挤压态6061铝合金的力学性能及显微组织

doi:10.13251/j.issn.0254-6051.2020.09.032

金属热处理 ›› 2020, Vol. 45 ›› Issue (9): 172-177.DOI: 10.13251/j.issn.0254-6051.2020.09.032

挤压态6061铝合金的力学性能及显微组织

刘伟^1,2, 吴远志^1,2, 邓彬^1,2, 刘安民^1,2, 刘巍², 许子砚², 叶拓^1,2

1.湖南工学院汽车零部件技术研究院,湖南衡阳 421002;
2.湖南工学院机械工程学院,湖南衡阳 421002

收稿日期:2020-03-23 出版日期:2020-09-25 发布日期:2020-12-29
通讯作者: 叶拓(1987—),男,讲师,博士,E-mail:hnuyetuo@163.com
作者简介:刘伟(1988—),男,讲师,硕士,主要研究方向为铝合金等轻金属材料高低温变形行为,E-mail:hitliuwei1105@163.com
基金资助:
国家级大学生创新创业训练计划平台项目(201811528002);湖南省自然科学基金(2019JJ30009,2018JJ4031,2019JJ50110)

Mechanical properties and microstructure of extruded 6061 aluminum alloy

Liu Wei^1,2, Wu Yuanzhi^1,2, Deng Bin^1,2, Liu Anmin^1,2, Liu Wei², Xu Ziyan², Ye Tuo^1,2

1. Research Institute of Automobile Parts Technology,Hunan Institute of Technology,Hengyang Hunan 421002,China;
2. School of Mechanical and Engineering,Hunan Institute of Technology,Hengyang Hunan 421002,China

Received:2020-03-23 Online:2020-09-25 Published:2020-12-29

摘要/Abstract

摘要： 对挤压态6061铝合金分别进行了固溶处理和时效处理,采用万能试验机测试了其力学性能,通过SEM和TEM表征了合金的微观组织,研究了不同热处理条件下挤压态6061铝合金的组织演变规律。结果表明:固溶和时效处理后的挤压态6061铝合金均表现出明显的力学性能各向异性,且时效处理能有效提升合金的强度;同时,经时效处理后的挤压态6061铝合金表现出应变速率敏感性,而固溶处理的挤压态6061铝合金则无明显的应变速率敏感性;固溶处理和时效处理的挤压态6061铝合金的晶粒形态为等轴晶,但是有大小两种晶粒尺寸等级,大晶粒尺寸可达200 μm,小晶粒尺寸则小于10 μm。固溶和时效处理的挤压态6061铝合金均由较强的{001}<100>立方织构和较弱的{011}<100>高斯织构组成,且种类和强度相同;拉伸变形后的6061铝合金出现了大量的位错堆积,而经时效处理的合金中均匀分布短棒状的析出相能有效阻碍位错的运动,提高材料的变形抗力。

关键词: 挤压态6061铝合金, 热处理, 力学性能, 微观组织

Abstract: As-extruded 6061 aluminum alloy was subjected to solution treatment and aging treatment,respectively.The mechanical properties of the alloy were tested by universal testing machine,and the microstructure was characterized by means of SEM and TEM to investigate the microstructure evolution law of the alloy in different heat treatment states.The results show that the extruded 6061 aluminum alloy after solution treatment and aging treatment show obvious anisotropic mechanical properties,and aging treatment can effectively improve the strength of the alloy.At the same time,the extruded alloy after aging treatment shows strain rate sensitivity,however,the alloy after solution treatment has no obvious strain rate sensitivity.The extruded 6061 aluminum alloy after solution treatment and aging treatment are composed of equiaxed grains with two kinds of grain sizes,which the larger one being up to 200 μm and the smaller one being less than 10 μm.The types and strength of texture components of the extruded 6061 aluminum alloy solution-treated or as-aged are the same,both are composed of strong {001} <100>cubic texture and weak {011} <100>Goss texture.After tensile deformation,a large number of dislocations pile up,and the short rod like precipitates will be evenly distributed in the alloy after aging treatment,which can effectively block the movement of dislocations and improve the deformation resistance of materials.

