42CrMo钢连续冷却转变曲线的测定与分析

李凯¹, 胡建文^1,2,3, 石少坤¹

1.河北科技大学材料科学与工程学院,河北石家庄 050018;
2.河北省材料近净成形技术重点实验室,河北石家庄 050018;
3.航空轻质复合材料与加工技术河北省工程实验室,河北石家庄 050018

收稿日期:2020-03-12 出版日期:2020-09-25 发布日期:2020-12-29
通讯作者: 胡建文,教授,博士,E-mail:hujianwen05@163.com
作者简介:李凯(1995—),女,硕士研究生,主要研究方向为金属材料及热处理,E-mail:1305847629@qq.com

Measurement and analysis of continuous cooling transformation curves for 42CrMo steel

Li Kai¹, Hu Jianwen^1,2,3, Shi Shaokun¹

1. School of Materials Science and Engineering,Heibei University of Science and Technology,Shijiazhuang Hebei 050018,China;
2. Hebei Key Laboratory of Material Near-Net Forming Technology,Shijiazhuang Hebei 050018,China;
3. Hebei Engineering Laboratory of Aviation Lightweight Composite Materials and Processing Technology,Shijiazhuang Hebei 050018,China

Received:2020-03-12 Online:2020-09-25 Published:2020-12-29

摘要/Abstract

摘要： 利用JMat-Pro软件模拟了42CrMo钢的连续冷却转变曲线,并采用DIL805L相变淬火膨胀仪实测了钢的各相变点,对不同冷却速度下的组织转变和贝氏体含量进行了分析,并绘制其CCT曲线。结果表明:42CrMo钢Ac₁=743 ℃,Ac₃=792 ℃。冷速小于0.5 ℃/s时,组织为先共析铁素体与珠光体混合组织;冷速0.5~10 ℃/s之间,存在一定量的贝氏体,随冷速加快,贝氏体量先增后降,马氏体含量逐渐增多,使得硬度呈现较大增幅。冷速大于10 ℃/s,组织为基体马氏体+少量贝氏体的混合组织。

关键词: 42CrMo钢, CCT曲线, 冷却速度, 贝氏体, JMat-Pro软件

Abstract: Microstructure transformation and bainite content at different cooling rates were analyzed to obtain the CCT curves of 42CrMo steel by using JMat-Pro software to simulate the continuous cooling transformation curve and by using DIL805L thermal dilatometer to determine the phases transformation temperatures.The results show that Ac₁ and Ac₃ of the 42CrMo steel are 743 ℃ and 792 ℃,respectively.When the cooling rates are less than 0.5 ℃/s,the transformation products are proeutectoid ferrite and pearlite.In the cooling rate range of 0.5-10 ℃/s,a certain amount of bainite appears which increases first and then decreases with the cooling rate increasing,meanwhile the martensite content increases gradualy and resulting to a large increase of hardness.When the cooling rate is over 10 ℃/s,the resulted microstructure is the mixed collective composed of martensite matrix and a small amount of bainite.

Key words: 42CrMo steel, CCT curves, cooling rate, bainite, JMat-Pro software

中图分类号:

TG113.25

李凯, 胡建文, 石少坤. 42CrMo钢连续冷却转变曲线的测定与分析[J]. 金属热处理, 2020, 45(9): 237-239.

Li Kai, Hu Jianwen, Shi Shaokun. Measurement and analysis of continuous cooling transformation curves for 42CrMo steel[J]. Heat Treatment of Metals, 2020, 45(9): 237-239.

参考文献

[1] 张宇,刘仁东,王科强,等.42CrMo钢动态CCT曲线及组织转变[J].金属热处理,2012,37(12):37-39.
Zhang Yu,Liu Rendong,Wang Keqiang,et al.Dynamic continuous cooling transformation curves and microstructure evolution of 42CrMo steel[J].Heat Treatment of Metals,2012,37(12):37-39.
[2] 肖洋,王刚.42CrMo钢退火工艺的优化研究[J].金属世界,2016(3):32-34.
Xiao Yang,Wang Gang.Study on optimization of annealing process of 42CrMo steel[J].Metal World,2016(3):32-34.
[3] 周同,索进平.42CrMo钢连杆失效分析[J].化学工程与装备,2016(4):21-24.
Zhou Tong,Suo Jinping.Failure analysis of 42CrMo steel connecting rod[J].Chemical Engineering and Equipment,2016(4):21-24.
[4] 郝震宇,汪开忠,胡芳忠,等.淬火介质对不同规格42CrMo钢组织及性能的影响[J].安徽冶金,2016(4):15-19.
Hao Zhenyu,Wang Kaizhong,Hu Fangzhong,et al.Effect of quenching medium on microstructure and mechanical properties of 42CrMo steel of different specifications[J].Anhui Metallurgy,2016(4):15-19.
[5] 蔡笑樱.42CrMo4大型锻件显微组织对低温冲击性能的影响[D].济南:山东大学,2018.
Cai Xiaoying.Effect of microstructure of 42CrMo4 heavy forgings on low temperature impact properties[D].Jinan:Shandong University,2018.
[6] 徐佐仁,许国英,郁金星.轴承钢马氏体等温处理的研究[J].上海交通大学学报,1985,19(3):38-50.
Xu Zuoren,Xu Guoying,Yu Jinxing.A study of modified martempering of ball bearing steel[J].Journal of Shanghai Jiao Tong University,1985,19(3):38-50.
[7] 薛贯鲁,刘庆锁,姜训勇.含硅钢上贝氏体组织演变特征研究[J].热加工工艺,2008(24):31-33.
Xue Guanlu,Liu Qingsuo,Jiang Xunyong.Research on microstructure evolution of upper bainite in silicon-containing steel[J].Hot Working Technology,2008(24):31-33.
[8] 文超,董雯,梁会雷,等.42CrMo钢的等温淬火和回火[J].金属热处理,2014,39(12):50-54.
Wen Chao,Dong Wen,Liang Huilei,et al.Isothermal quenching and tempering of 42CrMo steel[J].Heat Treatment of Metals,2014,39(12):50-54.

