Nb添加对FeCo基合金高温性能与时效态性能的影响

doi:10.13251/j.issn.0254-6051.2020.09.041

金属热处理 ›› 2020, Vol. 45 ›› Issue (9): 223-226.DOI: 10.13251/j.issn.0254-6051.2020.09.041

Nb添加对FeCo基合金高温性能与时效态性能的影响

王东玲, 王炫东, 张敬霖, 于一鹏, 张建福

钢铁研究总院功能材料研究所,北京 100081

收稿日期:2020-03-21 出版日期:2020-09-25 发布日期:2020-12-29
作者简介:王东玲(1973——),女,高级工程师,博士,主要研究方向为磁性材料,E-mail:wanglongling@cisri.com.Cn

Effect of Nb addition on high temperature and aged properties of FeCo based alloy

Wang Dongling, Wang Xuandong, Zhang Jinglin, Yu Yipeng, Zhang Jianfu

Functional Matenials Research Institute,Central Iron and Steel Research Institute,Bejing 100081,China

Received:2020-03-21 Online:2020-09-25 Published:2020-12-29

摘要/Abstract

摘要： 对Fe-49Co-2V和Fe-49Co-2V-0.3Nb两种合金室温与高温时的磁性能和力学性能进行了测试。结果发现:与室温磁性能相比,两种合金在高温下的饱和磁化强度B_s与矫顽力H_c均降低;与室温力学性能相比,两种合金在500 ℃时的高温抗拉强度都有所增加,其中 Nb元素的添加使合金力学性能强化的效果十分明显。两种合金经500 ℃时效处理168 h后,Fe-49Co-2V-0.3Nb合金经过高温时效后依然能保证具有良好的力学性能,添加了Nb元素后有助于改善合金的高温时效稳定性。

关键词: FeCo基软磁合金, Nb添加, 高温力学性能, 时效处理

Abstract: Magnetic properties and mechanical properties of Fe 49Co-2V and Fe 49Co-2 V_0.3Nb alloys were measured at room temperature and high tempernature,respectively.The results show that the saturation magnetization B。and coercivity H。of both alloys decrease compared with room tempera ture,and tensile strength at 500 C of two kinds of alys is improved comparing with room temperature.The strengthening effct of Nb addition on mechanical properties is obvious.It is found that Fe 49Co-2V 0.3Nb alloy still has good mechanical properties after ageing at 500 C for 168 h.The addition Nb is helpful for the stabilty of high tempenature aging.

Key words: FeCo based soft magnet alloy, Nb addition, high temperature mechanical properties, aging treatment

中图分类号:

TK91

王东玲, 王炫东, 张敬霖, 于一鹏, 张建福. Nb添加对FeCo基合金高温性能与时效态性能的影响[J]. 金属热处理, 2020, 45(9): 223-226.

Wang Dongling, Wang Xuandong, Zhang Jinglin, Yu Yipeng, Zhang Jianfu. Effect of Nb addition on high temperature and aged properties of FeCo based alloy[J]. Heat Treatment of Metals, 2020, 45(9): 223-226.

参考文献

[1] 王龙妹.稀土元素在新一代高强韧钢中的作用和应用前景[J].中国稀土学报,2004,22(1):48-54.
Wang Longmei.Application prospects and behavior of RE in new generation high strength steels with superior toughness[J].Journal of the Chinese Society of Rare Earths,2004,22(1):48-54.
[2] 刘琳琳,冯运莉,侯冰.低温取向硅钢热轧态组织及织构的研究[J].热加工工艺,2014,43(12):99-104.
Liu Linlin,Feng Yunli,Hou Bing.Microstructure and texture in hot rolling strip of low temperature oriented silicon steel[J].Hot Working Technology,2014,43(12):99-104.
[3] 刘丽珍,金自力,任慧平,等.稀土对取向硅钢初次再结晶组织及织构的影响[J].稀土,2015,36(6):1-6.
Liu Lizhen,Jin Zili,Ren Huiping,et al.Influence of RE on primarily recrystallized texture and microstructure of grain oriented silicon steel[J].Chinese Rare Earths,2015,36(6):1-6.
[4] 颜建新,凌晨,付兵,等.钒钛对取向硅钢组织、织构和析出物的影响[J].金属热处理,2014,39(6):109-114.
Yan Jianxin,Ling Chen,Fu Bing,et al.Effects of V and Ti on microstructure,texture and precipitation of conventional grain-oriented silicon steel[J].Heat Treatment of Metals,2014,39(6):109-114.
[5] 陈志军,任慧平,金自力,等.稀土Ce对取向硅钢脱碳退火组织及抑制剂的影响[J].金属热处理,2018,43(11):26-30.
Chen Zhijun,Ren Huiping,Jin Zili,et al.Effect of rare earth Ce on microstructure and inhibitor for oriented silicon steel during decarburizing annealing[J].Heat Treatment of Metals,2018,43(11):26-30.
[6] 王海军,付兵,项利,等.普通取向硅钢组织及织构的演变特征[J].材料热处理学报,2016,37(2):90-97.
Wang Haijun,Fu Bing,Xiang Li,et al.Evolution characteristics of microstructure and texture of CGO steel[J].Transactions of Materials and Heat Treatment,2016,37(2):90-97.

