退火工艺对冷轧低碳热镀锌钢板组织均匀性的影响

doi:10.13251/j.issn.0254-6051.2020.12.007

摘要/Abstract

摘要： 通过模拟退火试验及工业试制,研究了退火工艺对冷轧低碳热镀锌钢板组织均匀性的影响,探讨了钢板出现混晶组织的原因,并制定了解决方案。结果表明:加热速率偏低是造成混晶组织的主要原因,随着加热速率的升高,组织细化且均匀性改善;在较低加热速率下,延长均热时间和提高退火温度在一定程度上加剧了组织的不均匀性。针对镀锌机组降速生产引起混晶的问题,结合模拟退火试验结果,降低退火温度可以改善降速导致的混晶问题,制定了降速生产的退火工艺并应用于实际生产。

关键词: 退火工艺, 热镀锌钢板, 混晶, 加热速率

Abstract: Effect of annealing process on the microstructure uniformity of cold-rolled low-carbon steel plate for hot dip galvanizing was studied by simulated annealing experiment and industrial trial production. The causes of mixed grain microstructure in the steel were analyzed and the solution was developed. The results show that lower heating rate is the main reason for the mixed grain microstructure. With the increase of heating rate, the microstructure becomes finer and more uniform. At lower heating rate, both extending the soaking time and raise the annealing temperature aggravate the inhomogeneity of microstructure. Aiming at the problem of the mixed grain resulted from the rate decline during the galvanizing unit production and combined with the simulated annealing test results, it is found that lowering the annealing temperature can improve such mixed grain problem, and based on which the annealing process for the rate reducing production is formulated and applied to the actual production.

Key words: annealing process, hot dip galvanizing plate, mixed grain, heating rate

中图分类号:

TG156.2

徐晓涵, 宋乙峰, 刘志桥, 岳重祥. 退火工艺对冷轧低碳热镀锌钢板组织均匀性的影响[J]. 金属热处理, 2020, 45(12): 35-40.

Xu Xiaohan, Song Yifeng, Liu Zhiqiao, Yue Chongxiang. Effect of annealing process on microstructure uniformity of cold-rolled low-carbon steel plate for hot dip galvanizing[J]. Heat Treatment of Metals, 2020, 45(12): 35-40.

