超声表面滚压工艺对304不锈钢耐腐蚀性的影响

doi:10.13251/j.issn.0254-6051.2024.09.045

金属热处理 ›› 2024, Vol. 49 ›› Issue (9): 268-274.DOI: 10.13251/j.issn.0254-6051.2024.09.045

超声表面滚压工艺对304不锈钢耐腐蚀性的影响

陈新健¹, 隋荣娟¹, 王燕飞², 程延海³, 高林皓¹

1.山东交通学院工程机械学院, 山东济南 250357;
2.济南锅炉集团有限公司, 山东济南 250023;
3.中国矿业大学机电工程学院, 江苏徐州 221116

收稿日期:2024-04-22 修回日期:2024-07-30 出版日期:2024-09-25 发布日期:2024-10-29
通讯作者: 隋荣娟,副教授,博士,E-mail:suirongjuan@sdjtu.edu.cn
作者简介:陈新健(1999—),男,硕士研究生,主要研究方向为材料表面改性,E-mail:2294716293@qq.com。
基金资助:
国家重点研发计划(2023YFE0201600)

Effect of ultrasonic surface rolling process on corrosion resistance of 304 stainless steel

Chen Xinjian¹, Sui Rongjuan¹, Wang Yanfei², Cheng Yanhai³, Gao Linhao¹

1. School of Engineering Machinery, Shandong Jiaotong University, Jinan Shandong 250357, China;
2. Jinan Boiler Group Co., Ltd., Jinan Shandong 250023, China;
3. School of Mechanical and Electrical Engineering, China University of Mining and Technology, Xuzhou Jiangsu 221116, China

Received:2024-04-22 Revised:2024-07-30 Online:2024-09-25 Published:2024-10-29

摘要/Abstract

摘要： 采用超声表面滚压工艺(USRP)对304不锈钢进行表面处理,研究了其对304不锈钢耐蚀性的影响。利用扫描电镜、X射线衍射仪和金属表面粗糙度仪对表面形貌、微观结构、残余应力和粗糙度进行分析。采用电化学测试、邻菲啰啉显色试验评估了氧化膜的耐腐蚀性和完整性。结果表明,经USRP处理后,304不锈钢表面粗糙度R_a由0.60 μm降低到0.28 μm,表面晶粒尺寸从23.13 μm降低到20.80 nm,表面残余应力由20 MPa转变为-329 MPa。与未处理试样比较,超声表面滚压试样的自腐蚀电流密度I_corr最小为0.94×10^-5 A/cm²,降低了71％;氧化膜层电阻R_p达到2.59×10⁶ Ω·cm²,提升了2倍;邻菲啰啉显色值范围变窄,显色面积减小,表明表面缺陷减少,表面氧化膜的质量得到提高。分析认为,超声表面滚压处理促使304不锈钢近表面层晶粒细化、产生残余压应力,使表面缺陷减少、氧化膜更加致密,进而阻滞304不锈钢的电化学反应进程,提高了材料的耐腐蚀性。

关键词: 超声表面滚压工艺, 304不锈钢, 表面残余应力, 耐腐蚀性

Abstract: Effect of ultrasonic surface rolling process (USRP) on the corrosion resistance of 304 stainless steel surface was investigated. The surface morphology, microstructure, residual stress and surface roughness were analyzed by means of scanning electron microscopy, X-ray diffraction analysis, and metal surface roughness meter, respectively. The corrosion resistance and integrity of the oxide film was assessed using electrochemical tests and o-phenanthroline color development experiments. The results indicate that the value of R_a for the 304 stainless steel is reduced from 0.60 μm to 0.28 μm after USRP treatment. The surface grain size is reduced from 23.13 μm to 20.80 nm, and the surface residual stress is changed from 20 MPa to -329 MPa. Compared with the untreated specimen, the minimum corrosion current density I_corr of the USRP treated specimen is 0.94×10^-5 A/cm², which is reduced by 71%. The oxide film resistance R_p is 2.59×10⁶ Ω·cm², increased by 2 times. The range of color rendering value of phenanthroline is narrowed and the color rendering area is decreased, indicating that the surface defects are reduced and the quality of the surface oxide film is improved. For the 304 stainless steel, USRP treatment promotes the grain refinement near the surface layer, produces residual compressive stress, reduces surface defects, denseres oxide film, and then blocks the electrochemical reaction process, and improves the corrosion resistance.

Key words: ultrasonic surface rolling process, 304 stainless steel, surface residual stress, corrosion resistance

中图分类号:

TG174.4

陈新健, 隋荣娟, 王燕飞, 程延海, 高林皓. 超声表面滚压工艺对304不锈钢耐腐蚀性的影响[J]. 金属热处理, 2024, 49(9): 268-274.

