超导磁体热处理对N50H不锈钢铠甲力学性能的影响

doi:10.13251/j.issn.0254-6051.2024.09.026

金属热处理 ›› 2024, Vol. 49 ›› Issue (9): 165-168.DOI: 10.13251/j.issn.0254-6051.2024.09.026

超导磁体热处理对N50H不锈钢铠甲力学性能的影响

涂正平¹, 吴逸飞^2,3, 于安华¹, 陈晓伟¹, 王维俊²

1.浙江久立特材科技股份有限公司, 浙江湖州 313008;
2.中国科学院合肥物质科学研究院, 安徽合肥 230031;
3.中国科学技术大学研究生院科学岛分院, 安徽合肥 230026

收稿日期:2024-04-18 修回日期:2024-07-29 出版日期:2024-09-25 发布日期:2024-10-29
通讯作者: 吴逸飞,博士研究生,E-mail: yifei.wu@ipp.ac.cn
作者简介:涂正平(1983—),男,高级工程师,主要研究方向为不锈钢及镍基合金无缝管的开发及生产,E-mail: tzp@jiuli.com。
基金资助:
国家自然科学基金青年基金(12305196);中国博士后科学基金第74批面上基金(2023M743538)

Effect of superconducting magnet heat treatment on mechanical properties of N50H stainless steel jacket

Tu Zhengping¹, Wu Yifei^2,3, Yu Anhua¹, Chen Xiaowei¹, Wang Weijun²

1. The Zhejiang Jiuli Hi-Tech Metals Company Ltd., Huzhou Zhejiang 313008, China;
2. Hefei Institutes of Physical Science, Chinese Academy of Sciences, Hefei Anhui 230031, China;
3. Science Island Branch, Graduate School of USTC, Hefei Anhui 230026, China

Received:2024-04-18 Revised:2024-07-29 Online:2024-09-25 Published:2024-10-29

摘要/Abstract

摘要： 目前,低温超导体(LTS)中应用最成熟的是铌三锡(Nb₃Sn)超导体,高温超导体(HTS)中钇钡铜氧(YBCO)超导体因其优异的性能,且不需要热处理成为中国聚变工程试验堆(CFETR)中超导线圈的候选材料。而316L、316LN、JK2LB等铠甲材料低温下的力学性能不满足未来超导磁体的使用要求。因此,以N50H奥氏体不锈钢为研究对象,对冷加工样品热处理后的力学性能进行测试,探究热处理工艺对N50H不锈钢力学性能的影响。结果表明,在4.2 K下,热处理前的N50H不锈钢试样抗拉强度为1800 MPa左右,屈服强度在1500 MPa以上。经两种Nb₃Sn热处理制度后N50H不锈钢试样的抗拉强度均远大于1800 MPa,屈服强度较未热处理略有提高。同时,断后伸长率在两种热处理制度后均高于25%,对比未热处理时的变化幅度最大为5%左右。验证了N50H不锈钢未来作为YBCO和Nb₃Sn CICC铠甲材料应用的可行性。

关键词: 热处理, N50H不锈钢, CICC导体铠甲, 力学性能

Abstract: At present, the most mature low-temperature superconductor (LTS) is the Nb₃Sn superconductor, and YBCO in high-temperature superconductor (HTS) has become a candidate material for superconducting coils in China Fusion Engineering Test Reactor (CFETR) because of its excellent properties and no need for heat treatment. However, the mechanical properties of 316L, 316LN, JK2LB and other jacket materials do not meet the requirements of future superconducting magnets at low temperatures. Therefore, taking N50H austenitic stainless steel as the research object, the mechanical properties of the cold-worked specimens after heat treatment were tested to explore the effect of heat treatment on the mechanical properties of the N50H stainless steel. The results show that before heat treatment, the tensile strength of the N50H stainless steel is about 1800 MPa and the yield strength is above 1500 MPa at 4.2 K. After the two Nb₃Sn heat treatments, the tensile strength of the N50H stainless steel increases to more than 1800 MPa, and the yield strength is slightly higher than that without heat treatment. At the same time, the elongation is higher than 25% after both heat treatments and the maximum change is 5% compared with that without heat treatment. These further verifie the feasibility of the N50H stainless steel as YBCO and Nb₃Sn CICC jacket material in the future.

Key words: heat treatment, N50H steel, CICC jacket, mechanical properties

中图分类号:

TG156

涂正平, 吴逸飞, 于安华, 陈晓伟, 王维俊. 超导磁体热处理对N50H不锈钢铠甲力学性能的影响[J]. 金属热处理, 2024, 49(9): 165-168.

Tu Zhengping, Wu Yifei, Yu Anhua, Chen Xiaowei, Wang Weijun. Effect of superconducting magnet heat treatment on mechanical properties of N50H stainless steel jacket[J]. Heat Treatment of Metals, 2024, 49(9): 165-168.

