短流程CSP和2250mm轧制生产50W600无取向硅钢组织及性能对比

doi:10.13251/j.issn.0254-6051.2020.03.023

金属热处理 ›› 2020, Vol. 45 ›› Issue (3): 119-121.DOI: 10.13251/j.issn.0254-6051.2020.03.023

短流程CSP和2250mm轧制生产50W600无取向硅钢组织及性能对比

董丽丽^1,2, 卢晓禹², 杨源远², 麻永林¹, 杨维宇²

1. 内蒙古科技大学材料与冶金学院, 内蒙古包头 014010;
2. 内蒙古包钢钢联股份有限公司技术中心, 内蒙古包头 014010

收稿日期:2019-09-21 出版日期:2020-03-25 发布日期:2020-04-03
作者简介:董丽丽(1987—),女,工程师,博士研究生,主要从事硅钢新产品研发,E-mail:donglilibest@126.com。
基金资助:
内蒙古科技大学产学研培育基金(2016CXY01)

Comparison of microstructure and properties of 50W600 non-oriented silicon steel produced by CSP short process and 2250 mm rolling process

Dong Lili^1,2, Lu Xiaoyu², Yang Yuanyuan², Ma Yonglin¹, Yang Weiyu²

1. School of Materials and Metallurgy, Inner Mongolia University of Science and Technology, Baotou Inner Mongolia 014010, China;
2. Technology Center of Inner Mongolia Baogang Steel Union Co., Ltd., Baotou Inner Mongolia 014010, China

Received:2019-09-21 Online:2020-03-25 Published:2020-04-03

摘要/Abstract

摘要：

针对短流程CSP和半连轧2250 mm两种不同热轧工艺所生产的50W600无取向硅钢,进行力学拉伸试验、显微组织观察及织构分析,研究两种工艺生产的无取向硅钢在组织状态和整体性能上的差异。结果表明:短流程CSP工艺生产的50W600无取向硅钢显微组织较为均匀,平均晶粒尺寸较2250 mm热轧工艺生产的粗大,热轧板力学性能略低。短流程CSP工艺生产的50W600无取向硅钢成品板酸轧、连续退火后不利织构相对较少,磁性能优于2250 mm热轧工艺生产的50W600钢。

关键词: 50W600无取向硅钢, 短流程CSP, 2250mm轧制工艺, 显微组织, 磁性能

Abstract:

The mechanical tensile test, microstructure observation and texture analysis for 50W600 non oriented silicon steel produced by two different hot rolling processes (CSP and 2250 mm semi continuous rolling) were carried out to study the difference of microstructure and comprehensive properties between the two processes. The results show that the microstructure of the non oriented silicon steel 50W600 produced by CSP process is more uniform, the average grain size is larger than that of produced by 2250 mm hot rolling process, and the mechanical properties of the hot rolled plate are slightly lower. The unfavorable texture of 50W600 non-oriented silicon steel produced by short-process CSP after acid rolling and continuous annealing is relatively less, and the magnetic properties are better than that of produced by 2250 mm hot rolling process.

Key words: non-oriented silicon steel 50W600, CSP short process, 2250 mm rolling process, microstructure, magnetic properties

中图分类号:

TG142

董丽丽, 卢晓禹, 杨源远, 麻永林, 杨维宇. 短流程CSP和2250mm轧制生产50W600无取向硅钢组织及性能对比[J]. 金属热处理, 2020, 45(3): 119-121.

Dong Lili, Lu Xiaoyu, Yang Yuanyuan, Ma Yonglin, Yang Weiyu. Comparison of microstructure and properties of 50W600 non-oriented silicon steel produced by CSP short process and 2250 mm rolling process[J]. HTM, 2020, 45(3): 119-121.

