热氢处理对TA15钛合金组织及性能的影响

郝国建¹, 杨刚^1,2, 梁培新¹, 朱卫东¹, 孙剑飞³, 陈哲铭³

1.北京机电研究所有限公司,北京 100083;
2.北京科技大学新金属材料国家重点实验室,北京 100083;
3.北京航天航空大学机械工程及自动化学院,北京 100083

收稿日期:2020-06-20 出版日期:2021-01-25 发布日期:2021-01-26
作者简介:郝国建(1978—),男,工程师,博士,主要研究方向为新型金属结构材料与先进成形技术,E-mail:619083514@qq.com
基金资助:
“高档数控机床与基础制造装备”国家科技重大专项(2019ZX04017001)

Effect of thermal hydrogen treatment on microstructure and properties of TA15 titanium alloy

Hao Guojian¹, Yang Gang^1,2, Liang Peixin¹, Zhu Weidong¹, Sun Jianfei³, Chen Zheming³

1. Beijing Research Institute of Mechanical & Electrical Technology Ltd.,Beijing 100083,China;
2. State Key Laboratory for Advanced Metals and Materials,University of Science and Technology Beijing,Beijing 100083,China;
3. School of Mechanical Engineering and Automation,Beihang University,Beijing 100083,China

Received:2020-06-20 Online:2021-01-25 Published:2021-01-26

摘要/Abstract

摘要： 采用真空气相热氢处理炉得到不同氢含量的TA15钛合金试样,利用扫描电镜、夏比冲击设备以及带传感器的机床等对不同氢含量的钛合金试样进行切削力获取及组织形貌观察,研究热氢处理过程中不同氢含量TA15钛合金试样的组织结构演变和力学性能规律。结果表明,TA15钛合金试样热氢处理后会出现不同程度的组织细化;热氢处理后的TA15钛合金试样的主切削力会随着氢含量的增加而增加,在氢含量为0.51%时,主切削力随着切削速度增加而减少,其他氢含量的TA15钛合金试样的主切削力随切削速度增加而先增加后减小;热氢处理后的TA15钛合金试样冲击吸收能量会随着氢含量的增加而降低。

关键词: TA15 合金, 热氢处理, 组织演变, 力学性能, 切削加工性

Abstract: TA15 titanium alloy specimen with different hydrogen contents was obtained by using a vacuum gas-phase thermal hydrogen treatment furnace,and the cutting force and microstructure of the specimen was tested and observed by means of a machine tool with sensors,and scanning electron microscope,Charpy impact tester,respectively.At the same time,the structural evolution and mechanical properties laws of TA15 titanium alloy specimen with different hydrogen content during thermal hydrogen treatment were studied.The results show that the TA15 titanium alloy specimen have different degrees of microstructure refinement after thermal hydrogen treatment;the main cutting force of the TA15 titanium alloy specimen after thermal hydrogen treatment increases with the increase of hydrogen content,and when the hydrogen content is 0.51%,the main cutting force decreases with the increase of cutting speed.The main cutting force of TA15 titanium alloy specimen with other hydrogen content first increases and then decreases with the increase of cutting speed;the impact absorbed energy of TA15 titanium alloy specimen after thermal hydrogen treatment decreases as the hydrogen content increases.

Key words: TA15 alloy, thermal hydrogen treatment, microstructure evolution, mechanical properties, machinability

中图分类号:

TG146.2

郝国建, 杨刚, 梁培新, 朱卫东, 孙剑飞, 陈哲铭. 热氢处理对TA15钛合金组织及性能的影响[J]. 金属热处理, 2021, 46(1): 38-42.

Hao Guojian, Yang Gang, Liang Peixin, Zhu Weidong, Sun Jianfei, Chen Zheming. Effect of thermal hydrogen treatment on microstructure and properties of TA15 titanium alloy[J]. Heat Treatment of Metals, 2021, 46(1): 38-42.

