冷却温度对热轧双相钢组织和力学性能的影响

doi:10.13251/j.issn.0254-6051.2025.01.033

金属热处理 ›› 2025, Vol. 50 ›› Issue (1): 213-218.DOI: 10.13251/j.issn.0254-6051.2025.01.033

冷却温度对热轧双相钢组织和力学性能的影响

王成¹, 刘亚军², 陈志辉², 童善康², 甘晓龙^2,3

1.武汉钢铁有限公司热轧厂, 湖北武汉 430080;
2.武汉科技大学省部共建耐火材料与冶金国家重点实验室, 湖北武汉 430081;
3.武汉科技大学钢铁冶金及资源利用省部共建教育部重实验室, 湖北武汉 430081

收稿日期:2024-07-29 修回日期:2024-11-08 出版日期:2025-01-25 发布日期:2025-03-12
通讯作者: 甘晓龙,教授,博士,E-mail:ganxiaolong@wust.edu.cn
作者简介:王成(1983—),男,高级工程师,硕士,主要研究方向为高强钢开发,E-mail:wangcheng1103@163.com。
基金资助:
湖北省教育厅指导性项目(B2022010)

Effect of cooling temperature on microstructure and mechanical properties of a hot-rolled dual-phase steel

Wang Cheng¹, Liu Yajun², Chen Zhihui², Tong Shankang², Gan Xiaolong^2,3

1. Hot Rolling Plant, Wuhan Iron and Steel Co., Ltd., Wuhan Hubei 430080, China;
2. State Key Laboratory of Refractories and Metallurgy, Wuhan University of Science and Technology, Wuhan Hubei 430081, China;
3. Key Laboratory for Ferrous Metallurgy and Resources Utilization of Ministry of Education, Wuhan University of Science and Technology, Wuhan Hubei 430081, China

Received:2024-07-29 Revised:2024-11-08 Online:2025-01-25 Published:2025-03-12

摘要/Abstract

摘要： 基于薄板坯连铸连轧工艺条件,通过光学显微镜、万能拉伸机、显微硬度计和X射线衍射仪研究了不同冷却温度对双相钢DP600组织和性能的影响。研究发现,随着冷却温度从640 ℃升高到720 ℃,屈服强度和抗拉强度先下降后上升,断裂总延伸率降低。此外,硬度随着冷却温度增加呈先降低后增加趋势,与强度变化趋势相吻合。试验钢在720 ℃进行冷却后可以获得较高的强度和硬度。铁素体晶粒尺寸随着冷却温度的升高先升高再降低,马氏体体积分数逐渐增加。根据双相钢的强化机理计算表明不同冷却温度下试样的强度差异主要来源于细晶强化、相变强化和位错强化的不同,其中以细晶强化和位错强化为主,强度理论计算结果与试验结果的趋势相吻合。

关键词: 双相钢, 冷却温度, 组织, 力学性能, 强化机理

Abstract: Based on the process of thin slab continuous casting and rolling, the effect of various cooling temperatures after hot rolling on the microstructure and properties of a hot-rolled dual-phase steel was studied by using optical microscope, universal tensile machine, microhardness tester, and X-ray diffractometer. The results show that the yield strength and tensile strength first decrease and then increase, while the total elongation gradually decreases with the cooling temperature increases from 640 ℃ to 720 ℃. In addition, the hardness decreases first and then increases with the increase of cooling temperature, which is consistent with the trend of strength changes, indicating that higher strength and hardness can be obtained after cooling at 720 ℃. The grain size of ferrite first increases and then decreases with the increase of increasing cooling temperature, and the martensite content gradually increases. It is shown from the calculation according to the strengthening mechanism of the dual-phase steel that the difference in strength of the specimens under different cooling temperatures is mainly due to the differences in grain refinement strengthening, transformation strengthening and dislocation strengthening, among which the grain refinement strengthening and dislocation strengthening are the main mechanisms, and the theoretical strength calculation results are in agreement with the experimental results.

