mo4Cr5V6 steel after different heat treatments is significantly improved compared with that of the as-cast steel. Under the same test condition, the wear mass loss after heat treatment is 17-24.9 mg less than that of the as-cast. After quenching at 1100 ℃ for 1 h and tempering at 550 ℃ for 2 h, the wear mass loss of the specimen is less, the hardness uniformity is better and the wear resistance is excellent. With the increase of wear time, the surface roughness of different specimens decreases gradually. Among them, that of the specimen quenched at 1100 ℃ for 1 h and tempered at 550 ℃ for 2 h decreases from Ra=9.30 μm to Ra=7.60 μm, and the roughness value between different fields of view is stable. The mass loss of the specimens during the wear process is mainly caused by abrasive ploughing, brittle fracture and fatigue shedding.

Key words: high speed steel, heat treatment, abrasive wear, roughness

中图分类号:

赵峥嵘, 曹玉龙, 樊明强, 张雲飞, 赵英利. 热处理工艺对W3Mo4Cr5V6钢耐冲击磨粒磨损性能的影响[J]. 金属热处理, 2024, 49(12): 33-39.

Zhao Zhengrong, Cao Yulong, Fan Mingqiang, Zhang Yunfei, Zhao Yingli. Effect of heat treatment on impact abrasive wear resistance of W3Mo4Cr5V6 steel[J]. Heat Treatment of Metals, 2024, 49(12): 33-39.

参考文献

[1]王硕煜, 叶文虎, 解明祥, 等. 球墨铸铁轧辊表面镍基激光合金化层及其磨损性能[J]. 金属热处理, 2020, 45(6): 220-225.
Wang Shuoyu, Ye Wenhu, Xie Mingxiang, et al. Ni-based laser alloyed layer on ductile iron roller surface and its wear properties[J]. Heat Treatment of Metals, 2020, 45(6): 220-225.
[2]葛浩彬, 徐锟, 陈伟, 等. 冷轧工作辊工频淬火开裂原因分析[J]. 金属热处理, 2011, 36(9): 88-90.
Ge Haobin, Xu Kun, Chen Wei, et al. Cracking analysis of cold mill work rolls during power frequency induction hardening[J]. Heat Treatment of Metals, 2011, 36(9): 88-90.
[3]马陟祚, 张永振, 魏世忠, 等. 高钒高速钢冲击磨损性能与机理的研究[J]. 摩擦学学报, 2006, 26(2): 169-173.
Ma Zhizuo, Zhang Yongzhen, Wei Shizhong, et al. Impact wear and wear mechanism study of high vanadium high speed steel[J]. Tribology, 2006, 26(2): 169-173.
[4]Wang S F, Cui Q H, Zou J P, et al. Impact wear mechanism of 2Cr13 steel under small stress multi-impact conditions[J]. Wear, 2020, 462: 203492.
[5]薛屺, 易诚, 周毅, 等. 淬火温度对高钒高速钢摩擦磨损性能的影响[J]. 金属热处理, 2017, 42(11): 156-160.
Xue Qi, Yi Cheng, Zhou Yi, et al. Effect of quenching temperature on friction and wear properties of high vanadium high speed steel[J]. Heat Treatment of Metals, 2017, 42(11): 156-160.
[6]刘志强, 曹环军, 郑喜平, 等. 高钒高速钢的研究与应用[J]. 热加工工艺, 2014, 43(16): 23-26.
Liu Zhiqiang, Cao Huanjun, Zheng Xiping, et al. Research and application of high vanadium high speed steel[J]. Hot Working Technology, 2014, 43(16): 23-26.
[7]Zhao Z R, Cao Y L, Wan X L, et al. Effect of cooling rate on carbide characteristics of the high vanadium high-speed steel[J]. ISIJ
International, 2022, 62(3): 524-531.
[8]赵峥嵘, 曹玉龙, 万响亮, 等. W3Mo4Cr5V6高速钢中碳化物的高温转变行为[J]. 武汉科技大学学报, 2022, 45(1): 1-8.
Zhao Zhengrong, Cao Yulong, Wan Xiangliang, et al. High-temperature carbide transformation behavior of W3Mo4Cr5V6 high-speed steel[J]. Journal of Wuhan University of Science and Technology, 2022, 45(1): 1-8.
[9]彭龙生, 林英华, 黄伟, 等. 感应淬火对Cr12MoV钢轧辊硬度和硬化层深度的影响[J]. 金属热处理, 2022, 47(8): 118-122.
Peng Longsheng, Lin Yinghua, Huang Wei, et al. Effect of induction hardening on hardness and hardened layer depth of Cr12MoV steel roll[J]. Heat Treatment of Metals, 2022, 47(8): 118-122.
[10]张大伟, 陈伟. 锻钢冷轧辊X射线应力测试中附加应力层研究[J]. 金属热处理, 2015, 40(9): 203-205.
Zhang Dawei, Chen Wei. Additional stress layer of forged steel cold roller during X-ray stress test[J]. Heat Treatment of Metals, 2015, 40(9): 203-205.
[11]焦岩, 李祖来, 山泉, 等. 等温淬火热处理工艺对Fe-0.5C-2.0Si-2.5Mn钢冲击磨损性能的影响[J]. 摩擦学学报, 2017, 37(1): 52-58.
Jiao Yan, Li Zulai, Shan Quan, et al. Effect of impact wear on isothermal quenching of Fe-0.5C-2.0Si-2.5Mn steel[J]. Tribology, 2017, 37(1): 52-58.
[12]高强, 王文珍, 易戈文, 等. 热处理对Ni/Ti₂AlC复合材料显微组织和摩擦学性能的影响[J]. 摩擦学学报, 2022, 42(2): 242-253.
Gao Qiang, Wang Wenzhen, Yi Gewen, et al. Influences of annealing on microstructures and tribological properties of Ni/Ti₂AlC composites[J]. Tribology, 2022, 42(2): 242-253.
[13]陈雷雷. 高速钢合金碳化物控制研究[D]. 南京: 东南大学, 2016.
[14]Boccalini M, Goldenstein H. Solidification of high speed steels[J]. International Materials Reviews, 2001, 46(2): 92-115.
[15]邓彪, 陈蓬, 王国栋. 回火温度对二次硬化马氏体不锈钢组织和性能的影响[J]. 金属热处理, 2021, 46(9): 65-71.
Deng Biao, Chen Peng, Wang Guodong. Effect of tempering temperature on microstructure and properties of secondary hardening martensitic stainless steel[J]. Heat Treatment of Metals, 2021, 46(9): 65-71.
[16]张强, 陈永平, 毕国喜, 等. 大型精轧支撑辊疲劳断裂失效分析[J]. 金属热处理, 2022, 47(10): 270-274.
Zhang Qiang, Chen Yongping, Bi Guoxi, et al. Failure analysis on fatigue fracture of large finishing mill back up roller[J]. Heat Treatment of Metals, 2022, 47(10): 270-274.

