系泊链用R4(22MnCrNiMo)钢CCT曲线测定及分析

doi:10.13251/j.issn.0254-6051.2020.03.041

金属热处理 ›› 2020, Vol. 45 ›› Issue (3): 208-210.DOI: 10.13251/j.issn.0254-6051.2020.03.041

系泊链用R4(22MnCrNiMo)钢CCT曲线测定及分析

方光锦

西宁特殊钢股份有限公司, 青海西宁 810005

收稿日期:2019-09-29 出版日期:2020-03-25 发布日期:2020-04-03
作者简介:方光锦(1984—),男,工程师,硕士,主要从事特殊钢产品设计开发、管理工作,E-mail:515023318@qq.com。
基金资助:
青海省重点企业技术创新项目(2019-JC-04)

Determination and analysis of CCT curves of R4 (22MnCrNiMo) steel for mooring chain

Fang Guangjin

Xining Special Steel Co., Ltd., Xining Qinghai 810005, China

Received:2019-09-29 Online:2020-03-25 Published:2020-04-03

摘要/Abstract

摘要：

利用DIL805A型热膨胀仪测定R4(22MnCrNiMo)钢膨胀曲线,并结合金相、硬度检验绘制出试验钢的CCT曲线,研究不同冷却速度对该钢的组织转变影响。结果表明,R4(22MnCrNiMo)钢的临界转变点为:Ar₃=819.5 ℃,Ar₁=778.5 ℃;当冷速为0.1~0.5 ℃/s时,冷却得到的组织主要为下贝氏体+残留奥氏体+极少量马氏体;当冷速达到3 ℃/s时,显微组织中只有极少量下贝氏体组织存在;继续增大冷速,显微组织均为板条状、针状马氏体+残留奥氏体。

关键词: R4(22MnCrNiMo)钢, CCT曲线, 相转变, 显微组织

Abstract:

The expansion curve of R4 (22MnCrNiMo) steel was measured by DIL805A thermal expansion instrument. CCT curves of the steel were drawn by metallographic and hardness test. The effects of different cooling rates on microstructure transformation of the steel were studied. The results show that the critical transition point of R4 (22MnCrNiMo) steel is: Ar₃=819.5 ℃, Ar₁=778.5 ℃. When the cooling rate is in the range of 0.1-0.5 ℃/s, the microstructure obtained by cooling is mainly lower bainite+retained austenite+small amount of martensite structure, only a small amount of lower bainite structure is obtained when the cooling rate reaches 3 ℃/s, as the cooling rate further increases, the microstructure is lath-like, needle-shaped martensite+residual austenite structure.

Key words: R4 (22MnCrNiMo) steel, CCT curves, phase transformation, microstructure

中图分类号:

TG115.21

方光锦. 系泊链用R4(22MnCrNiMo)钢CCT曲线测定及分析[J]. 金属热处理, 2020, 45(3): 208-210.

Fang Guangjin. Determination and analysis of CCT curves of R4 (22MnCrNiMo) steel for mooring chain[J]. HTM, 2020, 45(3): 208-210.

参考文献

[1]谌冬冬, 周旭东, 郭未昀. ST52-3G钢CCT曲线的测定与分析[J]. 金属热处理, 2017, 42(7): 168-171.
Chen Dongdong, Zhou Xudong, Guo Weiyun. Measurement and analysis of CCT curve for ST52-3G steel[J]. Heat Treatment of Metals, 2017, 42(7): 168-171.
[2]Xu F Y, Wang Y W, Bai B Z, et al. CCT curves of low-carbon Mn-Si steels and development of water-cooled bainitic steels[J]. Journal of Iron and Steel Research, International, 2010, 17(3): 46-50.
[3]朱茂华, 王福明, 文学荣, 等. Nb-V微合金中碳非调质钢CCT曲线的测定与分析[J]. 金属热处理, 2017, 42(8): 20-24.
Zhu Maohua, Wang Fuming, Wen Xuerong, et al. Determination and analysis of CCT curve of Nb-V microalloyed medium carbon non-quenched-tempered steel[J]. Heat Treatment of Metals, 2017, 42(8): 20-24.
[4]左锦中, 曾海霞, 樊启航, 等. 海洋采油平台R4S级系泊链用钢热处理工艺研究[J]. 山西冶金, 2017, 40(6): 42-44, 73.
Zuo Jinzhong, Zeng Haixia, Fan Qihang, et al. Study on heat treatment process of mooring chain of rank R4S grade for offshore platform[J]. Shanxi Metallurgy, 2017, 40(6): 42-44, 73.
[5]Johanning L, Smith G H, Wolfram J. Measurements of static and dynamic mooring line damping and their importance for floating WEC devices[J]. Ocean Engineering, 2007, 34(14/15): 1918-1934.
[6]Cheng X Y, Zhang H X, Li H, et al. Effect of tempering temperature on the microstructure and mechanical properties in mooring chain steel[J]. Materials Science and Engineering A, 2015, 636: 164-171.
[7]赵宝纯, 李桂艳, 柳永浩, 等. 含Mo低碳微合金钢CCT曲线的测定与分析[J]. 热加工工艺, 2008, 37(22): 37-39.
Zhao Baochun, Li Guiyan, Liu Yonghao, et al. Detection and analysis of CCT curve of low-carbon micro-alloyed steel with Mo[J]. Hot Working Technology, 2008, 37(22): 37-39.
[8]Letkowska B, Dziurka R, Bala P. The analysis of phase transformation of undercooled austenite and selected mechanical properties of low-alloy steel with boron addition[J]. Archives of Civil and Mechanical Engineering, 2015, 15(2): 308-316.
[9]侯彩云, 宗铎, 黄文涛, 等. SAE4320H钢奥氏体连续冷却转变[J]. 热加工工艺, 2015, 44(8): 79-81, 84.
Hou Caiyun, Zong Duo, Huang Wentao, et al. Austenite continuous cooling transformation curve of SAE4320H steel[J]. Hot Working Technology, 2015, 44(8): 79-81, 84.