Key words: dual-phase steel, cooling temperature, microstructure, mechanical properties, strengthening mechanism

中图分类号:

TG142.1

王成, 刘亚军, 陈志辉, 童善康, 甘晓龙. 冷却温度对热轧双相钢组织和力学性能的影响[J]. 金属热处理, 2025, 50(1): 213-218.

Wang Cheng, Liu Yajun, Chen Zhihui, Tong Shankang, Gan Xiaolong. Effect of cooling temperature on microstructure and mechanical properties of a hot-rolled dual-phase steel[J]. Heat Treatment of Metals, 2025, 50(1): 213-218.

参考文献

[1]Liu Yajun, Gan Xiaolong, Wang Shuize, et al. Effect of coiling temperature on microstructure and properties of a Ti-Nb microalloyed high speed guardrail steel[J]. Steel Research International, 2023, 94: 2200840.
[2]Liu B, Wu R, Hu J. Effect of cooling process on mechanical properties of thin-gauge hot-rolled dual-phase steel[C]//IOP Conference Series: Materials Science and Engineering. IOP Publishing, 2019, 474(1): 012020.
[3]Li Zhuang, Wu Di, Lü Wei, et al. Effect of holding time on the microstructure and mechanical properties of dual-phase steel during intercritical annealing[J]. Journal of Wuhan University of Technolog, 2015, 30: 156-161.
[4]颜文超, 高波, 肖礼容, 等. 温轧和临界退火制备超细晶异构双相钢的微观结构及力学性能[J]. 金属热处理, 2024, 49(7): 54-62.
Yan Wenchao, Gao Bo, Xiao Lirong, et al. Microstructure and mechanical properties of ultrafine grained heterostructured dual-phase steel prepared by warm rolling and intercritical annealing[J]. Heat Treatment of Metals, 2024, 49(7): 54-62.
[5]薛峰, 耿志宇, 刘旭明, 等. 高强双相钢DP980成形极限性能及微观组织分析[J]. 金属热处理, 2024, 49(6): 164-168.
Xue Feng, Geng Zhiyu, Liu Xuming, et al. Forming limit properties and microstructure analysis of high strength dual phase steel DP980[J]. Heat Treatment of Metals, 2024, 49(6): 164-168.
[6]张家豪, 陈连生, 高天洋, 等. 过时效温度对连续退火制备DP1180钢组织性能的影响[J]. 金属热处理, 2023, 48(1): 149-154.
Zhang Jiahao, Chen Liansheng, Gao Tianyang, et al. Effect of over-aging temperature on microstructure and properties of DP1180 steel under continuous annealing process[J]. Heat Treatment of Metals, 2023, 48(1): 149-154.
[7]杨灿, 校振华, 冯启生, 等. 高强汽车双相钢的连续退火与组织性能研究[J]. 精密成形工程, 2023, 15(10): 168-176.
Yang Can, Jiao Zhenhua, Feng Qisheng, et al. Research on continuous annealing and microstructure and properties of high strength automotive dual phase steel[J]. Precision Forming Engineering, 2023, 15(10): 168-176.
[8]Wang Zhigang, Zhao Aimin, Zhao Zhengzhi, et al. Microstructures and mechanical properties of C-Mn-Cr-Nb and C-Mn-Si-Nb ultra-high strength dual-phase steels[J]. International Journal of Minerals, Metallurgy, and Materials, 2012, 19(10): 915-922.
[9]Sayed A A, Kheirandish S. Effect of the tempering temperature on the microstructure and mechanical properties of dual phase steels[J]. Materials Science and Engineering A, 2012, 532: 21-25.
[10]Jamei F, Mirzadeh H, Zamani M. Synergistic effects of holding time atintercritical annealing temperature and initial microstructure on the mechanical properties of dual phase steel[J]. Materials Science and Engineering A, 2019, 750: 125-131.
[11]徐勇, 段星宇, 曾祥成, 等. 不同应变速率下DP980双相钢微观组织特征及变形机制[J]. 钢铁研究学报, 2023, 35(5): 595-604.
Xu Yong, Duan Xingyu, Zeng Xiangcheng, et al. Microstructural characteristics and deformation mechanism of DP980 dual phase steel under different strain rates[J]. Journal of Iron and Steel Research, 2023, 35(5): 595-604.