[1]	陈连生, 张露友, 田亚强, 杨子旋, 李红斌, 潘红波, 魏英立. 低碳高强舰船用钢的CCT曲线及其组织性能[J]. 金属热处理, 2022, 47(4): 63-68.
[2]	王云龙, 余伟, 张昳, 史佳新, 李明辉. 奥氏体化温度对贝氏体钢等温转变及力学性能的影响[J]. 金属热处理, 2022, 47(4): 80-85.
[3]	杨杰, 汪西, 周杰, 武建祥, 屈志远, 代合平, 彭海军. 转向节锻件枝丫结构淬火裂纹形成机理[J]. 金属热处理, 2022, 47(4): 263-267.
[4]	张宁, 高星, 王芝林, 蒋波, 刘雅政. 18CrNiMo7-6钢齿轮组织性能异常分析[J]. 金属热处理, 2022, 47(4): 268-273.
[5]	刘志桥, 冯庆晓, 李化龙, 李腾飞. 退火工艺对低碳贝氏体钢组织与力学性能的影响[J]. 金属热处理, 2022, 47(3): 53-56.
[6]	宁静, 高坤元, 李浩楠, 文胜平, 黄晖, 吴晓蓝, 魏午, 聂祚仁. 成分和冷却速度对Al-xEr合金凝固组织的影响[J]. 金属热处理, 2022, 47(3): 151-154.
[7]	郭亚洲, 宋宁宏, 倪雷, 凌华, 毕文珍, 韦习成. B1800HS热成形钢组织转变的JMatPro计算和试验研究[J]. 金属热处理, 2022, 47(3): 239-244.
[8]	吴辉, 林升垚, 李新凯, 龚玉辉, 魏德强. 感应淬火对42CrMo钢曲轴连杆轴颈组织性能的影响[J]. 金属热处理, 2022, 47(2): 119-124.
[9]	俞波, 张宜, 王占业, 柴立涛. 连续退火工艺对4.5%Cr冷轧耐候钢组织性能的影响[J]. 金属热处理, 2022, 47(2): 137-140.
[10]	董瑞, 陈林, 岑耀东, 包喜荣. 不同热处理条件下贝氏体钢的微观组织和疲劳裂纹扩展[J]. 金属热处理, 2022, 47(2): 153-158.
[11]	马启林, 刘刚, 郑健, 阴树标, 李拔, 刘清友. Nb-V复合微合金化高钢级管线钢的奥氏体连续冷却转变[J]. 金属热处理, 2022, 47(1): 13-18.
[12]	朱赫男, 陈刚, 杨佳伟, 张志建. Ti微合金化对22MnB5热成形钢组织和性能的影响[J]. 金属热处理, 2022, 47(1): 125-129.
[13]	蔡著文, 李玲, 沈俞涛, 吴晓春. 热处理工艺对4Cr3Mo2Si1V钢组织与性能的影响[J]. 金属热处理, 2022, 47(1): 226-232.
[14]	李梦鸽, 程巨强, 尹思博. 不同截面尺寸贝氏体非调质钢的组织和性能[J]. 金属热处理, 2021, 46(8): 65-69.
[15]	李缘, 栾道成, 胡志华, 邓天鑫, 任阳, 左城铭, 王正云. 城际及高铁轨道用辙叉贝氏体钢的组织与性能[J]. 金属热处理, 2021, 46(8): 70-72.

42CrMo钢连续冷却转变曲线的测定与分析

Measurement and analysis of continuous cooling transformation curves for 42CrMo steel

PDF

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

本文评价