双级时效对变形2A12铝合金组织与性能的影响

doi:10.13251/j.issn.0254-6051.2020.04.020

摘要/Abstract

摘要： 采用拉伸试验机、扫描电镜、金相显微镜等仪器,研究了双级时效对变形2A12铝合金组织与性能的影响。结果表明:初始态2A12铝合金经495 ℃×12 h均匀化退火处理后,组织趋于均匀,析出较多弥散T相。双级时效对镦粗变形铝合金抗拉强度的提升相比单级时效有更明显的作用,且双级时效的二级时效温度和时间是提高强度的主导因素,二级时效温度不宜超过200 ℃,保温时间不宜超过6.5 h,否则会导致材料过烧,强度下降。因此2A12铝合金最佳热处理工艺为495 ℃×1 h固溶+100 ℃×2 h+180 ℃×6.5 h时效,经该工艺处理后,晶粒细化,第二相强化作用增强,材料综合性能优异。

关键词: 2A12铝合金, 固溶处理, 双级时效, 抗拉强度, 组织

Abstract: Effect of two-stage aging on the microstructure and properties of deformed 2A12 aluminum alloy were studied by using tensile testing machine, scanning electron microscope, metallographic microscope and other instruments. The results show that the microstructure of the alloy tends to be uniform after homogenized and annealed at 495 ℃×12 h, and more dispersed T phases are precipitated. The two-stage aging has more significant effect on improving the tensile strength of upset deformed aluminum alloy than the single-stage aging, and the temperature and time of the two-stage aging are the main factors for improving the strength. The second-stage aging temperature can't exceed 200 ℃, and the time should not exceed 6.5 h, otherwise it will cause over-melted of the material and decrease the strength.Therefore, the best heat treatment process for 2A12 aluminum alloy is 495 ℃×1 h solid solution, 100 ℃×2 h+180 ℃×6.5 h aging. After this process, the grains are refined, the secondary phase strengthening is enhanced, and the comprehensive properties of the alloy are excellent.

Key words: 2A12 aluminum alloy, solid solution treatment, two-stage aging, tensile strength, microstructure

中图分类号:

闫凡, 徐健, 张星, 闫林. 双级时效对变形2A12铝合金组织与性能的影响[J]. 金属热处理, 2020, 45(4): 99-104.

Yan Fan, Xu Jian, Zhang Xing, Yan Lin. Effect of two-stage aging on microstructure and properties of deformed 2A12 aluminum alloy[J]. Heat Treatment of Metals, 2020, 45(4): 99-104.