参考文献

[1]Song Y T, Li J G, Wan Y X, et al. Engineering design of the CFETR machine[J]. Fusion Engineering Design, 2022, 183: 113247.
[2]高翔, 万宝年, 宋云涛, 等. CFETR物理与工程研究进展[J]. 中国科学: 物理学力学天文学, 2019, 49(4): 3-10.
Gao Xiang, Wan Baonian, Song Yuntao, et al. Progress on CFETR physics and engineering[J]. Scientia Sinica Physica, Mechanica & Astronomica, 2019(4): 3-10.
[3]Wang W J, Zhao C Y, Jin J, et al. The research on high-strength CICC jackets with YS>1500 MPa at 4.2 K for future fusion applications[J]. Nuclear Materials and Energy, 2023, 36: 101474.
[4]Qin J G, Dai C, Liao G J, et al. Tensile test of SS 316LN jacket with different conditions[J]. Cryogenics, 2014, 64: 16-20.
[5]Jin H, Wu Y, Qin J G, et al. Microstructure and mechanical properties of high manganese steel processed by cold working and aging at 4.2 K[J]. IEEE Transactions on Applied Superconductivity, 2018, 28(3): 2800709.
[6]Kass J N, Bell W L, Wang M T, et al. Influence of recrystallization behavior on the mechanical properties of XM-19 stainless steel (22Cr-13Ni-5Mn-2Mo-0.3N)[J]. Metallurgical Transactions A, 1979, 10: 715-725.
[7]Mcrae D M, Walsh R P, Dalder E N C, et al. Fatigue and fracture properties of a super-austenitic stainless steel at 295 K and 4 K[J]. Advances in Cryogenic Engineering, 2014, 60(1): 59-66.
[8]Hartwig Z S, Vieira R F, Dunn D, et al. The SPARC Toroidal field model coil program[J]. IEEE Transactions on Applied Superconductivity, 2024, 34(2): 1-16.
[9]Zhai R Z, Zhang H L, Liu S, et al. Influence of carbon content on the microstructure and cryogenic tensile properties of N50 austenitic stainless steel after aging treatment[J]. Journal of Nuclear Materials: Materials Aspects of Fission and Fusion, 2022, 571: 154023.
[10]Wang W J, Zhao C Y, Jin J, et al. Mechanical properties evaluation of ReBCO CICC jacket based on super-austenitic stainless steel for CFETR high-field magnet[J]. Nuclear Materials and Energy, 2023, 34: 101344.
[11]ASTM E1450-16, Standard Test Method for Tension Testing of Structural Alloys in Liquid Helium[S].

[1]	周浩, 王帅, 曾燕屏, 马志宝, 周德, 郭德瑞, 董树青. 长时在役Inconel 783高温合金螺栓的显微组织和力学性能[J]. 金属热处理, 2024, 49(9): 36-42.
[2]	陈子健, 林业佳, 李传强, 邓仁昡, 董勇, 章争荣. 微合金化调控7075铝合金的微观组织与力学性能[J]. 金属热处理, 2024, 49(9): 58-63.
[3]	任广笑, 王超, 曹喜娟, 王凯, 王红霞, 程伟丽, 牛晓峰. 时效处理对Mg-Y-Gd-Zn-Zr合金中LPSO相演变及性能的影响[J]. 金属热处理, 2024, 49(9): 96-102.
[4]	任鹏帅, 秦凤, 周骞, 赵雷杰, 崔护, 彭子奥, 武常生. 等温淬火对含铝无碳化物贝氏体钢组织和性能的影响[J]. 金属热处理, 2024, 49(9): 103-109.
[5]	张宇, 李圣阳, 魏晓蓼, 柴志松, 李泳. 铬合金化Q&P钢的热处理工艺优化与碳配分行为[J]. 金属热处理, 2024, 49(9): 110-116.
[6]	张青科, 诸汇涛, 陈根保, 陈立田, 夏亚金, 胡方勤, 宋振纶. 形变热处理对新型无Ti马氏体时效钢焊缝组织与力学性能的影响[J]. 金属热处理, 2024, 49(9): 117-124.
[7]	魏文逸. 热处理对激光沉积制造Ti-5321近β钛合金组织和性能的影响[J]. 金属热处理, 2024, 49(9): 132-138.
[8]	夏琳燕, 史湘琴, 刘逸卿, 周模豪, 邓蔚. 时效对铸造Al-Si-Cu-Mg合金力学性能和耐蚀性能的影响[J]. 金属热处理, 2024, 49(9): 152-157.
[9]	万志健, 安涛, 于文坛, 刘学华, 童乐, 赵海. 热处理工艺对42CrMo-R钢轮箍组织及力学性能的影响[J]. 金属热处理, 2024, 49(9): 158-164.
[10]	赖春明, 李琴, 周家林, 吴兴欢, 黄艳. 焊后热处理对热丝TIG焊接10Cr9Mo1VNb锅炉用钢组织性能的影响[J]. 金属热处理, 2024, 49(9): 169-175.
[11]	刘强, 盛智勇, 张超, 李杰, 陈泽, 陈送义, 陈康华. 预变形对7085超强铝合金环件组织与性能的影响[J]. 金属热处理, 2024, 49(9): 176-184.
[12]	徐锋, 孙强, 贾云浩. 时效处理对15-5PH不锈钢室温和低温力学性能的影响[J]. 金属热处理, 2024, 49(9): 191-197.
[13]	马蓼奕, 董志, 杨立新, 李世键, 崔晶, 康冲. 淬火转移时间对16CrSiNi钢回火组织和性能的影响[J]. 金属热处理, 2024, 49(9): 198-203.
[14]	杨含, 兰超锋, 王雄, 万静斌. 43 kg/m爬坡式尖轨的离线热处理[J]. 金属热处理, 2024, 49(9): 204-208.
[15]	杨哲, 陈水胜. 时效工艺对ADC12铝合金析出相与力学性能的影响[J]. 金属热处理, 2024, 49(9): 216-220.

超导磁体热处理对N50H不锈钢铠甲力学性能的影响

Effect of superconducting magnet heat treatment on mechanical properties of N50H stainless steel jacket

PDF

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

本文评价