汽车用800 MPa级冷轧低合金高强钢的研制

doi:10.13251/j.issn.0254-6051.2021.01.023

摘要/Abstract

摘要： 采用C-Si-Mn-Nb-Ti-Cr-Mo合金成分体系,全流程控制关键生产工艺参数,研发出具有良好塑性和成形性的800 MPa级冷轧低合金高强钢。结果表明,试验钢的显微组织由铁素体、马氏体和少量贝氏体组成,铁素体基体中有弥散分布的第二相粒子和碳化物沉淀相。试验钢的屈服强度在800 MPa以上,断后伸长率大于10.5%,抗拉强度和屈服强度相差小于35 MPa,扩孔率在56.5%以上,180°冷弯角度下弯曲无可见裂纹,表现出良好的成形性能。

关键词: 低合金高强钢, 连续退火, 组织性能, 析出物, 成形性

Abstract: Cold-rolled 800 MPa low alloy high strength steel with good ductility and formability was developed by means of C-Si-Mn-Nb-Ti-Cr-Mo chemical composition design and key production process parameters control.The results show that the microstructure of the tested steel is composed of ferrite,martensite and a small amount of bainite.The second phase particles and carbide precipitation phases are dispersed in the ferrite matrix.The yield strength of the tested steel is more than 800 MPa,the elongation is more than 10.5%,the difference between tensile strength and yield strength is less than 35 MPa,the hole expansion rate is more than 56.5%,and there is no visible crack on the 180° cold bending test,which showing good formability.

Key words: high strength low alloy(HSLA), continuous annealing, microstructure and properties, precipitates, formability

中图分类号:

TG142.1

王科强, 刘仁东, 郭金宇, 付薇, 黄秋菊, 孙荣生. 汽车用800 MPa级冷轧低合金高强钢的研制[J]. 金属热处理, 2021, 46(1): 120-124.

Wang Keqiang, Liu Rendong, Guo Jinyu, Fu Wei, Huang Qiuju, Sun Rongsheng. Development of cold-rolled 800 MPa grade high strength low alloy steel for automobile[J]. Heat Treatment of Metals, 2021, 46(1): 120-124.

参考文献

[1] 毛新平,高吉祥,李烈军,等.屈服强度550 MPa级高强度高成形性钢板的开发研究[J].汽车工艺与材料,2006(11):1-5.
Mao Xinping,Gao Jixiang,Li Liejun,et al.Development and research of 550 MPa high strength and high formability plate[J].Automobile Technology and Material,2006(11):1-5.
[2] Fernández,Illescas S,Guilemany J M.Effect of microalloying elements on the austenitic grain growth in a low carbon HSLA steel[J].Material Letters,2007,61(11/12):2389-2392.
[3] 米振莉,潘殿军,江海涛.700 MPa冷轧低合金超高强钢的典型连续退火工艺[J].工程科学学报,2015,37(2):185-189.
Mi Zhenli,Pan Dianjun,Jiang Haitao.Typical continuous annealing technology of cold-rolled 700 MPa ultra-high strength low-alloy steel[J].Chinese Journal of Engineering,2015,37(2):185-189.
[4] 王科强,刘仁东,王旭,等.汽车结构用590 MPa级高屈服强度钢的研制[J].金属热处理,2015,40(1):156-160.
Wang Keqiang,Liu Rendong,Wang Xu,et al.Development of 590 MPa grade high yield strength steel for automobile structure[J].Heat Treatment of Metals,2015,40(1):156-160.
[5] 马鸣图.先进汽车用钢[M].北京:化学工业出版社,2007.
[6] 董瀚,马党参,郎宇平,等.钼在合金钢中的特性与应用[J].世界有色金属,2010(11):66-69.
[7] 王涛亮,路妍,任凤章,等.低合金超高强度钢研究进展[J].金属热处理,2015,40(2):13-20.
Wang Taoliang,Lu Yan,Ren Fengzhang,et al.Research progress of ultra-high strength low alloy steels[J].Heat Treatment of Metals,2015,40(2):13-20.
[8] 李树索,陈希杰.超高锰钢加工硬化及耐磨性的研究[J].钢铁研究学报,1997,9(4):38-41.
Li Shusuo,Chen Xijie.Work hardening and wearability of superhigh manganese steel[J].Journal of Iron and Steel Research,1997,9(4):38-41.
[9] 黄浩,徐光,胡海江.冷却模式对Ti-Nb微合金高强钢组织和性能的影响[J].金属热处理,2018,43(3):114-119.
Huang Hao,Xu Guang,Hu Haijiang.Effect of cooling mode on microstructure and properties of high-strength Ti-Nb microalloyed steel[J].Heat Treatment of Metals,2018,43(3):114-119.
[10] 周晓光,曾才有,徐少华,等.控制冷却对含Nb钢组织性能的影响研究[J].机械工程学报,2014,50(22):57-62.
Zhou Xiaoguang,Zeng Caiyou,Xu Shaohua,et al.Research of the effect of controlling cooling on microstructure and mechanical properties for Nb bearing steel[J].Journal of Mechanical Engineering,2014,50(22):57-62.
[11] 施雄樑,张建平,刘永刚,等.连续退火工艺对低硅型冷轧低合金高强钢板力学性能的影响[J].北京科技大学学报,2008,30(8):870-874.
Shi Xiongliang,Zhang Jianping,Liu Yonggang,et al.Effect of continuous annealing process on the mechanical properties of cold-rolled low silicon HSLA steel sheets[J].Journal of University of Science and Technology Beijing,2008,30(8):870-874.
[12] 张继明,喻春明.时效对含Nb低合金高强钢显微组织和力学性能的影响[J].材料热处理学报,2019,40(6):123-129.
Zhang Jiming,Yu Chunming.Effect of aging on microstructure and mechanical properties of low alloy high strength steel containing Nb[J].Transactions of Materials and Heat Treatment,2019,40(6):123-129.
[13] 周文强,潘利波,王立辉,等.低合金高强钢平整延伸率的控制与屈服平台的消除[J].武钢技术,2016,54(5):49-53.
Zhou Wenqiang,Pan Libo,Wang Lihui,et al.Research on the reduction rate and yield platform elimination during temper rolling of HSLA[J].Wuhan Iron and Steel Corporation Technology,2016,54(5):49-53.
[14] 马鸣图,吴宝榕.双相钢-物理和力学冶金[M].北京:冶金工业出版社,2009.
[15] 齐俊杰,黄运华,张跃.微合金化钢[M].北京:冶金工业出版社,2006.
[16] Sun J L,Kang Y L,Wei X Y,et al.Analysis on the process and mechanical of 800 MPa grade low-alloyed plate[R].Workshop on New Generation Steel.Beijing:Chinese Society for Metals,2001.