Chen Xinjian, Sui Rongjuan, Wang Yanfei, Cheng Yanhai, Gao Linhao. Effect of ultrasonic surface rolling process on corrosion resistance of 304 stainless steel[J]. Heat Treatment of Metals, 2024, 49(9): 268-274.

参考文献

[1]张东玖, 程从前, 杨华, 等. 氧化膜完整性对不锈钢海洋大气腐蚀的影响及其质检方法[J]. 腐蚀与防护, 2023, 44(5): 46-50, 56.
Zhang Dongjiu, Cheng Congqian, Yang Hua, et al. Effect of passivation film integrity on marine atmospheric corrosion of stainless steel and its quality inspection methods[J]. Corrosion and Protection, 2023, 44(5): 46-50, 56.
[2]隋松言, 田宇, 曲帅, 等. 304L奥氏体不锈钢中厚板的晶粒度控制[J]. 金属热处理, 2023, 48(12): 184-188.
Sui Songyan, Tian Yu, Qu Shuai, et al. Grain size control of medium-thickness 304L stainless steel plates[J]. Heat Treatment of Metals, 2023, 48(12): 184-188.
[3]Sun Z Y, Ren S, Hu T M, et al. Effect of ultrasonic surface rolling process on the hot compression behavior of Inconel 718 superalloy at 700 ℃[J]. Nanomaterials, 2019, 9(4): 9040658.
[4]Li C Y, Zhu R T, Zhang X X, et al. Impact of surface ultrasonic rolling on cavitation erosion behavior of 304 stainless steel[J]. Surface and Coatings Technology, 2020, 383: 125280.
[5]Xia T T, Zeng L F, Zhang X H, et al. Enhanced corrosion resistance of a Cu-10Ni alloy in a 3.5wt%NaCl solution by means of ultrasonic surface rolling treatment[J]. Surface and Coatings Technology, 2019, 363: 390-399.
[6]叶仁虎, 李刚. 超声滚压对热处理Ti-6Al-4V表面摩擦性能的影响[J/OL]. 热加工工艺, 2024(3): 1-6.
Ye Renhu, Li Gang. Effect of ultrasonic rolling on surface friction properties of heat-treated Ti-6Al-4V[J/OL]. Hot Working Technology, 2024(3): 1-6.
[7]王世杰, 邓建新, 孟莹, 等. 超声滚压加工表面微织构的研究[J]. 制造技术与机床, 2022(2): 73-79.
Wang Shijie, Deng Jianxin, Meng Ying, et al. Study on surface micro texture processing by ultrasonic rolling[J]. Manufacturing Technology and Machine Tool, 2022(2): 73-79.
[8]焦传继. 表面滚压强化304不锈钢组织与性能的研究[D]. 沈阳: 沈阳工业大学, 2023.
[9]Liu C, Liu D, Zhang X, et al. On the influence of ultrasonic surface rolling process on surface integrity and fatigue performance of Ti-6Al-4V alloy[J]. Surface and Coatings Technology, 2019, 370: 24-34.
[10]Meng Y, Deng J, Lu Y, et al. Fabrication of AlTiN coatings deposited on the ultrasonic rolling textured substrates for improving coatings adhesion strength[J]. Applied Surface Science, 2021, 550: 149394.
[11]王世杰. 表面微织构的超声滚压制备技术研究[D]. 济南: 山东大学, 2023.
[12]马晓晖, 毛晶, 龙丽霞, 等. XRD测试材料表面微区残余应力[J]. 实验室科学, 2022, 25(2): 10-13, 18.
Ma Xiaohui, Mao Jing, Long Lixia, et al. Measurement of residual stress in the micro-zone of the specimen by X ray diffractometer[J]. Laboratory Science, 2022, 25(2): 10-13, 18.
[13]Salahi S, Kazemipour M, Nasiri A. Effects of microstructural evolution on the corrosion properties of AISI 420 martensitic stainless steel during cold rolling process[J]. Materials Chemistry and Physics, 2021, 258: 123916.
[14]金一豪, 胡勇, 游小凡, 等. 再结晶对FeCoCrNiMn高熵合金组织及耐蚀性的影响[J/OL]. 热加工工艺, 2024(1): 1-4.
Jin Yihao, Hu Yong, You Xiaofan, et al. Effect of recrystallization on microstructures and corrosion resistance of FeCoCrNiMn high entropy alloy[J/OL]. Hot Working Technology, 2024(1): 1-4.
[15]Anwar S, Khan F, Zhang Y, et al. Optimization of zinc‐nickel film electrodeposition for better corrosion resistant characteristics[J]. The Canadian Journal of Chemical Engineering, 2019, 97(9): 2426-2439.
[16]Qin P, Chen L Y, Liu Y J, et al. Corrosion and passivation behavior of laser powder bed fusion produced Ti-6Al-4V in static/dynamic NaCl solutions with different concentrations[J]. Corrosion Science, 2021, 191: 109728.
[17]Takakuwa O, Soyama H. Effect of residual stress on the corrosion behavior of austenitic stainless steel[J]. Advances in Chemical Engineering and Science, 2015, 5(1): 62-71.
[18]Liu X, Frankel G S. Effects of compressive stress on localized corrosion in AA2024-T3[J]. Corrosion Science, 2006, 48(10): 3309-3329.