Key words: extruded 6061 aluminum alloy, heat treatment, mechanical properties, microstructure

中图分类号:

TG146.2

刘伟, 吴远志, 邓彬, 刘安民, 刘巍, 许子砚, 叶拓. 挤压态6061铝合金的力学性能及显微组织[J]. 金属热处理, 2020, 45(9): 172-177.

Liu Wei, Wu Yuanzhi, Deng Bin, Liu Anmin, Liu Wei, Xu Ziyan, Ye Tuo. Mechanical properties and microstructure of extruded 6061 aluminum alloy[J]. Heat Treatment of Metals, 2020, 45(9): 172-177.

参考文献

[1] Yuan X,Liu X,Zuo J.The development of new energy vehicles for a sustainable future:A review[J].Renewable and Sustainable Energy Reviews,2015,42:298-305.
[2] Zhu H,Yuen K V,Mihaylova L,et al.Overview of environment perception for intelligent vehicles[J].IEEE Transactions on Intelligent Transportation Systems,2017,18(10):2584-2601.
[3] 陈辉,景财年.热成形技术在汽车轻量化中的应用与发展[J].金属热处理,2016,41(3):61-66.
Chen Hui,Jing Cainian.Application and development of hot forming technology for automobile lightening[J].Heat Treatment of Metals,2016,41(3):61-66.
[4] Delogu M,Del Pero F,Pierini M.Lightweight design solutions in the automotive field:Environmental modelling based on fuel reduction value applied to diesel turbocharged vehicles[J].Sustainability,2016,8(11):1167.
[5] 郑晖,赵曦雅.汽车轻量化及铝合金在现代汽车生产中的应用[J].锻压技术,2016,41(2):1-5.
Zheng Hui,Zhao Xiya.Lightweight automobile and application of aluminum alloys in modern automobile production[J].Forging and Stamping Technology,2016,41(2):1-5.
[6] Kimura T,Nakamoto T.Microstructures and mechanical properties of A356(AlSi₇Mg_0.3)aluminum alloy fabricated by selective laser melting[J].Materials and Design,2016,89:1294-1301.
[7] Chen J,Yuan X,Hu Z,et al.Microstructure and mechanical properties of resistance-spot-welded joints for A5052 aluminum alloy and DP600 steel[J].Materials Characterization,2016,120:45-52.
[8] Li H,Yan Z,Cao L.Bake hardening behavior and precipitation kinetic of a novel Al-Mg-Si-Cu aluminum alloy for lightweight automotivebody[J].Materials Science and Engineering A,2018,728:88-94.
[9] Seffer O,Pfeifer R,Springer A,et al.Investigations on laser beam welding of different dissimilar joints of steel and aluminum alloys for automotive lightweight construction[J].Physics Procedia,2016,83:383-395.
[10] Lipinska M,Chrominski W,Olejnik L,et al.Ultrafine-grained plates of Al-Mg-Si alloy obtained by incremental equal channel angular pressing:Microstructure and mechanical properties[J].Metallurgical and Materials Transactions A,2017,48(10):4871-4882.
[11] Yuan S,Chen L,Tang J,et al.Correlation between homogenization treatment and subsequent hot extrusion of Al-Mg-Si alloy[J].Journal of Materials Science,2019,54(13):9843-9856.
[12] Mei L,Chen X,Huang G,et al.Improvement of mechanical properties of acryorolled Al-Mg-Si alloy through warm rolling and aging[J].Journal of Alloys and Compounds,2019,777:259-263.
[13] Petroušek P,Kvaškaj T,Koćiško R,et al.Evaluation of formability of thin sheets based on Al-Mg-Si for automotive industry[J].Acta Metallurgica Slovaca,2015,21(3):176-183.
[14] Lu H,Zhang J,Tian N,et al.Recycle-friendly aluminum alloy sheets for automotive applications based on hemming[J].Automotive Innovation,2018,1(1):70-75.
[15] Klos A,Kahrimanidis A,Wortberg D,et al.Experimental and numerical studies on the forming behavior of high strain Al-Mg-Si(-Cu)sheet alloys[J].Procedia Engineering,2017,183:95-100.

