油气工程用Inconel 718合金激光焊接头的氢脆行为

doi:10.13251/j.issn.0254-6051.2020.08.011

金属热处理 ›› 2020, Vol. 45 ›› Issue (8): 50-55.DOI: 10.13251/j.issn.0254-6051.2020.08.011

油气工程用Inconel 718合金激光焊接头的氢脆行为

曾强¹, 吴颖¹, 肖辉进¹, 朱绍维²

1.四川文理学院智能制造学院, 四川达州 635000;
2.成都飞机工业(集团)有限责任公司, 四川成都 610092

收稿日期:2020-01-25 出版日期:2020-08-25 发布日期:2020-09-07
作者简介:曾强(1975—),男,副教授,硕士,主要研究方向为金属材料的制备、加工及金属热处理工艺,E-mail: luofang1022@163.com
基金资助:
国家科技重大专项(2014ZX04014-031)

Hydrogen embrittlement behavior of oilfield-grade Inconel 718 alloy laser welded joint

Zeng Qiang¹, Wu Ying¹, Xiao Huijin¹, Zhu Shaowei²

1. School of Intelligent Manufacturing, Sichuan University of Arts and Science, Dazhou Sichuan 635000, China;
2. Chengdu Aircraft Industrial (Group) Co. , Ltd. , Chengdu Sichuan 610092, China

Received:2020-01-25 Online:2020-08-25 Published:2020-09-07

摘要/Abstract

摘要： 采用激光焊接工艺,对油气工程用4 mm厚经1030 ℃×2 h固溶+780 ℃×8 h时效和1030 ℃×2 h固溶+780 ℃×16 h时效两种热处理后的Inconel 718合金进行激光焊接,结合微观组织分析、拉伸性能分析和断口形貌分析,对合金母材及激光焊接头在原位充氢条件下的氢脆行为进行了研究。结果表明:长时间时效导致δ相大量析出,使合金母材的氢脆敏感性指数从正常时效态的0.27提高到过时效态的0.48。激光焊接头整体的氢脆敏感性没有受焊前热处理的影响,分别为0.39和0.38;由于焊缝内Laves相的析出,导致激光焊接头的氢脆敏感性高于正常时效态的母材。

关键词: 激光焊接, Inconel 718合金, 时效, 氢脆

Abstract: The oilfield-grade Inconel 718 alloy, which was respectively heat treated by 1030 ℃×2 h solution treatment+780 ℃×8 h aging and 1030 ℃×2 h solution treatment+780 ℃×16 h aging, was welded by laser beam welding process. The hydrogen embrittlement behaviors of the base metal and welded joint of the alloy were studied during in situ hydrogen charging by analyses of microstructure, tensile properties and fracture morphologies. The results show that longer time aging induces large amount of δ phase, resulting in the hydrogen embrittlement susceptibility index of the base metal increasing from 0.27 to 0.48. The hydrogen embrittlement susceptibility of the welded joint is not affected by the heat treatment before welding, which is 0.39 and 0.38, respectively. However, the precipitation of Laves phase in welded zone induces that the hydrogen embrittlement susceptibility of the welded joints is higher than that of base metal aged for 8 h.

Key words: laser welding, Inconel 718 alloy, aging, hydrogen embrittlement

中图分类号:

TG142.1

曾强, 吴颖, 肖辉进, 朱绍维. 油气工程用Inconel 718合金激光焊接头的氢脆行为[J]. 金属热处理, 2020, 45(8): 50-55.

Zeng Qiang, Wu Ying, Xiao Huijin, Zhu Shaowei. Hydrogen embrittlement behavior of oilfield-grade Inconel 718 alloy laser welded joint[J]. Heat Treatment of Metals, 2020, 45(8): 50-55.