[1]	陈东俊, 李广阳, 刘刚. 时效处理对AlSi9Cu3压铸铝合金组织和力学性能的影响[J]. 金属热处理, 2022, 47(4): 53-56.
[2]	胡静, 陶科, 杨庆松, 李刚, 张德汉. 机械抛光后的时效工艺对0Cr25Al5电热合金拉拔性能的影响[J]. 金属热处理, 2022, 47(4): 171-177.
[3]	杨春苗, 王珊, 王淑慧, 李延珍, 刘文文. RRA过程中预时效时间对7A85铝合金组织性能的影响[J]. 金属热处理, 2022, 47(3): 44-47.
[4]	王英虎, 郑淮北, 白青青, 宋令玺, 胡进, 黄博. Mn18Cr18N高氮奥氏体不锈钢的高温力学性能[J]. 金属热处理, 2022, 47(1): 172-177.
[5]	谭皎, 张伯岩, 朱文光, 孙巧艳. 时效温度对Ti-5Al-4Zr-10Mo-3Cr钛合金微观组织及力学性能的影响[J]. 金属热处理, 2022, 47(1): 217-225.
[6]	丁轩, 甘玉荣, 蒋爱娟, 李辉, 杨明球. 时效处理对7A55铝合金微观组织和性能的影响[J]. 金属热处理, 2021, 46(9): 120-123.
[7]	高志喆, 程福超, 冯一帆, 孙健, 王永金. 时效时间对低密度超高锰铸钢组织性能的影响[J]. 金属热处理, 2021, 46(8): 115-120.
[8]	韩茜, 李茂扬, 秦国飞, 李旭东, 董超, 张美丽, 代卫丽. 固溶时效处理对8030铝合金导线组织性能的影响[J]. 金属热处理, 2021, 46(8): 125-132.
[9]	张可人, 许晓静, 张洁. 多级固溶时效对7×××系超高强冷挤压铝合金组织性能的影响[J]. 金属热处理, 2021, 46(7): 165-167.
[10]	刘吉兆, 刘巍, 袁浩登, 吴远志, 叶拓, 刘伟, 邓彬. 固溶时效处理对挤压态6082铝合金力学性能和组织的影响[J]. 金属热处理, 2021, 46(6): 82-87.
[11]	董福元, 张明旭, 侯俊峰. 时效时间对SLM 18Ni300马氏体时效钢组织性能的影响[J]. 金属热处理, 2021, 46(6): 88-91.
[12]	曹艳艳, 黄甜甜, 韦春华, 严伟林. 多向强应变-时效下7075合金组织、拉伸及抗晶间腐蚀性能[J]. 金属热处理, 2021, 46(6): 168-171.
[13]	朱高杰, 邹龙江, 任晓磊, 李春辉, 刘书潭. 6082-T6铝合金的微观组织与拉伸断裂的关系[J]. 金属热处理, 2021, 46(5): 47-54.
[14]	杜星霖, 鞠泉, 马惠萍, 杜金辉. GH3230合金M₂₃C₆型碳化物的析出行为[J]. 金属热处理, 2021, 46(2): 50-54.
[15]	吴玉博, 杨成斌, 侯为学, 荣义, 李春, 录云杰, 李伶俐. 时效处理对优质GH738合金组织及力学性能的影响[J]. 金属热处理, 2021, 46(12): 13-18.

Nb添加对FeCo基合金高温性能与时效态性能的影响

Effect of Nb addition on high temperature and aged properties of FeCo based alloy

PDF

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

本文评价