挤压态6061铝合金的力学性能及显微组织

Mechanical properties and microstructure of extruded 6061 aluminum alloy

PDF

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

本文评价

[1]	梁恩溥, 徐乐, 杨勇, 王毛球. 添加Al、Cu对40CrNi3MoV钢组织和力学性能的影响[J]. 金属热处理, 2022, 47(4): 17-23.
[2]	祁晓亮, 李岩, 定巍, 赵增武. 含Al中锰TRIP钢原始组织对临界退火后组织与力学性能的影响[J]. 金属热处理, 2022, 47(4): 24-29.
[3]	陈保安, 张静媛, 祝志祥, 韩钰, 潘学东, 张磊, 陈素红. 化学成分对高强Al-Mg-Si合金组织和性能的影响[J]. 金属热处理, 2022, 47(4): 30-38.
[4]	陈东俊, 李广阳, 刘刚. 时效处理对AlSi9Cu3压铸铝合金组织和力学性能的影响[J]. 金属热处理, 2022, 47(4): 53-56.
[5]	陈连生, 张露友, 田亚强, 杨子旋, 李红斌, 潘红波, 魏英立. 低碳高强舰船用钢的CCT曲线及其组织性能[J]. 金属热处理, 2022, 47(4): 63-68.
[6]	王云龙, 余伟, 张昳, 史佳新, 李明辉. 奥氏体化温度对贝氏体钢等温转变及力学性能的影响[J]. 金属热处理, 2022, 47(4): 80-85.
[7]	骆再斌, 范子泽, 彭振. 轻质高熵合金的研究进展[J]. 金属热处理, 2022, 47(4): 100-107.
[8]	李立, 曾艳, 吴晓春. 4Cr5Mo2VCo钢的热处理工艺优化[J]. 金属热处理, 2022, 47(4): 133-140.
[9]	吕杰晟, 宋志刚, 何建国, 丰涵, 郑文杰, 朱玉亮. S32205双相不锈钢冷轧退火组织转变及强塑化机理分析[J]. 金属热处理, 2022, 47(4): 141-145.
[10]	王琪, 吴光亮. 回火温度对1100 MPa级高强钢组织与性能的影响[J]. 金属热处理, 2022, 47(4): 146-150.
[11]	张骥俊, 邢彦锋, 曹菊勇. 超声振动对CMT电弧增材制造铝合金组织与性能的影响[J]. 金属热处理, 2022, 47(4): 159-164.
[12]	刘文彬, 乔龙阳, 潘新宇, 程格, 李爱娜, 裴新军. 淬火温度对刀剪用M390粉末冶金不锈钢组织和性能的影响[J]. 金属热处理, 2022, 47(4): 189-195.
[13]	王瑞琴, 葛鹏, 廖强, 侯鹏, 刘宇. 固溶冷却方式对短时用高温钛合金板材组织和性能的影响[J]. 金属热处理, 2022, 47(4): 196-198.
[14]	王方军, 王东哲, 万红, 时瑶, 沈涛. 热处理和冷变形量对定膨胀合金4J32C线膨胀系数的影响[J]. 金属热处理, 2022, 47(4): 199-203.
[15]	王绍灼, 孟晗, 王芬, 樊海卫, 李燕, 唐超. 改善低氧TC4-LC及重熔TC4钛合金性能的热处理工艺[J]. 金属热处理, 2022, 47(4): 204-207.