Al含量及均匀化处理对Mg-Al二元合金组织及阻尼性能的影响

doi:10.13251/j.issn.0254-6051.2024.07.011

金属热处理 ›› 2024, Vol. 49 ›› Issue (7): 70-77.DOI: 10.13251/j.issn.0254-6051.2024.07.011

Al含量及均匀化处理对Mg-Al二元合金组织及阻尼性能的影响

刘华燊¹, 孙有平^1,2,3, 何江美¹, 罗国健¹, 裴梦雨¹

1.广西科技大学机械与汽车工程学院, 广西柳州 545006;
2.广西土方机械协同创新中心, 广西柳州 545006;
3.广西汽车零部件与整车技术重点实验室, 广西柳州 545006

收稿日期:2024-01-22 修回日期:2024-04-30 出版日期:2024-07-25 发布日期:2024-08-29
通讯作者: 孙有平,教授,博士,E-mail:syptaiji@126.com
作者简介:刘华燊(1998—),女,硕士研究生,主要研究方向为镁合金阻尼与力学性能,E-mail:1569005906@qq.com。
基金资助:
广西高等学校高水平创新团队资助项目(桂教师范[2019]52号);中央引导地方科技发展专项(2021ZYZX1012)

Effect of Al content and homogenization on microstructure and damping properties of Mg-Al binary alloys

Liu Huashen¹, Sun Youping^1,2,3, He Jiangmei¹, Luo Guojian¹, Pei Mengyu¹

1. School of Mechanical and Automotive Engineering, Guangxi University of Science and Technology, Liuzhou Guangxi 545006, China;
2. Guangxi Earthmoving Machinery Collaborative Innovation Center, Liuzhou Guangxi 545006, China;
3. Guangxi Key Laboratory of Automobile Components and Vehicle Technology, Liuzhou Guangxi 545006, China

Received:2024-01-22 Revised:2024-04-30 Online:2024-07-25 Published:2024-08-29

摘要/Abstract

摘要： 采用光学显微镜、X射线衍射仪、扫描电镜以及拉伸试验机等研究了Al含量(0.25%、0.5%、1.0%,质量分数)及均匀化处理(420 ℃×24 h)对铸态Mg-Al合金显微组织、力学性能和阻尼性能的影响。结果表明:Al元素的添加可以减小合金的平均晶粒尺寸,且添加量越多,平均晶粒尺寸越小,而均匀化处理后的平均晶粒尺寸明显增加。随着Al含量的增加,铸态Mg-Al合金的力学性能逐渐增加,Mg-1.0%Al合金的抗拉强度、屈服强度和伸长率均最高,分别为148.320 MPa、135.862 MPa和8.467%。均匀化处理后Mg-Al合金平均晶粒尺寸的增大导致力学性能有所下降,而Mg-0.5%Al和Mg-1.0%Al合金的伸长率较铸态有所增加。Mg-Al合金的阻尼性能与Al含量呈负相关,同时临界应变振幅随Al含量的增加而逐渐增加,铸态Mg-1.0%Al合金在应变振幅点ε_0.1的阻尼值Q^-1为0.1160,属于高阻尼镁合金范畴(Q^-1≥0.01),而均匀化处理后Mg-Al合金的阻尼值均较铸态有所增加。当频率一定时,Mg-Al合金的阻尼性能随着Al含量的增加而减小,当Al含量一定时,阻尼性能随着频率的增加而减小,均匀化处理对高温时阻尼性能的影响不明显。

关键词: Mg-Al合金, Al含量, 均匀化处理, 力学性能, 阻尼性能

Abstract: Effects of Al content (0.25%, 0.5% and 1.0%, mass fraction) and homogenization (420 ℃ for 24 h) on microstructure, mechanical properties and damping properties of as-cast Mg-Al alloys were investigated by using optical microscope, X-ray diffractometer, scanning electron microscope and tensile testing machine. The results show that the addition of Al element reduces the average grain size of the alloy, and the more the addition, the smaller the average grain size, while the average grain size significantly increases after homogenization. The mechanical properties of as-cast Mg-Al alloy gradually increase with the increase of Al content, and the tensile strength, yield strength and elongation of the Mg-1.0%Al alloy are 148.320 MPa, 135.862 MPa, and 8.467%, respectively. After the homogenization, the mechanical properties of Mg-Al alloy decrease due to the increase of average grain size, while the elongation of Mg-0.5%Al and Mg-1.0%Al alloys is increased compared to the as-cast state. The damping properties of the Mg-Al alloys decrease with the increase of Al content, and the critical strain amplitude gradually increases, the damping value Q^-1 for the as-cast Mg-1.0%Al alloy at ε_0.1 is 0.1160, which belongs to the category of highly damped magnesium alloys (Q^-1≥0.01), meanwhile, the damping values of the Mg-Al alloys after homogenization is all higher than that of as-cast state. The damping properties decreases with the increase of Al content for a specific frequency, and decreases with the increase of frequency when the Al content is constant, and the effect of homogenization on the damping properties at high temperatures is not apparent.