参考文献

[1]于英录, 祁艳华, 刘翠波. 提高2A12铝合金厚壁管力学性能的试验[J]. 轻合金加工技术, 2002(5): 33-34.
Yu Yinglu, Qi Yanhua, Liu Cuibo. Experiments on improving the mechanical properties of 2A12 aluminum alloy thick-walled pipes[J]. Light Alloy Processing Technology, 2002(5): 33-34.
[2]刘春燕, 邱义伦, 王斌. 2A12铝合金热处理工艺研究[J]. 热处理, 2008(5): 59-61.
Liu Chunyan, Qiu Yilun, Wang Bin. Study on heat treatment process of 2A12 aluminum alloy[J]. Heat Treatment, 2008(5): 59-61.
[3]吴私. 杂质元素对2A12铝合金显微组织与力学性能的影响[D]. 辽宁: 辽宁石油化工大学, 2014.
[4]曹秀萍. 淬火制度对 2A12 T4 小规格管材力学性能的影响[J]. 有色金属加工, 2010, 39(6): 51-55.
Cao Xiuping. Effect of quenching system on mechanical properties of 2A12 T4 small size pipe[J]. Nonferrous Metal Processing, 2010, 39(6): 51-55.
[5]王少华, 张兴国, 杨守杰, 等. 时效制度对 Al-7.1Zn-1.1Mg-1.6Cu-0.14Zr 合金断裂行为的影响[J]. 稀有金属材料与工程, 2011, 40(3): 453-456.
Wang Shaohua, Zhang Xingguo, Yang Shoujie, et al. Effect of aging system on fracture behavior of Al-7.1Zn-1.1Mg-1.6Cu-0.14Zr alloy[J]. Rare Metal Materials and Engineering, 2011, 40(3): 453-456.
[6]贺双喜, 刘向阳, 谢广辉, 等. 时效制度对2A12铝合金组织与性能的影响[J]. 金属热处理, 2014, 39(6): 94-96.
He Shuangxi, Liu Xiangyang, Xie Guanghui, et al. Effect of aging system on microstructure and properties of 2A12 aluminum alloy[J]. Heat Treatment of Metals, 2014, 39(6): 94-96.
[7]田秀云, 刘艳红, 高立柱. 2024铝合金新人工时效制度的探讨[J]. 航空材料学报, 2000(2): 35-39.
Tian Xiuyun, Liu Yanhong, Gao Lizhu. Discussion on the new artificial aging system of 2024 aluminum alloy[J]. Journal of Aeronautical Materials, 2000(2): 35-39.
[8]Song Y F, Ding X F, Xiao L R. Effects of two-stage aging on the dimensional stability of Al-Cu-Mg alloy[J]. Alloys and Compounds, 2017, 701: 508-514.
[9]杨胜利, 沈健, 蒋鹏, 等. 热处理制度对新型Al-Cu-Li合金组织与性能的影响[J]. 中国有色金属学报, 2018, 28(6): 1111-1119.
Yang Shengli, Shen Jian, Jiang Peng, et al. Effect of heat treatment system on microstructure and properties of new Al-Cu-Li alloy[J]. The Chinese Journal of Nonferrous Metals, 2018, 28(6): 1111-1119.
[10]韩念梅, 张新明, 刘胜胆, 等. 固溶处理对7050铝合金强度和断裂韧性的影响[J]. 中南大学学报(自然科学版), 2012, 43(3): 855-863.
Han Nianmei, Zhang Xinming, Liu Shengdan, et al. Effect of solution treatment on the strength and fracture toughness of 7050 aluminum alloy[J]. Journal of Central South University (Science and Technology), 2012, 43(3): 855-863.
[11]贾科. 高强高韧耐蚀7050铝合金的时效与腐蚀行为研究[D]. 长沙: 中南大学, 2013.
[12]陈刚, 高平平, 范才河, 等. 热处理对挤压铸造2024铝合金组织与性能的影响[J]. 湖南大学学报(自然科学版), 2010, 37(5): 74-77.
Chen Gang, Gao Pingping, Fan Caihe, et al. Effect of heat treatment on microstructure and properties of 2024 aluminum alloy by extrusion casting[J]. Journal of Hunan University (Natural Science), 2010, 37(5): 74-77.
[13]尚勇, 张立武, 李建康. 重固溶再多级时效处理对7175铝合金组织和性能的影响[J]. 热加工工艺, 2005(7): 41-43.
Shang Yong, Zhang Liwu, Li Jiankang. Effects of heavy solution and multi-stage aging treatment on microstructure and properties of 7175 aluminum alloy[J]. Hot Working Technology, 2005(7): 41-43.
[14]邵华, 刘兆晶, 刘君, 等. 分级时效和冷热循环对2024铝合金微塑变抗力的影响[J]. 中国有色金属学报, 2000, 10(3): 330-333.
Shao Hua, Liu Zhaojing, Liu Jun, et al. Effects of classification aging and cold-heat cycle on microplastic resistance of 2024 aluminum alloy[J]. The Chinese Journal of Nonferrous Metals, 2000, 10(3): 330-333.
[15]李红英, 张孝军, 张建飞, 等. 分级时效对新型Al-Cu-Li合金组织与性能的影响[J]. 中国有色金属学报, 2008, 18(3): 426-432.
Li Hongying, Zhang Xiaojun, Zhang Jianfei, et al. Effect of classification aging on microstructure and properties of new Al-Cu-Li alloy[J]. The Chinese Journal of Nonferrous Metals, 2008, 18(3): 426-432.
[16]莫灼强, 曹宇, 邓松云, 等. 热处理对IT产品用高纯6463铝合金组织和力学性能的影响[J]. 热加工工艺, 2019(6): 236-239.
Mo Zhuoqiang, Cao Yu, Deng Songyun, et al. Effect of heat treatment on microstructure and mechanical properties of high-purity 6463 aluminum alloy for IT products[J]. Hot Working Technology, 2019(6): 236-239.
[17]Wang Y L, Jiang H C, Li Z M. Two-stage double peaks ageing and its effect on stress corrosion cracking susceptibility of Al-Zn-Mg alloy[J]. Materials Science and Technology, 2018, 34(7): 1250-1257.