参考文献

[1]张晓明. CSP工艺与传统工艺热轧板组织性能比较的研究[D]. 南京: 南京理工大学, 2009.
[2]万勇, 吴绍杰, 陈伟庆. 终轧温度对50W600无取向硅钢组织、织构和电磁性能的影响[J]. 金属热处理, 2015, 40(9): 135-139.
Wan Yong, Wu Shaojie, Chen Weiqing. Effects of finishing temperature on microstructure, texture and magnetic properties of 50W600 non-oriented silicon steel[J]. Heat Treatment of Metals, 2015, 40(9): 135-139.
[3]康永林, 柳得橹, 傅杰, 等. 薄板坯连铸连轧CSP生产低碳钢板的组织特征[J]. 钢铁, 2001, 36(6): 40-43.
Kang Yonglin, Liu Delu, Fu Jie, et al. Microstructure characteristics of low carbon steel plate produced by thin slab CSP[J]. Iron and Steel, 2001, 36(6): 40-43.
[4]朱涛, 施立发, 董梅, 等. CSP 与传统工艺生产无取向电工钢的组织和织构对磁性能影响的对比分析[J]. 钢铁研究学报, 2009, 21(11): 36-40.
Zhu Tao, Shi Lifa, Dong Mei, et al. Comparative analysis of effect of microstructure and texture on magnetic properties of non-oriented electrical steel produced by CSP and traditional processes[J]. Journal of Iron and Steel Research, 2009, 21(11): 36-40.
[5]张云祥, 徐光, 赵刚, 等. CSP 与常规热轧工艺生产Q345B 钢带的组织性能对比[J]. 钢铁研究, 2007, 35(1): 30-35.
Zhang Yunxiang, Xu Guang, Zhao Gang, et al. Comparison of microstructure and properties of 0345B strip produced by compact strip production (CSP) with conventional process[J]. Journal of Iron and Steel Research, 2007, 35(1): 30-35.
[6]邹翔, 项利, 仇圣桃, 等. 50W470 无取向硅钢热轧板的组织与织构演变[J]. 金属热处理, 2017, 42(2): 7-11.
Zou Xiang, Xiang Li, Qiu Shengtao, et al. Microstructure and texture evolution of 50W470 non-oriented electrical steel hot rolled sheet[J]. Heat Treatment of Metals, 2017, 42(2): 7-11.
[7]朱志勇, 王锋, 李化龙. 0.8%Si无取向硅钢织构及其对磁性能的影响[J]. 金属热处理, 2016, 41(2): 58-62.
Zhu Zhiyong, Wang Feng, Li Hualong. Texture of 0.8%Si non-oriented silicon steel and its effect on magnetic properties[J]. Heat Treatment of Metals, 2016, 41(2): 58-62.

[1]	张子延, 陈君, 陈晓亚, 李全安, 刘建鑫. 固溶时效处理对Mg-4Sm-3Gd-0.5Zr合金显微组织和耐蚀性能的影响[J]. 金属热处理, 2022, 47(4): 10-16.
[2]	梁恩溥, 徐乐, 杨勇, 王毛球. 添加Al、Cu对40CrNi3MoV钢组织和力学性能的影响[J]. 金属热处理, 2022, 47(4): 17-23.
[3]	陈连生, 张露友, 田亚强, 杨子旋, 李红斌, 潘红波, 魏英立. 低碳高强舰船用钢的CCT曲线及其组织性能[J]. 金属热处理, 2022, 47(4): 63-68.
[4]	王琪, 吴光亮. 回火温度对1100 MPa级高强钢组织与性能的影响[J]. 金属热处理, 2022, 47(4): 146-150.
[5]	孙凯, 陈研, 杨绍斌. 时效温度对激光选区熔化TC21钛合金微观组织及硬度的影响[J]. 金属热处理, 2022, 47(4): 155-158.
[6]	章建军, 庄晓伟, 汤晓峰. 提高低碳钢磁性能的球化退火工艺试验[J]. 金属热处理, 2022, 47(4): 182-184.
[7]	刘文彬, 乔龙阳, 潘新宇, 程格, 李爱娜, 裴新军. 淬火温度对刀剪用M390粉末冶金不锈钢组织和性能的影响[J]. 金属热处理, 2022, 47(4): 189-195.
[8]	王瑞琴, 葛鹏, 廖强, 侯鹏, 刘宇. 固溶冷却方式对短时用高温钛合金板材组织和性能的影响[J]. 金属热处理, 2022, 47(4): 196-198.
[9]	王绍灼, 孟晗, 王芬, 樊海卫, 李燕, 唐超. 改善低氧TC4-LC及重熔TC4钛合金性能的热处理工艺[J]. 金属热处理, 2022, 47(4): 204-207.
[10]	张宁, 高星, 王芝林, 蒋波, 刘雅政. 18CrNiMo7-6钢齿轮组织性能异常分析[J]. 金属热处理, 2022, 47(4): 268-273.
[11]	王敬元, 吴松全, 张博华, 辛社伟, 杨义, 王皞, 黄爱军. 固溶时效处理对BT25y钛合金显微组织及硬度的影响[J]. 金属热处理, 2022, 47(3): 14-19.
[12]	孙建, 黄贞益, 李景辉, 王萍. 固溶和时效处理对Fe-Mn-Al-C轻质钢组织和硬度的影响[J]. 金属热处理, 2022, 47(3): 34-38.
[13]	王方军, 刘应龙, 时瑶, 万红, 刘斌斌. 等温退火处理对Inconel 625合金箔材组织和性能的影响[J]. 金属热处理, 2022, 47(3): 77-81.
[14]	张曼雪, 景然, 张雄, 张晴, 吴倩, 刘以柔. 铸态Ti-20Zr-10Nb-xMo合金的微观组织和耐腐蚀性能[J]. 金属热处理, 2022, 47(3): 147-150.
[15]	宁静, 高坤元, 李浩楠, 文胜平, 黄晖, 吴晓蓝, 魏午, 聂祚仁. 成分和冷却速度对Al-xEr合金凝固组织的影响[J]. 金属热处理, 2022, 47(3): 151-154.

短流程CSP和2250mm轧制生产50W600无取向硅钢组织及性能对比

Comparison of microstructure and properties of 50W600 non-oriented silicon steel produced by CSP short process and 2250 mm rolling process

PDF

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

本文评价