AZ33M镁合金激光熔覆Al-Si涂层的组织与性能

doi:10.13251/j.issn.0254-6051.2021.05.035

摘要/Abstract

摘要： 利用激光熔覆技术在AZ33M镁合金表面制备了Al-Si涂层,通过采用腐蚀电化学测试结合X射线衍射仪(XRD)、扫描电镜(SEM)及显微硬度计等对熔覆层微观组织和性能进行了表征。结果表明,熔覆层主要由Mg和Mg₁₇Al₁₂、Mg₂Si及Mg₂Al₃相组成。熔覆层显微组织由柱状树枝晶和方向各异的树枝晶组成。由于第二相强化和细晶强化等原因,制备的Al-Si涂层相比镁合金基体具有更高的硬度。熔覆层的自腐蚀电位相比基体提高了约400 mV,自腐蚀电流降低了一个数量级,熔覆层的耐蚀性明显优于基体镁合金。

关键词: 激光熔覆, 镁合金, Al-Si共晶合金, 耐蚀性, 硬度

Abstract: Al-Si coating was prepared on the surface of AZ33M magnesium alloy by laser cladding technology. The microstructure and properties of the clad layer were characterized through corrosion electrochemical method test combined with X-ray diffractometer (XRD), scanning electron microscope (SEM), microhardness tester, etc.. The results show that the clad layer is mainly composed of Mg matrix, Mg₁₇Al₁₂, Mg₂Si, and Mg₂Al₃ phases. The microstructure is composed of columnar dendrites and dendrites with different directions. Due to second phase strengthening and fine-grain strengthening, the prepared Al-Si coating has higher hardness compared with magnesium alloy matrix. Compared with the matrix, the self-corrosion potential of the clad layer is increased by 400 mV, the self-corrosion current is reduced by an order of magnitude, and the corrosion resistance of the clad layer is significantly better than that of the magnesium alloy matrix.

Key words: laser cladding, magnesium alloy, Al-Si eutectic alloy, corrosion resistance, hardness

中图分类号:

TG146

王鑫, 潘希德, 牛强, 何向前. AZ33M镁合金激光熔覆Al-Si涂层的组织与性能[J]. 金属热处理, 2021, 46(5): 202-206.

Wang Xin, Pan Xide, Niu Qiang, He Xiangqian. Microstructure and properties of laser clad Al-Si coating on AZ33M magnesium alloy[J]. Heat Treatment of Metals, 2021, 46(5): 202-206.