Key words: Mg-Al alloy, Al content, homogenization, mechanical properties, damping properties

中图分类号:

TG146.2⁺2

刘华燊, 孙有平, 何江美, 罗国健, 裴梦雨. Al含量及均匀化处理对Mg-Al二元合金组织及阻尼性能的影响[J]. 金属热处理, 2024, 49(7): 70-77.

Liu Huashen, Sun Youping, He Jiangmei, Luo Guojian, Pei Mengyu. Effect of Al content and homogenization on microstructure and damping properties of Mg-Al binary alloys[J]. Heat Treatment of Metals, 2024, 49(7): 70-77.

参考文献

[1]Nishiyama K, Matsui R, Ikeda Y, et al. Damping properties of a sintered Mg-Cu-Mn alloy[J]. Journal of Alloys and Compounds, 2003, 355(1/2): 22-25.
[2]Wu Y W, Wu K, Deng K K, et al. Damping capacities and microstructures of magnesium matrix composites reinforced by graphite particles[J]. Materials and Design, 2010, 31(10): 4862-4865.
[3]Watanabe H, Sasakura Y, Ikeo N, et al. Effect of deformation twins on damping capacity in extruded pure magnesium[J]. Journal of Alloys and Compounds, 2015, 626: 60-64.
[4]Mukai T, Yamanoi M, Watanabe H, et al. Ductility enhancement in AZ31 magnesium alloy by controlling its grain structure[J]. Scripta Materialia, 2001, 45(1): 89-94.
[5]任政, 张兴国, 房灿峰, 等. Mg-Al基镁合金晶粒细化的研究进展[J]. 材料导报, 2008, 22(1): 98-101.
Ren Zheng, Zhang Xingguo, Fang Canfeng, et al. Research and development of grain refinement of Mg-Al magnesium alloys[J]. Materials Reports, 2008, 22(1): 98-101.
[6]万迪庆, 于田. 高阻尼铸造Mg-Si合金研究现状及展望[J]. 铸造, 2012, 61(10): 1135-1137.
Wan Diqing, Yu Tian. Research status and prospect of high damping casting Mg-Si alloys[J]. Foundry, 2012, 61(10): 1135-1137.
[7]Sugimoto K, Niiya K, Okamoto T, et al. A study of damping capacity in magnesium alloys[J]. Transactions of the Japan Institute of Metals, 1977, 18(3): 277-288.
[8]Granato A V, Lucke K. Application of dislocation theory to internal friction phenomena at high frequencies[J]. Journal of Applied Physics, 1956, 27(7): 789-805.
[9]Granato A V, Lucke K. Theory of mechanical damping due to dislocations[J]. Journal of Applied Physics, 1956, 27(6): 583-593.
[10]马家轩, 韦琪, 魏福安, 等. Mg-3Al-1Zn-xSn镁合金的温度阻尼特性[J]. 特种铸造及有色合金, 2020, 40(12): 1405-1410.
Ma Jiaxuan, Wei Qi, Wei Fuan, et al. Temperature damping characteristics of Mg-3Al-1Zn-xSn magnesium alloy[J]. Special Casting and Nonferrous Alloys, 2020, 40(12): 1405-1410.
[11]周明扬, 苏鑫鑫, 任凌宝, 等. 挤压态Mg-3Al-3Zn-1Ti-0.6RE镁合金的高温拉伸变形行为[J]. 稀有金属材料与工程, 2017, 46(8): 2149-2155.
Zhou Mingyang, Su Xinxin, Ren Lingbao, et al. Tensile deformation behavior of as-extruded Mg-3Al-3Zn-1Ti-0.6RE magnesium alloy at elevated temperature[J]. Rare Metal Materials and Engineering, 2017, 46(8): 2149-2155.
[12]Liu X, Liu Z, Liu G, et al. First-principles study of solid solution strengthening in Mg-X(X=Al, Er) alloys[J]. Bulletin of Materials Science, 2019, 42(1): 16.
[13]Somekawa H, Tsuru T. Effect of alloying elements on grain boundary sliding in magnesium binary alloys: Experimental and numerical studies[J]. Materials Science and Engineering A, 2017, 708: 267-273.
[14]Somekawa H, Inoue T, Tsuzaki K. Effect of solute atoms on fracture toughness in dilute magnesium alloys[J]. Philosophical Magazine, 2013, 93(36): 4582-4592.
[15]Somekawa H, Schuh C A. Effect of solid solution elements on nanoindentation hardness, rate dependence, and incipient plasticity in fine grained magnesium alloys[J]. Acta Materialia, 2011, 59(20): 7554-7563.
[16]Hu Y, Zhang C, Meng W, et al. Microstructure, mechanical and corrosion properties of Mg-4Al-2Sn-xY-0.4Mn alloys[J]. Journal of Alloys and Compounds, 2017, 727: 491-500.