超声表面滚压工艺对304不锈钢耐腐蚀性的影响

Effect of ultrasonic surface rolling process on corrosion resistance of 304 stainless steel

PDF

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

本文评价

[1]	夏琳燕, 史湘琴, 刘逸卿, 周模豪, 邓蔚. 时效对铸造Al-Si-Cu-Mg合金力学性能和耐蚀性能的影响[J]. 金属热处理, 2024, 49(9): 152-157.
[2]	张泽疆, 李新梅, 朱春金, 李航, 杨定力. B₄C添加量对42CrMo钢表面Stellite6+B₄C激光熔覆层形貌与性能的影响[J]. 金属热处理, 2024, 49(7): 200-207.
[3]	董泰励, 李昉, 陈庚, 张晨, 郭子龙, 陈康华, 陈送义. 自然时效耦合预拉伸提升Al-Zn-Mg-Cu合金力学性能和腐蚀抗力[J]. 金属热处理, 2024, 49(4): 104-110.
[4]	李云峰, 王嘉圣, 石岩, 姜广君, 唐术锋, 何晓东. 载气流量对激光熔覆添加Y₂O₃的镍基涂层组织和耐腐蚀性的影响[J]. 金属热处理, 2024, 49(2): 281-290.
[5]	王军亮, 周铁柱, 付利国, 郁炎, 李春辉. 去应力退火对B10铜镍合金厚壁三通表面残余应力及组织性能的影响[J]. 金属热处理, 2023, 48(7): 111-116.
[6]	侯世香, 刘燕, 刘东雨. 镍基合金Inconel 740H和617B的组织稳定性和耐蚀性对比[J]. 金属热处理, 2023, 48(5): 18-24.
[7]	刘阳, 吴晓蓝, 饶茂, 毛雪晶, 高坤元, 魏午, 熊湘沅, 黄晖. Er、Zr微合金化对Al-Zn-Mg合金组织及性能的影响[J]. 金属热处理, 2023, 48(4): 18-22.
[8]	孙威威, 剌玲敏, 张静, 梁凤啸, 秦林. TA2钛板掺杂钒离子渗碳层的耐腐蚀性能[J]. 金属热处理, 2023, 48(3): 230-235.
[9]	杨胶溪, 黄凯, 武飞宇, 孙宏波, 阳代军, 李曙光, 葛学元, 王淼辉. Mg-Gd-Y-Zr镁合金高速激光熔覆Al-Si涂层的组织与性能[J]. 金属热处理, 2023, 48(1): 217-223.
[10]	夏朋昭, 许莹, 蔡艳青, 赵思坛, 娄冰洁. 微波烧结工艺对Ti-Mg复合材料组织和性能的影响[J]. 金属热处理, 2022, 47(9): 18-26.
[11]	牛毅, 贺占胥, 王明利, 张杰, 牛文朋, 刘贯军. 离子渗氮对304不锈钢组织和性能的影响[J]. 金属热处理, 2022, 47(8): 287-291.
[12]	赵堃, 蒋鹏, 王虎虎, 王博, 王沛锦, 杨兴中. (FeCoNiCr)_100-xMn_x高熵合金在NaCl和NaOH溶液中的抗腐蚀性能[J]. 金属热处理, 2022, 47(5): 40-46.
[13]	李鹏, 孔令华, 练国富, 黄旭, 李铸. 体能量密度对SLM成形316L不锈钢耐腐蚀性的影响[J]. 金属热处理, 2022, 47(5): 148-154.
[14]	陈今良, 冯中学, 张利民, 易健宏. 冷轧变形对CrCoNi合金组织与性能的影响[J]. 金属热处理, 2022, 47(5): 204-207.
[15]	李梦, 武美萍, 陆佩佩, 赵子硕, 缪小进. 选区激光熔化MnSi₂增强316L不锈钢复合材料的表面质量及耐蚀性能[J]. 金属热处理, 2022, 47(4): 165-170.