[12]杨海根, 喻进安. 热轧双相钢的轧制工艺研究[J]. 金属世界, 2009(1): 46-50.
Yang Haigen, Yu Jin'an. Research on rolling process of hot rolled dual phase steel[J]. Metal World, 2009(1): 46-50.
[13]Liu Yajun, Gan Xiaolong, Liang Wen, et al. Microstructure evolution and mechanical response of a direct quenched and partitioned steel at different finishing rolling temperatures[J]. Materials, 2023, 16(9): 3575.
[14]Karam-abian M, Zarei-hanzaki A, Abedi H R, et al. Micro and macro-mechanical behavior of a transformation-induced plasticity steel developed by thermomechanical processing followed by quenching and partitioning[J]. Materials Science and Engineering A, 2016, 651: 233-240.
[15]Williamson G K, Hall W H. X-ray line broadening from filed aluminium and wolfram[J]. Acta Metallurgica, 1953, 1(1): 22-31.
[16]Williamson G K, Smallman R E. III. Dislocation densities in some annealed and cold-worked metals from measurements on the X-ray debye-scherrer spectrum[J]. Philosophical Magazine, 1956, 1(1): 34-46.
[17]Cai Feng, Zhou Mingxing, Tian Junyu, et al. Comparative study of the role of niobium in low-carbon ferritic and bainitic steels[J]. Materials Science and Engineering A, 2022, 851: 143579.
[18]张志强, 刘洪旭, 李鑫, 等. 冷却工艺对DP700热轧双相钢组织及性能的影响[J]. 钢铁研究学报, 2022, 34(12): 1457-1464.
Zhang Zhiqiang, Liu Hongxu, Li Xin, et al. The effect of cooling process on the microstructure and properties of DP700 hot-rolled dual phase steel[J]. Journal of Iron and Steel Research, 2022, 34(12): 1457-1464.
[19]董毅, 韩斌, 时晓光, 等. 冷却工艺对Si-Mn系热轧双相钢组织和性能的影响[J]. 钢铁, 2011, 46(10): 66-69, 74.
Dong Yi, Han Bin, Shi Xiaoguang, et al. The effect of cooling process on the microstructure and properties of Si-Mn hot-rolled dual phase steel[J]. Iron and Steel, 2011, 46(10): 66-69, 74.
[20]刘斌, 王志刚, 王孟, 等. 冷却工艺对高强度热轧双相钢组织与力学性能的影响[J]. 热加工工艺, 2017, 46(17): 174-176.
Liu Bin, Wang Zhigang, Wang Meng, et al. The effect of cooling process on the microstructure and mechanical properties of high-strength hot-rolled dual phase steel[J]. Hot Working Technology, 2017, 46(17): 174-176.
[21]轧制技术及连轧自动化国家重点试验室(东北大学). 热轧双相钢先进生产工艺研究与开发[M]. 北京: 冶金工业出版社, 2015.
State Key Laboratory of Rolling Technology and Continuous Rolling Automation (Northeastern University). Research and Development of Advanced Production Process of Hot Rolled Dual Phase Steel[M]. Beijing: Metallurgical Industry Press, 2015.
[22]Grange R A, Hribal C R, Porter L F. Hardness of tempered martensite in carbon and low-alloy steels[J]. Metallurgical Transactions A (Physical Metallurgy and Materials, Science), 1977, 8(11): 1775-1785.
[23]Pickering F B. Physical Metallurgy and the Design of Steels[M]. Applied Science Publishing, 1978.
[24]陈良, 张超, 朱帅, 等. CSP线生产薄规格超高强带钢的轧制工艺与组织性能[J]. 钢铁, 2014, 49(1): 57-61.
Chen Liang, Zhang Chao, Zhu Shuai, et al. Rolling process and microstructure properties of thin specification ultra-high strength strip produced by CSP line[J]. Iron and Steel, 2014, 49(1): 57-61.
[25]温东辉. 金相组织对双相钢强度影响的研究[J]. 上海金属, 2005, 27(6): 51-55.
Wen Donghui. Study on the influence of metallographic structure on the strength of duplex steel[J]. Shanghai Metal, 2005, 27(6): 51-55.