[17]Tahreen N, Zhang D F, Pan F S, et al. Strengthening mechanisms in magnesium alloys containing ternary Ⅰ, W and LPSO phases[J]. Journal of Materials Science and Technology, 2018, 34(7): 1110-1118.
[18]胡小石. 热处理和变形对镁合金低频阻尼性能的影响及机理研究[D]. 哈尔滨: 哈尔滨工业大学, 2007.
Hu Xiaoshi. Effect of heat treatment and deformation on low-frequency damping properties of magnesium alloys and mechanism research[D]. Harbin: Harbin Institute of Technology, 2007.
[19]刘华燊, 孙有平, 何江美, 等. 轧制压下量对ZK60镁合金组织和阻尼性能的影响[J]. 矿冶工程, 2023, 43(2): 154-159.
Liu Huashen, Sun Youping, He Jiangmei, et al. Effect of rolling reduction on microstructure and damping properties of ZK60 magnesium alloy[J]. Mining and Metallurgical Engineering, 2023, 43(2): 154-159.
[20]焦琰珂, 熊毅, 姚怀. Al含量对Mg-2.0Zn-0.4Mn合金组织、力学性能及耐腐蚀性能的影响[J]. 材料热处理学报, 2022, 43(10): 10-18.
Jiao Yanke, Xiong Yi, Yao Huai. Effect of Al content on microstructure, mechanical properties and corrosion resistance of Mg-2.0Zn-0.4Mn alloy[J]. Transactions of Materials and Heat Treatment, 2022, 43(10): 10-18.
[21]Pan H, Pan F, Wang X, et al. Correlation on the electrical and thermal conductivity for binary Mg-Al and Mg-Zn alloys[J]. International Journal of Thermophysics, 2013, 34(7): 1336-1346.
[22]秦晨, 赵莉萍, 陈利超, 等. Al含量对含稀土AZ系镁合金组织及性能的影响[J]. 金属热处理, 2020, 45(3): 68-72.
Qin Chen, Zhao Liping, Chen Lichao, et al. Effect of Al content on microstructure and properties of AZ series magnesium alloy containing rare earth[J]. Heat Treatment of Metals, 2020, 45(3): 68-72.
[23]肖雪, 刘怀海, 耿家源, 等. 挤压态Mg-9Li-xAl-0.6Y合金组织与力学性能研究[J]. 有色金属工程, 2021, 11(4): 1-7.
Xiao Xue, Liu Huaihai, Geng Jiayuan, et al. Microstructure and mechanical properties of as-extruded Mg-9Li-xAl-0.6Y alloys[J]. Nonferrous Metals Engineering, 2021, 11(4): 1-7.
[24]Butt M Z, Feltham P. Solid-solution hardening[J]. Acta Metallurgica, 1978, 28(10): 2557-2576.
[25]Zhu S Q, Yan H G, Chen J H, et al. Fabrication of Mg-Al-Zn-Mn alloy sheets with homogeneous fine-grained structures using high strain-rate rolling in a wide temperature range[J]. Materials Science and Engineering A, 2013, 559: 765-772.
[26]陈连生, 郑亚琪, 张源, 等. 医用可降解镁合金腐蚀疲劳行为研究进展[J]. 稀有金属材料与工程, 2021, 50(9): 3375-3387.
Chen Liansheng, Zheng Yaqi, Zhang Yuan, et al. Research progress on corrosion fatigue behavior of biomedical degradable magnesium-based alloys[J]. Rare Metal Materials and Engineering, 2021, 50(9): 3375-3387.
[27]Rivière A. Measurement of high damping: Techniques and analysis[J]. Journal of Alloys and Compounds, 2003, 355(1/2): 201-206.
[28]Jun J H. Damping behaviors of as-cast and solution-treated AZ91-Ca magnesium alloys[J]. Journal of Alloys and Compounds, 2014, 610: 169-172.
[29]王金, 雷波, 李育川, 等. 热处理对Cu-Al-Mn形状记忆合金阻尼能力的影响[J]. 延安大学学报(自然科学版), 2022, 41(3): 97-101.
Wang Jin, Lei Bo, Li Yuchuan, et al. Effect of thermal treatment on the damping capacity of Cu-Al-Mn shape memory alloy[J]. Journal of Yan'an University(Natural Science Edition), 2022, 41(3): 97-101.
[30]Wu Y W, Wu K, Nie K B, et al. Damping capacities and tensile properties in Grp/AZ91 and SiCp/Grp/AZ91 magnesium matrix composites[J]. Materials Science and Engineering A, 2010, 527(29/30): 7873-7877.
[31]Belamri C, Belhas S, Riviere A. Damping of a high-purity aluminum single crystal at high temperatures[J]. Materials Science and Engineering A, 2006, 442(1/2): 142-146.
[32]Sugimoto K, Niiya K, Okamoto T, et al. A Study of damping capacity in magnesium alloys[J]. Transactions of the Japan Institute of Metals, 1977, 18(3): 277-288.