[1]	张子延, 陈君, 陈晓亚, 李全安, 刘建鑫. 固溶时效处理对Mg-4Sm-3Gd-0.5Zr合金显微组织和耐蚀性能的影响[J]. 金属热处理, 2022, 47(4): 10-16.
[2]	梁恩溥, 徐乐, 杨勇, 王毛球. 添加Al、Cu对40CrNi3MoV钢组织和力学性能的影响[J]. 金属热处理, 2022, 47(4): 17-23.
[3]	陈连生, 张露友, 田亚强, 杨子旋, 李红斌, 潘红波, 魏英立. 低碳高强舰船用钢的CCT曲线及其组织性能[J]. 金属热处理, 2022, 47(4): 63-68.
[4]	王琪, 吴光亮. 回火温度对1100 MPa级高强钢组织与性能的影响[J]. 金属热处理, 2022, 47(4): 146-150.
[5]	孙凯, 陈研, 杨绍斌. 时效温度对激光选区熔化TC21钛合金微观组织及硬度的影响[J]. 金属热处理, 2022, 47(4): 155-158.
[6]	刘文彬, 乔龙阳, 潘新宇, 程格, 李爱娜, 裴新军. 淬火温度对刀剪用M390粉末冶金不锈钢组织和性能的影响[J]. 金属热处理, 2022, 47(4): 189-195.
[7]	王瑞琴, 葛鹏, 廖强, 侯鹏, 刘宇. 固溶冷却方式对短时用高温钛合金板材组织和性能的影响[J]. 金属热处理, 2022, 47(4): 196-198.
[8]	王绍灼, 孟晗, 王芬, 樊海卫, 李燕, 唐超. 改善低氧TC4-LC及重熔TC4钛合金性能的热处理工艺[J]. 金属热处理, 2022, 47(4): 204-207.
[9]	张宁, 高星, 王芝林, 蒋波, 刘雅政. 18CrNiMo7-6钢齿轮组织性能异常分析[J]. 金属热处理, 2022, 47(4): 268-273.
[10]	王敬元, 吴松全, 张博华, 辛社伟, 杨义, 王皞, 黄爱军. 固溶时效处理对BT25y钛合金显微组织及硬度的影响[J]. 金属热处理, 2022, 47(3): 14-19.
[11]	孙建, 黄贞益, 李景辉, 王萍. 固溶和时效处理对Fe-Mn-Al-C轻质钢组织和硬度的影响[J]. 金属热处理, 2022, 47(3): 34-38.
[12]	王方军, 刘应龙, 时瑶, 万红, 刘斌斌. 等温退火处理对Inconel 625合金箔材组织和性能的影响[J]. 金属热处理, 2022, 47(3): 77-81.
[13]	张曼雪, 景然, 张雄, 张晴, 吴倩, 刘以柔. 铸态Ti-20Zr-10Nb-xMo合金的微观组织和耐腐蚀性能[J]. 金属热处理, 2022, 47(3): 147-150.
[14]	宁静, 高坤元, 李浩楠, 文胜平, 黄晖, 吴晓蓝, 魏午, 聂祚仁. 成分和冷却速度对Al-xEr合金凝固组织的影响[J]. 金属热处理, 2022, 47(3): 151-154.
[15]	王荣, 龚玉辉, 殷学俊, 魏德强. 多道电子束扫描搭接率对40Cr钢组织与性能的影响[J]. 金属热处理, 2022, 47(3): 191-197.

系泊链用R4(22MnCrNiMo)钢CCT曲线测定及分析

Determination and analysis of CCT curves of R4 (22MnCrNiMo) steel for mooring chain

PDF

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

本文评价