一种无碳化物贝氏体钢的CCT与TTT曲线

doi:10.13251/j.issn.0254-6051.2025.02.011

金属热处理 ›› 2025, Vol. 50 ›› Issue (2): 74-80.DOI: 10.13251/j.issn.0254-6051.2025.02.011

一种无碳化物贝氏体钢的CCT与TTT曲线

杨斯媛¹, 李爱国², 罗平¹, 张文良¹, 李贤君¹, 张明皓^1,3, 安伟骋¹, 王恺择¹

1.中国机械总院集团北京机电研究所有限公司, 北京 100083;
2.中国机械科学研究总院集团有限公司, 北京 100089;
3.北京科技大学机械工程学院, 北京 100083

收稿日期:2024-06-13 修回日期:2024-12-11 发布日期:2025-04-10
通讯作者: 李爱国,正高级工程师,E-mail:liag@jds.ac.cn
作者简介:杨斯媛(1999—),女,硕士研究生,主要研究方向为先进热处理工艺,E-mail:m17822012378@163.com。

CCT and TTT curves of a carbide-free bainitic steel

Yang Siyuan¹, Li Aiguo², Luo Ping¹, Zhang Wenliang¹, Li Xianjun¹, Zhang Minghao^1,3, An Weicheng¹, Wang Kaize¹

1. China Academy of Machinery Beijing Research Institute of Mechanical & Electrical Technology Co., Ltd., Beijing 100083, China;
2. China Academy of Machinery Science and Technology Group Co., Ltd., Beijing 100089, China;
3. School of Mechanical Engineering, University of Science and Technology Beijing, Beijing 100083, China

Received:2024-06-13 Revised:2024-12-11 Published:2025-04-10

摘要/Abstract

摘要： 利用DIL-805A相变仪对无碳化物贝氏体钢开展过冷奥氏体连续冷却转变和等温转变试验,获得了试验钢的CCT曲线和TTT曲线。结果表明,试验钢的奥氏体开始转变温度和终止转变温度分别760 ℃和860 ℃,马氏体开始转变温度约为300 ℃。当冷却速度在0.1~15 ℃/s之间,过冷奥氏体主要转变为贝氏体+马氏体复相组织;冷却速度在15~50 ℃/s之间,过冷奥氏体全部转变为马氏体组织;随着冷却速度增加,试验钢硬度增加,最高可达740 HV0.5。当试验钢进行等温转变时,其贝氏体转变温度范围为300～400 ℃,“鼻尖”温度约为360 ℃。

关键词: 无碳化物贝氏体钢, CCT曲线, TTT曲线

Abstract: Continuous cooling transformation and isothermal transformation tests of undercooled austenite were carried out on a carbide-free bainitic tested steel by using the DIL-805A phase transformation tester. The CCT and TTT curves of the tested steel were obtained. The results show that the starting and ending transformation temperatures of austenite of the tested steel are 760 ℃ and 860 ℃, respectively, and the starting transformation temperature of martensite is approximately 300 ℃. When the cooling rate is between 0.1-15 ℃/s, the undercooled austenite mainly transforms to bainite+martensite complex structure. When the cooling rate is between 15-50 ℃/s, the undercooled austenite transforms into martensite. The microhardness of the tested steel increases with the increase of cooling rate, up to 742 HV0.5. When the tested steel undergoes isothermal transformation, the bainite transformation temperature range is 300-400 ℃, and the "nose tip" temperature is about 360 ℃.

Key words: carbide-free bainitic steel, CCT curve, TTT curve

中图分类号:

TG151.3

杨斯媛, 李爱国, 罗平, 张文良, 李贤君, 张明皓, 安伟骋, 王恺择. 一种无碳化物贝氏体钢的CCT与TTT曲线[J]. 金属热处理, 2025, 50(2): 74-80.

Yang Siyuan, Li Aiguo, Luo Ping, Zhang Wenliang, Li Xianjun, Zhang Minghao, An Weicheng, Wang Kaize. CCT and TTT curves of a carbide-free bainitic steel[J]. Heat Treatment of Metals, 2025, 50(2): 74-80.