参考文献

[1] 胡华东, 李洪翠, 高广洲, 等. 高端家电用热镀锌耐指纹钢板产品开发[J]. 钢铁钒钛, 2019, 40(2): 161-165.
Hu Huadong, Li Hongcui, Gao Guangzhou, et al.Development offingerprint resistant hot dip galvanized steel sheet for high-end household appliance[J]. Iron Steel Vanadium Titanium, 2019, 40(2): 161-165.
[2] 李研, 李铁军, 滕华湘, 等. 热镀锌汽车板波纹度的控制技术[J]. 金属热处理, 2019, 44(4): 207-210.
Li Yan, Li Tiejun, Teng Huaxiang, et al.Control technology of waviness on galvanized auto sheet[J]. Heat Treatment of Metals, 2019, 44(4): 207-210.
[3] 黄浩, 徐光, 戴方钦, 等. 退火工艺对热镀锌用冷轧低碳高强钢组织和性能的影响[J]. 金属热处理, 2019, 44(6): 117-121.
Huang Hao, Xu Guang, Dai Fangqin, et al.Effect of annealing process on microstructure and properties of cold-rolled high-strength low carbon steel for hot-dip galvanizing[J]. Heat Treatment of Metals, 2019, 44(6): 117-121.
[4] 刘靖宝, 张洪波, 杜明山, 等. 退火温度对镀锌780 MPa级双相钢组织性能的影响[J]. 轧钢, 2018, 35(3): 41-44.
Liu Jingbao, Zhang Hongbo, Du Mingshan, et al.Influence of different annealing temperature on microstructure and properties of 780 MPa cold rolled hot-dip galvanized dual-phase steel[J]. Steel Rolling, 2018, 35(3): 41-44.
[5] 王滕, 赵云龙, 柴立涛. 退火工艺对极薄规格热镀锌钢板的影响[J]. 中国冶金, 2018, 28(1): 22-26.
Wang Teng, Zhao Yunlong, Chai Litao.Effect of annealing process on thin specification hot dipped galvanized sheet[J]. China Metallurgy, 2018, 28(1): 22-26.
[6] 胡宽辉, 田德新, 冯冠文, 等. 热镀锌连续退火工艺对高强IF钢组织和性能的影响[J]. 材料工程, 2012(7): 50-54.
Hu Kuanhui, Tian Dexin, Feng Guanwen, et al.Influence ofcontinuous annealing on microstructure and properties high-strength IF steel[J]. Journal of Materials Engineering, 2012(7): 50-54.
[7] 王力达, 王淑华, 梅淑文. 高强度热镀锌板S550GD+Z的研制与开发[J]. 河北冶金, 2015(12): 11-13.
Wang Lida, Wang Shuhua, Mei Shuwen.Development of high-strength hot galvanizing plate S550GD+Z[J]. Hebei Metallurgy, 2015(12): 11-13.
[8] 陈斌锴, 仲海峰, 张启富. IF440高强钢退火过程中形成的氧化物及其对镀锌板表面质量的影响[J]. 金属热处理, 2013, 38(9): 78-82.
Chen Binkai, Zhong Haifeng, Zhang Qifu.Annealing formed oxides of IF440 high strength steel and its effect on surface quality of galvanized sheet[J]. Heat Treatment of Metals, 2013, 38(9): 78-82.
[9] 杨伟, 李婷婷, 李腾飞, 等. 热镀锌表面亮点缺陷分析及控制[J]. 金属热处理, 2016, 41(7): 168-172.
Yang Wei, Li Tingting, Li Tengfei, et al.Analysis and control for bright spot defect on surface of hot dip galvanized sheet[J]. Heat Treatment of Metals, 2016, 41(7): 168-172.
[10] 吴剑胜, 林红春. 镀锌板冲压开裂缺陷分析[J]. 轧钢, 2016, 33(2): 70-72.
Wu Jiansheng, Lin Hongchun.Analysis of stamping crack of hot galvanized sheet[J]. Steel Rolling, 2016, 33(2): 70-72.
[11] 李萧, 杨平, 林瑞民, 等. 低碳钢退火板中粗大晶粒成因的EBSD分析[J]. 电子显微学报, 2009, 28(1): 34-38.
Li Xiao, Yang Ping, Lin Ruimin, et al.Formation of the coarse grains in annealed low carbon steel sheets by EBSD analysis[J]. Journal of Chinese Electron Microscopy Society, 2009, 28(1): 34-38.
[12] 李萧, 杨平, 林瑞民, 等. 低碳冲压钢板桔皮缺陷的成因[J]. 北京科技大学学报, 2010, 32(5): 589-594.
Li Xiao, Yang Ping, Lin Ruimin, et al.Formation mechanism of orange peel defects in low carbon deep drawing steel sheets[J]. Journal of Beijing University of Science and Technology, 2010, 32(5): 589-594.
[13] 徐海卫, 于洋, 王畅, 等. LCAK钢表层粗晶缺陷的产生原因及机理研究[J]. 轧钢, 2014, 31(1): 19-23.
Xu Haiwei, Yu Yang, Wang Chang, et al.Study on the mechanism of surface local coarse grain of LCAK steel[J]. Steel Rolling, 2014, 31(1): 19-23.
[14] 邓峤, 候自勇, 燕际军, 等. 加热速率对Nb-IF钢退火组织及织构特征的影响[J]. 材料与冶金学报, 2012, 11(1): 38-42.
Deng Qiao, Hou Ziyong, Yan Jijun, et al.Influence of heating rate on the microstructure and texture of Nb-IF steel sheet[J]. Journal of Materials and Metallurgy, 2012, 11(1): 38-42.
[15] 李腾飞, 李婷婷, 汤茜, 等. 低碳钢退火板中粗大晶粒成因探讨[J]. 材料热处理学报, 2014, 35(S1): 170-174.
Li Tengfei, Li Tingting, Tang Qian, et al.Formation of the coarse grains in annealed low carbon steel[J]. Transactions of Materials and Heat Treatment, 2014, 35(S1): 170-174.