热处理工艺对W3Mo4Cr5V6钢耐冲击磨粒磨损性能的影响

Effect of heat treatment on impact abrasive wear resistance of W3Mo4Cr5V6 steel

PDF

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

本文评价

[1]	任广笑, 王超, 曹喜娟, 王凯, 王红霞, 程伟丽, 牛晓峰. 时效处理对Mg-Y-Gd-Zn-Zr合金中LPSO相演变及性能的影响[J]. 金属热处理, 2024, 49(9): 96-102.
[2]	张青科, 诸汇涛, 陈根保, 陈立田, 夏亚金, 胡方勤, 宋振纶. 形变热处理对新型无Ti马氏体时效钢焊缝组织与力学性能的影响[J]. 金属热处理, 2024, 49(9): 117-124.
[3]	魏文逸. 热处理对激光沉积制造Ti-5321近β钛合金组织和性能的影响[J]. 金属热处理, 2024, 49(9): 132-138.
[4]	万志健, 安涛, 于文坛, 刘学华, 童乐, 赵海. 热处理工艺对42CrMo-R钢轮箍组织及力学性能的影响[J]. 金属热处理, 2024, 49(9): 158-164.
[5]	涂正平, 吴逸飞, 于安华, 陈晓伟, 王维俊. 超导磁体热处理对N50H不锈钢铠甲力学性能的影响[J]. 金属热处理, 2024, 49(9): 165-168.
[6]	赖春明, 李琴, 周家林, 吴兴欢, 黄艳. 焊后热处理对热丝TIG焊接10Cr9Mo1VNb锅炉用钢组织性能的影响[J]. 金属热处理, 2024, 49(9): 169-175.
[7]	杨含, 兰超锋, 王雄, 万静斌. 43 kg/m爬坡式尖轨的离线热处理[J]. 金属热处理, 2024, 49(9): 204-208.
[8]	刘姿, 孔为民. 焊后局部热处理区域布置对厚壁圆筒环缝残余应力的影响[J]. 金属热处理, 2024, 49(9): 221-225.
[9]	兰贤辉, 葛正福, 马鹏, 陈传, 周涛, 刘伟, 李超. 热处理对奥氏体不锈钢磁导率的影响[J]. 金属热处理, 2024, 49(9): 255-259.
[10]	高玉魁, 方文奕. 碳含量与热处理对高铌钛铝合金微观组织及力学性能的影响[J]. 金属热处理, 2024, 49(8): 9-14.
[11]	徐超, 曹欣旺, 王晨阳, 王玉婷, 张倩, 杨其全, 胡杰. 热处理工艺对高速列车用51CrV4钢轴箱弹簧力学性能及服役性能的影响[J]. 金属热处理, 2024, 49(8): 53-59.
[12]	任云飞, 潘新元, 万天剑, 李景辉, 张明亚. T6热处理对高压压铸ADC12铝合金微观结构和性能的影响[J]. 金属热处理, 2024, 49(8): 108-112.
[13]	郭昊东, 杨超飞, 孙磊, 张玉祥, 黄冬, 仝智远. 10CrNi8MoV钢的包申格效应及恢复热处理[J]. 金属热处理, 2024, 49(8): 119-123.
[14]	徐锋, 孙强, 孟吉炜. 固溶温度对超低碳15-5PH沉淀硬化不锈钢组织和性能的影响[J]. 金属热处理, 2024, 49(8): 124-129.
[15]	张勇, 李如杨, 马青山, 胡效东. 热处理对09MnNiDR低温钢焊接接头组织及力学性能的影响[J]. 金属热处理, 2024, 49(8): 136-142.