参考文献

[1]孙敏, 代朋超. 油气田用Inconel 718合金腐蚀性能研究综述[J]. 宝钢技术, 2017(2): 10-14.
Sun Min, Dai Pengchao. Review on corrosion resistance properties of Inconel 718 alloy in oil and gas industry[J]. Baosteel Technology, 2017(2): 10-14.
[2]周元贵, 彭志方, 陈方玉, 等. IN718合金时效后的组织及其典型元素分布特征[J]. 金属热处理, 2009, 34(6): 19-24.
Zhou Yuangui, Peng Zhifang, Chen Fangyu, et al. Microstructure and typical elements distribution of IN718 alloy after aging treatment[J]. Heat Treatment of Metals, 2009, 34(6): 19-24.
[3]Tarzimoghadam Z, Ponge D, Klöwer J, et al. Hydrogen-assisted failure in Ni-based superalloy 718 studied under in situ hydrogen charging: The role of localized deformation in crack propagation[J]. Acta Materialia, 2017, 128: 365-374.
[4]Li Xinfeng, Zhang Jin, Fu Qinqin, et al. Tensile mechanical properties and fracture behaviors of nickel-based superalloy 718 in the presence of hydrogen[J]. International Journal of Hydrogen Energy, 2018, 43: 20118-20132.
[5]Zhang Zhenbo, Katie L Moore, Greg McMahon, et al. On the role of precipitates in hydrogen trapping and hydrogen embrittlement of a nickel-based superalloy[J]. Corrosion Science, 2019, 146: 58-69.
[6]Florian Galliano, Eric Andrieu, Christine Blanc, et al. Effect of trapping and temperature on the hydrogen embrittlement susceptibility of alloy 718[J]. Materials Science and Engineering A, 2014, 611: 370-382.
[7]Rezende M C, Araujo L S, Gabriel S B, et al. Hydrogen embrittlement in nickel-based superalloy 718: Relationship between γ′+γ″ precipitation and the fracture mode[J]. International Journal of Hydrogen Energy, 2015, 40(47): 17075-17083.
[8]唐瑞, 刘海定, 王东哲, 等. 油气工程用镍基耐蚀合金718的研究进展[J]. 金属热处理, 2018, 43(7): 54-59.
Tang Rui, Liu Haiding, Wang Dongzhe, et al. Developing progress of oilfield-grade corrosion resistant alloy 718[J]. Heat Treatment of Metals, 2018, 43(7): 54-59.
[9]Qu Fengsheng, Liu Xuguang, Xing Fei, et al. High temperature tensile properties of laser butt-welded plate of Inconel 718 superalloy with ultra-fine grains[J]. Transactions of Nonferrous Metals Society of China, 2012, 22(10): 2379-2388.
[10]Hong J K, Park J H, Park N K, et al. Microstructures and mechanical properties of Inconel 718 welds by CO₂ laser welding[J]. Journal of Materials Processing Technology, 2007, 201(1): 515-520.
[11]郑传波, 唐祝君, 申小兰. 微观组织对2205双相不锈钢氢脆敏感性的影响[J]. 金属热处理, 2015, 40(9): 39-44.
Zheng Chuanbo, Tang Zhujun, Shen Xiaolan. Effect of microstructure on hydrogen embrittlement of 2205 duplex stainless steel[J]. Heat Treatment of Metals, 2015, 40(9): 39-44.
[12]Mei Yunpeng, Liu Yongchang, Liu Chenxi, et al. Effect of base metal and welding speed on fusion zone microstructure and HAZ hot-cracking of electron-beam welded Inconel 718[J]. Materials and Design, 2016, 89: 964-977.
[13]Jothi Sathiskumar, Merzlikin V Sergiy, Croft Nick, et al. An investigation of micro-mechanisms in hydrogen induced cracking in nickel-based superalloy 718[J]. Journal of Alloys and Compounds, 2016, 664: 664-681.
[14]Li Xinfeng, Li Qizhen, Wang Tan, et al. Hydrogen-assisted failure of laser melting additive manufactured IN718 superalloy[J]. Corrosion Science, 2019, 160: 108171.

[1]	张子延, 陈君, 陈晓亚, 李全安, 刘建鑫. 固溶时效处理对Mg-4Sm-3Gd-0.5Zr合金显微组织和耐蚀性能的影响[J]. 金属热处理, 2022, 47(4): 10-16.
[2]	陈东俊, 李广阳, 刘刚. 时效处理对AlSi9Cu3压铸铝合金组织和力学性能的影响[J]. 金属热处理, 2022, 47(4): 53-56.
[3]	陈思君, 陈送义, 陈庚, 袁丁玲, 陈康华. Mg含量对2A14铝合金组织和力学性能的影响[J]. 金属热处理, 2022, 47(4): 86-92.
[4]	孙凯, 陈研, 杨绍斌. 时效温度对激光选区熔化TC21钛合金微观组织及硬度的影响[J]. 金属热处理, 2022, 47(4): 155-158.
[5]	胡静, 陶科, 杨庆松, 李刚, 张德汉. 机械抛光后的时效工艺对0Cr25Al5电热合金拉拔性能的影响[J]. 金属热处理, 2022, 47(4): 171-177.
[6]	孙建, 黄贞益, 李景辉, 王萍. 固溶和时效处理对Fe-Mn-Al-C轻质钢组织和硬度的影响[J]. 金属热处理, 2022, 47(3): 34-38.
[7]	杨春苗, 王珊, 王淑慧, 李延珍, 刘文文. RRA过程中预时效时间对7A85铝合金组织性能的影响[J]. 金属热处理, 2022, 47(3): 44-47.
[8]	姜中涛, 汪鑫, 周志明, 林海涛, 杨绪盛, 代芳芳. 双级固溶工艺对7050铝合金组织与力学性能的影响[J]. 金属热处理, 2022, 47(3): 102-106.
[9]	闵旭东, 黄元春, 肖政兵, 刘宇, 任贤魏, 邹倜. 预处理对汽车用Al-Mg-Si合金组织和晶间腐蚀行为的影响[J]. 金属热处理, 2022, 47(2): 78-85.
[10]	曾煜, 吴畏, 莫燕. 一种汽车发动机气阀用节镍型高温合金的固溶时效工艺[J]. 金属热处理, 2022, 47(2): 188-192.
[11]	邱旭扬帆, 杨卓越, 丁雅莉. 提高Cr-Ni-Mo-Ti马氏体时效不锈钢超低温韧性的固溶处理工艺[J]. 金属热处理, 2022, 47(1): 44-48.
[12]	崔岩, 董和谦, 曹雷刚, 杨越, 蒙毅. 55%SiC_p/2024Al复合材料时效过程的微观组织与力学性能[J]. 金属热处理, 2022, 47(1): 142-148.
[13]	谭皎, 张伯岩, 朱文光, 孙巧艳. 时效温度对Ti-5Al-4Zr-10Mo-3Cr钛合金微观组织及力学性能的影响[J]. 金属热处理, 2022, 47(1): 217-225.
[14]	王佳慧, 陈文浩, 张玉, 江卓奥, 王庆航, 赵玲玉. 喷射成形7055高强铝合金的热处理工艺优化及其应用[J]. 金属热处理, 2022, 47(1): 239-244.
[15]	白韶斌, 肖文涛, 牛伟强, 梁伟, 李大赵. 退火和退火-时效工艺对热轧中锰钢组织及性能的影响[J]. 金属热处理, 2022, 47(1): 245-249.

油气工程用Inconel 718合金激光焊接头的氢脆行为

Hydrogen embrittlement behavior of oilfield-grade Inconel 718 alloy laser welded joint

PDF

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

本文评价