参考文献

[1]Zhang Xiaolin, Zhang Kemin, Zou Jianxin. Microstructures and properties in surface layers of Mg-6Zn-1Ca magnesium alloy laser-clad with Al-Si powders[J]. Transactions of Nonferrous Metals Society of China, 2018, 28(1): 96-102.
[2]Cao Fuyong, Song Guangling, Atrens Andrej. Corrosion and passivation of magnesium alloys[J]. Corrosion Science, 2016, 111: 835-845.
[3]Pan Fusheng, Yang Mingbo, Chen Xianhua. A review on casting magnesium alloys: Modification of commercial alloys and development of new alloys[J]. Journal of Materials Science and Technology, 2016, 32(12): 1211-1221.
[4]Zhang Jinghuai, Liu Shujuan, Wu Ruizhi, et al. Recent developments in high-strength Mg-RE-based alloys: Focusing on Mg-Gd and Mg-Y systems[J]. Journal of Magnesium and Alloys, 2018, 6(3): 277-291.
[5]Esmaily M, Svensson J E, Fajardo S, et al. Fundamentals and advances in magnesium alloy corrosion[J]. Progress in Materials Science, 2017, 89: 92-193.
[6]吴刚刚, 汪选国, 曾鲜, 等. TC4表面激光熔覆AlCoCrFeNiTi_0.5高熵合金层的组织与性能[J]. 金属热处理, 2019, 44(12): 1-5.
Wu Ganggang, Wang Xuanguo, Zeng Xian, et al. Microstructure and properties of laser clad AlCoCrFeNiTi_{0. 5} high-entropy alloy coating on TC4 surface[J]. Heat Treatment of Metals, 2019, 44(12): 1-5.
[7]林熙, 孙荣禄, 牛伟. 扫描速度对激光熔覆TC4-Ni包B₄C复合涂层组织与性能的影响[J]. 金属热处理, 2018, 43(7): 197-203.
Lin Xi, Sun Ronglu, Niu Wei. Effect of scanning speed on microstructure and properties of TC4-Ni package B₄C composite coating prepared by laser cladding[J]. Heat Treatment of Metals, 2018, 43(7): 197-203.
[8]范佳承, 刘宁, 周慧玲, 等. 激光熔覆Al_0.1CoCrFeNi高熵合金涂层的组织和性能[J]. 金属热处理, 2020, 45(12): 155-159.
Fan Jiacheng, Liu Ning, Zhou Huiling, et al. Microstructure and properties of Al_0.1CoCrFeNi high entropy alloy coating fabricated by laser cladding[J]. Heat Treatment of Metals, 2020, 45(12): 155-159.
[9]Liu Hongxi, Xu Qian, Wang Chuanqi, et al. Corrosion and wear behavior of Ni60CuMoW coatings fabricated by combination of laser cladding and mechanical vibration processing[J]. Journal of Alloys and Compounds, 2015, 621: 357-363.
[10]Weng Fei, Yu Huijun, Chen Chuanzhong, et al. Microstructures and wear properties of laser cladding Co-based composite coatings on Ti-6Al-4V[J]. Materials and Design, 2015, 80: 174-181.
[11]Majumdar J Dutta, Galun R, Mordike B L, et al. Effect of laser surface melting on corrosion and wear resistance of a commercial magnesium alloy[J]. Materials Science and Engineering A, 2003, 361(1/2): 119-129.
[12]Rolink G, Weisheit A, Biermann T, et al. Investigations of laser clad, thermal sprayed and laser remelted AlSi20-coatings on magnesium alloy AZ31B under constant and cycling thermal load[J]. Surface and Coatings Technology, 2014, 259: 751-758.
[13]Sahasrabudhe Himanshu, Soderlind Julie, Bandyopadhyay Amit. Laser processing of in situ TiN/Ti composite coating on titanium[J]. Journal of the Mechanical Behavior of Biomedical Materials, 2016, 53: 239-249.
[14]靳坤, 张英乔, 张涛, 等. AZ91D镁合金表面激光熔覆Al-Ti-Ni/C涂层的电化学腐蚀行为[J]. 电焊机, 2019, 49(10): 83-87.
Jin Kun, Zhang Yinqiao, Zhang Tao, et al. Electrochemical corrosion behavior of laser cladding Al-Ti-Ni/C coating on AZ91D magnesium alloy[J]. Electric Welding Machine, 2019, 49(10): 83-87.
[15]刘德坤, 张可敏, 刘应瑞. AZ31镁合金表面Al-Ti-TiB₂激光熔覆层的组织和性能[J]. 机械工程材料, 2018, 42(10): 24-28.
Liu Dekun, Zhang Kemin, Liu Yingrui. Microstructure and properties of Al-Ti-TiB₂ laser cladding layer on surface of AZ31magnesium alloy[J]. Materials for Machine Engineering, 2018, 42(10): 24-28.
[16]朱刚贤, 张安峰, 李涤尘. 激光熔覆工艺参数对熔覆层表面平整度的影响[J]. 中国激光, 2010, 37(1): 296-301.
Zhu Gangxian, Zhang Anfeng, Li Dichen. Effect of process parameters on surface smoothness in laser cladding[J]. Chinese Journal of Lasers, 2010, 37(1): 296-301.
[17]高义民. 金属凝固原理[M]. 西安: 西安交通大学出版社, 2010: 79.
Gao Yimin. Principles of Metal Solidification[M]. Xi'an: Xi'an Jiaotong University Press, 2010: 79.
[18]Lunder O, Lein J E, Aune T K R, et al. The role of Mg₁₇Al₁₂ phase in the corrosion of Mg alloy AZ91[J]. Corrosion, 1989, 45(9): 741-748.
[19]高亚丽. 镁合金激光表面处理研究[M]. 北京: 科学出版社, 2019: 52.
Gao Yali. Research on Laser Surface Treatment of Magnesium Alloy[M]. Beijing: Science Press, 2019: 52.