参考文献

[1] Peter J, Peaslee K D, Robertson D G. Review of progress in developing continuous steelmaking[J]. Iron and Steel Technology, 2005, 2(2): 53-60.
[2] 李缘, 栾道成, 胡志华, 等. 城际及高铁轨道用辙叉贝氏体钢的组织与性能[J]. 金属热处理, 2021, 46(8): 70-72.
Li Yuan, Luan Daocheng, Hu Zhihua, et al. Microstructure and properties of bainitic steel for frog used in intercity and high-speed railway track[J]. Heat Treatment of Metals, 2021, 46(8): 70-72.
[3] 齐祥羽, 严玲, 李广龙, 等. 逆转变奥氏体稳定性对中锰钢强韧性的影响[J]. 金属热处理, 2021, 46(9): 205-210.
Qi Xiangyu, Yan Ling, Li Guanglong, et al. Effect of reversed austenite stability on strength and toughness of medium-Mn steel[J]. Heat Treatment of Metals, 2021, 46(9): 205-210.
[4] 郑红红, 赵爱民, 曹佳丽, 等. 水韧处理对高锰钢铸件组织与性能的影响[[J]. 金属热处理, 2014, 39(2): 112-115.
Zheng Honghong, Zhao Aimin, Cao Jiali, et al. Effect of water toughening on microstructure and mechanical properties of high manganese steel casting[J]. Heat Treatment of Metals, 2014, 39(2): 112-115.
[5] Long Xiaoyan, Liu Wei, Zhu Ranran, et al. Effect of the cooling rate in the medium temperature zone on the phase transformation and microstructure of carbide-free bainitic steel[J]. Journal of Materials Research and Technology, 2024, 29: 50-66.
[6] 田亚强, 田耕, 郑小平, 等. 低碳高强贝氏体钢的研究现状[J]. 钢铁研究学报, 2018, 30(7): 505-514.
Tian Yaqiang, Tian Geng, Zheng Xiaoping, et al. Research status of low carbon high strength bainitic steel[J]. Journal of Iron and Steel Research, 2018, 30(7): 505-514.
[7] 罗平. 基于组织调控改善贝氏体钢轨钢的抗磨损和抗接触疲劳性能[D]. 北京: 北京交通大学, 2016.
Luo Ping. Modification the resistance to wear and RCF for bainitic railway by tailoring microstructure[D]. Beijing: Beijing Jiaotong University, 2016.
[8] 张家涛, 王洪纲, 钟毅. 加热奥氏体化过程的数学模拟[J]. 昆明理工大学学报, 1997, 22(1): 135-138.
Zhang Jiatao, Wang Honggang, Zhong Yi. Mathsmatical anology on process of austenizing during heating[J]. Journal of Kunming University of Science and Technology, 1997, 22(1): 135-138.

[1]	赵峥嵘, 张雲飞, 赵英利, 樊明强, 白丽娟, 刘丽君. 塑料模具用4Cr13钢的连续冷却转变分析[J]. 金属热处理, 2025, 50(2): 69-73.
[2]	王程明, 白丽娟, 宋月, 刘丽君, 谷秀锐, 李惠敏. 海洋平台用EH36钢的SHCCT曲线测定与分析[J]. 金属热处理, 2025, 50(1): 58-62.
[3]	田亚强, 么志强, 年保国, 张俊粉, 张晓磊, 宋进英, 张明山, 陈连生. 热轧65Mn带钢等温相变行为及组织性能与扁卷的协同调控[J]. 金属热处理, 2024, 49(9): 24-30.
[4]	高兴成, 吴博雅, 吴晓春. 4Cr5Mo2V热作模具钢的CCT曲线及碳化物沿晶析出温度测定[J]. 金属热处理, 2024, 49(9): 72-79.
[5]	袁静, 陈飞达, 钟海清, 唐小勇, 朱映玉, 冷烨旻, 肖虎, 田世伟. XGTC300L搪瓷钢的连续冷却转变行为与析出规律[J]. 金属热处理, 2024, 49(9): 80-85.
[6]	任鹏帅, 秦凤, 周骞, 赵雷杰, 崔护, 彭子奥, 武常生. 等温淬火对含铝无碳化物贝氏体钢组织和性能的影响[J]. 金属热处理, 2024, 49(9): 103-109.
[7]	黄剑涛, 张明赫, 冯运莉, 尹绍江, 陈春生, 王厚昕. V-Nb微合金化Q420B大规格角钢的连续冷却转变规律[J]. 金属热处理, 2024, 49(7): 121-127.
[8]	陈作宁, 师仲然, 胡骞, 展之德, 罗小兵. 390 MPa级抗碰撞船体钢的奥氏体连续冷却转变[J]. 金属热处理, 2024, 49(7): 146-151.
[9]	董丽丽, 崔成波, 袁晓鸣, 刘泽田. BTP500钢板过冷奥氏体连续冷却转变行为[J]. 金属热处理, 2024, 49(7): 157-160.
[10]	刘阳, 高茗, 马莉, 胡祯, 孙中梅, 张士震. 低成本无钒热轧钢筋HRB400E的生产工艺优化[J]. 金属热处理, 2024, 49(7): 294-300.
[11]	刘干, 孔祥磊, 黄明浩, 王杨, 张英慧. 冷却速率对超高强度X90M管线钢相变行为的影响[J]. 金属热处理, 2024, 49(5): 162-167.
[12]	黄东, 蒋义然. S355低合金结构钢的动态连续冷却转变曲线及力学性能[J]. 金属热处理, 2024, 49(4): 38-41.
[13]	童炀, 张婧, 辛文彬, 罗果萍, 彭军, 侯蹬云. Nb含量对V-Ti-N工程结构用钢连续冷却转变规律及组织性能的影响[J]. 金属热处理, 2024, 49(3): 236-243.
[14]	曹佳丽, 靳红泽, 李康立, 徐亚鹏, 赵强, 王翠萍, 李梦楠. 水电用Q690CFD低合金高强钢SH-CCT曲线测定与分析[J]. 金属热处理, 2024, 49(2): 60-65.
[15]	高鑫, 宁静, 苏杰, 高齐, 姜庆伟. 中碳Cr-Mn-Si低合金钢的过冷奥氏体连续冷却转变曲线[J]. 金属热处理, 2024, 49(12): 142-147.