Al含量及均匀化处理对Mg-Al二元合金组织及阻尼性能的影响

Effect of Al content and homogenization on microstructure and damping properties of Mg-Al binary alloys

PDF

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

本文评价

[1]	马蓼奕, 杜青胤, 李世键, 杨立新, 刘刚, 王新宇. 利用JMatPro软件模拟计算16CrSiNi钢热处理参数及热物理性能[J]. 金属热处理, 2024, 49(7): 42-46.
[2]	颜文超, 高波, 肖礼容, 周浩. 温轧和临界退火制备超细晶异构双相钢的微观结构及力学性能[J]. 金属热处理, 2024, 49(7): 54-62.
[3]	冀宣名. 冷轧Ti-3.5Al-5Mo-4V合金板材再结晶晶粒长大行为及其对时效行为的影响[J]. 金属热处理, 2024, 49(7): 63-69.
[4]	李忠波, 吴志方, 吴润. 低合金马氏体耐磨钢的研究进展[J]. 金属热处理, 2024, 49(7): 132-138.
[5]	蒋军杰, 王永彪, 肖志玲, 樊江磊, 张正文. 退火温度对激光选区熔化成形TA15钛合金微观组织与力学性能的影响[J]. 金属热处理, 2024, 49(7): 241-248.
[6]	卢明霞, 张磊, 王新社. 正火温度对胀断连杆用36MnVS4和46MnVS5钢组织及性能的影响[J]. 金属热处理, 2024, 49(7): 249-253.
[7]	蒙品品, 张晓波. 退火处理对纯铜微观组织及力学性能的影响[J]. 金属热处理, 2024, 49(7): 267-273.
[8]	徐双钱, 戴志勇, 王子瑜. 热处理工艺对Al-6.5Zn-2.3Mg-2.5Cu-0.1Zr-0.2Sc合金组织和力学性能的影响[J]. 金属热处理, 2024, 49(7): 274-280.
[9]	陈捷, 高天宇, 王爽, 王勇, 王亮亮. 基于正交分析法探究600 MPa级水电钢的热处理制度[J]. 金属热处理, 2024, 49(7): 307-312.
[10]	赵希庆, 王付杰, 张丙军. 回火对直接淬火A387Gr11CL2钢板组织和性能的影响[J]. 金属热处理, 2024, 49(7): 322-325.
[11]	张新宇, 隋欣, 罗旭东, 程素玲, 张义, 陈金生, 张伟. 汽车用6014铝合金冷轧板的热处理工艺[J]. 金属热处理, 2024, 49(7): 331-335.
[12]	吴斯, 李非凡, 王学敏, 尚学良, 徐翔宇. 退火温度对转向架用低密度钢组织性能的影响[J]. 金属热处理, 2024, 49(6): 8-16.
[13]	刘怡然, 李磊. 退火工艺对SLM AlSi10Mg合金拉伸变形行为的影响[J]. 金属热处理, 2024, 49(6): 23-28.
[14]	安庆生, 万德成, 马少康, 李杰, 张千禧. 逆相变退火对中锰钢组织演变和力学性能的影响[J]. 金属热处理, 2024, 49(6): 36-42.
[15]	张淼, 万德成, 张波, 冯运莉. Fe-0.13C-2.0Mn-0.6Al复相钢在不同退火温度下的组织与性能[J]. 金属热处理, 2024, 49(6): 43-48.