参考文献

[1] 刘全明,张朝晖,刘世锋,等.钛合金在航空航天及武器装备领域的应用与发展[J].钢铁研究学报,2015,27(3):1-4.
Liu Quanming,Zhang Zhaohui,Liu Shifeng,et al.Application and development of titanium alloy in aerospace and military hard ware[J].Journal of Iron and Steel Research,2015,27(3):1-4.
[2] 于超,王焱,鲍永杰,等.渗氢温度为650 ℃时氢含量对钛合金切削加工性影响的试验研究[J].工具技术,2010,44(1):26-28.
Yu Chao,Wang Yan,Bao Yongjie,et al.Experimental research on effect of hydrogen content on machinability of titanium alloy when the temperature of permeating hydrogen is at 650 ℃[J].Tool Engineering,2010,44(1):26-28.
[3] 李毅.基于切屑形态的钛合金切削性能研究[J].光电技术应用,2020,35(1):70-74.
Li Yi.Research on cutting performance of titanium alloy based on chip morphology[J].Electro-Optic Technology Application,2020,35(1):70-74.
[4] 王蕊宁,孙润军,查刚强.热处理参数对TA15钛合金静态球化显微组织及动力学的影响[J].金属热处理,2018,43(6):79-83.
Wang Ruining,Sun Runjun,Zha Gangqiang.Effect of heat treatment parameters on static globularization microstructure and kinetics of TA15 titanium alloy[J].Heat Treatment of Metals,2018,43(6):79-83.
[5] 裴烈勇,戴爱丽,刘勇德,等.渗氧温度和时间对TA15合金α处理层深度及硬度的影响[J].金属热处理,2019,44(12):154-156.
Pei Lieyong,Dai Aili,Liu Yongde,et al.Effect of oxygen permeation temperature and time on depth and hardness ofα-layer of TA15 alloy[J].Heat Treatment of Metals,2019,44(12):154-156.
[6] 杨光,王文东,钦兰云,等.α+β区退火对激光沉积TA15钛合金组织及硬度的影响[J].金属热处理,2017,42(12):39-43.
Yang Guang,Wang Wendong,Qin Lanyun,et al.Effect of α+β phase zone annealing on microstructure and microhardness of laser deposition manufactured TA15 titanium alloy[J].Heat Treatment of Metals,2017,42(12):39-43.
[7] 侯红亮,李志强,王亚军,等.钛合金热氢处理技术及其应用前景[J].中国有色金属学报,2003,13(3):533-549.
Hou Hongliang,Li Zhiqiang,Wang Yajun,et al.Technology of hydrogen treatment for titanium alloy and its application prospect[J].The Chinese Journal of Nonferrous Metals,2003,13(3):533-549.
[8] 姜波,侯红亮,王耀奇,等.钛合金置氢过程的氢分布规律[J].中国有色金属学报,2010,20(S1):369-376.
Jiang Bo,Hou Hongliang,Wang Yaoqi,et al.Hydrogen distribution of hydrogen treatment process for titanium alloy[J].The Chinese Journal of Nonferrous Metals,2010,20(S1):369-376.
[9] 梁培新,朱卫东,杨刚,等.渗氢工艺对TA15钛合金氢含量和显微组织的影响[J].锻压技术,2020,45(8):190-194.
Liang Peixin,Zhu Weidong,Yang Gang,et al.Influence of hydrogen permeation process on hydrogen content andmicrostructure of TA15 titanium alloy[J].Foring and Stamping Technology,2020,45(8):190-194.
[10] 王耀奇,李红,侯红亮.Ti-6Al-4V合金置氢动力学与氢分布规律[J].北京科技大学学报,2010,32(5):634-637.
Wang Yaoqi,Li Hong,Hou Hongliang.Hydrogen absorption kinetics and hydrogen distribution of Ti-6Al-4V alloy[J].Journal of University of Science and Technology Beijing,2010,32(5):634-637.
[11] 危卫华.热氢处理改善钛合金切削加工性的基础研究[D].南京:南京航空航天大学,2010.
Wei Weihua.Basic research on improving the machinability of titanium alloy by thermal hydrogen treatment[D].Nanjing:Nanjing University of Aeronautics and Astronautics,2010.

[1]	梁恩溥, 徐乐, 杨勇, 王毛球. 添加Al、Cu对40CrNi3MoV钢组织和力学性能的影响[J]. 金属热处理, 2022, 47(4): 17-23.
[2]	祁晓亮, 李岩, 定巍, 赵增武. 含Al中锰TRIP钢原始组织对临界退火后组织与力学性能的影响[J]. 金属热处理, 2022, 47(4): 24-29.
[3]	陈保安, 张静媛, 祝志祥, 韩钰, 潘学东, 张磊, 陈素红. 化学成分对高强Al-Mg-Si合金组织和性能的影响[J]. 金属热处理, 2022, 47(4): 30-38.
[4]	陈连生, 张露友, 田亚强, 杨子旋, 李红斌, 潘红波, 魏英立. 低碳高强舰船用钢的CCT曲线及其组织性能[J]. 金属热处理, 2022, 47(4): 63-68.
[5]	贾昌远, 霍元明, 何涛, 霍存龙, 刘克然. 40CrNiMo钢高温拉伸变形行为和组织演变规律[J]. 金属热处理, 2022, 47(4): 69-74.
[6]	王云龙, 余伟, 张昳, 史佳新, 李明辉. 奥氏体化温度对贝氏体钢等温转变及力学性能的影响[J]. 金属热处理, 2022, 47(4): 80-85.
[7]	刘丽艳, 毕文珍, 韦习成. Mn元素对热冲压钢镀锌层组织演变的影响[J]. 金属热处理, 2022, 47(4): 93-99.
[8]	骆再斌, 范子泽, 彭振. 轻质高熵合金的研究进展[J]. 金属热处理, 2022, 47(4): 100-107.
[9]	吕杰晟, 宋志刚, 何建国, 丰涵, 郑文杰, 朱玉亮. S32205双相不锈钢冷轧退火组织转变及强塑化机理分析[J]. 金属热处理, 2022, 47(4): 141-145.
[10]	王琪, 吴光亮. 回火温度对1100 MPa级高强钢组织与性能的影响[J]. 金属热处理, 2022, 47(4): 146-150.
[11]	张骥俊, 邢彦锋, 曹菊勇. 超声振动对CMT电弧增材制造铝合金组织与性能的影响[J]. 金属热处理, 2022, 47(4): 159-164.
[12]	刘文彬, 乔龙阳, 潘新宇, 程格, 李爱娜, 裴新军. 淬火温度对刀剪用M390粉末冶金不锈钢组织和性能的影响[J]. 金属热处理, 2022, 47(4): 189-195.
[13]	王瑞琴, 葛鹏, 廖强, 侯鹏, 刘宇. 固溶冷却方式对短时用高温钛合金板材组织和性能的影响[J]. 金属热处理, 2022, 47(4): 196-198.
[14]	王绍灼, 孟晗, 王芬, 樊海卫, 李燕, 唐超. 改善低氧TC4-LC及重熔TC4钛合金性能的热处理工艺[J]. 金属热处理, 2022, 47(4): 204-207.
[15]	陈强, 陈林芳, 杨明华. 18CrNiMo7-6钢的可控气氛高温渗碳工艺[J]. 金属热处理, 2022, 47(4): 231-239.

热氢处理对TA15钛合金组织及性能的影响

Effect of thermal hydrogen treatment on microstructure and properties of TA15 titanium alloy

PDF

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

本文评价