冷却温度对热轧双相钢组织和力学性能的影响

Effect of cooling temperature on microstructure and mechanical properties of a hot-rolled dual-phase steel

PDF

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

本文评价

[1]	沃建行, 沈寅忠. 标准热处理态11%Cr铁素体/马氏体钢辐照前后的显微组织[J]. 金属热处理, 2025, 50(1): 6-11.
[2]	李建国, 贾冬生, 赵银虎, 刘玉宝, 王旭, 赵磊城, 兰岳光. 稀土Ce对32MnMoNiCu铸钢微观组织与力学性能的影响[J]. 金属热处理, 2025, 50(1): 47-52.
[3]	刘宏武, 高帆, 冯像征, 李臻熙, 戴松嵒, 王青峰. TiAl-V-Cr合金近α相区的热变形行为[J]. 金属热处理, 2025, 50(1): 53-57.
[4]	任宇鹏, 张鹤松, 李声慈, 刘维朋, 富聿晶. 连续退火热镀锌工艺对含铌DP780双相钢组织与性能的影响[J]. 金属热处理, 2025, 50(1): 68-74.
[5]	黄威明, 周海安, 赵秋红, 许文兵, 于鑫泓, 冯以盛, 张云山, 赵而团. 热处理对51CrMnV弹簧钢力学性能和疲劳性能的影响[J]. 金属热处理, 2025, 50(1): 75-80.
[6]	高鑫, 李明东, 苏杰, 姜庆伟, 夏世洪, 张永强, 宁静. 两相区淬火温度对Cr-Mn-Si低合金钢组织及性能的影响[J]. 金属热处理, 2025, 50(1): 119-125.
[7]	郝莹, 王明伟. 时效处理对石墨烯/Al-Zn-Mg-Cu合金复合材料性能的影响[J]. 金属热处理, 2025, 50(1): 133-139.
[8]	兰昊天, 宋乙峰, 岳重祥, 杨佳伟. 不同氮含量镀锡板连续退火后的组织与性能[J]. 金属热处理, 2025, 50(1): 140-145.
[9]	马光宗, 谷田, 王淑华, 姜嘉玮, 孙璐, 王耐. 连续退火温度对冷轧含钛超低碳钢组织和性能的影响[J]. 金属热处理, 2025, 50(1): 146-149.
[10]	滕宏胤, 王银军, 吴索团. 不同材料夹送辊堆焊层退火处理后的组织及性能对比[J]. 金属热处理, 2025, 50(1): 155-161.
[11]	赵晓宇, 张铮, 杨慧君, 石晓辉, 张敏, 乔珺威. 300M钢等温淬火相变特性及力学性能[J]. 金属热处理, 2025, 50(1): 173-179.
[12]	韩强, 高智敏, 贾欣, 李涛, 孙昭琦, 代从伟. 回火对含稀土空冷贝氏体油套管用钢组织与性能的影响[J]. 金属热处理, 2025, 50(1): 180-186.
[13]	朱晓龙, 王争辉, 王文焱, 谢敬佩, 刁晓刚, 张飞扬. TiC纳米颗粒强化9Cr耐热钢的微观组织及力学性能[J]. 金属热处理, 2025, 50(1): 187-194.
[14]	刘锦润, 郎宇平, 陈海涛, 冯翰秋, 高智君, 张正富. 氮对冷轧022Cr18Ni8N亚稳奥氏体不锈钢组织及力学性能的影响[J]. 金属热处理, 2025, 50(1): 195-200.
[15]	郭婧, 温晓灿, 王强, 何歆, 吕少敏, 谢兴飞, 曲敬龙, 杜金辉. 晶粒尺寸对GH4720Li镍基合金650 ℃拉伸性能的影响[J]. 金属热处理, 2025, 50(1): 201-205.